Examination method to apprais corundum that has undergone beryllium diffusion treatment

Abstract

This invention is within the technical field of corundum appraisal, and it involves an examination method to determine whether corundum has undergone beryllium diffusion treatment. Procedurally, a highly sensitive Raman spectrometer (S/N>10,000) is used to scan and examine the samples. The spectrometer is fitted with a tailor-made probe having a large facula and surface area. Specially developed software is then used to perform an intensity correction and a background elimination to obtain a specific Raman spectral range (250-120 cm-1) with the corrected intensity and a smooth baseline. The corrected and standardized Raman characteristic peak at 804 cm-1 (side-band) is used as a basis to determine whether the corundum has undergone beryllium diffusion treatment. This invention method has the advantages of being non-destructive, simple, fast, and practical. Also, it can accurately determine whether corundum has been treated.

Claims

1. An examination method to appraise corundum that has undergone beryllium diffusion treatment, comprising: providing a Raman spectrometer having a laser beam of wavelength 785 nm and total laser power of 450 mw; three continuous scans being performed using a probe with a large facula and surface area to obtain three spectra, from which an average Raman spectra is determined; defining a collection range of the spectrometer as 250-1200 cm.sup.−1; and after the collection of the Raman spectral data, the intensity being subjected to two operations: (a) correction and standardization, and (b) background elimination that result in a Raman spectrogram with a smooth baseline and enhanced intensity; wherein Raman characteristic peaks for natural corundum occur at 375, 412, 572, 640, and 745 cm.sup.−1, whereas treated corundum has an extra Raman characteristic peak with a raised baseline at 804 cm.sup.−1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic chart illustrating Raman spectra of beryllium diffused corundum of the present invention; and

(2) FIG. 2 is a schematic chart illustrating overlaid Raman spectra for natural and beryllium treated corundum.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

(3) A simple yet intuitive signal of the characteristic peak of the Raman spectra for a rapid examination method to appraise whether corundum has been treated. The procedures comprising the technique are detailed below and illustrated in FIGS. 1 and 2.

(4) The examination method comprises: providing a Raman spectrometer which is highly sensitive (S/N>10,000) and has a laser beam of wavelength 785 nm and total laser power of 450 mw; three continuous scans being performed using a probe with a large facula and surface area to obtain three spectra, from which an average Raman spectra is determined; defining a collection range of the spectrometer as 250-1200 cm.sup.−1; and after the collection of the Raman spectral data, the intensity being subjected to two operations: (a) correction and standardization, and (b) background elimination that result in a Raman spectrogram with a smooth baseline and enhanced intensity; wherein Raman characteristic peaks for natural corundum occur at 375, 412, 572, 640, and 745 cm.sup.−1, whereas treated corundum has an extra Raman characteristic peak with a raised baseline at 804 cm.sup.−1.

(5) As shown in FIGS. 1 and 2, the Raman characteristic peak at 804 cm.sup.−1 (side-band) is indicated by a bold arrow. FIG. 2 is a schematic chart illustrating overlaid Raman spectra for natural and beryllium treated corundum. It is noted that the Raman spectrum for the corundum that has undergone beryllium diffused treatment is indicated by a first line 1, and that for the natural corundum is indicated by a second line 2. The presence of the Raman characteristic peak at 804 cm.sup.−1 (side-band) with a raised baseline can be used to determine whether the corundum has been treated.

(6) Under the proposed method, the Raman spectra of dozens of treated corundum samples were collected (FIG. 1). These were overlaid onto the Raman spectra of natural corundum for comparison (FIG. 2). The Raman peak at 804 cm.sup.−1 (side-band) does not appear for the natural corundum. Thus, it can be used as a basis to appraise whether the corundum has been treated.

(7) The use of the Raman spectra in the proposed invention method has the following advantages: it is non-destructive, there is no requirement for pre-processing, and it allows a rapid analysis. The method can be used to determine whether corundum has undergone beryllium diffusion treatment and is summarized as follows:

(8) (a) The presence of a Raman characteristic peak is used as an indicator that the corundum has been treated. It is a scientific, impartial, and objective appraisal method.

(9) (b) This method can be applied for the appraisal of both loose and inlaid corundum and can be used on corundum samples of all sizes.

(10) (c) Specially developed software and standard samples were used to perform the correction and standardization, as well as the baseline processing. This reduces the slight differences in the intensities of the Raman peaks of the corundum samples between analyses, thereby ensuring data consistency for each analysis.
It is understood that the invention may be embodied in other forms within the scope of the claims. Thus the present examples and embodiments are to be considered in all respects as illustrative, and not restrictive, of the invention defined by the claims.