Apparatus And Method For Selective Laser Sintering An Object With A Void

Abstract

A method of producing an object from a polymer powder using a laser sintering system, whereby the laser sintering system introduces heat energy to solidify select points of a layer of polymer powder according to build data of the object and adjusts the heat energy according to solidification of select points of other layers.

Claims

1. A method of producing an object from a polymer powder using a laser sintering system comprising the steps of: (i) Providing a build data of an object, the build data comprising a plurality of cross-section patterns according to a geometry description data of the object, each cross-section pattern comprising data specifying select points in the cross-section for solidification and each of the select points in a cross-section pattern selected for solidification having a unique position in the cross-section pattern, (ii) applying a layer L.sub.0 of a polymer powder on a bed of a laser sintering system, (iii) solidifying select points of the polymer powder of layer L.sub.0 by a heat energy introduced by electromagnetic radiation according to the cross-section pattern assigned to layer L.sub.0, (iv) adjusting the heat energy introduced by electromagnetic radiation to solidify a select point at a first position (x, y) in the layer L.sub.0 depending on whether the build data specifies solidification of a select point at the first position in one or more of: a previous layer L.sub.−n and a subsequent layer L.sub.+n.

2. The method of claim 1, wherein n is a positive integer and L.sub.−1 is a layer immediately preceding layer L.sub.0, L.sub.−2 is a layer immediately preceding L.sub.−1, and so forth, and L.sub.+1 is the layer immediately subsequent layer L.sub.0, L.sub.+2 is the layer immediately subsequent L.sub.+1, and so forth.

3. The method of claim 2, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of a select point at the first position in the layer L.sub.−n.

4. The method of claim 3, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of a select point at the first position in layer L.sub.−1.

5. The method of claim 4, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of a select point at the first position in layers L.sub.−1, L.sub.−2, and L.sub.−3.

6. The method of claim 2, wherein the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 is reduced if the build data does not specify solidification of a select point at the first position in a layer L.sub.−n.

7. The method of claim 3, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of a select point at the first position in one or more layer L.sub.−n, wherein the one or more layer L.sub.−n is in a heat affected zone.

8. The method of claim 4, wherein in the step of solidifying selected points the heat energy is introduced by laser radiation and the heat energy amount is adjusted at least in party by variation of one or more of a laser light intensity, a deflection velocity of the laser beam, and a variation of the distance between the laser beam tracks on the powder layer.

9. The method of claim 8, wherein the polymer powder has a solid-to-powder ratio of less than 50:1.

10. The method of claim 8, wherein the polymer powder comprises one or more of PEK, PEEK, PEKK, PEEK, PEKEKK.

11. The method of claim 10, wherein the polymer powder comprises PEKK.

12. The method of claim 4, wherein the adjustment of heat energy introduced by electromagnetic radiation to solidify a select point at a first position in the layer L.sub.0 does not depend on whether the build data specifies solidification of points other than the first position in one or more relied upon layer L.sub.−n and layer L.sub.+n.

13. A system for producing an object from a polymer powder, comprising; a housing defining a chamber; a support platform deposed in the chamber and moveable therein along at least one axis for supporting one or more layers of a polymer powder and any part formed therein; a spreader for applying a layer of polymer powder to a bed defined by an upper surface of the support platform or an upper surface of a layer of powder deposed thereon; an irradiation source for irradiating select points in the powdered layer prepared most recently on the support platform; a database for storing build data for an object to be produced, the build data comprising a plurality of cross-section patterns according to a geometry description data, each cross-section pattern comprising data specifying select points in the cross-section for solidification, each of the select points in a cross-section pattern selected for solidification having a unique position in the cross-section pattern; a controller for controlling the irradiation device to solidify select points of the polymer powder of a layer L.sub.0 by a heat energy introduced by controlled electromagnetic radiation via the irradiation device according to the cross-section pattern assigned to the layer L.sub.0 in the build data, and a software executing on the controller for adjusting the heat energy introduced by electromagnetic radiation to solidify a select point at a first position in the layer L depending on whether the build data specifies solidification of a select point at the first position in one or more of: a previous layer L.sub.−n and a subsequent layer L.sub.+n.

14. The system of claim 13, wherein n is a positive integer and L.sub.1 is a layer immediately preceding layer L.sub.0, L.sub.−2 is a layer immediately preceding L.sub.−1, and so forth, and L.sub.+1 is the layer immediately subsequent layer L.sub.0, L.sub.+2 is the layer immediately subsequent L.sub.+1, and so forth.

15. The system of claim 14, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of the select point at the first position in a layer L.sub.−n.

16. The system of claim 15, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of the select point at the first position in layer L.sub.−1.

17. The system of claim 16, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of the select point at the first position in layers L.sub.−1, L.sub.−2, and L.sub.−3.

18. The system of claim 17, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of the select point at the first position in layers L.sub.−1 through L.sub.−5.

19. The method of claim 15, wherein the adjustment to the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depends on whether the build data specifies solidification of a select point at the first position in one or more layer L.sub.−n, wherein the one or more layer L.sub.−n is in a heat affected zone.

20. The method of claim 19, wherein in the step of solidifying selected points the heat energy is introduced by laser radiation and the heat energy amount is adjusted at least in part by variation of one or more of a laser light intensity, a deflection velocity of the laser beam, and a variation of the distance between the laser beam tracks on the powder layer.

21. The method of claim 20, wherein the polymer powder has a solid-to-powder ratio of less than 50:1.

22. The method of claim 20, wherein the polymer powder comprises one or more of PEK, PEEK, PEKK, PEEK, PEKEKK.

23. The method of claim 22, wherein the polymer powder comprises PEKK.

24. The method of claim 16, wherein the adjustment of heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 does not depend on whether the build data specifies solidification of points other than the first position in one or more relied upon layer L.sub.−n and layer L.sub.+n.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0030] FIG. 1 illustrates an LS machine in accordance with one embodiment of the present invention.

[0031] FIG. 2A shows a front view of an object.

[0032] FIG. 2B shows a top view of the object in FIG. 2A.

[0033] FIG. 3A illustrates an over sinter problem associated with known system and methods.

[0034] FIG. 3B illustrates a method used in the prior art to address over sinter.

[0035] FIG. 4A illustrates a plurality of cross-sections corresponding to layers for the manufacture of an object by the LS method.

[0036] FIG. 4B shows a front view of a portion of the object shown in 4A.

[0037] FIG. 4C shows a top view of a portion of the object shown in 4B.

[0038] FIG. 5 illustrates a view of build data used in accordance with the present invention.

[0039] FIG. 6 illustrates a view of build data used in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0040] The present disclosure describes aspects of the present invention with reference to the exemplary embodiments illustrated in the drawings; however, aspects of the present invention are not limited to the exemplary embodiments illustrated in the drawings. It will be apparent to those of ordinary skill in the art that aspects of the present invention include many more embodiments. Accordingly, aspects of the present invention are not to be restricted in light of the exemplary embodiments illustrated in the drawings. It will also be apparent to those of ordinary skill in the art that variations and modifications can be made without departing from the true scope of the present disclosure. For example, in some instances, one or more features disclosed in connection with one embodiment can be used alone or in combination with one or more features of one or more other embodiments.

[0041] The present invention is especially useful for LS with polymer powders. One such class of polymer powders is Polyaryletherketones (“PAEK”) polymers. PAEKs are of interest in the LS process because parts that have been manufactured from PAEK powder or PAEK granulates are characterized by a low flammability, a good biocompatibility, and a high resistance against hydrolysis and radiation. The thermal resistance at elevated temperatures as well as the chemical resistance distinguishes PAEK powders from ordinary plastic powders. A PAEK polymer powder may be a powder from the group consisting of polyetheretherketone (“PEEK”), polyetherketoneketone (“PEKK”), polyetherketone (“PEK”), polyetheretherketoneketone (“PEEKK”) or polyetherketoneetherketoneketone (“PEKEKK”).

[0042] PEKKs are well-known in the art and can be prepared using any suitable polymerization technique, including the methods described in the following patents, each of which is incorporated herein by reference in its entirety for all purposes: U.S. Pat. Nos. 3,065,205; 3,441,538; 3,442,857; 3,516,966; 4,704,448; 4,816,556; and 6,177,518. PEKK polymers differ from the general class of PAEK polymers in that they often include, as repeating units, two different isomeric forms of ketone-ketone. These repeating units can be represented by the following Formulas I and II:

-A-C(═O)—B—C(═O)—  I

-A-C(═O)-D-C(═O)—  II

[0043] where A is a p,p′-Ph-O-Ph-group, Ph is a phenylene radical, B is p-phenylene, and D is m-phenylene. The Formula I:Formula II isomer ratio, commonly referred to as the T:I ratio, in the PEKK is selected so as to vary the total crystallinity of the polymer. The T:I ratio is commonly varied from 50:50 to 90:10, and in some embodiments 60:40 to 80:20. A higher T:I ratio such as, 80:20, provides a higher degree of crystallinity as compared to a lower T:I ratio, such as 60:40.

[0044] The crystal structure, polymorphism and morphology of homopolymers of PEKK have been studied and have been reported in, for example, Cheng, Z. D. et al, “Polymorphism and crystal structure identification in poly(aryl ether ketone ketone)s,” Macromol. Chem. Phys. 197, 185-213 (1996), the disclosure of which is hereby incorporated by reference in its entirety. This article studied PEKK homopolymers having all para-phenylene linkages [PEKK(T)], one meta-phenylene linkage [PEKK(I)] or alternating T and I isomers [PEKK(T/I)]. PEKK(T) and PEKK(T/I) show crystalline polymorphism depending upon the crystallization conditions and methods.

[0045] In PEKK(T), two crystalline forms, forms I and II, are observed. Form I can be produced when samples are crystallized from melting at low supercoolings, while Form II is typically found via solvent-induced crystallization or by cold-crystallization from the glassy state at relatively high supercooling. PEKK(I) possesses only one crystal unit cell which belongs to the same category as the Form I structure in PEKK(T). The c-axis dimension of the unit cell has been determined as three phenylenes having a zig-zag conformation, with the meta-phenylene lying on the backbone plane. PEKK(T/I) shows crystalline forms I and II (as in the case of PEKK(T)) and also shows, under certain conditions, a form III.

[0046] Suitable PEKKs are available from several commercial sources under various brand names. For example, polyetherketoneketones are sold under the brand name OXPEKK® polymers by Oxford Performance Materials, South Windsor, Conn., including OXPEKK®-C, OXPEKK®-CE, OXPEKK®-D and OXPEKK®-SP, OXPEKK®-N, OXPEKK®-ESD polymers. Polyetherketoneketone polymers are also manufactured and supplied by Arkema. In addition to using polymers with a specific T:I ratio, mixtures of polyetherketoneketones may be employed.

[0047] The powders used in these applications are produced by a variety of processes such as grinding, air milling, spray drying, freeze-drying, or direct melt processing to fine powders. The heat treatment can be accomplished before or after the powders are produced, but if treated prior to forming the powders, the temperature of the powder forming process must be regulated to not significantly reduce the melting temperature or the quantity of the crystallinity formed in the heat treatment process.

[0048] Although the present disclosure is provided in reference to PAEK polymers, and more specifically PEKK polymers, the present disclosure is not so limited. A person of ordinary skill in the art and familiar with this disclosure would understand that the present invention may be employed with other types of polymers useful in LS and with other materials useful in LS, including, but not limited to, metals and ceramics.

[0049] In reference to FIG. 1, an LS system 10 in accordance with the present invention is illustrated. The system 10 includes a first chamber 20 having an actuatable piston 24 deposed therein. A bed 22 is deposed at an end of the piston 24. It should be understood that the term bed may refer to the physical structure supported on the piston or the uppermost layer of powder deposed thereon.

[0050] The temperature of the bed 22 can be variably controlled via a controller 60 in communication with heating elements (not shown) in and or around the bed 22. Furthermore, the LS system 10 according to the invention may include a heating device above the bed 22, which preheats a newly applied powder layer up to a working temperature below a temperature at which the solidification of the powder material occurs. The heating device may be a radiative heating device (e.g., one or more radiant heaters) which can introduce heat energy into the newly applied powder layer in a large area by emitting electromagnetic radiation.

[0051] A second chamber 30 is adjacent to the first chamber 20. The second chamber 30 includes a table surface 32 deposed on an end of a piston 34 deposed therein. A powder 36 for use in the LS system 10 is stored in the second chamber 30 prior to the sintering step. It will be understood to a person of ordinary skill in the art and familiar with this disclosure that while a specific embodiment of an LS system is disclosed, the present invention is not limited and different known LS systems may be employed in the practice of the present invention.

[0052] During operation of the LS system 10, a spreader 40 translates across a top surface of the first chamber 20, evenly distributing a layer of powder 36 across either the top surface of the bed 22, or the material previously deposed on the bed 22. The LS system 10 preheats the powder material 36 deposed on the bed 22 to a temperature proximate to a melting point of the powder. Typically, a layer of powder is spread to have a thickness of 125 μm, however the thickness of the layer of powder can be increased or decreased depending on the specific LS process and within the limits of the LS system.

[0053] A laser 50 and a scanning device 54 are deposed above the bed 22. The laser 50 transmits a beam 52 to the scanner 54, which then distributes a laser beam 56 across the layer of powder 36 deposed on the bed 22 in accordance with a build data. The laser selectively fuses powdered material by scanning cross-sections generated from a three-dimensional digital description of the part on the surface of the bed having a layer of the powdered material deposed thereon. The laser 50 and the scanner 54 are in communication with the controller 60. After a cross-section is scanned, the bed 22 is lowered by one layer thickness (illustrated by the downward arrow), a new layer of powdered material is deposed on the bed 22 via the spreader 40, and the bed 22 is rescanned by the laser. This process is repeated until a build 28 is completed. During this process, the piston 34 in the second chamber is incrementally raised (illustrated by the upward arrow) to ensure that there is a sufficient supply of powder 36.

[0054] In reference to FIGS. 2A-2B, an object 100 having a void to be constructed in accordance with the inventive method is shown. FIG. 2A shows a front view of the object 100 and FIG. 2B shows a top view of the object 100. The object 100 is a block. It will be understood that it is possible to manufacture an essentially unlimited number of geometries using the LS layer-wise construction method.

[0055] The block 100 shown in FIGS. 2A-2B is approximately a right prism rectangle. The block 100 has a front surface 120, a top surface 118, a bottom surface 116, a first side surface 112 and a second side surface 114, and a rear surface 122. The block 100 defines a bore 130 that extends through the block along an axis between a first opening 132 in the front surface 120 and a second opening 134 in the rear surface 122. The bore 132 is generally cylindrical. The cross-section of the bore 130 is circular in a cross-section plane being perpendicular to the bore axis. An upper portion 133 of the wall of the bore 130 defines an overhang. The overhang may also be referred to as a downskin. The upper portion 133 is referred to as an overhang because it is above the void in the block 100 as the block 100 is oriented in the construction process. This upper portion 133 may also be referred to as a downskin because during the LS layer-wise construction process the upper portion 133 is sintered in successive layers that are adjacent to previously deposed layers of unsintered powder. Likewise, a lower portion 131 of the wall of the bore 130 defines an underhang. The underhang may also be referred to as an upskin. The lower portion 131 is referred to as an underhang because it is below the void in the block 100 as the block 100 is oriented in the construction process. This lower portion 131 may also be referred to as an upskin because during the LS layer-wise construction process the lower portion 131 is sintered in successive layers that are adjacent to subsequently deposed layers of unsintered powder.

[0056] In reference to FIGS. 4A-4C, build data 400 for construction of the block 100 shown in FIGS. 2A-2B is represented. In practice, a part (e.g., block 100) is prepared using a CAD software program. In preparing for the build, the CAD model is sectioned into layers, wherein each layer corresponds to a layer in the LS build process. In reference to FIGS. 4A-4C, a perimeter 411 of the build data 400 is shown. The perimeter 411 is commensurate in scope with the inside dimensions of the build chamber. The present invention, for example, may be practiced using the EOSINT P 800 Additive Manufacture System. The P800 has a build volume that measures 700 mm×380 mm×560 mm (27.6 in×15 in×22.05 in). Although a single object, the block 100, is shown in the build data 400 it is common for a LS build to include multiple objects.

[0057] The CAD model is sectioned into a plurality of successive layers corresponding to layers of the build. Each layer has a cross-section pattern of the object for construction. The cross-section pattern comprises data specifying select points in the cross-section for solidification. Each point selected for solidification in a layer has a unique x-coordinate and y-coordinate in the cross-section. A software program, for example one executing on the LS machine controller or on a computer in communication therewith, determines an amount of heat energy to introduce to each point selected for solidification. The amount of heat energy can be a number of different controls. For example, in the P800 it is possible to adjust the power of the laser, the width of the laser, the tracking speed of the laser, laser deflection velocity, the hatch pattern of the laser, and/or the contour pattern of the laser. It is possible to base the amount of heat energy introduced at select points on different inputs, including those related to the type of material and desired properties.

[0058] In reference to FIG. 4A, the area of the build data 400 for sintering in each layer is shown in gray 410, while the area not designate for sintered, i.e. will remain unsintered, is shown in white 420. The bore 130 that extends through the block 100 is shown in white because it is not sintered during the build process. For example, during a cross-section that includes the bore, heat energy is not introduced at select points corresponding to the bore in the cross-section.

[0059] In reference to FIGS. 4B-4C, a close-up the portion of the build data 400 shown in FIG. 4A and identified by an enlargement circle 422 is shown. FIG. 4B shows a front view of the layers included in the enlargement circle 422, while FIG. 4C shows a bottom view of the layers included in the enlargement circle 422. It will be understood to a person of ordinary skill the art and familiar with this disclosure, that the cross-sections in FIG. 4A are scaled larger in the Z direction for the purpose of illustrating the present invention. In practice, the layer is typically 125 μm in thickness.

[0060] In reference to FIG. 4B, the individual layers that comprise a portion of the block are shown 410. Each individual layer in the build data can be referred to as L.sub.n, where n is an integer. In the present disclosure, L.sub.0 may refer to a specific layer in the build data 400. L.sub.−1 is the layer immediately below the layer L.sub.0. During the build process, L.sub.−1 is deposed on the bed and then sintered according the build data. Then L.sub.0 is deposed on the bed and sintered. L.sub.−2 is the layer below L.sub.−1 and so forth. Likewise, L.sub.+1 is the layer that is prepared after L.sub.0, and L.sub.+2 is the layer that is prepared after L.sub.+1, and so forth.

[0061] In further reference to FIG. 4B a plurality of layers are shown L. The opening of the bore 130 is also shown. Specifically, the downskin portion of the bore is shown. Although the CAD model indicates that the bore 130 has a circular cross-section, it is manufactured as a plurality of steps sintered into successive layers. A portion of layer defining the wall of the bore comprises a downskin sinter. Downskins, for example, are illustrated by reference numbers 444, 442, 440.

[0062] As discussed in the background section of the pending disclosure, the inventors have discovered that heat energy introduced to sinter a select point in L.sub.0 will penetrate several layers below L.sub.0. This is referred to as the heat affected zone (HAZ). A problem arises when a downskin portion is sintered because unsintered power in the layers below will adhere to the downskin layer, thus causing a deviation in the geometry of the formed object relative to the geometry of the CAD model.

[0063] FIG. 3A illustrates the problem caused by HAZ as it relates to the manufacture of an object with a void. A block 200 includes a bore 236 that extends therethrough and has a constant circular cross-section in a plane perpendicular to the bore axis. The dashed line 230 illustrates the circular cross-section specified by the CAD model. Known LS building methods do not account for the downskin sinters. As a result, the heat energy introduced to the select points in the downskin causes an oversinter and binds several layers of below. This results in the overhang portion of the bore having a flat surface as opposed to the specified circular cross-section. The geometric difference is illustrated by the gray area 240 in FIG. 3A.

[0064] The current common practice to correct this problem is to modify the CAD design so that the bore has a cross-section that is more oval or egg shaped. The goal of this approach is to arrive at a bore having a circular cross-section relying on the oversinter to fill in the modified geometry that adds to the upper part of the void. This method is illustrated in FIG. 3B with a block 300 having a bore 336 defining an oval cross-section 330. The over sinter of material at the downskin results in a block having a bore with a circular cross-section. A disadvantage of this method is that it is very difficult to determine the correct geometry modifications to achieve the desired result. Furthermore, if a preferred geometry modification is known, it is very difficult to scale the modification to different sized voids having the same geometry. Finally, it is very difficult to practice this correction method when preparing voids having complex geometric patterns.

[0065] The inventors have discovered a method of adjusting the heat energy introduced to a select point of a layer to reduce the problems with oversinter, and more specifically the problem of fusing a select point for solidification to select points in previously deposed layers that were not solidified during the LS process.

[0066] An adjustment factor according to the present invention may be succinctly described by means of the following equation, in which E.sub.adjusted is the heat energy amount per unit area actually introduced at a position, E.sub.standard is the heat energy amount per unit area without consideration of the build data and previous or subsequent layers and K is a pre-factor that depends on the total exposure time of a region to be solidified in the previous and/or the current layer:

E.sub.adjusted=K.Math.E.sub.standard  (1)

[0067] The pre-factor can be determined and applied according to the following method. The determination of the pre-factor can for example be made empirically by pre-tests in the same additive manufacturing device in which the three-dimensional objects shall be manufactured. In doing so, before the actual manufacturing of the object, test objects are manufactured from the same building material and are measured.

[0068] The method includes the step of providing build data of an object for construction in an LS system. The build data is derived from a CAD model of the object and includes a plurality of cross-section patterns according to a geometry description of the object. This may be, for example, a CAD file. Each cross-section pattern corresponds to a layer in the layer-wise building process. Thus, each cross-section may have a thickness in the z-axis that corresponds to the thickness of the applied layers in the LS system. The cross-section pattern comprises data specifying select points in the cross-section for solidification. Each of the select points in the cross-section pattern selected for solidification has a unique position in the cross-section pattern. The select points can, for example, be represented by Cartesian coordinates in an (x,y) plane.

[0069] The LS machine applies a layer L.sub.0 of a polymer powder on a bed of a laser sintering system. The thickness of L.sub.0 can correspond to a thickness of a cross-section in the build data. The LS machine then solidifies select points of the polymer powder of layer L.sub.0 by introducing heat energy to the select points by controlled electromagnetic radiation according to the cross-section pattern assigned to L.sub.0. The amount of heat energy is initially set according to previously known methods that fail to account for the geometry of the manufactured part, and more specifically fail to account for unsintered material layers (e.g., voids) proximate to the selected point. To account for these voids, the method adjusts the heat energy introduced by electromagnetic radiation to solidify a select point at a first position in the layer L.sub.0 depending on whether the build data specifies solidification of a select point at the first position in one or more of: a previous layer L.sub.−n and a subsequent layer L.sub.+n.

[0070] In the above described method, n is a positive integer and L.sub.−1 is a layer immediately preceding layer L.sub.0, L.sub.−2 is a layer immediately preceding L.sub.−1, and so forth, and L.sub.+1 is the layer immediately subsequent layer L.sub.0, L.sub.+2 is the layer immediately subsequent L.sub.+1, and so forth. To correct for oversinter on downskin builds, the method adjusts the heat energy introduced by electromagnetic radiation to solidify the select point at the first position in the layer L.sub.0 depending on whether the build data specifies solidification of a select point at the first position in a layer L.sub.−n. That is, the method looks to the layers previously deposed that are below the current layer L.sub.0. In some embodiments of the present invention, the method will adjust the heat energy introduced based on whether the build data specifies solidification of a select point at the first position in layer L.sub.−1. In other embodiments of the present invention, the method will adjust the heat energy introduced based on whether the build data specifies solidification of a select point at the first position in layers L.sub.−1, L.sub.−2, and L.sub.−3. In yet other embodiments of the present invention, the method will adjust the heat energy introduced based on whether the build data specifies solidification of a select point at the first position in layers L.sub.−1 through L.sub.−5. It is preferred that the method looks the build data in one or more layers L.sub.−n in a HAZ caused by an unadjusted introduction of heat energy, i.e., the amount of heat energy originally specified according to known methods. The inventors have discovered that, for a PEKK polymer, this is typically the first three layers below the layer of construction. A person of ordinary skill in the art and familiar with this disclosure will understand the HAZ, as determined in the Z− direction, will vary based on the material and the heat energy introduced into the material.

[0071] FIG. 5 illustrates the construction of a downskin layer L.sub.0 540. A block 510 having a bore 520 with a circular cross-section extending therethrough is being constructed in accordance with the LS method of the present disclosure. In the construction, several layers have been constructed by the LS method L.sub.−1, L.sub.−2, L.sub.−3 . . . 542. The previously constructed layers 542 are illustrated in gray. The method is currently preparing to sinter layer L.sub.0 540, which has been applied to the bed. The build data includes information for subsequent layers L.sub.+1, L.sub.+2, L.sub.+3 . . . 544.

[0072] FIG. 5 illustrates several select points for solidification in L.sub.0 to illustrate the present invention. The select point for solidification is x.sub.1, y.sub.1, z.sub.n 531, where z.sub.n is L.sub.0. Prior to building, the system specifies an amount of heat energy to be introduced to the select point for solidification at the first position. In the example shown, the amount of heat is adjusted based on whether select points at the first position in previous layers were solidified during the build process. It should be noted that this determination can be made prior to the build during an analysis of the CAD model to create the build data. In the case of select point 531 the method looks to the build data of the prior layers L.sub.−1, L.sub.−2, L.sub.−3 . . . 542. More specifically, the method looks to build data at the first position in the prior layers 542. That is, layers at the same position in the (x.sub.n, y.sub.n) plane as select point in the layer L.sub.0. For example, the adjustment is made based on whether the build data specifies solidification in the three preceding layers L.sub.−1, L.sub.−2, L.sub.−3. In the example shown, the build data for the select point in the first position in the preceding layer x.sub.1, y.sub.1, L.sub.−1 does not specify solidification. Likewise, for the first position in x.sub.1, y.sub.1, L.sub.−2, and x.sub.1, y.sub.1, L.sub.−3. Accordingly, the heat energy introduced a x.sub.1, y.sub.1, L.sub.0 is reduced to inhibit oversinter and unwanted fusion in the layers below x.sub.1, y.sub.1, L.sub.0, thereby constructing a more geometrically accurate part.

[0073] In further reference to FIG. 5, several more examples are illustrated. In reference to select points along the axis (x.sub.2, y.sub.2, z.sub.n) 532, the method of the present invention adjusts the heat introduced to select point x.sub.2, y.sub.2, L.sub.0 based on whether the build data for select points in the first position in the preceding layers specify solidification. The first position at x.sub.2, y.sub.2, L.sub.−1 specifies solidification. However, the first position at x.sub.2, y.sub.2, L.sub.−2, and x.sub.2, y.sub.2, L.sub.−3 does not specify solidification. Accordingly, the heat energy introduced a x.sub.2, y.sub.2, L.sub.0 is reduced to inhibit oversinter and unwanted fusion in the layers below x.sub.2, y.sub.2, L.sub.0, thereby constructing a more geometrically accurate part. This is because the HAZ can extend several layers below the layer of incidence. In some embodiments of the present invention, the heat energy is reduced, however, such reduction is less than the reduction applied to a select point having an unsintered layer at a first position in an immediately preceding layer, and specifying unsintered positions below.

[0074] In reference to a select point at x.sub.3, y.sub.3, L.sub.0 533 the build data at the first position in the three preceding layers specifies solidification. Therefore, there is no need to adjust the heat energy introduced at x.sub.3, y.sub.3, L.sub.0 533. If, however, the HAZ extends more than three layers, the method may reduce the heat energy introduced at the select point because build data specifies no solidification at the first position at x.sub.3, y.sub.3, L.sub.4. In reference to a select point at x.sub.4, y.sub.4, L.sub.0 534, the build data at the first position in all preceding layers specifies solidification. Therefore, there is no adjustment to the heat energy introduced at x.sub.4, y.sub.3, L.sub.0 534.

[0075] In the present method, the adjustment to the heat energy introduced to the select point at the first position is made based on whether the build data at the first position in preceding layers because this is the area of the heat affected zone. This method has the advantage over the prior art that relies on thermal conductivity in large three dimensional volumes near the select point for solidification because it can more accurately account for the geometry of the object and void therein being constructed. In some embodiments of the present invention, the adjustment of heat energy introduced by electromagnetic radiation to solidify a select point at a first position in the layer L.sub.0 does not account for whether the build data specifies solidification of points other than the first position in one or more relied upon layer L.sub.−n and layer L.sub.+n.

[0076] As discussed above, the disclosed method is also used to inhibit fusion of subsequent layers in the solidification of upskin sinters in the LS process. Polymers in general have a relatively low thermal conductivity as compared to metals commonly used in LS or LM techniques. Such low thermal conductivity of polymer powders relative to metals is derived in part from the solid-to-powder ratio in the materials. Metals used in LS or LM techniques typically possess a solid-to-powder ratio of 100:1. By comparison, the polymer powders described herein may possess a solid-to-powder ratio of less than 50:1. Higher solid-to-powder ratios typically correspond with greater thermal conductivity, especially in metals, which may have much greater thermal conductivity in solid form relative to powder form.

[0077] Accordingly, the polymer powders described herein have relatively low thermal conductivity. For example, the polymer powders may have a thermal conductivity of less than 1.0 W/K*M. In addition, there is little to no material change in the thermal conductivity between sintered polymer and powder polymer. As a result, the solidified portions of a cross-section can retain heat for a period such that when a subsequent layer is deposed on the bed having unsintered portions, the retained heat in the sintered portions may cause a fusion to the newly deposed layer. Although the oversinter problems associated with downskin sinters and the problems caused in upskin sinters with unwanted fusion in subsequent unsintered layers caused by latent heat are different, the disclosed method can be used to reduce the latter issue as well.

[0078] FIG. 6 illustrates the construction of a upskin layer L.sub.0 640. A block 610 having a bore 620 with a circular cross-section extending therethrough is being constructed in accordance with the LS method of the present disclosure. In the construction, several layers have been constructed by the LS method L.sub.−1, L.sub.−2, L.sub.−3 . . . 642. The previously constructed layers 642 are illustrated in gray. The method is currently preparing to sinter layer L.sub.0 640 which has been applied to the bed. The build data includes information for subsequent layers L.sub.+1, L.sub.+2, L.sub.+3 . . . 644.

[0079] FIG. 6 illustrates several select points for solidification in L.sub.0 to illustrate the present invention as it pertains to minimizing unwanted interlayer fusion in upskin sinters. The select point for solidification is x.sub.1, y.sub.1, z.sub.n 631, where z.sub.n is L.sub.0. Prior to building, the system specifies an amount of heat energy to be introduced to the select point for solidification at the first position. In the example shown, the amount of heat energy is adjusted based on whether select points at the first position in subsequent layers are to be solidified during the build process. It should be noted that this determination can be made prior to build during an analysis of the CAD model to create the build data. In the case of select point 631 the method looks to the build data of the prior layers L.sub.+1, L.sub.+2, L.sub.+3 . . . 644. More specifically, the method looks to build data at the first position in the subsequent layers 644. For example, the adjustment is made based on whether the build data specifies solidification in the first position in the three subsequent layers L.sub.+1, L.sub.+2, L.sub.+3 644. In the example shown, the build data for the select point in the first position in the subsequent layer x.sub.1, y.sub.1, L.sub.+1 does not specify solidification. Likewise, for the first position in x.sub.1, y.sub.1, L.sub.+2, and x.sub.1, y.sub.1, L.sub.+3. Accordingly, the heat energy introduced at x.sub.1, y.sub.1, L.sub.0 is reduced to reduce unwanted fusion in one or more layers subsequent to x.sub.1, y.sub.1, L.sub.0, thereby constructing a more geometrically accurate part.

[0080] In further reference to FIG. 6, several more examples are illustrated. In reference to select points along the axis (x.sub.2, y.sub.2, z.sub.n) 632, the method of the present invention adjusts the heat introduced to select point x.sub.2, y.sub.2, L.sub.0 based on whether the build data for select points in the first position in the subsequent layers specify solidification. x.sub.2, y.sub.2, L.sub.+1 specifies solidification. However, the first position at x.sub.2, y.sub.2, L.sub.+2, and x.sub.2, y.sub.2, L.sub.+3 does not specify solidification. Accordingly, the heat energy introduced a x.sub.2, y.sub.2, L.sub.0 is reduced to inhibit unwanted fusion in the layers above x.sub.2, y.sub.2, L.sub.0, thereby constructing a more geometrically accurate part. In reference to a select point at x.sub.3, y.sub.3, L.sub.0 633, the build data at the first position in the three subsequent layers specifies solidification. Therefore, there is no need to adjust the heat energy introduced at x.sub.3, y.sub.3, L.sub.0 633. In reference to a select point at x.sub.4, y.sub.4, L.sub.0 634 the build data at the first position in all subsequent layers specifies solidification. Therefore, there is no adjustment to the heat energy introduced at x.sub.4, y.sub.4, L.sub.0 634.