MANUFACTURING METHOD OF A SLIDER

Abstract

A manufacturing method of a slider includes steps of: (a) providing a row bar with a plurality of slider elements connecting together; (b) lapping surfaces of the row bar so as to obtain a predetermined requirement; (c) lowering the temperature of the surfaces lapped in the step (b) before and/or during lapping; and (d) cutting the row bar into a plurality of sliders. The present invention can prevent a local high temperature generated on the magnetic head during lapping so that the performance of the magnetic head is improved.

Claims

1. A manufacturing method of a slider, comprising steps of: (a) providing a row bar with a plurality of slider elements connecting together; (b) lapping surfaces of the row bar so as to obtain a predetermined requirement; (c) lowering the temperature of the surfaces lapped in the step (b) before and/or during lapping, and controlling the temperature of the surfaces in a range of 0° C.˜15° C.; and (d) cutting the row bar into a plurality of sliders.

2. The manufacturing method of a slider according to claim 1, wherein the temperature of the surface is in a range of 5° C.˜15° C.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0030] The accompanying drawings facilitate an understanding of the various embodiments of this invention. In such drawings:

[0031] FIG. 1 is an ABS view of a conventional CPP-TMR element read head;

[0032] FIG. 2 schematically illustrates a manufacturing process of a slider according to one embodiment of the present invention;

[0033] FIG. 3 illustrates a wafer provided in the manufacturing process shown in FIG. 2;

[0034] FIG. 4 illustrate a row bar cut down from the wafer shown in FIG. 3;

[0035] FIG. 5a shows an individual slider finally made by the manufacturing method according to the present invention;

[0036] FIG. 5b is a partial cross-section view of the magnetic head of the slider shown in FIG. 5a, which illustrates the structure of a read head of the magnetic head; and

[0037] FIG. 6 is a schematic view of a manufacturing apparatus according to one embodiment of the present invention.

DETAILED DESCRIPTION OF ILLUSTRATED EMBODIMENTS

[0038] Various preferred embodiments of the invention will now be described with reference to the figures, wherein like reference numerals designate similar parts throughout the various views. As indicated above, the invention is directed to a manufacturing method of a slider, which can prevent a local high temperature generated on the magnetic head during lapping so that the performance of the magnetic head is improved.

[0039] The conventional magnetic head for a slider typically includes a read portion for reading data from the disk, and a write portion for writing data into the disk. The read portion is generally formed by a MR read head, specifically, the present description only concentrates on the CPP-TMR read head. Obviously, the persons ordinarily skilled in the art can understand the application of the present invention on the other read heads after reading the following descriptions.

[0040] FIG. 2 schematically illustrates a manufacturing process of a slider according to one embodiment of the present invention, and FIG. 3 and FIG. 4 illustrate a wafer and a row bar made in the manufacturing process shown in FIG. 2, respectively. Hereinafter, the whole manufacturing process of the slider according to the present invention will be schematically described with reference to these figures.

[0041] At first, a wafer process is performed (step 21). In this wafer process, many slider elements with magnetic heads are formed by a thin-film technology on a wafer 20 made of a ceramic material. Each magnetic head is provided with a CPP-TMR read head and an inductive write head.

[0042] Then, a machining process is performed (step 22). In this process, first, the wafer 20 is cut into a plurality of blocks, and then each block is further cut to obtain a plurality of row bars 210. On each row bar 210, a plurality of slider 220 are aligned and arranged. As shown in FIG. 4, the row bar 210 has an ABS 211, a back surface 213 opposite the ABS 211, a bonding surface 212, a bottom surface 214 opposite the bonding surface 212, and two side surfaces 215. Each slider element 220 is provided with a magnetic head 230 embedded therein.

[0043] Then, a necessary and important machining step is performed which is lapping process (steps 23 and 24, at least). For increasing the lapping effect, a coarse grinding will be performed before the fine lapping, concretely, the bottom surface 214 of the row bar 210 is grinded to a predetermined size (step 23). Then, the ABS 211 of the row bar 210 is lapped to control characteristics of the magnetic head 230, for example magnetoresistive height (MR height) of the TMR element. Preferably, the back surface 213 of the row bar 210 can be lapped according to the actual demand. As an improvement of the present invention, it further includes step (25) of lowering the temperature of the surfaces of the row bar 210 before and/or during the surfaces are lapped or grinded.

[0044] This lapping process is performed using a conventional lapping machine including a lapping plate for lapping the row bar 210 and some lapping medium for helping the lapping, for example. The lapping medium may include lapping oil or diamond slurry and the like.

[0045] As one embodiment, the step (25) includes refrigerating the lapping medium which is applied on the lapping plate. Concretely, the lapping oil and/or the diamond slurry are refrigerated before they are supplied to the lapping plate and contacted with the row bar 210, and the lapping medium will be maintained under a lower temperature during lapping process. Preferably, the temperature controlled is in the range of 0° C.˜15° C., such as 5° C.˜10° C.

[0046] Based on the above design, a local high temperature generated on the lapped surfaces including the bottom surface 214, ABS 211 and back surface 213 will be cooled and dispersed by the cooling lapping medium contacted with these lapped surfaces. Thus, the magnetic moment directions or magnetization directions of the part of read head (including AFM layer, and/or hard magnet, and/or free layer, and/or shielding layers) may not disordered or affected by the local high temperature, which improved the stability of the read head. At the same time, little high temperature noises will be generated on the free layer of the read head, thereby the stability of the free layer is further improved, and in turn the reading performance of the magnetic head is improved. Furthermore, the yield of the slider is increased due to less poor sliders are produced.

[0047] As another embodiment, the step (25) may include lowering the temperature of the row bar 210 before and/or during the lapping process. As still another embodiment, the step (25) may include lowering the temperature of the lapping condition. Similarly, the options also can cool or alleviate the local high temperature generated on the lapped surfaces.

[0048] After the lapping process for the lapped surfaces, this row bar 210 is cut to separate into a plurality of individual sliders 220 (step 26). Preferably, during the cutting process, the temperature of the cutting surface is lowered so as to alleviate the local high temperature generated on the cutting surface which may disserve the performance of the read head.

[0049] FIG. 5a show an individual slider 220 with a magnetic head 230 finally made by the manufacturing method mentioned above, and FIG. 5b is a partial cross-section view of the magnetic head 230 of the slider 220, which illustrates the structure of a read head 300 of the magnetic head 230.

[0050] As shown in FIG. 5b, the read head 300 includes a first shielding layer 311 formed on a substrate 310, a second shielding layer 314, and a TMR element 312 sandwiched between the first and second shielding layers 311, 314, and a pair of hard magnets 313 formed on two sides of the TMR element 312.

[0051] Concretely, the TMR element 312 is multiple-layer structure which includes a pinning layer 331, two pinned layers 332, 333, a tunnel barrier layer 334, a free layer 335, and a cap layer 336 stacked together in turn. The pinning layer 331 is formed on the first shielding layer 311, which is made of AFM material, such as NiO or IrMn. The pinned layer 332 has a series of magnetic moment directions 93 perpendicular to the ABS 211 and parallel to the bonding surface 212 of the slider 220. The free layer 335 contains a ferromagnetic substance and has a direction of magnetization 94 that changes in responds to an external magnetic field. The magnetization direction or the magnetic moment 94 of the free layer 335 orients generally parallel to the ABS 211 in the absence of an applied external magnetic field.

[0052] As mentioned above, when lapping the bottom surface 214, ABS 211 and the back surface 213, a local high temperature will be generated on the bottom surface 214, ABS 211 and the back surface 213 which will disorder the magnetic moment directions of the part of the read head 300 (AFM materials, and/or hard magnets 313, and/or free layer, and/or shielding layers 311, 314). Since the temperature of the lapped surfaces is cooled and dispersed by the means described above, thus the magnetic moment directions of the part of the read head 300 (including AFM layer, and/or hard magnet 313, and/or free layer 335, and/or shielding layers 311, 314) are not easy to change and disordered, at the same time, little high temperature noises will generate on the free layer 335 of the TMR element 312, which is beneficial to improve the stability of the read head 300.

[0053] Alternatively, an AFM layer (not shown) may be configured in the side surface 215 of the slider 220 and near the TMR element 312 so as to achieve a certain function (stabilizing the TMR element 312 for example), which has magnetic moment directions which are perpendicular to the bonding surface 212 and parallel to the ABS 211. Regarding to this type of slider, when cutting the row bar 210 along the side surface 215, a local high temperature also will be generated on the side surface 215 which will affect the magnetic moment directions of the second AFM layer arranged perpendicular to the bonding surface 212 and parallel to the ABS 211. Therefore, during the cutting process, because the temperature of the cutting surface is lowered, thus the magnetic moment directions of the AFM layer are maintained in the initial order without disorder, which is beneficial to maintain the stability of the read head 300 as well.

[0054] Accordingly, FIG. 6 shows a manufacturing apparatus used during the manufacturing method described above. The manufacturing apparatus 600 of a slider according to a preferred embodiment of the present invention includes a grinding machine 601, a lapping machine 602, a cooling device 603 and a cutting machine 604. Concretely, the grinding machine 601 is adapted for coarsely grinding the bottom surface 214 of the row bar 210 to a predetermined size. The lapping machine 602 is adapted for lapping the ABS 211 of the row bar 210 to control characteristics of the magnetic head 230, and lapping the back surface 213 of the row bar 210 optionally. The cooling device 603 is adapted for lowering the temperature of the lapped surfaces including the bottom surface 214, ABS 211 and back surface 213 before and/or during grinding and lapping.

[0055] Concretely, the lapping machine 602 includes a fixture (not shown) for clamping and controlling the row bar 210, a lapping plate (not shown) for lapping the row bar 210, and a lapping medium supply device (not shown) for supplying lapping medium on the lapping plate. The lapping medium is abrasives which include lapping oil and/or diamond slurry for example. Furthermore, the lapping medium supply device includes a ceramic ring for homogenizing the lapping medium on the lapping plate.

[0056] More concretely, the cooling device 603 is used for refrigerating the lapping medium and/or the lapping medium supply device. Optionally, the cooling device 603 is further used for lowering the temperature of the row bar 210, and/or lowering the temperature of the lapping condition, and/or lowering the temperature of cutting surfaces of the row bar 210 before and/or cutting the row bar 210.

[0057] Preferably, the temperature of the lapped surfaces controlled by the cooling device 603 in the range of 0° C.˜15° C., such as 5° C.˜10° C. in the present embodiment.

[0058] Based on the above design, a local high temperature generated on the lapped surfaces including the bottom surface 214, ABS 211 and back surface 213 will be cooled and dispersed by the cooling lapping medium contacted with these lapped surfaces or alleviated due to the cooled lapping condition and cooled row bar 210. Thus, the magnetic moment directions or magnetization directions of the part of read head (including AFM layer, and/or hard magnet, and/or free layer, and/or shielding layers) may not disordered or affected by the local high temperature, thereby improving the stability of the read head. At the same time, little high temperature noises will be generated on the free layer of the read head, thereby the stability of the free layer is further improved, and in turn the reading performance of the magnetic head is improved. As a result, stable sliders such as with little noise, little hysteresis and good characteristic curve with little jumps may be produced, finally the yield of the slider is increased due to less poor sliders are produced.

[0059] While the invention has been described in connection with what are presently considered to be the most practical and preferred embodiments, it is to be understood that the invention is not to be limited to the disclosed embodiments, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the invention.