Partial anodizing apparatus and anodizing method using the same

Abstract

An apparatus and a method are disclosed that form an anodic oxide coating on part of the outer surface of a profile having an irregular cross-sectional shape. A partial anodizing apparatus that is used to partially anodize a profile having an irregular cross-sectional shape includes an electrolytic bath that is divided into two or more partial baths. The profile is held using the two or more partial baths so that part of the profile is situated outside the electrolytic bath to form a sealed electrolysis chamber.

Claims

1. A partial anodizing method that partially anodizes an extruded profile having an irregular cross-sectional shape, the method comprising: providing an electrolytic bath that includes: a first partial bath member having an approximately box shape that includes a bottom wall and a sidewall, and being formed of an insulating material, a cathode disposed on an inner side of the first partial bath member, a second partial bath member having an approximately plate shape, and being formed of an insulating material, disposing a first part of the extruded profile on the second partial bath member by way of a seal member, the first part being a first non-anodizing part; joining the first partial bath member and the second partial bath member so that: the extruded profile is sandwiched between the sidewall of the first partial bath member and the seal member formed on the second partial bath member so that a second part of the extruded profile is situated outside an area of the electrolytic bath at which the first partial bath member and the second partial bath member are overlapped with one another in a plan view, the second part being a second non-anodizing part, and an electrolysis chamber having inlets and outlets for an electrolyte solution is formed by the joining of the first partial bath member and the second partial bath member; discharging the electrolyte solution through the inlets; and partially anodizing the extruded profile at locations where a design surface of the extruded profile comes into contact with the electrolyte solution by applying a voltage between the extruded profile as an anode and the cathode while anodizing is not occurring at the first and second non-anodizing parts with which the electrolyte solution does not come into contact.

2. The partial anodizing method as defined in claim 1, the extruded profile being anodized so that 22SJ<30V is satisfied, S being a treatment area (dm.sup.2) in which the extruded profile is partially anodized, J being an electrolysis current density (A/dm.sup.2), and V being a flow rate (I/min) of the electrolyte solution that is circulated through the electrolysis chamber.

Description

BRIEF DESCRIPTION OF DRAWINGS

(1) FIGS. 1A to 1C illustrate an example of the structure of an electrolytic bath according to one embodiment of the invention, wherein FIG. 1A is a cross-sectional view, FIG. 1B is a view A, and FIG. 1C is a view B.

(2) FIG. 2A illustrates a state in which two partial baths are separated, FIG. 2B illustrates a state in which an electrolysis chamber is formed so that a profile is placed therein, and FIG. 2C illustrates a state in which a partially anodized profile has been removed.

(3) FIG. 3A is a cross-sectional view illustrating a state before an electrolytic bath is assembled, FIG. 3B illustrates a state after an electrolytic bath has been assembled, and

(4) FIG. 3C illustrates a state in which an electrolysis chamber is filled with an electrolyte solution.

(5) FIG. 4A illustrates a state in which a profile is anodized, FIG. 4B illustrates a state in which an electrolyte solution 20a is drained after anodizing, and FIG. 4C illustrates a state in which a profile has been removed.

(6) FIG. 5 shows evaluation sample preparation conditions and evaluation results.

DESCRIPTION OF EMBODIMENTS

(7) FIGS. 1A and 4C illustrate an example of the structure of a partial anodizing apparatus according to one embodiment of the invention.

(8) An electrolytic bath 10 can be divided into a first partial bath 11 and a second partial bath 12, the first partial bath 11 having an approximately box-like shape, and being formed of an insulating material, a cathode 13 being disposed on the inner side of the first partial bath 11, and the second partial bath 12 having an approximately plate-like shape, and being formed of an insulating material.

(9) In one embodiment of the invention, a profile 1 is held between one end 11a of the first partial bath 11 and the second partial bath 12. Seal members 11c and 12a are provided to come in contact with the profile 1.

(10) An end 11b of the first partial bath 11 is situated opposite to the second partial bath 12 through the seal member 12a.

(11) Part of the profile 1 that does not form a design surface (i.e., a part 1a for which an anodic oxide coating is unnecessary) is sealed with the second partial bath 12.

(12) An electrolyte solution is introduced into an electrolysis chamber 20 through an inlet 21, and drained through an outlet 22.

(13) The electrolyte solution drained through the outlet 22 is cooled using a cooler or the like, and re-introduced into the electrolysis chamber 20 through the inlet 21 using a circulation device such as a pump.

(14) A plurality of inlets 21 are provided at equal intervals so that the electrolyte solution is uniformly discharged toward the profile 1. A plurality of outlets 22 are provided at equal intervals between the corner of the electrolysis chamber and the inlet 21 so that the electrolyte solution does not remain at the corner of the electrolysis chamber 20.

(15) Anodizing, corrosion resistance, and the like were evaluated as described below using the electrolytic bath.

(16) An aluminum alloy extruded profile was degreased, and subjected to an etching pretreatment according to a normal method. The extruded profile was then anodized in an electrolysis chamber having a given volume using a 200 g/l sulfuric acid aqueous solution as the electrolyte solution for a given time at a given current density.

(17) The temperature of the electrolyte solution is preferably set to 15 to 25° C. so that a hard anodic oxide coating is not formed from the viewpoint of design.

(18) As illustrated in FIG. 2A, the profile 1 was positioned between the first partial bath 11 and the second partial bath 12 so that part of the profile 1 was situated outside the electrolytic bath, and the first partial bath 11 and the second partial bath 12 were assembled as illustrated in FIG. 2B (see also FIGS. 3A and 3B).

(19) FIG. 3C illustrates a state in which the electrolytic bath was filled with the electrolyte solution 20a.

(20) The electrolyte solution that was drained through each outlet 22 was discharged toward the profile 1 through each inlet 21 using a circulation device (not illustrated in the drawings) (see the arrows in FIGS. 1B and 1C).

(21) The electrolysis chamber and the circulation device were connected through a pipe or the like (not illustrated in the drawings).

(22) As illustrated in FIG. 4A, a voltage was applied between the profile 1 (anode) and the cathode 13 to effect electrolysis.

(23) Either direct-current electrolysis or alternating-current electrolysis may be employed. In the examples, direct current was applied.

(24) As illustrated in FIG. 4C, the electrolytic bath 10 was divided into two section after completion of electrolysis, and the profile 1 was removed.

(25) An anodic oxide coating lb had been formed on part of the profile 1.

(26) The profile 1 was then washed with water, and subjected to a boiling water sealing treatment for 20 minutes.

(27) FIG. 5 shows the results of a Corrodkote test performed in accordance with JIS H 8502 (“Methods of corrosion resistance test for metallic coatings”).

(28) In Examples 1 and 2, a profile having a length of 250 mm was used. In Example 1, the volume of the electrolysis chamber was 0.4 l, the circulation flow rate of the electrolyte solution was 40 l/min, and the profile was anodized for 4 minutes at a current density of 10 A/dm.sup.2.

(29) In Example 2, the profile was anodized in the same manner as in Example 1, except that the current density was set to 8 A/dm.sup.2.

(30) In Example 3, the volume of the electrolysis chamber was 1.3 l, and a profile having the same cross-sectional shape as that of the profile used in Examples 1 and 2, and having a length of 800 mm was used.

(31) The treatment conditions are shown in FIG. 5.

(32) In Comparative Example 1, the outlets 22a and 22b were closed. In Comparative Example 2, the flow rate of the electrolyte solution was reduced.

(33) In Examples 1 to 3, the profile had an excellent surface, and the corrosion ratio determined by the Corrodkote test was 10% or less.

(34) In Comparative Example 1, the electrolyte solution stagnated, and local burning occurred. In Comparative Example 2, the value 30V (V: flow rate (1/min)) was smaller than the value 22SJ (S: treatment area (dm.sup.2), J: current density (A/dm.sup.2)), and burning occurred.

INDUSTRIAL APPLICABILITY

(35) The invention is suitable for forming an anodic oxide coating on part of an extruded profile formed of a light alloy, and various products can be produced using an extruded profile obtained by such a treatment.