RARE EARTH METAL INCORPORATED ZEOLITE MODIFIED ELECTRODES FOR DETECTION AND QUANTIFICATION OF HEAVY METAL IONS IN AQUEOUS SOLUTION
20170315079 · 2017-11-02
Assignee
Inventors
- Ismail ABDULAZEEZ (Dhahran, SA)
- Abdel-Naser M. KAWDE (Dhahran, SA)
- Oki Muraza (Dhahran, SA)
- Abdul-Rahman AL-BETAR (Dhahran, SA)
Cpc classification
G01N27/3277
PHYSICS
G01N27/48
PHYSICS
International classification
Abstract
Electrodes comprising conducting graphite, paraffin oil pasting liquid, and a rare earth metal impregnated zeolite, such as lanthanum or cerium impregnated mordenite electrodes. Methods and voltammetric applications, such as square wave anodic stripping voltammetry, of these rare earth metal impregnated zeolite modified electrodes for the detection and quantification of heavy metal ions such as Pb(II) and Cd(II) in aqueous solutions.
Claims
1: An electrode, comprising: graphite powder; paraffin oil; and a zeolite impregnated with a rare earth metal.
2: The electrode of claim 1, wherein the zeolite is a mordenite zeolite which has a silica to alumina ratio in the range of 5 to 40.
3: The electrode of claim 1, wherein the rare earth metal is at least one selected from the group consisting of lanthanum and cerium.
4: The electrode of claim 1, wherein the zeolite impregnated with the rare earth metal has a weight percentage of the rare earth metal in the range of 1-15% relative to the total weight of the zeolite impregnated with the rare earth metal.
5: The electrode of claim 1, which has a weight percentage of the graphite powder in the range of 45-75% relative to the total weight of the electrode.
6: The electrode of claim 1, which has a weight percentage of the zeolite impregnated with the rare earth metal in the range of 1-30% relative to the total weight of the electrode.
7: The electrode of claim 1, which has a weight percentage of the paraffin oil in the range of 20-40% relative to the total weight of the electrode.
8: The electrode of claim 1, which has a 10-40% greater electroactive surface area relative to a substantially similar electrode lacking the zeolite impregnated with the rare earth metal.
9: A method for detecting and quantifying a heavy metal ion in an aqueous solution, comprising: contacting the aqueous solution with the electrode of claim 1; generating a negative deposition potential at the electrode to reduce the heavy metal ion and form a reduced heavy metal that is deposited onto the electrode; scanning a potential range from the negative deposition potential in the positive direction at the electrode to oxidize and strip the reduced heavy metal from the electrode; and measuring the current during the scanning.
10: The method of claim 9, wherein the heavy metal ion is at least one selected from the group consisting of Pb(II) and Cd(II).
11: The method of claim 9, wherein the scanning and the measuring are performed with square wave voltammetry.
12: The method of claim 9, wherein the negative deposition potential is in the range of −2.0 V to −0.2 V.
13: The method of claim 9, wherein the scanning is performed at a scan rate of 2-500 mV s.sup.−1.
14: The method of claim 9, wherein the reduced heavy metal is deposited over a time period in the range of 10-250 seconds.
15: The method of claim 9, wherein the aqueous solution has a pH in the range of 3-5.
16: The method of claim 9, wherein the rare earth metal is lanthanum and the heavy metal ion is Pb(II), and the method has a Pb(II) detection limit in the range of 0.15-0.30 μg L.sup.−1.
17: The method of claim 9, wherein the rare earth metal is lanthanum and the heavy metal ion is Cd(II), and the method has a Cd(II) detection limit in the range of 0.05-0.20 μg L.sup.−1.
18: The method of claim 9, wherein the rare earth metal is cerium and the heavy metal ion is Pb(II), and the method has a Pb(II) detection limit in the range of 0.02-0.15 μg L.sup.−1.
19: The method of claim 9, wherein the rare earth metal is cerium and the heavy metal ion is Cd(II), and the method has a Cd(II) detection limit in the range of 0.01-0.10 μg L.sup.−1.
20: The method of claim 9, which has a reproducibility as measured by a relative standard deviation in the range of 1-5%.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0056] A more complete appreciation of the disclosure and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
[0057]
[0058]
[0059]
[0060]
[0061]
[0062]
[0063]
[0064]
[0065]
[0066]
[0067]
[0068]
[0069]
[0070]
[0071]
[0072]
[0073]
[0074]
[0075]
[0076]
[0077]
[0078]
[0079]
[0080]
[0081]
[0082]
[0083]
[0084]
[0085]
[0086]
[0087]
[0088]
[0089]
[0090]
[0091]
[0092]
[0093]
[0094]
[0095]
[0096]
[0097]
[0098]
[0099]
[0100]
[0101]
[0102]
[0103]
[0104]
[0105]
[0106]
[0107]
[0108]
[0109]
[0110]
[0111]
[0112]
[0113]
[0114]
[0115]
[0116]
[0117]
[0118]
[0119]
[0120]
[0121]
[0122]
[0123]
[0124]
[0125]
[0126]
[0127]
[0128]
[0129]
[0130]
[0131]
[0132]
[0133]
[0134]
[0135]
[0136]
[0137]
DETAILED DESCRIPTION OF THE EMBODIMENTS
[0138] Referring now to the drawings, wherein, like reference numerals designate identical or corresponding parts throughout the several views. Embodiments of the present disclosure will now be described more fully hereinafter with reference to the accompanying drawings, in which some, but not all of the embodiments of the disclosure are shown.
[0139] Within the description of this disclosure, where a numerical limit or range is stated, the endpoints are included unless stated otherwise. Also, all values and subranges within a numerical limit or range are specifically included as if explicitly written out. As used herein, the words “a” and “an” and the like carry the meaning of “one or more”. The phrases “selected from the group consisting of”, “chosen from”, and the like include mixtures of the specified materials. Terms such as “contain(s)” and the like are open terms meaning “including at least” unless otherwise specifically noted.
[0140] According to a first aspect, the present disclosure relates to an electrode comprising: i) graphite powder, ii) paraffin oil, and iii) a zeolite impregnated with a rare earth metal.
[0141] As used herein, an electrode refers to an electrical conductor used to make contact with a nonmetallic part of a circuit (i.e. a semiconductor, an electrolyte, a vacuum or air), preferably an electrolyte. In certain embodiments, the term electrode may include the electroactive material of the electrode. In certain embodiments, the electrode of the present disclosure may be present in a holder or an electrochemical cell and the term electrode may refer to the full the electrode in the holder and/or the electrochemical cell. As used herein, an electrochemical cell refers to a device capable of either generating electrical energy from chemical reactions or facilitating chemical reactions through the introduction of electrical energy. The electrode in an electrochemical cell may be referred to as either an anode or a cathode. As used herein, an anode refers to the electrode at which electrons leave the cell and oxidation occurs, and a cathode refers to the electrode at which electrons enter the cell and reduction occurs. Each electrode may become either the anode or the cathode depending on the direction of current through the cell. In addition a bipolar electrode describes an electrode that functions as the anode of one cell and the cathode of another cell. Chemically modified electrodes are electrodes that have their surface chemically modified to change the electrode's physical, chemical, electrochemical, optical, electrical, and/or transport properties. These electrodes are used for advanced purposes in research and investigation.
[0142] As used herein, a chemically modified electrode (CME) is an electrical conductor (material that has the ability to transfer electricity) that has its surface or material modified for different electrochemical functions. At a modified electrode, an oxidation-reduction substance accomplishes electrocatalysis by transferring electrons from the electrode to a reactant, or a reaction substrate. Electrodes can be modified in a variety of ways including, but not limited to, adsorption (chemisorption), covalent bonding, polymer film coating, and composite formation. Composite formation refers to a method that has the chemical modifier mixed with an electrode matrix material (i.e. having a zeolite, the chemical modifier, mixed with carbon particles in a carbon paste electrode, the electrode matrix). Exemplary electrodes that can be chemically modified include, but are not limited to, carbon paste electrodes, glassy carbon paste electrodes, glassy carbon electrodes, pyrolytic carbon electrodes, and the like. Chemically modified electrodes have been employed for the analysis of a variety of organic and inorganic species.
[0143] In a preferred embodiment, the electrode of the present disclosure may be considered as a chemically modified electrode (CME), preferably a modified carbon paste electrode (CPE or MCPE), specifically a zeolite modified carbon paste electrode (ZMCPE). As used herein, a carbon paste electrode refers an electrode made from a mixture of conducting graphite powder and a pasting liquid (i.e. paraffin oil). These electrodes are simple to construct and offer an easily renewable surface for electron exchange. Carbon paste electrodes belong to a special group of heterogeneous carbon electrodes. These electrodes are widely used mainly for voltammetric measurements; however, carbon paste based sensors are also applicable in coulometry (both amperometry and potentiometry). In general, carbon paste electrodes are advantageous because carbon pastes are easily obtainable at minimal costs and are especially suitable for preparing an electrode material modified with admixtures (i.e. zeolites) of other compounds thus giving the electrode certain predetermined properties. Electrodes prepared in this way can serve as highly selective sensors for both inorganic and organic electrochemistry. Carbon paste electrodes, glassy carbon paste electrodes, glassy carbon electrodes (GCE), pyrolytic graphite electrodes (PyGE), etc. when modified are termed as chemically modified electrodes. Chemically modified electrodes have been employed for the analysis of inorganic and organic species. In a preferred embodiment the electrode is a rare earth metal impregnated zeolite modified carbon paste electrode representing a homogeneous mixture of the graphite powder, the paraffin oil, and the zeolite impregnated with a rare earth metal.
[0144] In a preferred embodiment, the electrode of the present disclosure comprises graphite powder as a conductive carbon. Graphite is essentially made up of hundreds, preferably thousands or tens to hundreds of thousands of layers of graphene. As used herein, graphite (or plumbago) refers to a crystalline form of carbon, a semimetal, a native element mineral, and one of the allotropes of carbon. Graphite is the most stable form of carbon under standard conditions. Graphite may be considered the highest grade of coal, just above anthracite and alternatively called meta-anthracite. Graphite has a layered, planar structure. In each layer the carbon atoms arranged in a honeycomb lattice with separation of 0.14-0.15 nm, preferably 0.14-0.145 nm or about 0.142 nm and a distance between planes of 0.3-0.35 nm, preferably 0.32-0.345 nm, preferably 0.33-0.34 nm, or about 0.335 nm. Atoms in the plane are bonded covalently, with only three of the four potential bonding sites satisfied. The fourth electron is free to migrate in the plane, making graphite electrically conductive; however, it does not conduct in a direction at right angles to the plane. Bonding between the layers is via weak van der Waals bonds, which allows layers of graphite to be easily separated, or to slide past each other. In one embodiment, the graphite material of the electrode described herein comprises 10-500000 layers of graphene, preferably 100-400000 layers of graphene, preferably 500-300000 layers of graphene, preferably 1000-250000 layers of graphene, preferably 5000-200000 layers of graphene, preferably 10000-150000 layers of graphene, preferably 25000-125000 layers of graphene, preferably 50000-100000 layers of graphene.
[0145] The two known forms of graphite are alpha (a, hexagonal) and beta (β, rhombohedral). The two forms have very similar physical properties, except the graphene layers stack slightly differently. The hexagonal graphite may be either flat or buckled. The alpha form can be converted to the beta form through mechanical treatment and the beta form reverts to the alpha form when heated to sufficiently high temperatures (˜1300° C.). In terms of the present disclosure, the graphite material of the electrode described herein may be alpha, beta, or mixtures thereof.
[0146] There are three principal types of natural graphite, each occurring in different types of ore deposit. Crystalline flake graphite (or flake graphite) occurs as isolated, flat, plate-like particles with hexagonal edges if unbroken and when broken the edges can be irregular or angular. Amorphous graphite refers to very fine flake graphite. Lump graphite (or vein graphite) occurs in fissure veins or fractures and appears as massive platy intergrowths of fibrous or acicular crystalline aggregates. Highly ordered or oriented pyrolytic graphite (HOPG) refers to graphite with an angular spread between the graphite sheets of less than 1°. Graphite fiber is also sometimes used to refer to carbon/fiber and/or carbon fiber reinforced polymer. In terms of the present disclosure, the graphite material employed may be natural graphite, synthetic graphite, crystalline flake graphite, amorphous graphite, highly oriented pyrolytic graphite, lump graphite, graphite fiber, graphite nanofiber, chemically modified graphite, expanded graphite, intercalated graphite, and mixtures thereof, preferably graphite in the form of flakes, rods, or powder, most preferably commercially available graphite powder.
[0147] Exemplary commercially available graphite powders include, but are not limited to CR (Czech Republic), RW (Germany, Austria), BDH (Scandinavia and United Kingdom), SMMC (China), Acheson, UCP, GP, and SP (United States). In a preferred embodiment, the graphite powder has an average particle (grain) size in the ranges of micrometers or tens of micrometers, preferably 10-90 μm, preferably 10-50 μm, preferably 15-40 μm, preferably 20-30 μm and a relatively uniform particle size distribution (i.e. 5-20 μm). In some embodiments the graphite powder has an average particle (grain) size in the range of 20-100 nm, preferably 30-80 nm. In certain embodiments, the graphite powder is substantially free of impurities, such as oxygen, and possesses low adsorption capabilities, meaning the graphite powder pure graphite content is greater than 80% by weight graphite relative to the total weight of the graphite powder, preferably greater than 85% by weight, preferably greater than 90% by weight, preferably greater than 95% by weight, preferably greater than 96% by weight, preferably greater than 97% by weight, preferably greater than 98% by weight, preferably greater than 99% by weight, preferably greater than 99.5% by weight, preferably greater than 99.9% by weight, preferably greater than 99.99% by weight, preferably greater than 99.995% by weight pure graphite content relative to the total weight of the graphite powder.
[0148] In a preferred embodiment, the electrode of the present disclosure has a weight percentage of the graphite powder in the range of 45-75% relative to the total weight of the electrode, preferably 50-70% by weight, preferably 55-69% by weight, preferably 60-68% by weight, preferably 62-66% by weight, or about 65% by weight relative to the total weight of the electrode.
[0149] It is equally envisaged that the electrode of the present disclosure may further comprise or may be adapted to comprise additional carbonaceous materials as conductive carbon. Exemplary suitable carbonaceous materials include, but are not limited to, acetylene black (AB), obtained by controlled combustion of acetylene in inert atmosphere or chemical decomposition, carbon black, an amorphous material obtainable by the incomplete combustion of heavy petroleum fractions, colloidal graphite, hexagonal carbon with extremely fine flakes and enhanced conductivity, both natural and synthetic forms of diamond applied as fine powders, soot, activated charcoal, coal (“black coal”), lignite (“brown coal”), glassy carbon (GC), fullerene (C-60), carbon nanomaterials (carbon nanotubes, CNTs, carbon nanohorns, carbon nanoparticles, carbon nanofibers), porous carbon foam, porous carbon microspheres, template carbon, ordered mesoporous carbon (OMC) and the like.
[0150] Mechanical connection of the individual carbon particles into a uniform mass is not the only role of binders. Each pasting liquid, including highly chemically inert substances, codetermines principal physicochemical and electrochemical properties of the electrode. Typical parameters of a suitable pasting liquid or binder include, but are not limited to, chemical inertness and electroinactivity, low volatility, minimal solubility in water, and controlled miscibility with organic solvents.
[0151] In a preferred embodiment, the electrode of the present disclosure comprises paraffin (mineral) oils as a pasting liquid or binder. As used herein, mineral oil or paraffin oil refers to any of various colorless, odorless light mixtures of higher alkanes from a mineral source, particularly a distillate of petroleum. Most often, mineral oil is a liquid by-product of refining crude oil to make gasoline and other petroleum products. This type of mineral oil is a transparent, colorless oil composed mainly of alkanes and cycloalkanes related to petroleum jelly. The mineral oil or paraffin oil of the present disclosure may be light, medium or heavy grade in terms of density and viscosity. The mineral oil or paraffin oil preferably has a density of 0.75-0.92 g/mL, preferably 0.80-0.90 g/mL, preferably 0.81-0.89 g/mL, preferably 0.83-0.86 g/mL and a viscosity of 5-15 mm.sup.2/s, preferably 7-13 mm.sup.2/s, preferably 8.5-11 mm.sup.2/s. Three basic classes of mineral oils exist: i) alkanes and alkane oils based on light n-alkanes, ii) naphthenic oils, based on cycloalkanes, and iii) aromatic oils, based on aromatic hydrocarbons (distinct from essential oils). In terms of the present disclosure, the mineral oil or paraffin oil may be an alkane oil, a naphthenic oil, an aromatic oil, and mixtures thereof. Typical paraffin oil is formed by a mixture of liquid aliphatic hydrocarbons and is often marketed under a tradename. Exemplary suitable products of this kind include, but are not limited to Nujol and Uvasol.
[0152] In a preferred embodiment, the electrode of the present disclosure has a weight percentage of the paraffin oil in the range of 20-40% relative to the total weight of the electrode, preferably 22-38% by weight, preferably 24-36% by weight, preferably 26-34% by weight, preferably 28-32% by weight, or about 30% by weight relative to the total weight of the electrode. In a preferred embodiment, the ratio of graphite to paraffin oil is in the range of 1.0 g graphite to 0.1-5.0 mL paraffin oil, preferably 1.0 g graphite to 0.2-2.0 mL paraffin oil, preferably 1.0 g graphite to 0.4-1.0 mL paraffin oil.
[0153] It is equally envisaged that the electrode of the present disclosure may further comprise or may be adapted to comprise additional pasting liquids or binders. Exemplary suitable pasting liquids or binders include, but are not limited to, aliphatic and aromatic hydrocarbons (C.sub.8-C.sub.20, C.sub.10-C.sub.14 such as for example benzene, naphthalene, phenanthrene, and hexadecane), silicone oils and greases (polymerized siloxanes optionally with organic side chains, halogenated hydrocarbons and similar derivatives (bromoform, carbon tetrachloride, α-bromonaphthalene, p-dichlorobenzene, and trans-1,2-dibromocyclohexane), 1,2,3-trichloropropane (TCP), dioctyl phthalate (DOP), di-iso-nonyl phthalate (DINP), 1-(2-nitrophenoxy)octane (NPOE), diphenyl ether, glycerol, castor oil, vaseline oil, polycationic electrolytes, room temperature ionic liquids (RTILs) and the like.
[0154] In a preferred embodiment, the electrode of the present disclosure is a chemically modified carbon paste electrode, preferably a zeolite modified carbon paste electrode, comprising a zeolite as an electroactive material, preferably a zeolite impregnated with a rare earth metal. As used herein, a zeolite refers to a microporous aluminosilicate mineral. Many zeolites occur naturally but are also produced industrially on a large scale. Zeolites are crystalline solid structures made of silicon, aluminum and oxygen that form a framework with cavities and channels inside where cations, water, and/or small molecules may reside. Zeolites have a porous structure that can accommodate a wide variety of cations, such as Na.sup.+, K.sup.+, Ca.sup.2+, Mg.sup.2+ and others. These positive ions are rather loosely held and can readily be exchanged for others in a contact solution. Alternatively, zeolites are the aluminosilicate members of the family of microporous solids known as “molecular sieves”. Several varied unique zeolite frameworks have been discovered, at present there are nearly 200 unique zeolite frameworks identified and over 40 naturally occurring zeolite frameworks are known. Zeolites are crystalline materials that afford molecular sized frames and pores, the major building units of zeolites are [SiO4].sup.4− and [AlO4].sup.5− tetrahedra. Zeolites are crystalline aluminosilicates with open 3D framework structures built of SiO.sub.4 and AlO.sub.4 tetrahedra linked to each other by sharing all the oxygen atoms to form regular intra-crystalline cavities and channels of molecular dimensions. In a defining feature zeolite frameworks are made up of 4-coordinated atoms forming tetrahedra. These tetrahedra are linked together by their corners leading to a wide variety of structures. These units can link in several ways, resulting in arrays producing three-dimensional anionic networks. The extra negative charge on [AlO4]5− tetrahedra is counter balanced by a cation, maintaining the overall neutrality of the zeolite. The framework structure may contain linked cages, cavities, and/or channels which are big enough for small molecules to enter and/or occupy. The system of large voids explains the low specific density of these compounds.
[0155] In terms of the present disclosure a variety of zeolite mineral species may be suitable. The zeolite structural group (Nickel-Strunz classification) includes, but is not limited to, 09.GA zeolites, 09.GB zeolites, 09.GC zeolites, 09.GD zeolites, 09.GE zeolites and mixtures thereof. The 09.GA zeolites with T.sub.5O.sub.10 units (T=combined Si and Al) are known as the fibrous zeolites and include, but are not limited to, the natrolite framework (NAT; gonnardite, natrolite, mesolite, paranatrolite, scolecite, tetranatrolite), the edingtonite framework (EDI; edingtonite, kalborsite), the thomsonite framework (THO; thomsonite series), and mixtures thereof. The 09.GB zeolites with chains of single connected 4-membered rings include, but are not limited to, the analcime framework (ANA; analcime, leucite, pollucite, wairakite), laumontite (LAU), yugawaralite (YUG), goosecreekite (GOO), montesommaite (MON), and mixtures thereof. The 09.GC zeolites with chains of doubly connected 4-membered rings include, but are not limited to, the phillipsite framework (PHI; harmotome, phillipsite series), the gismondine framework (GIS; amicite gismondine, garronite, gobbinsite), boggsite (BOG), merlinoite (MER), the mazzite series (MAZ), the paulingite series (PAU), perlialite (Linde type L framework, zeolite L, LTL), and mixtures thereof. The 09.GD zeolites with chains of 6-membered rings are known as tabular zeolites and include, but are not limited to, the chabazite framework (CHA; chabazite series, herschelite, willhendersonite, SSZ-13), the faujasite framework (FAU; faujasite series, Linde type X, zeolite X, X zeolites, Linde type Y, zeolite Y, Y zeolites), the mordenite framework (MOR; maricopaite, mordenite), the offretite-wenkite subgroup 09.GD.25 such as offretite (OFF) and wenkite (WEN), belilbergite (TMA-E, Aiello and Barrer, framework type EAB), bikitaite (BIK), the erionite series (ERI), ferrierite (FER), gmelinite (GME), the levyne series (LEV), the dachiardite series (DAC), epistilbite (EPI), and mixtures thereof. The 09.GE zeolites with chains of T.sub.10O.sub.20 tetrahedra (T=combined Si and Al) include, but are not limited to, the heulandite framework (HEU; clinoptilolite, heulandite series), the stilbite framework (STI; barrerite, stellerite, stilbite series); brewsterite framework (BRE; brewsterite series), and mixtures thereof. Other acceptable structural group frameworks may include, but are not limited to, cowlesite, pentasil (also known as ZSM-5, framework type MFI), tschernichite (beta polymorph A, disordered framework, BEA), Linde type A framework (zeolite A, LTA), and the like. In terms of the present disclosure, the zeolite and/or the zeolite impregnated with a rare earth metal may have a 09.GA, 09.Gb, 09.GC, 09.GD, or 09.GE structural group framework, preferably a 09.GD structural group framework.
[0156] Often zeolites may be classified into groups according to the Si/Al ratio in their frameworks: i) “low silica” or aluminum rich zeolites A and X (silica to alumina molar ratio Si/Al ˜1), ii) “intermediate silica” zeolites such as for example zeolite Y, mordenite, zeolite L, and natural zeolites (silica to alumina molar ratio Si/Al 2 to 5), and iii) “high silica” zeolites such as zeolite beta and ZSM-5 (silica to alumina molar ratio Si/Al≧10).
[0157] The “low silica” zeolites represent a fortunate balance of composition, pore volume, and channel structure. These zeolites are nearly “saturated” in aluminum in the framework composition with a molar ratio of Si/Al ˜1, which is considered the highest aluminum content possible in tetrahedral aluminosilicate frameworks. Consequently, they contain the maximum number of cation exchange sites balancing the framework aluminum, and thus the highest cation contents and exchange capacities. These compositional characteristics provide the moost highly heterogeneous surface known among porous materials, due to exposed cationic charges nested in an aluminosilicate framework which results in high field gradients. Their surfaces are highly selective for water, polar, and polarizable molecules. The “intermediate silica” zeolites represent superior stability characteristics reflecting higher Si/Al molar ratios (1.5-5, preferably 2.5-4, preferably 3-3.5) that improve both thermal and acid stability as aluminum positions in the zeolite frameworks pose a site of instability to attack by acid and water vapor. In addition to improvement in stability the difference in composition and structures provided additional catalysis benefits. The “high silica” zeolites are zeolites with molar Si/Al ratios from 10 to 100 or higher, with distinct surface characteristics. In contrast to the “low” and “intermediate” silica zeolites, representing heterogeneous hydrophilic surfaces within a porous crystal, the surface of the high silica zeolites is more homogeneous with an organophilic-hydrophobic selectivity. They generally adsorb stronger the less polar organic molecules and only weakly interact with water and other polar molecules. In terms of the present disclosure, the zeolite and/or zeolite impregnated with a rare earth metal may be a low silica zeolite, an intermediate silica zeolite, or high silica zeolite, preferably a high silica zeolite. In a preferred embodiment, the zeolite of the electrode of the present disclosure has a silica to alumina ratio in the range of 5 to 40, preferably 6 to 35, preferably 7 to 30, preferably 8 to 25, preferably 9 to 22, more preferably 10 to 20, more preferably 12 to 18, more preferably 14 to 16, or about 15.
[0158] In a preferred embodiment, the zeolite of the zeolite impregnated with a rare earth metal is a mordenite zeolite. As used herein, mordenite refers to a zeolite mineral with the general chemical formula (Ca, Na.sub.2, K.sub.2)Al.sub.2Si.sub.10O.sub.24.7H.sub.2O, preferably Na.sub.8Al.sub.8Si.sub.40O.sub.96.n-H.sub.2O, preferably having the molar composition 6Na.sub.2O:Al.sub.2O.sub.330SiO.sub.2:780H.sub.2O. Mordenite is one of the six most abundant zeolites and is used commercially. Mordenite is orthorhombic (a,b,c are all unequal and all angles are 90 degrees). It often crystallizes in the form of fibrous aggregates, masses and vertically striated prismatic crystals. It may be colorless, white, or faintly yellow or pink. It typically has a Mohs hardness of 1-10, preferably 2-8, preferably 4-6, or about 5 and a density of 1.5-3.0 g/cm.sup.3, preferably 1.75-2.5 g/cm.sup.3, preferably 2.0-2.25 g/cm.sup.3 or about 2.1 g/cm.sup.3. In cases where mordenite forms well developed crystals they are often hairlike; very long, thin and delicate. Mordenite's molecular structure is a framework containing chains of five membered rings of linked silicate and aluminate tetrahedral (four oxygen atoms arranged at the points of a triangular pyramid about a central silicon or aluminum atom). Its framework is built on 5-membered rings arranged in columns parallel to the [001] axis. Hence, the framework includes elliptical micropore (6-7×6.5-7.5 {acute over (Å)}, preferably 6.7×7.0 {acute over (Å)}) tunnels parallel to the c-axis and (2-3×5-6 {acute over (Å)}, preferably 2.6×5.7{acute over (Å)}) tunnels parallel to the b-axis. By virtue of the small nature of the latter axis, molecules are unable to pass through, and as such mordenite is generally regarded as a one-dimensional zeolite. Mordenite's high ratio of silicon to aluminum atoms makes it relatively more resistant to attack by acids than many other zeolites. Mordenite is one of the most abundant zeolites in altered volcanic deposits; it is found in volcanic rock such as rhyolite, andesite, and basalt. It may be associated with other zeolites such as stilbite and heulandite.
[0159] In a preferred embodiment, the zeolite of the zeolite impregnated with a rare earth metal is a mordenite zeolite. In a preferred embodiment, the zeolite of the zeolite impregnated with a rare earth metal is a mordenite zeolite, preferably having the molar composition 6Na.sub.2O:Al.sub.2O.sub.330SiO.sub.2:780H.sub.2O, which has a silica to alumina molar ratio (Si/Al) in the range of 5 to 40, preferably 6 to 35, preferably 7 to 30, preferably 8 to 25, preferably 9 to 22, more preferably 10 to 20, more preferably 12 to 18, more preferably 14 to 16, or about 15. Several morphologies of the mordenite zeolite are suitable including, but not limited to spherical, circular pie, flat prismic, ellipsoidal, hexagonal star-like prism, and the like. In a preferred embodiment, the zeolite of the zeolite impregnated with a rare earth metal is a mordenite zeolite which has a flat prismic crystal with an average crystal size estimated using the Scherer equation and defined as an average crystal dimension perpendicular to the reflection plane, of 2-15 μm, preferably 2.5-12 μm, preferably 3-10 μm, preferably 4-9.5 μm, preferably 5.5-8 μm, preferably 6-7 μm.
[0160] In certain embodiments, the zeolite of the zeolite impregnated with a rare earth metal is a mordenite zeolite and is prepared by a sol-gel method. Sol-gel processing refers to a process of slow crystallization of a silica-alumina gel in the presence of alkalis and/or organic templates. The product properties depend on the reaction mixture composition, pH of the system, operating temperature, pre-reaction “seeding time” reaction time as well as templates used. The silicate sol formed by the hydrothermal method is very stable. The method of preparation of the mordenite zeolite is not viewed as particularly limiting. The method of preparation of the rare earth metal impregnated zeolite is not viewed as particularly limiting. These methods should be known to those of ordinary skill in the art.
[0161] In a preferred embodiment, the electrode of the present disclosure comprises a zeolite, preferably mordenite impregnated with a rare earth metal, preferably cerium and/or lanthanum. As used herein, “impregnated”, “incorporated” or “exchanged” describes being completely or partially filled throughout, permeated, and/or infused. The rare earth metal elements or cations may be affixed inside of and/or on an outer surface of the zeolite. The rare earth metal cations or elements may be affixed on one or more surfaces of the zeolite. The rare earth metal cations or elements may be affixed to the zeolite in any reasonable chemical or physical manner, such as affixed to one or more surfaces of the zeolite, incorporated into the chemical framework of the zeolite, or alternatively, at least partially embedded within cavities and/or pore spaces of the zeolite. In a preferred embodiment, the rare earth metal ions are incorporated into the chemical framework of the zeolite, preferably mordenite. In certain embodiments, some of the Al atoms have been replaced by the rare earth metal element in the framework of the zeolite. After impregnation with rare earth metal ions the crystallinity of the zeolite, preferably mordenite, as well as the crystal morphology of the zeolite, preferably mordenite is retained. In certain embodiments, scanning electron microscopy (SEM) analysis reveals several spots on the rare earth metal impregnated zeolite indicating the binding between the zeolite crystal and the impregnated rare earth metals (
[0162] As used herein, a rare earth metal or rare earth element may refer to any member of the lanthanide series (lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium), the actinide series (actinium, thorium, protactinium, uranium, neptunium, plutonium, americium, curium, berkelium, californium, einsteinium, fermium, mendelevium, nobelium, lawrencium), as well as scandium, yttrium and mixtures thereof. As used herein, the terms rare earth (RE), rare earth element (REE), rare earth metal (REM), rare earth oxides (REO), rare earth elements and yttrium (REY), light rare earth elements (LREE, Sc, La, Ce, Pr, Nd, Pm, Sm, Eu, and Gd; also known as the cerium group), and heavy rare earth elements (Y, Tb, Dy, Ho, Er, Tm, Yb, and Lu; also known as the yttrium group) are used synonymously. In a preferred embodiment, the rare earth metal is at least one selected from the group consisting of lanthanum and cerium. It is equally envisaged that any rare earth metal as described herein may be employed in addition to, or in lieu, of lanthanum and/or cerium.
[0163] In a preferred embodiment, the zeolite impregnated with the rare earth metal has a weight percentage of the rare earth metal in the range of 1-15 wt % relative to the total weight of the zeolite impregnated with the rare earth metal, preferably 1.5-12 wt % preferably 2-10 wt %, preferably 4-9 wt %, preferably 5-8 wt % relative to the total weight of the zeolite impregnated with the rare earth metal. In certain embodiments, the zeolite is mordenite and the rare earth metal is lanthanum and the mordenite zeolite impregnated with lanthanum has a weight percentage of lanthanum in the range of 1-15 wt % relative to the total weight of the mordenite zeolite impregnated with lanthanum, preferably 1.25-10 wt %, preferably 1.5-5 wt %, preferably 1.75-3 wt %, or about 2 wt % relative to the total weight of the mordenite zeolite impregnated with lanthanum. In certain embodiments, the zeolite is mordenite and the rare earth metal is cerium and the mordenite zeolite impregnated with cerium has a weight percentage of cerium in the range of 1-15 wt % relative to the total weight of the mordenite zeolite impregnated with cerium, preferably 4-14 wt %, preferably 6-13 wt %, preferably 8-12 wt %, or about 10 wt % relative to the total weight of the mordenite zeolite impregnated with cerium.
[0164] In a preferred embodiment, the electrode of the present disclosure has a weight percentage of the zeolite impregnated with the rare earth metal in the range of 1-30% relative to the total weight of the electrode, preferably 2-25% by weight, preferably 3-20% by weight, preferably 4-15% by weight, preferably 5-10% by weight, or about 5% by weight relative to the total weight of the electrode.
[0165] The construction of the actual physical electrode and holders or housings is not viewed as particularly limiting. Exemplary holders and/or housings include, but are not limited to tubings and rods (plugs) with hollow ends, rotated disc electrodes, piston-driven electrode holders, and a variety of commercially available electrode holders. In certain embodiments, the electrode material (i.e the electrode) in the form of a paste may be packed into a plastic micropipette tip (10-100 mm long, preferably 20-75 mm long, preferably 30-50 mm long, or about 40 mm long an 0.01-1.0 mm in diameter, preferably 0.05-0.5 mm in diameter, or about 0.01 mm in diameter). The working electrode held or housed in this manner may further comprise an electrical contact, such as for example a copper wire (
[0166] In a preferred embodiment, the rare earth impregnated zeolite modified electrode of the present disclosure in any of its embodiments has a greater electroactive surface area relative to a substantially similar electrode lacking the zeolite impregnated with the rare earth metal, such as an electrode comprising a substantially similar zeolite free of rare earth metal exchange or incorporation. In a preferred embodiment, the rare earth impregnated zeolite modified electrode of the present disclosure in any of its embodiments has a 10-40% greater electroactive surface area relative to a substantially similar electrode lacking the zeolite impregnated with the rare earth metal, preferably 15-35%, preferably 20-30% greater electroactive surface area relative to a substantially similar electrode lacking the zeolite impregnated with the rare earth metal. In a preferred embodiment, the rare earth impregnated zeolite modified electrode of the present disclosure in any of its embodiments has an electroactive surface area of greater than 5 mm.sup.2, preferably greater than 10 mm.sup.2, preferably greater than 15 mm.sup.2, preferably greater than 20 mm.sup.2, preferably greater than 22 mm.sup.2, preferably greater than 24 mm.sup.2, preferably greater than 26 mm.sup.2, preferably greater than 28 mm.sup.2, preferably greater than 30 mm.sup.2, preferably greater than 35 mm.sup.2, preferably greater than 40 mm.sup.2, preferably greater than 50 mm.sup.2.
[0167] It is equally envisaged that the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments may be further modified in addition to zeolite impregnation. Additional suitable chemical modifications include, but are not limited to intrinsic modification, extrinsic modification (surface modification and bulk modification, chemical modifiers including, but not limited to, inorganic materials (Prussian-blue derivatives, polyoxometallates, clays, zeolites, molecular sieves, metal oxides and sol-gel derived inorganic materials), organic and organometallic compounds (organic ligands, organic catalysts, organometallic complexes, surfactants, amphiphilic modifiers, lipophilic modifiers, organic polymers and macromolecules), organic-inorganic hybrid materials, nanomaterials, surface treatments, coatings, and alterations. Additional suitable biological modifications include, but are not limited to, enzymes (oxidases, dehydrogenases, hydrolases, auxiliary enzymes), nucleic acids, immunosensors, tissues, cells, and other biomolecules.
[0168] According to a second aspect, the present disclosure relates to a method for detecting and quantifying a heavy metal ion in an aqueous solution comprising: i) contacting the aqueous solution with the electrode in any of its embodiments, ii) generating a negative deposition potential at the electrode to reduce the heavy metal ion and form a reduced heavy metal that is deposited onto the electrode, iii) scanning a potential range from the negative deposition potential in the positive direction at the electrode to oxidize and strip the reduced heavy metal from the electrode, and iv) measuring the current during the scanning. In general, the rare earth metal impregnated zeolite modified electrode in any of its embodiments is contacted with an aqueous sample and in electrical communication with a reference electrode. A potential is applied between the reference electrode and the rare earth metal impregnated zeolite modified electrode produce a current. Changes in the current as a result of reduction/oxidation/decomposition of detected analytes (i.e. heavy metal ions) can be used to determine the amount of the analyte in the sample into which the electrode is placed.
[0169] Non-limiting examples of aqueous solutions (i.e. heavy metal contaminated and/or Cd(II)/Pb(II) contaminated aqueous solutions), water sources and systems include, but are not limited to, surface water that collects on the ground or in a stream, aquifer, river, lake, reservoir or ocean, ground water that is obtained by drilling wells, run-off, industrial water, public water storage towers, public recreational pools and/or bottled water. Methods for the detection and quantification of heavy metals in aqueous solutions according to the present disclosure include contacting the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments with heavy metal contaminated water sources and systems. The methods may be carried out in tanks, containers, or small scale applications in both batch mode and fixed-bed or column mode. In a preferred embodiment, the aqueous solution comprises greater than 80% v/v of water, preferably greater than 85% v/v water, preferably greater than 90% v/v water, preferably greater than 95% v/v water, preferably greater than 99% v/v water.
[0170] In a preferred embodiment, the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments may be utilized to detect analytes. As used herein, the term “analyte” refers to a substance that is (or whose chemical constituents are) being identified, detected, and/or measured by the rare earth metal impregnated zeolite modified electrode described herein. An analyte may be a component of a fluid (i.e. vapor or liquid) sample in which the rare earth metal impregnated zeolite modified electrode is immersed or contacted with. The analyte may be various organic (i.e. uric acid and biologically important catecholamines) and inorganic species (i.e. toxic metals), preferably metal ions, more preferably heavy metal ions, in various matrices. In one embodiment, the aqueous solution is an environmental sample such as for example drinking water and the analyte is a heavy metal ion and the electrodes described herein display a lack of toxicity compared to traditional mercury electrodes. In a preferred embodiment, the aqueous solution has an initial analyte concentration of 10.sup.−3 to 10.sup.−12 M, preferably 10.sup.−4 to 10.sup.−10 M, preferably 10.sup.−5 to 10.sup.−9 M, or alternatively 1-1000 ppb, preferably 5-500 ppb, preferably 50-250 ppb.
[0171] The metal ions that are detected and/or quantified are preferably heavy metal ions. In a preferred embodiment, a heavy metal ion has a density of greater than 3.5 g/cm.sup.3 and/or an atomic weight of greater than 20. Exemplary metal ions that can be detected and/or quantified by the electrode and method of the present disclosure in any of their embodiments are of a wide range and include, but are not limited to ions of Ag, Ca, K, Zn, Na, Pb, Mn, Fe, Co, Ni, Al, Cu, Sn, Cd, Hg, Cr, Fe, Bi, Ga, Ge, Au, In, TI, Rb, Cs, As, Sb, Cr, Zn, V, Pt, Pd, Rh, and mixtures thereof. Further, these metal ions may be of any oxidation state M.sup.+1, M.sup.+2, M.sup.+3, etc. In a preferred embodiment, the heavy metal is at least one selected from the group consisting of Co, Cu, Zn, Hg, As, Sr, Mo, Cd, and Pb, most preferably the heavy metal ion is at least one selected from the group consisting of lead (II), Pb (II) and cadmium (II), Cd (II). It is equally envisaged that the rare earth metal impregnated zeolite modified carbon paste electrode may be adapted or chemically modified to detect and/or quantify one or more additional metal ions in addition to, or in lieu of lead (II) and cadmium (II). In one embodiment, the additional metal ion may be any ion which is detected and/or quantified selectively or collectively by the electrode in any of its embodiments. Exemplary additional metal ions include, but are not limited to, an alkali metal (Li, Na, K, etc.), an alkaline earth metal (Mg. Ca, Sr, etc.) a lanthanide metal (La, Ce, Eu, Yb, etc.), an actinide metal (Ac, Th, etc.), or a post-transition metal (Al, Sn, Pb, In, etc.). Preferably the additional metal ion is a transition metal ion, preferably a heavy metal ion. Exemplary additional transition metals of the metal ion include, but are not limited to, Sc, Ti, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Pd, Ag, W, Os, Au, and Hg.
[0172] In preferred embodiments, the method can be described as voltammetric or as a voltammetry method. As used herein, voltammetry refers to a category of electroanalytical methods used in analytical chemistry and various industrial processes. In voltammetry, information about an analyte (i.e. a heavy metal ion) is obtained by measuring the current as the potential is varied. In general, voltammetry experiments or voltammetry methods investigate the half-cell reactivity of an analyte. Voltammetry is a study of current as a function of applied potential. The corresponding curves (I=f(E)) are referred to as voltammograms. The potential may be varied arbitrarily step by step or continuously, and the actual current value is measured as the dependent variable. The opposite (i.e. amperometry) is also possible but uncommon. The shape of the voltammogram curves depends on the speed of the potential variation (nature of driving force) and on whether the solution is stirred or quiescent (mass transfer). Most experiments and methods control the potential (volts) of an electrode in contact with the analyte while measuring the resulting current (amperes). Exemplary voltammetric methods that may characterize the method of the present disclosure in any of its embodiments, often in terms of applied waveform of the applied biasing potential include, but are not limited to, linear sweep voltammetry, staircase voltammetry, squarewave voltammetry, cyclic voltammetry, anodic stripping voltammetry, cathodic stripping voltammetry, adsorptive stripping voltammetry, alternating current voltammetry, polarography, rotated electrode voltammetry, normal pulse voltammetry, differential pulse voltammetry, chronoamperometry, and the like. In a preferred embodiment, the method of the present disclosure is a stripping voltammetry method, most preferably an anodic stripping voltammetry method.
[0173] Voltammetry is an electrochemical technique in which the current-potential behavior at an electrode surface is measured. The potential is varied in a systematic manner to cause electroactive chemical species to be reduced or oxidized at the electrode. The resultant current is proportional to the concentration of the chemical species. Stripping voltammetry is a two-step technique in which the first step consists of the electrolytic deposition of a chemical species or analyte onto an inert electrode surface at a constant potential. This preconcentration step can involve either an anodic or cathodic process. The most common use of stripping voltammetry involves a anodic and/or cathodic process in which a metal ionic species is reduced from the solution onto an electrode. The second step consists of the application of a voltage scan to the electrode that causes an electrolytic dissolution, or “stripping”, of the various species deposited at the electrode back into solution at characteristic potentials.
[0174] The remarkable sensitivity of stripping voltammetry is attributable to the preconcentration that takes place during deposition. For preconcentration to take place, the deposited material must adhere to the electrode surface, stripping voltammetry can be used to determine those chemical species that will be retained by the electrode. Stripping voltammetry is primarily a trace analytical technique. It can be used to make routine analytical determination at the sub-ppm level. In a preferred embodiment, the method is an anodic stripping voltammetry (ASV) method. As used herein anodic stripping voltammetry is a voltammetric method for quantitative determination of specific ionic species. Anodic stripping voltammetry is used to determine the concentration of trace metals. The analyte of interest (i.e. one or more heavy metal ions in an aqueous solution) is contacted with the electrode of the present disclosure in any of its embodiments, the analyte of interest is electroplated on the working electrode during a deposition (or accumulation) step, and oxidized from the electrode during a stripping step. Anodic stripping voltammetry consists of a deposition potential that is more negative than the half-wave potential of the analytes or metals to be determined and an anodic (positive going) scan to oxidize the reduced analyte or metal back into solution. The current is measured during the stripping step. The oxidation of a species is registered as a peak in the current signal at the potential at which the species begins to be oxidized. The stripping step can be either linear, staircase, squarewave, or pulse. In certain embodiments, it is equally envisaged that the working electrode or method of the present disclosure may be adapted to a cathodic stripping voltammetry (CSV) method wherein a relatively positive potential is applied during the deposition and stripping consists of a cathodic (negative going) to reduce the analyte back into solution. Exemplary analytes detected by cathodic stripping voltammetry include, but are not limited to arsenic, chloride, bromide, iodide, selenium (IV), sulfide, mercaptans (RSH), thiocyanate (SCN), and thio compounds.
[0175] This type of method or experiment generally requires at least two electrodes to perform. The working electrode, which makes contact with the analyte, must apply the desired potential in a controlled way and facilitate the transfer of charge to and from the analyte. In a preferred embodiment, the working electrode is the rare earth impregnated zeolite modified carbon paste electrode (RE-ZMCPE) described herein in any of its embodiments. A second electrode, or counter electrode, acts as the other half of the cell. This second electrode, or counter electrode, must have a known potential with which to gauge the potential of the working electrode, furthermore it must balance the charge added or removed by the working electrode. While this is a viable setup it suffers from it being difficult for a single electrode to maintain a constant potential while passing current to counter redox events at the working electrode. In a solution to this problem, the roles of supplying electrons and providing a reference potential are divided between two separate electrodes. Anodic stripping voltammetry generally incorporates three electrodes, a working electrode, an auxiliary electrode (also referred to as a counter electrode) and a reference electrode. The reference electrode is a half cell with a known reduction potential. Its only role is to act as reference in measuring and controlling the working electrode's potential and at no point does it pass any current. The auxiliary (second or counter) electrode passes all the current needed to balance the current observed at the working electrode. In order to achieve this current, the auxiliary electrode will often swing to extreme potentials at the edges of the solvent window, where it oxidizes or reduces the solvent or supporting electrolyte. These electrodes the working, reference, and auxiliary make up the modern three electrode system. In a preferred embodiment, the method is performed in a three electrode system, comprising a working electrode, an auxiliary (or counter) electrode and a reference electrode.
[0176] In a preferred embodiment, the rare earth impregnated zeolite modified carbon paste electrode (RE-ZMCPE) described herein in any of its embodiments functions as a working electrode. The auxiliary or counter electrode is not viewed as particularly limiting as long as it does not react with the bulk of the analyte solution and conducts well. In a preferred embodiment, the counter electrode comprises or is fabricated from electrochemically inert materials including, but not limited to, platinum, gold or carbon, in a most preferred embodiment the counter electrode is a platinum wire. In another embodiment, the counter or auxiliary electrode may be isolated from the working electrode, such as by means of a glass flit. Such isolation prevents any byproducts generated at the auxiliary electrode from contaminating the main test solution. The reference electrode is preferably an aqueous electrode. Exemplary reference electrodes include, but are not limited to, a standard hydrogen electrode (SHE), a normal hydrogen electrode (NHE), a reversible hydrogen electrode (RHE), a saturated calomel electrode (SCE), a copper-copper(II) sulfate electrode (CSE), a silver chloride (Ag/AgCl) electrode, a pH buffered solution pH electrode, a palladium-hydrogen electrode, a dynamic hydrogen electrode (DHE), a mercury-mercurrous sulfate electrode (MSE), and the like. In a most preferred embodiment, the reference electrode is a silver chloride (Ag/AgCl) electrode.
[0177] In certain embodiments, the aqueous solution may further comprise a supporting electrolyte. As used herein, a supporting electrolyte in electrochemistry refers to an electrolyte containing chemical species that are not electroactive (within the range of potentials used). Supporting electrolytes are widely used in electrochemical measurements when control of electrode potentials is required. This may increase the conductivity of the solution, eliminate the transport of electroactive species by ion migration in the electric field, maintain constant ionic strength or maintain constant pH. In a preferred embodiment, the aqueous solution further comprises a buffer solution as a supporting electrolyte. As used herein, a buffer solution (more precisely, pH buffer or hydrogen ion buffer) refers to an aqueous solution consisting of a mixture of a weak acid and its conjugate base, or vice versa. Its pH changes very little when a small or moderate amount of strong acid or base is added to it and thus it is used to prevent changes in the pH of a solution. Buffer solutions are used as a means of keeping pH at a nearly constant value in a wide variety of chemical applications. In certain embodiments, the aqueous sample further comprises a buffer solution selected from the group consisting of citrate buffer, phthalate buffer, acetate buffer, phosphate buffer, and sulphate buffer, more preferably phosphate buffer. In a preferred embodiment, the concentration of the buffer in the aqueous solution may range from 0.01-1.0 M, preferably 0.01-0.5 M, preferably 0.05-0.25 M, preferably 0.08-0.2 M, or about 0.1 M. In a preferred embodiment, the aqueous sample has a pH in the range of 3-5, preferably 3.2-4.8, preferably 3.4-4.6, preferably 3.5-4.5, preferably 3.6-4.4, preferably 3.8-4.2 or about 4.0.
[0178] In one step of the method for detecting and quantifying a heavy metal ion in an aqueous solution, the aqueous solution is contacted with the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments. Preferably at least one end of the electrode is in contact with the aqueous solution or sample, preferably the length of the electrode material immersed in the aqueous solution may range from 10-100 mm, preferably 20-80 mm, preferably 30-70 mm, preferably 40-60 mm. In certain embodiments, the method may further comprise a deaerating step subsequent to the contacting wherein the aqueous solution is purged for 1-15 minutes, preferably 2-10 minutes with a purified inert gas (i.e. nitrogen, argon) to eliminate interferences from oxygen. Optionally the inert gas may be passed through a scrubbing tower filled with supporting electrolyte in order to allow the nitrogen stream to be saturated with the electrolyte solution to eliminate the possibility of pH changes or volatilization in the cell. In certain embodiments, the method may further comprise a conditioning or cleaning step subsequent to the deaerating. As used herein, conditioning is a term that denotes electrolytic cleaning of the electrode surface. A specified potential, preferably a more oxidizing potential than the analyte of interest, is applied to the electrode for a controlled time in order to remove contaminants or materials not removed during a stripping step from the electrode. In certain embodiments, conditioning is not required with the electrode of the present disclosure as a new electrode is fabricated for each determination or analysis. In contrast, conditioning may be a necessity when the same electrode surface is used in subsequent determinations or analyses. In embodiments where the electrode is used to detect and quantify metals, the conditioning potential should be positive with respect to the half-wave potential of the analyte to ensure the oxidation of metals back into solution. In a preferred embodiment, the conditioning potential is greater than −0.5 V, preferably greater than −0.4 V, preferably greater than −0.3 V, preferably greater than −0.2 V, preferably greater than 0.1 V, preferably greater than 0.0 V and is generally suitable for removing any such contaminants without affecting the electrode. The solution is optionally stirred during conditioning, preferably stirred, and in preferred embodiments the conditioning time is 10-360 seconds, preferably 20-240 seconds, preferably 30-180 seconds, preferably 60-120 seconds.
[0179] In one step of the method for detecting and quantifying a heavy metal ion in an aqueous solution, a negative deposition potential is generated at the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments to reduce the heavy metal ion and form a reduced heavy metal that is deposited onto the electrode. Briefly, the potential is held at a lowered potential, low enough to reduce the analyte and deposit it on the electrode.
[0180] In the deposition step, the deposition potential is applied to the working electrode (i.e. the rare earth metal impregnated zeolite modified electrode) to cause the material of interest to be deposited onto the surface of the working electrode. The solution is optionally and preferably stirred during deposition to maximize analyte-electrode contact, preferably stirred at 100-1000 rpm, preferably 200-800 rpm, preferably 400-700 rpm, or about 600 rpm. Generally, the selection of the deposition potential depends upon whether the material to be determined is oxidized or reduced. For a reducible metal, the deposition potential should be negative with respect to the half-potential of the metal. In contrast, for oxidizable materials, the deposition potential should be selected such that it is positive with respect to the half-wave potential. The choice of the deposition potential can provide some selectivity in the measurement. For example, a dc polarogram of lead and cadmium shows a first plateau as the diffusion-limited current due to the reduction of lead and a second plateau due to the diffusion-limited current of both lead and cadmium. Deposition at a certain potential may only yield a stripping peak for lead. There is no contribution to the stripping voltammogram from the cadmium also present in solution since deposition at this potential reduces lead only. Deposition at a more negative potential yields a somewhat higher stripping peak still with no contribution from cadmium. Deposition at an even more negative potential (more negative than −0.6 V) yields two stripping peaks since deposition at this potential is negative enough to reduce cadmium and lead simultaneously. In this manner, multiple heavy metal ions, 2-12, preferably 2-8, preferably 2-6, preferably 2-3 may be simultaneously detected and/or quantified. In a preferred embodiment, the deposition potential is negative, and the negative deposition potential is in the range of −2.0 V to −0.2 V, preferably −1.8 V to −0.4 V, preferably −1.6 V to −0.6 V, preferably −1.5 V to −0.8 V, preferably −1.4 V to −1.0 V, preferably −1.3 V to −1.1 V, or about −1.2 V.
[0181] The deposition time is an important experimental parameter that is unique to stripping voltammetry. If more sensitivity is required, an analyst may increase the deposition time. This increases the degree of preconcentration, making a greater amount of deposited analyte available at the electrode during the stripping step. In a preferred embodiment, the reduced heavy metal is deposited over a time period (i.e. the deposition time) in the range of 10-250 seconds, preferably 15-225 seconds, preferably 20-200 seconds, preferably 30-180 seconds, preferably 50-175 seconds, preferably 75-150 seconds, preferably 100-140 seconds, preferably 110-125 seconds, or about 120 seconds. In certain embodiments, this deposition step may further comprise an equilibration period. During equilibration, the deposition potential is applied to the working electrode, but stirring is halted. This may allow convection currents from the stirring to decrease to a negligible level and also allow time for the deposited material to stabilize. In a preferred embodiment, the equilibration time is 1-120 seconds, preferably 10-60 seconds, preferably 20-40 seconds, or about 30 seconds.
[0182] In one step of the method for detecting and quantifying a heavy metal ion in an aqueous solution, a potential range is scanned from the negative deposition potential in the positive direction at the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments to oxidize and strip the reduced heavy metal from the electrode and the current is measured during the scanning.
[0183] In the stripping step, an excitation waveform is applied which electrolyzes the deposited material back into the solution. The current is then measured versus the applied potential. The materials deposited at the electrode will strip at potentials very close to their half-wave potentials. The measured current at these potentials is proportional to the concentration of the analyte in the original sample. Increases in sensitivity may be noted for different waveforms of the biasing or striping potential, the biasing or stripping potential may have a waveform of linear voltammetry, linear sweep voltammetry, square wave voltammetry, cyclic voltammetry, or pulse voltammetry. In a preferred embodiment, the scanning and the measuring are performed with square wave voltammetry and the biasing potential or stripping potential has the waveform of square wave voltammetry. In a preferred embodiment, the waveform has amplitude ranging from 0.01-1.0V, preferably 0.05-0.5 V, preferably 0.08-0.4 V, preferably 0.1-0.35 V, preferably 0.15-0.3 V and the waveform has a frequency of 1-150 Hz, preferably 5-100 Hz, preferably 10-80 Hz, preferably 15-60 Hz, preferably 20-50 Hz. In a preferred embodiment, the stripping is performed without stripping. A slow (2-5 mV/sec) or a more rapid (10-100 mV/sec) scan rate may be applied to the electrode. In a preferred embodiment, the scanning is performed at a scan rate of 2-500 mV/s, preferably 5-400 mV/s, preferably 10-350 mV/s, preferably 15-300 mV/s, preferably 20-250 mV/s, preferably 25-200 mV/s, preferably 50-150 mV/s. The scanning range must span the potential region where the chemical specie(s) of interest are electrolyzed back into solution and the current of peaks corresponding to the analytes that are present are measured, thus each metal phase species is selectively oxidized during the anodic potential sweep, such as for example −2.0 to 0.0 V, preferably −1.8 to 0.0 V, preferably −1.6 to 0.0 V, preferably −1.4 to 0.0 V.
[0184] In certain embodiments, the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments is not reused and a new electrode is fabricated for each determination or analysis. In certain embodiments, the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments may be reusable and may be capable of repeated detection without calibration or replacement.
[0185] In certain embodiments, the electrode may be polished before immersion in the aqueous solution or reuse, such as for example with alumina particles with a size ranging from 0.05-0.5 μm, preferably 0.1-0.5 μm, more preferably 0.2-0.3 μm. The electrode may further be rinsed with solvents before immersion in the aqueous solution or reuse such as for example ethanol, acetone, and water to remove impurities.
[0186] In one or more embodiments, the heavy metal ion detection and quantification method described herein may further comprise and/or be preceded by calibration procedures with steps including measuring the voltammogram of a plurality of calibration samples comprising a series of known amounts of the analyte or heavy metal ion in the same medium as the aqueous solution to be tested, in order to obtain a calibration curve for the rare earth metal impregnated zeolite modified electrode. In a preferred embodiment, the calibration is performed over two concentration ranges of the analyte, such as for example 50-500 ppb and 5-50 ppb. Preferably, the square wave stripping voltammetry shows a linear relationship between the stripping current and the concentration of the analyte or heavy metal ion. In a preferred embodiment the concentration limits of detection for many metals is in the low ppb to high ppt range (S/N=3) and compares favorably with atomic absorption spectroscopy (AAS) or inductively coupled plasma (ICP) analysis In a preferred embodiment the method and the rare earth metal impregnated zeolite modified electrode has a limit of detection in the range of 0.005-0.5 μg L.sup.−1, preferably 0.01-0.45 μg L.sup.−1, preferably 0.02-0.4 μg L.sup.−1, preferably 0.03-0.35 μg L.sup.−1, preferably 0.035-0.3 μg L.sup.−1, preferably 0.05-0.25 μg L.sup.−1, preferably 0.10-0.20 μg L.sup.−1. In a preferred embodiment the method and the rare earth metal impregnated zeolite modified electrode has a limit of quantitation in the range of 1-15 μg L.sup.−1, preferably 2-12 μg L.sup.−1, preferably 3-10 μg L.sup.−1, preferably 3.5-8 μg L.sup.−1, preferably 4-6 μg L.sup.−1.
[0187] In a preferred embodiment, the rare earth metal is lanthanum and the heavy metal ion is Pb(II), and the method has a Pb(II) detection limit in the range of 0.15-0.30 μg L.sup.−1, preferably 0.18-0.28 μg L.sup.−1, preferably 0.20-0.25 μg L.sup.−1, preferably 0.21-0.24 μg L.sup.−1, or about 0.225 μg L.sup.−1. In a preferred embodiment, the rare earth metal is lanthanum and the heavy metal ion is Cd(II), and the method has a Cd(II) detection limit in the range of 0.05-0.20 μg L.sup.−1, preferably 0.08-0.18 μg L.sup.−1, preferably 0.10-0.15 μg L.sup.−1, preferably 0.11-0.14 μg L.sup.−1, or about 0.122 μg L.sup.−1. In a preferred embodiment, the rare earth metal is cerium and the heavy metal ion is Pb(II), and the method has a Pb(II) detection limit in the range of 0.02-0.15 μg L.sup.−1, preferably 0.04-0.12 μg L.sup.−1, preferably 0.05-0.10 μg L.sup.−1, preferably 0.06-0.08 μg L.sup.−1, or about 0.07 μg L.sup.−1. In a preferred embodiment, the rare earth metal is cerium and the heavy metal ion is Cd(II), and the method has a Cd(II) detection limit in the range of 0.01-0.10 μg L.sup.−1, preferably 0.02-0.08 μg L.sup.−1, preferably 0.03-0.07 μg L.sup.−1, preferably 0.04-0.06 μg L.sup.−1, preferably 0.04-0.05 μg L.sup.−1, or about 0.046 μg L.sup.−1.
[0188] In addition to the sensitivity of the method is preferably highly reproducible. As used herein, relative standard deviation (RSD) or coefficient of variation (CV) refers to a standardized measure of dispersion of a probability distribution or frequency distribution. It is often expressed as a percentage, and is defined as the ratio of the standard deviation to the mean (or its absolute value). The CV or RSD is widely used in analytical chemistry to express the precision and repeatability of an assay, technique, or method. In a preferred embodiment, the method of the present disclosure in any of its embodiments and the rare earth metal impregnated zeolite modified electrode of the present disclosure in any of its embodiments has a reproducibility as measured by a relative standard deviation in the range of 1-5%, preferably 1.5-4%, preferably 1.75-3.5%, preferably 2-3%, preferably 2.2-3.8%.
[0189] According to another aspect, the present disclosure relates to a sensing device. The electrode of the present disclosure described herein in any of its embodiments may be part of (i.e. integrated in) the sensing device which may further comprise an aforementioned reference electrode, counter electrode, or both. A number of voltammetric systems are produced commercially for the determination of specific species that are of interest in industry and research. Although these devices may sometimes be called electrodes, they are in fact more often complete voltammetric cells that are better referred to as sensors. These sensors or sensing devices can be employed for the analysis of various organic and inorganic analytes, preferably heavy metal ions, in various matrices and may take the form of inexpensive and field deployable instrumentation. The sensing device may also include a housing that comprises the electrode of the present disclosure in any of its embodiments and a fluid distribution manifold that comprises a fluid flow path that is in fluid communication with the electrode of the present disclosure in any of its embodiments, the counter electrode, and/or the reference electrode. In certain embodiments, the fluid flow path can bring a fluid comprising at least one analyte, preferably a metal ion, preferably a heavy metal ion, most preferably a Pb(II) and/or Cd(II) heavy metal ion into contact with the electrode of the present disclosure in any of its embodiments for sensing.
[0190] In certain embodiments, the sensing device may be in communication with at least one readout device that may generally be capable of measuring the current and/or potential at the electrode of the present disclosure in any of its embodiments. In most preferred embodiments, the readout device may be a set of electronics. An electronic readout device, for example, may be capable of detecting current changes. Moreover, the readout device may be a component of the sensing device or may be remotely separated from the sensing device. Furthermore, the readout device may also be linked to an adapter that can interface with a controller device. Preferably, a readout circuit is employed to enable determination of the presence and/or amount of an analyte, preferably a heavy metal ion, and may form part of the readout device.
[0191] In certain embodiments, the readout circuit may be configured to measure the current and/or the potential at the rare earth metal impregnated zeolite described herein. Further, the readout circuit may also be configured to indicate the current and/or potential value(s) to a user of the sensing device such that said user can detect the presence of the analyte, preferably a heavy metal ion, and quantify it based on this measurement. In certain embodiments, to achieve this, the readout circuit may comprise an electronic display and/or loudspeaker or other interface for presenting the current and/or potential value(s) to the user, and may further comprise a transmitter and/or transceiver for transmitting the data to another device. This latter feature is envisaged to enable the user to monitor the environment from a remote location. In another embodiment, the readout circuit may be configured to determine the presence and/or amount of analyte, preferably a heavy metal ion, using the current and/or potential value(s) and indicate the result to the user, with or without the current and/or potential value(s). In such embodiments, the user is provided with the end result without requiring derivation from the raw data.
[0192] In certain embodiments, the practice of this analysis may be performed by a processor in combination with a storage medium. For example, a processor may be configured to receive the current and/or potential value(s) from the readout circuit and compare this with predetermined calibration data (i.e. predetermined measurements of current and/or potential difference versus analyte concentration) from the storage medium to determine the presence and/or amount of analayte.
[0193] It is equally envisaged that the method, detectors and sensors described herein may be adapted to a variety of electroanalysis, including, but not limited to, the determination of inorganic ions, complex species, and molecules including, but not limited to, noble metals, heavy metals, metalloids, metals of the iron, manganese, chromium, and vanadium groups, platinum metals and uranium, metal of the fourth and third groups, metals of rare earths, metals of alkaline earths and alkaline metals, non-metallic ions, complexes, and neutral molecules, the determination of organic substances and environmental pollutants, pharmaceutical and clinical analysis, and the determination of biologically important compounds including, but not limited to alcohols, aldehydes, ketones and acids, amino compounds (i.e. amides, amines, amino acids), antioxidants and phenolic compounds, carbohydrates and related compounds, coenzymes, enzymes, proteins and related compounds, hormones, phytohormones and related compounds, purines, pyridines, and pyrimidines, vitamins, and to employ whole cells, microorganisms, tissues, and tissue extracts as modifiers.
[0194] The present embodiments are being described with reference to specific example embodiments included to illustrate not limit the scope of the invention. The examples below are intended to further illustrate methods protocols for preparing and characterizing the rare earth metal impregnated zeolite modified electrodes of the present disclosure. Further, they are intended to illustrate assessing the properties and applications of these electrodes. They are not intended to limit the scope of the claims.
Example 1
General Materials and Methods of Characterization for Prepared Electrodes
[0195] All solvent and reagents used were of standard purity and of analytical grade. The chemicals include: NaOH (PRS codex, Panreac Qumica), silica gel (pore size 60 {acute over (Å)}, 70-230 mesh, Sigma-Aldrich), colloidal silica (LUDOS, 40 wt %, Sigma-Aldrich), sodium silicate (reagent grade, Lot: MKBG3583, Sigma-Aldrich), fumed silica (175-225 m.sup.2/g surface, 99.8%, Sigma-Aldrich), NaAlO.sub.2 (anhydrous, Sigma-Aldrich), NaH.sub.2PO.sub.4 and Na.sub.2HPO.sub.4 (fluka), K.sub.4Fe(CN).sub.6 (BDH chemicals), KCl (anhydrous, Sigma-Aldrich), phosphoric acid (BDH, analar grade), NH.sub.4OH (Fisher scientific), H.sub.2SO.sub.4 (Panreac Quimica), glacial acetic acid and ammonium acetate (Fisher scientific). Solutions of Pb(II) and Cd(I) were prepared from 1000 ppm stock solutions (spectroscopic grade, BDH chemicals). All solutions were freshly prepared with double distilled water obtained from labstrong nanopure water distiller (Thermoscientific).
[0196] Powder X-ray diffraction (XRD) pattern of the crystal was recorded on Rigaku miniflex II X-ray diffractometer using CuKα radiation (?=1.5418 {acute over (Å)}) with 20 from 5° to 50° and a scanning step of 0.02. Morphology of the crystal was obtained by field emission scanning electron microscopy (FESEM) LYRA 3 dual beam, Tescan. Samples were coated with gold prior to analysis. Solid state .sup.27Al and .sup.29Si MAS NMR were carried out on a JEOL Lambda-500 Multi Nuclear Magnetic Resonance spectrometer with a solid state MAS probe. The .sup.29Si MAS Spectra were taken at a pulse interval of 10 s with 20,000 scans per sample and a spin of 4 kHz. The spectra were processed with 40 Hz line broadening and chemical shifts were determined relative to TMS as an external reference. Electrochemical experiments were performed on a CHI 760E electrochemical work station (CH instruments, US). An Ag/AgCl electrode was used as reference electrode and a platinum wire as the auxiliary electrode. The working electrode was a carbon paste electrode modified or unmodified with zeolite.
[0197] The present disclosure will be better understood with reference to the following abbreviations: atomic absorption spectrometry (AAS), anodic stripping voltammetry (ASV), cyclic voltammetry (CV), cathodic stripping voltammetry (CSV), chemically modified electrode (CME), differential pulse voltammetry (DPV), dropping mercury electrode (DME), double deionized water (DDW), environmental protection agency (EPA), energy dispersive X-ray spectrometry (EDX), fluid catalytic cracking (FCC), graphite furnace atomic absorption spectrometry (GFAAS), inductively coupled plasma optical emission spectrometry (ICP-OES), inductively coupled plasma mass spectrometry (ICP-MS), international zeolite association (IZA), linear sweep voltammetry (LSV), limit of detection (LOD), maximum contaminant level (MCL), mordenite (MOR), magic angle spinning (MAS), normal pulse voltammetry (NPV), nuclear magnetic resonance spectrometry (NMR), parts per million (ppm), parts per billion (ppb), rare earth (RE), revolutions per minute (rpm), square wave voltammetry (SWV), scanning electron microscopy (SEM), square wave anodic stripping voltammetry (SWASV), working electrode (WE), X-ray diffraction spectrometry (XRD), zeolite modified electrode (ZME), and zeolite modified carbon paste electrode (ZMCPE).
Example 2
General Fabrication of Prepared Electrodes
[0198] In one step the mordenite zeolite (MOR) was synthesized. A gel having the molar composition 6Na.sub.2O:Al.sub.2O.sub.3:30SiO.sub.2:780H.sub.2O was synthesized according to the following procedure; 2.10 g of NaOH was dissolved in 20 g of double deionized water (DDW). To this solution, 0.63 g of NaAlO.sub.2 was added and the mixture was stirred until dissolution. Thereafter, 34.13 g of DDW was added while stirring. Finally, 6.95 g of SiO.sub.2 was added and the mixture was stirred for 1 hour (aging time). The resulting gel was then transferred to a Teflon-lined stainless steel autoclave and crystallization was carried out under hydrothermal conditions at 180° C. for 48 h. The material resulting after crystallization was centrifuged and washed with DDW until the pH dropped below 9. The sample was allowed to dry overnight at room temperature in order to obtain the crystal powder. The crystal was calcined at 550° C. to expel all organic matter present. The zeolite whose molar composition was 6Na.sub.2O:Al.sub.2O.sub.3:30SiO.sub.2:780H.sub.2O was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and nuclear magnetic resonance (NMR).
[0199] This zeolite was further impregnated with rare earth metal. An appropriate amount of the metal precursors (La(NO.sub.3).sub.3.6H.sub.2O and/or Ce(NO.sub.3).sub.3.6H.sub.2O) required to make 2 wt %, 5 wt % and 10 wt % of La and/or Ce impregnated zeolites was dissolved in ethanol (40 g) and was mixed with 2 g of the prepared mordenite zeolite under vigorous stirring. The resulting slurry was dried overnight in a fume hood and was later calcined at 550° C. for 4 h in static air (temperature ramp 20° C./min). The metal impregnated zeolite was used in the fabrication of the final electrode.
[0200] The zeolite modified carbon paste electrode (ZMCPE) was prepared by mixing an appropriate amount of graphite, zeolite and paraffin oil in order to form a paste according to various ratios as described below. The paste was packed into the end of the tip of a micropipette (40 mm long, 0.1 mm in diameter) with copper wire as an electrical contact. The electrode was renewed after every experiment by packing in a fresh paste and smoothening by polishing the surface on a weighing paper. Bare carbon paste electrode was prepared in the same manner without the addition of zeolite (graphite and paraffin oil only) and was used for comparison.
Example 3
Synthesis and Characterization of a Prepared Lanthanum Impregnated Zeolite Modified Carbon Paste Electrode (La-ZMCPE)
[0201] Mordenite with different silica to alumina ratios was synthesized hydrothermally in the absence of organic template as previously described and investigated by X-ray diffraction (XRD). The XRD pattern is shown in
[0202] Several morphologies of this crystal have been synthesized in the literature, which includes; spherical, circular pie, flat prism, ellipsoidal, hexagonal star-like prism and the like [Mao, Y., et al., Morphology-controlled synthesis of large mordenite crystals. New Journal of Chemistry, 2014. 38(7): p. 3295-3301.—incorporated herein by reference in its entirety]. Scanning electron microscopy (SEM) micrographs of the prepared mordenite crystals are shown in
[0203] Following characterization of the MOR-15 mordenite zeolite, it was impregnated with 2 wt % lanthanum (La) and energy dispersive X-ray (EDX) spectroscopy was performed. The EDX results (Table 3 and
TABLE-US-00003 TABLE 3 Energy dispersive X-ray (EDX) results for La-MOR-15 Oxygen Aluminum Silicon Lanthanum Total Spectrum (wt %) (wt %) (wt %) (wt %) (wt %) Mean 56.48 4.39 37.45 1.68 100
Example 4
Electrochemical Characterization of a Prepared Lanthanum Impregnated Zeolite Modified Carbon Paste Electrode (La-ZMCPE)
[0204] Cyclic voltammetry was employed for the investigation of the electrochemical properties of the zeolite modified carbon paste electrode (ZMCPE) synthesized as previously described where 10 mM potassium ferrocyanide (K.sub.4Fe(CN).sub.6) and 0.1 M KCl were used as the electroactive specie and the supporting electrolyte, respectively. The La-impregnated zeolite (La-MOR-15, La-ZMCPE) and the unmodified zeolite (MOR-15, ZMCPE) were mixed separately with carbon graphite and paraffin oil in the ratios shown in Table 4 to obtain five composite electrodes (A, B, C, D, and E). The resulting homogeneous paste was packed into the tip of a micropipette and cyclic voltammetry was carried out in potassium ferrocyanide. The cyclic voltammograms show that composite electrode (B) with the ratio 65:5:30 (graphite:zeolite:paraffin) has the highest anodic peak current as show in
TABLE-US-00004 TABLE 4 Composite ratio of prepared zeolite modified carbon paste electrodes Graphite Zeolite Paraffin Designation (wt %) (wt %) (wt %) A 70 0 30 B 65 5 30 C 60 10 30 D 55 15 30 E 50 20 30
[0205] The obtained results demonstrated reproducible anodic and cathodic peaks ascribed to Fe(CN).sub.6.sup.3−/Fe(CN).sub.6.sup.4− redox couples at the surface of the zeolite modified carbon paste electrode. This was confirmed to be a quasi-reversible system that showed a peak separation potential (ΔEp=Ep.sub.a−Ep.sub.c) equal to 163 mV (0.294-0.131) which is greater than the 59 mV often seen for reversible systems [Hassaninejad-Darzi, S. and M. Rahimnejad, Electrocatalytic oxidation of methanol by ZSM-5 nanozeolite-modified carbon paste electrode in alkaline medium. Journal of the Iranian Chemical Society, 2014. 11(4): p. 1047-1056.—incorporated herein by reference in its entirety].
[0206] In order to determine the electroactive surface area of the composite electrodes, the scan rate was varied from 5 to 400 mV s.sup.−1 for both the bare carbon paste (composite A) and the La-MOR-15 electrodes.
[0207] The electroactive surface area of the composite electrodes was estimated from the slope of plots of peak current versus the square root of scan rate using the Randles-Sevcik equation as given by formula (II)
i.sub.p=(2.69×10.sup.5)n.sup.3/2AD.sup.1/2v.sup.1/2C (II):
In this equation, n is the number of electrons, v is the scan rate, D is the diffusion coefficient (cm.sup.2 s.sup.−1) of the electroactive species, A is the area of the working electrode, and C is the electrolyte concentration in mol L.sup.−1. The electroactive surface area estimated for the composite electrodes are 21.4 mm.sup.2 and 25.9 mm.sup.2 for composites A and B, respectively. It can be concluded that modifying the carbon paste electrode with a lanthanum impregnated zeolite (i.e. La-MOR-15) leads to an increase in the electroactive surface area of the electrode.
Example 5
Voltammetric Determination of Cd(II) at a Prepared Lanthanum Impregnated Zeolite Modified Carbon Paste Electrode (La-ZMCPE)
[0208] The electrode of composite B as previously described (i.e. La-MOR-15 composite electrode with a graphite:zeolite:paraffin ratio of 65:5:30) was applied to the determination of Cd(II) ions in 0.1 M phosphate buffer (pH=4) using square wave anodic stripping voltammetry with constant stirring at 600 rpm during the accumulation of the analyte. Accumulation parameters such as accumulation potential and accumulation time were evaluated before carrying out the Cd determination.
[0209] Accumulation potential and accumulation time are crucial parameters when carrying out an anodic stripping voltammetric determination of metal ions such as the Cd(II) ion. This is because unless an appropriate potential is applied to enable the reduction and pre-concentration of the metal ions onto the surface of the working electrode prior to stripping, the sensitivity of the electrode is greatly affected. The effect of accumulation potential was studied by Kokkinos, et al. [Kokkinos, C., et al., Lithographically fabricated disposable bismuth-film electrodes for the trace determination of Pb(II) and Cd(II) by anodic stripping voltammetry. Electrochimica Acta, 2008. 53(16): p. 5294-5299.—incorporated herein by reference in its entirety]. This study demonstrated that choosing a high potential (in the negative direction) leads to background hydrogen evolution. In addition, an accumulation potential which is too low is insufficient to reduce the metal onto the surface of the electrode before being stripped.
[0210] For the current procedure, evaluation was carried out in a 500 ppb Cd(II) solution in 0.1 M phosphate buffer (pH=4) and the accumulation potential was varied from −1.4 V to −0.6 V.
[0211] In a similar manner, the accumulation time was varied from 20 seconds to 200 seconds.
[0212] After the evaluation of the different parameters, the stripping of Cd (II) over two different concentration ranges of 50-500 ppb (
[0213] The performance parameters of the current lanthanum impregnated zeolite (i.e. La-MOR-15) modified carbon paste electrode compare favorably with other electrodes for the detection of Cd(II) that have been reported previously (Table 5) [Rico, M. Á. G., M. Olivares-Marin, and E. P. Gil, Modification of carbon screenprinted electrodes by adsorption of chemically synthesized Bi nanoparticles for the voltammetric stripping detection of Zn(II), Cd(II) and Pb(II). Talanta, 2009. 80(2): p. 631-635; and El Tall, O., et al., Anodic Stripping Voltammetry of Heavy Metals at Nanocrystalline Boron-Doped Diamond Electrode. Electroanalysis, 2007. 19(11): p. 1152-1159; and {hacek over (S)}vancara, I., et al., Recent Advances in Anodic Stripping Voltammetry with Bismuth-Modified Carbon Paste Electrodes. Electroanalysis, 2006. 18(2): p. 177-185; and Siriangkhawut, W., et al., Sequential injection monosegmented flow voltammetric determination of cadmium and lead using a bismuth film working electrode. Talanta, 2009. 79(4): p. 1118-1124; and Kefala, G. and A. Economou, Polymer-coated bismuth film electrodes for the determination of trace metals by sequential-injection analysis/anodic stripping voltammetry. Analytica Chimica Acta, 2006. 576(2): p. 283-289; and Lee, G.-J., H.-M. Lee, and C.-K. Rhee, Bismuth nano-powder electrode for trace analysis of heavy metals using anodic stripping voltammetry. Electrochemistry Communications, 2007. 9(10): p. 2514-2518.—each incorporated herein by reference in its entirety]. The current electrode compares well and in fact has one of the lowest detection limits for Cd(II) detection. The reproducibility of the stripping analysis of 50 ppb Cd (II) at the lanthanum impregnated zeolite (i.e. La-MOR-15) modified carbon paste electrode was also examined by carrying out five consecutive measurements with a single electrode. The relative standard deviation (RSD) was found as 2.7% implying that electrode is stable with reproducible Cd (II) detection ability (
TABLE-US-00005 TABLE 5 Detection limits and performance parameters of previously reported electrodes Detection Electrode Accumulation Accumulation Limit Type Analyte Technique Potential (V) Time (s) (μg/L) Ref. Carbon Cd(II) SWASV −1.4 120 1.3 Rico, et al. screen printed electrode modified by Bi- nanoparticle Boron-doped Cd(II) DPASV −1.7 60 0.36 El Tall, et al. diamond electrode Bi-modified Cd(II) SWASV −0.95 120 1.0 Svancara, et al. carbon paste electrode Bi-film Cd(II) SWASV −1.10 90 1.4 Siriangkhawut, electrode et al. Nafion- Cd(II) SWASV −1.4 — 2.0 Kefala, et al. coated Bi- film electrode Bi nano- Cd(II) SWASV −1.2 180 0.07 Lee, et al. powder electrode
Example 6
Synthesis and Characterization of a Prepared Lanthanum or Cerium Impregnated Zeolite Modified Carbon Paste Electrode (La/Ce-ZMCPE)
[0214] Mordenite zeolite with a silica to alumina ratio of 15 was synthesized by the sol-gel method. The resulting crystal was investigated by X-ray diffraction (XRD) spectroscopy in order to ascertain its crystallinity.
[0215] The energy-dispersive X-ray spectroscopy (EDX) result of the prepared mordenite (MOR-15) sample (
TABLE-US-00006 TABLE 6 Weight percent of elements of prepared mordenite zeolite (MOR-15) Oxygen Aluminum Silicon Total Element (wt %) (wt %) (wt %) (wt %) Mean 55.87 4.68 39.45 100
TABLE-US-00007 TABLE 7 Weight percent of elements of lanthanum impregnated mordenite zeolite (La-MOR-15) Oxygen Aluminum Silicon Lanthanum Total Material (wt %) (wt %) (wt %) (wt %) (wt %) 2 wt % La- 56.48 4.39 37.45 1.68 100 MOR 5 wt % La- 55.99 4.82 36.67 2.51 100 MOR 10 wt % La- 51.28 4.38 36.00 8.34 100 MOR
TABLE-US-00008 TABLE 8 Weight percent of elements of cerium impregnated mordenite zeolite (Ce-MOR-15) Oxygen Aluminum Silicon Cerium Total Material (wt %) (wt %) (wt %) (wt %) (wt %) 2 wt % Ce- 53.46 4.41 39.66 2.47 100 MOR 5 wt % Ce- 56.80 4.27 34.09 4.85 100 MOR 10 wt % Ce- 51.33 4.20 34.46 10.01 100 MOR
[0216] The incorporation of La (III) and Ce (III) ions into the framework of the zeolite was also confirmed by .sup.27Al MAS NMR. .sup.27Al NMR provides information about the environment of the aluminum atoms in the zeolite samples. Aluminum atoms tetrahedrally coordinated to the zeolite framework (Al(OSi).sub.4), appear as a chemical shift at ˜50 ppm, whereas external framework aluminum atoms which are octahedrally coordinated to the framework give a chemical shift signal of ˜0 ppm [Müller, M., G. Harvey, and R. Prins, Quantitative multinuclear MAS NMR studies of zeolites. Microporous and Mesoporous Materials, 2000. 34(3): p. 281-290.—incorporated herein by reference in its entirety]. In strongly dealluminated zeolite samples, a further peak is usually observed between 30 and 50 ppm, and this has been assigned in the literature to penta-coordinated aluminum atoms as wells as distorted tetrahedrally coordinated aluminum atoms in the external framework [Gilson, J.-P., et al., Penta-co-ordinated aluminium in zeolites and aluminosilicates. Journal of the Chemical Society, Chemical Communications, 1987(2): p. 91-92; and Samoson, A., et al., Quantitative high-resolution 27A1 NMR: tetrahedral nonframework aluminium in hydrothermally treated zeolites. Chemical Physics Letters, 1987. 134(6): p. 589-592.—each incorporated herein by reference in its entirety]. The results of the NMR analysis in this process indicates that the two peaks corresponding to the tetrahedral and octahedral aluminum atoms were both obtained for the parent unmodified zeolite and the rare earth metal impregnated zeolites. However, as the metal loading increases, the intensities of the peaks decreases implying that the ratio of the Al atoms have decreased as a result of the incorporation of the metals.
Example 7
Electrochemical Characterization of a Prepared Lanthanum or Cerium Impregnated Zeolite Modified Carbon Paste Electrode (La/Ce-ZMCPE)
[0217] The electrochemical behavior of the lanthanum/cerium modified mordenite zeolite (La/Ce-MOR) was investigated by the construction of a La/Ce-zeolite modified carbon paste electrode (La/Ce-ZMCPE) for the square wave anodic stripping voltammetric detection of Pb(II) and Cd(II) ions in aqueous solutions. Preliminary measurements were carried out in order to screen out appropriate electrodes since for each metal (La and Ce), three different loadings were synthesized (2, 5 and 10 wt %). It was therefore necessary to screen out the electrodes in order to obtain the one which would give the maximum detection ability. For the preliminary measurements, electrodes were constructed in the ratio of 50:25:25 (graphite:zeolite:paraffin) and the square wave anodic stripping experiments were carried out in 500 ppb Pb(II) solution in 0.1 M phosphate buffer (pH=4).
[0218] In contrast, the electrochemical behavior of the Ce-ZMCPE was the reverse of that of the La-ZMCPE as the square wave stripping peak increases as the metal loading increases, with 10 wt % Ce giving the highest peak.
[0219] Having selected the two most effective composite electrodes (2 wt % La-ZMCPE and 10 wt % Ce-ZMCPE) further screening was carried out by varying the ratio of the composite materials (graphite, zeolite, and paraffin oil). Ten composites were fabricated according to Table 9.
TABLE-US-00009 TABLE 9 Composite ratio of prepared zeolite modified carbon paste electrodes 2 wt % La-ZMCPE (A-E) and 10 wt % Ce-ZMCPE (F-J) Composite Designation Graphite Zeolite Paraffin oil A 70 0 30 B 65 5 30 C 60 10 30 D 55 15 30 E 50 10 30 F 70 0 30 G 65 5 30 H 60 10 30 I 55 15 30 J 50 20 30
[0220] The effects of the supporting electrolyte and its pH were also evaluated. A series of buffer solutions as supporting electrolytes were tested for their suitability in the detection of analytes in this procedure. The buffers include; 0.1 M acetate buffer; 0.1 M phosphate buffer; and 0.1 M sulfate buffer all at pH=4.
[0221] Square wave stripping voltammograms were also recorded at different pH values in 0.1 M phosphate buffer at composite B and composite G electrodes. The pH was varied between 3 and 8 by adjusting the buffer with H.sub.3PO.sub.4 and NaOH, respectively, until the desired pH value was reached. The pH of the electrolyte is important to the electroanalytical behavior of the composite electrodes.
Example 8
Voltammetric Determination of Pb(H) at a Prepared Lanthanum or Cerium Impregnated Zeolite Modified Carbon Paste Electrode (La/Ce-ZMCPE)
[0222] In order to maximize the peak current with good resolution and a minimum peak width, the amplitude and frequency of the square wave were evaluated. Amplitude was varied from 0.05 V to 0.5 V at both composite B and composite G electrodes, while frequency was varied from 20 Hz to 200 Hz at the composite B electrode and 20 Hz to 180 Hz at the composite G electrode. It was observed that as the amplitude increases, the peak current also increases with a slight shift in peak potential until it reaches an apex at 0.3 V at the composite B electrode and 0.2 V at the composite G electrode. However, a broadened peak was obtained at those amplitudes. Therefore, a compromise was made in order to obtain a good resolution, a less broadened peak, and a maximum peak current. As a result, amplitudes of 0.1 V and 0.2 V were selected for composite B and composite G electrodes respectively.
[0223] In the same manner when the frequency was varied there was a corresponding increase in the peak current.
[0224] The effect of deposition potential of the analyte onto the surface of the working electrode was evaluated by varying the deposition potential from −1.6 V to −0.4 V at the composite B electrode and −1.4 V to −0.4 V at the composite G electrode. Deposition potential is one of the essential experimental parameters while carrying out stripping voltammetric determination of analytes such as Pb(II) ions. This is because unless an appropriate potential is applied to enable the reduction and deposition of the metal ions onto the surface of the electrode, the sensitivity of the electrode is greatly affected. The effect of deposition potential was studied elsewhere, and it was demonstrated that choosing a high potential in the negative direction leads to background hydrogen evolution which interferes with the analyte's signal. At the same time, too low of a potential is not enough to bring about the reduction of the metal ions. Therefore, the deposition potential needs to be evaluated to ensure that no hydrogen evolution occurs while also ensuring a reasonable amount of the analyte is deposited on the working electrode before being stripped. From the results of the square wave stripping analysis peak current at the composite B electrode (
[0225] The deposition time dependence on the peak height was also examined for both composite B and composite G electrodes by varying the deposition time from 20 seconds to 180 seconds. It is generally accepted that lower detection limits can be reached with longer deposition times. However, longer deposition times can alter the surface of the electrode thereby affecting its analytical performance, as was evidenced in this procedure.
TABLE-US-00010 TABLE 10 Summary of advantageous square wave anodic stripping voltammetry parameters for determination of Pb(II) Composite Amplitude Frequency Deposition Deposition Electrode (V) (Hz) Potential (V) Time (sec) B 0.1 60 −1.2 120 G 0.2 40 −1.2 120
[0226] Calibration curves were constructed for anodic stripping voltammetric detection of Pb(II) ion at the composite B and composite G electrodes over two concentration ranges (50-500 ppb and 5-50 ppb).
TABLE-US-00011 TABLE 11 Summary of results for Pb(II) detection at a prepared lanthanum or cerium impregnated zeolite modified carbon paste electrode (La/Ce-ZMCPE) Limit of Composite Detection (LOD) Sensitivity Electrode Analyte R.sup.2 (ppb) (μA L μg.sup.−1) La-ZMCPE Pb(II) 0.9988 0.225 0.051 (Composite B) 0.9991 Ce-ZMCPE Pb(II) 0.9994 0.07 0.047 (Composite G) 0.9989
[0227] The results from both the composite B and composite G electrodes were subjected to the F test in order to check the precision among them (Table 12). The F test compares the variances of the two methods (or the two composites in this case) and allows a conclusion to be drawn as to whether the results obtained agree with one another. For the composite electrodes evaluated in the present disclosure, it was found that at a 95% confidence level, there was no significant difference between the currents obtained for Pb(II) detection at both composites.
TABLE-US-00012 TABLE 12 F test results for precision of prepared lanthanum or cerium impregnated zeolite modified carbon paste electrodes (La/Ce-ZMCPEs) F-Test Two Sample for Variances Ce-ZMCPE La-ZMCPE (Composite G) (Composite B) Mean 12.89 12.17 Variance 258.24 189.52 Observations 12 12 Degree of freedom 11 11 F 1.36 P (F <= f) 0.308 F Critical 2.81
[0228] The reproducibility of the stripping analysis for Pb(II) at both composite B and composite G electrodes was also checked by carrying out five consecutive measurements with a single electrode. The relative standard deviation (RSD) for both composites was found as 3.02% for the composite B electrode and 2.23% at the composite G electrode, implying good reproducibility of the electrodes for Pb(II) detection. When comparing the analytical performance of the electrodes in the current study with other electrodes that have been reported previously, it was found that the composites of the present disclosure compare favorably among other composites reported in the literature. Table 13 summarizes a comparison of the level of detection (LOD) of the composite electrodes of the present disclosure with other composites from the literature.
TABLE-US-00013 TABLE 13 Comparison of detection limits of a prepared lanthanum or cerium impregnated zeolite modified carbon paste electrode (La/Ce-ZMCPE) with previously reported composite electrodes Detection Electrode Metal Limit Type detected Technique (ppb) Ref. La-ZMCPE Pb(II) SWASV 0.225 Current Ce-ZMCPE Pb(II) 0.07 Disclosure Carbon screen Pb(II) SWASV 0.9 Rico, et al. printed electrode modified by Bi- nanoparticle Boron-doped Pb(II) DPASV 1.15 El Tall, et al. diamond electrode Bi-modified carbon Pb(II) SWASV 0.8 Svancara. et al. paste electrode Bi-film electrode Pb(II) SWASV 6.9 Sirianglthawut, et al. Nafion-coated Bi- Pb(II) SWASV 2 Kefala, et al. film electrode Bi nano-powder Pb(II) SWASV 0.15 Lee, et al. electrode
Example 9
Simultaneous Detection of Pb(II) and Cd(II) at a Prepared Lanthanum or Cerium Impregnated Zeolite Modified Carbon Paste Electrode (La/Ce-ZMCPE)
[0229] To further investigate the sensitivities of the composite electrodes of the present disclosure, simultaneous detection of two metal ions Pb(II) and Cd(II) was carried out. The aim of this was to investigate if the detection of a given analyte interferes with the detection of the other analyte.
TABLE-US-00014 TABLE 14 Summary of results for simultaneous Cd (II) and Pb(II) determination at a prepared lanthanum or cerium impregnated zeolite modified carbon paste electrode (La/Ce-ZMCPE) LOD Sensitivity Composite Analyte R.sup.2 (ppb) (μA L μg.sup.−1) La-ZMCPE Cd(II) 0.9985 0.122 0.1785 (Composite B) Pb(II) 0.9978 0.240 0.1287 Ce-ZMCPE Cd(II) 0.9976 0.046 0.0861 (Composite G) Pb(II) 0.9978 0.045 0.0717
[0230] In conclusion, rare earth impregnated zeolite modified carbon paste electrodes (RE-ZMCPEs) were successfully investigated as an alternative electrode for the anodic stripping voltammetric determination of Pb(II) and Cd(II) ions. Prior to the fabrication of the RE-ZMCPEs, mordenite zeolite with a silica to alumina ratio of 15 was synthesized and characterized by XRD, SEM, EDX, and NMR, the results of which show that a flat prismic crystal was obtained with an average crystal size of 6.8 rpm. Preliminary screening of the fabricated electrodes showed that the electrodes with 2 wt % La impregnation at 10 wt % Ce impregnation, and a composite ratio of 65:5:30 (graphite to zeolite to paraffin) gave a desired peak height and were thus adopted for this procedure. Deposition of the heavy metal ion or analyte of interest onto the surface of the electrodes was accomplished by holding the electrode at a potential of −1.2 V (compared to Ag/AgCl) for 120 seconds followed by a square wave stripping scan from −1.6 to 0 V. Calibration curves for Pb(II) and Cd(II) gave a linear relationship at both composite electrodes with correlation coefficients of 0.9978 and 0.9985 for Pb(II) and Cd(I) at La-ZMCPE and 0.9978 and 0.9976 at Ce-ZMCPE for Pb(II) and Cd(II), respectively and detection limits of 0.225 μg L.sup.−1, and 0.122 μg L.sup.−1 at the La-ZMCPE for Pb(II) and Cd(II) detection, and 0.07 μg L.sup.−1, and 0.046 μg L.sup.−1 at the Ce-ZMCPE for Pb(II) and Cd(II) detection, respectively. The reproducibility of the composite electrodes investigated by carrying out five consecutive runs using a single electrode gave a relatively good precision with RSD values of 3.02% and 2.23% for La-ZMCPE and Ce-ZMCPE for Pb(II) detection respectively. Based on the results of the calibration plots, limits of detection, sensitivities and reproducibility, the composite electrodes in this disclosure demonstrate the ability of being used for analysis of environmental samples such as drinking water due to their inexpensiveness and ease of fabrication as well as lack of toxicity compared to mercury based electrodes used in stripping analysis.
[0231] Thus, the foregoing discussion discloses and describes merely exemplary embodiments of the present invention. As will be understood by those skilled in the art, the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. Accordingly, the disclosure of the present invention is intended to be illustrative, but not limiting of the scope of the invention, as well as other claims. The disclosure, including any readily discernible variants of the teachings herein, defines, in part, the scope of the foregoing claim terminology such that no inventive subject matter is dedicated to the public.