ELECTROLYTE REPLENISHMENT METHOD FOR MOLTEN CARBONATE FUEL CELL STACK

Abstract

A method for replenishing an electrolyte of a molten carbonate fuel cell stack includes: preparing an electrolyte colloidal solution containing 10% to 20% of the electrolyte and having a viscosity of 200 to 800 Pa.Math.s; replenishing the electrolyte of the cell stack using the electrolyte colloidal solution prepared in step 1 to allow the electrolyte to adhere to an electrode and an internal channel of the cell stack; discharging excess electrolyte colloidal solution in the cell stack; and drying and discharging water or an organic solvent in the cell stack under an inert gas condition to complete replenishment of the electrolyte of the cell stack, and performing a discharge performance test.

Claims

1. A method for replenishing an electrolyte of a molten carbonate fuel cell stack, comprising: step 1: preparing an electrolyte colloidal solution containing 10% to 20% of the electrolyte and having a viscosity of 200 to 800 Pa.Math.s; step 2: replenishing the electrolyte of the cell stack using the electrolyte colloidal solution prepared in step 1 to allow the electrolyte to adhere to an electrode and an internal channel of the cell stack; step 3: discharging excess electrolyte colloidal solution in the cell stack; and step 4: drying and discharging water or an organic solvent in the cell stack under an inert gas condition to complete replenishment of the electrolyte of the cell stack, and performing a discharge performance test.

2. The method for replenishing the electrolyte of the molten carbonate fuel cell stack according to claim 1, wherein the electrolyte colloidal solution in step 1 is prepared by: mixing lithium carbonate and potassium carbonate in a molar ratio of 62:38 to form the electrolyte; and mixing the obtained electrolyte with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% to 3%, or with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% to prepare the electrolyte colloidal solution containing 10% to 20% of the electrolyte and having the viscosity of 200 to 800 Pa.Math.s.

3. The method for replenishing the electrolyte of the molten carbonate fuel cell stack according to claim 1, wherein the electrolyte colloidal solution in step 1 is prepared by: mixing lithium carbonate and sodium carbonate in a molar ratio of 53:47 to form the electrolyte; and mixing the obtained electrolyte with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% to 3%, or with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% to prepare the electrolyte colloidal solution containing 10% to 20% of the electrolyte and having the viscosity of 200 to 800 Pa.Math.s.

4. The method for replenishing the electrolyte of the molten carbonate fuel cell stack according to claim 1, wherein in step 2, replenishing the electrolyte of the cell stack using the electrolyte colloidal solution prepared in step 1 comprises: forming a circulation loop for replenishing the electrolyte by an anode or cathode inlet of the molten carbonate fuel cell, a container containing the electrolyte colloidal solution prepared in step 1, a circulating pump, and an anode or cathode outlet of the molten carbonate fuel cell; and initiating the circulation pump to fully circulate the electrolyte colloidal solution in the internal channel of the cell stack, and to allow a part of the electrolyte to adhere to the electrode and the internal channel of the cell stack during a circulation process.

5. The method for replenishing the electrolyte of the molten carbonate fuel cell stack according to claim 1, wherein discharging the excess electrolyte colloidal solution in the cell stack in step 3 comprises: introducing air or nitrogen with a flow rate of 15% to 30% of a cathode flow rate at full power of the cell stack into the cell stack from a cathode or anode inlet at an upper part of the cell stack, and completely discharging the excess electrolyte colloidal solution in the cell stack from a cathode or anode outlet at a lower part of the cell stack.

6. The method for replenishing the electrolyte of the molten carbonate fuel cell stack according to claim 1, wherein drying and discharging the water or the organic solvent in the cell stack in step 4 comprises: introducing nitrogen or carbon dioxide inert gas into the cell stack at a temperature of 66° C. to 80° C. for 24 to 48 hours.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] FIG. 1 is a schematic diagram showing an electrolyte replenishing loop device according to the present disclosure.

REFERENCE NUMERALS

[0012] 1: container containing an electrolyte colloidal solution; 2: circulating pump; 3: anode or cathode inlet; 4: cell; 5: molten carbonate fuel cell; 6: anode or cathode outlet; 7: circulation pipeline.

DETAILED DESCRIPTION

[0013] In the following, the present disclosure will be described in detail with reference to the drawings.

[0014] An object of the present disclosure is to provide a method for replenishing an electrolyte of a molten carbonate fuel cell stack, which solves the problem of electrolyte loss in the existing molten carbonate fuel cell stack, and greatly improves the life and operation stability of the cell stack.

[0015] In order to achieve the above-mentioned object, the technical solutions adopted in the present disclosure are as follows.

[0016] The present disclosure provides a method for replenishing an electrolyte of a molten carbonate fuel cell stack, which includes:

[0017] step 1: preparing an electrolyte colloidal solution containing 10% to 20% of the electrolyte and having a viscosity of 200 to 800 Pa.Math.s;

[0018] step 2: replenishing the electrolyte of the cell stack using the electrolyte colloidal solution prepared in step 1 to allow the electrolyte to adhere to an electrode and an internal channel of the cell stack;

[0019] step 3: discharging excess electrolyte colloidal solution in the cell stack; and

[0020] step 4: drying and discharging water or an organic solvent in the cell stack under an inert gas condition to complete replenishment of the electrolyte of the cell stack, and performing a discharge performance test.

[0021] In an embodiment of the present disclosure, the electrolyte colloidal solution in step 1 is prepared by:

[0022] mixing lithium carbonate and potassium carbonate in a molar ratio of 62:38 to form the electrolyte; and

[0023] mixing the obtained electrolyte with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% to 3%, or with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% to prepare the electrolyte colloidal solution containing 10% to 20% of the electrolyte and having the viscosity of 200 to 800 Pa.Math.s.

[0024] In an embodiment of the present disclosure, the electrolyte colloidal solution in step 1 is prepared by:

[0025] mixing lithium carbonate and sodium carbonate in a molar ratio of 53:47 to form the electrolyte; and

[0026] mixing the obtained electrolyte with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% to 3%, or with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% to prepare the electrolyte colloidal solution containing 10% to 20% of the electrolyte and having the viscosity of 200 to 800 Pa.Math.s.

[0027] In an embodiment of the present disclosure, in step 2, replenishing the electrolyte of the cell stack using the electrolyte colloidal solution prepared in step 1 includes:

[0028] forming a circulation loop for replenishing the electrolyte by an anode or cathode inlet of the molten carbonate fuel cell, a container containing the electrolyte colloidal solution prepared in step 1, a circulating pump, and an anode or cathode outlet of the molten carbonate fuel cell; and

[0029] initiating the circulation pump to fully circulate the electrolyte colloidal solution in the internal channel of the cell stack, and to allow a part of the electrolyte to adhere to the electrode and the internal channel of the cell stack during a circulation process.

[0030] In an embodiment of the present disclosure, discharging the excess electrolyte colloidal solution in the cell stack in step 3 includes:

[0031] introducing air or nitrogen with a flow rate of 15% to 30% of a cathode flow rate at full power of the cell stack into the cell stack from a cathode or anode inlet at an upper part of the cell stack, and completely discharging the excess electrolyte colloidal solution in the cell stack from a cathode or anode outlet at a lower part of the cell stack.

[0032] In an embodiment of the present disclosure, drying and discharging the water or the organic solvent in the cell stack in step 4 includes introducing nitrogen or carbon dioxide inert gas into the cell stack at a temperature of 66° C. to 80° C. for 24 to 48 hours.

[0033] Compared with the related art, beneficial effects of the present disclosure are as follows.

[0034] The method for replenishing the electrolyte of the molten carbonate fuel cell stack provided in the present disclosure is capable of adhering the electrolyte uniformly to the electrodes and the channels inside the flow field by taking advantage of the good fluidity and viscosity of the electrolyte colloidal solution, and replenishing the lost electrolyte in the cell stack based on a capillary infiltration principle of the molten electrolyte. This method effectively compensates the decline of the performance and service life of the molten carbonate fuel cell caused by the loss of the electrolyte during high-temperature operation, and has important guiding significance for improving the performance and service life of the stable molten carbonate fuel cell.

[0035] Further, the molten carbonate electrolyte is generally in solid, and melted into liquid under high temperature, so as to be sucked into micro-pores of the separator by a capillary force to isolate gases of two electrodes. The solid electrolyte is difficult to be evenly replenished into the cell stack, and may block internal channels of the cell. However, by dispersing the electrolyte with the binder and the solvent into liquid colloid, the electrolyte may be evenly transported to the interior of the cell and evenly distributed in the cell by continuous flow of the circulating pump.

[0036] Further, a content of the electrolyte replenished into the cell stack may be adjusted by adjusting a content of the electrolyte in the electrolyte colloid. In addition, the colloidal solution contains a small amount of the binder, and the electrolyte may be evenly dispersed in the colloidal solution, which ensures that the electrolyte is evenly distributed to various parts in the cell stack.

[0037] The present disclosure provides a method for replenishing an electrolyte of a molten carbonate fuel cell stack, which includes the following steps.

[0038] 1) A volume of a flow field and a flow channel in the cell stack is calculated according to a structure of cell stack bipolar plate and cell end plate.

[0039] 2) An electrolyte colloidal solution is prepared.

[0040] A first kind of electrolyte colloidal solution is prepared as follows. Lithium carbonate and sodium carbonate are mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte is mixed with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% to 3%, or with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% to prepare the electrolyte colloidal solution containing 10% to 20% of the electrolyte and having a viscosity of 200 to 800 Pa.Math.s.

[0041] A second kind of electrolyte colloidal solution is prepared as follows. Lithium carbonate and potassium carbonate are mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte is mixed with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% to 3%, or with a mixed solution of polyvinyl butyral and ethanol to prepare the electrolyte colloidal solution containing 10% to 20% of the electrolyte and having a viscosity of 200 to 800 Pa.Math.s.

[0042] The concentration of the mixed solution of polyvinyl butyral and ethanol is in a range of 3% to 5%, and the concentration of the ethanol is 95%.

[0043] 3) A circulation loop for replenishing the electrolyte is formed by an anode or cathode inlet 3 of the molten carbonate fuel cell 5, a container 1 containing the electrolyte colloidal solution, a circulating pump 2, and an anode or cathode outlet 6 of the molten carbonate fuel cell (MCFC). The circulation pump 2 is initiated to fully circulate the electrolyte colloidal solution in the internal channel of the cell stack for 24 to 48 hours, and ensure that a part of the electrolyte is adhered to the electrode and the internal channel of the cell stack during a circulation process.

[0044] 4) Air or nitrogen with a flow rate of 15% to 30% of a cathode flow rate at full power of the cell stack is introduced into the cell stack from the cathode or anode inlet at an upper part of the cell stack, and the excess electrolyte colloidal solution in the cell stack is discharged from the cathode or anode outlet at a lower part of the cell stack. The duration of ventilation is 24 to 48 hours, and the air flow rate is controlled to slowly blow the residual colloid out of the cell stack and allow the electrolyte to slowly adhere to walls of components inside the cell stack.

[0045] 5) Nitrogen or carbon dioxide inert gas is introduced into the cell stack at a temperature of 66° C. to 80° C. for 24 to 48 hours to dry and discharge water or an organic solvent in the cell stack, thereby eliminating the influence of the water and the organic solvent on cell's performance.

[0046] After replenishing the electrolyte, the cell stack is heated to 450° C. with a rate of 1° C./1 min to 1° C./3 min and held at this temperature for 5 hours, then is heated to 550° C. with a rate of 1° C./3 min to 1° C./5 min, and then is heated to 650° C. with a rate of 1° C./1 min to 1° C./3 min, and hydrogen was introduced into the anode to reduce the electrode. When the temperature reaches 650° C., air and carbon dioxide are introduced to the cathode to perform a discharge performance test.

[0047] The method for replenishing the electrolyte of the molten carbonate fuel cell stack provided in embodiments of the present disclosure has important guiding significance in the research and application fields of MCFC, which will be illustrated in detail with examples as follows.

EXAMPLE 1

[0048] 1) A 5 kW molten carbonate fuel cell stack was provided, which has operated for a certain period of time with decreased performance, and is composed of 36 single cells in series. An effective area of the single cell is 2000 cm.sup.2.

[0049] 2) According to a structure of cell stack bipolar plate and cell end plate of the 5 kW MCFC, a volume of a flow field and a flow channel in the cell stack was calculated, which is 0.036 m.sup.3. Lithium carbonate and potassium carbonate were mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte was mixed with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% under stirring to prepare an electrolyte colloidal solution containing 10% of the electrolyte and having a viscosity of 200 Pa.Math.s. An amount of the electrolyte colloidal solution is 3 times the volume of the flow field and the flow channel in the cell stack.

[0050] 3) The prepared electrolyte colloidal solution was put into a closed container with an inlet and an outlet. A circulation loop for replenishing the electrolyte was formed by connecting the inlet and outlet of the container, the cell stack and a circulating pump. The circulation pump was initiated to fully circulate the electrolyte colloidal solution in the internal channel of the cell stack for 24 hours, and after the circulation was stopped, the electrolyte colloidal solution in the cell stack was discharged from a bottom of the cell stack.

[0051] 4) Air or nitrogen with 15% of a cathode flow rate at full power of the cell stack was introduced into the cell stack from an upper part of the cell stack for 24 hours to discharge the excess electrolyte colloidal solution in the cell stack again.

[0052] 5) Nitrogen or carbon dioxide inert gas with 25% of the cathode flow rate at the full power of the cell stack was introduced into the cell stack at a temperature of 80° C. for 30 hours to dry and discharge water or the organic solvent in the cell stack to complete replenishment of the electrolyte.

[0053] Afterwards, the cell stack was heated to 450° C. with a rate of 1° C./3 min and held at this temperature for 5 hours, then was heated to 550° C. with a rate of 1° C./3 min, and then was heated to 650° C. with a rate of 1° C./1 min, and hydrogen was introduced into the anode to reduce the electrode. When the temperature reached 650° C., air and carbon dioxide were introduced to the cathode to perform a discharge performance test.

EXAMPLE 2

[0054] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0055] Lithium carbonate and potassium carbonate were mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte was mixed with an aqueous solution of polyvinyl alcohol with a concentration of 1.5% under stirring to prepare the electrolyte colloidal solution containing 15% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 3

[0056] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0057] Lithium carbonate and potassium carbonate were mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte was mixed with an aqueous solution of polyvinyl alcohol with a concentration of 3% under stirring to prepare the electrolyte colloidal solution containing 20% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 4

[0058] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0059] Lithium carbonate and potassium carbonate were mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte was mixed with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% under stirring to prepare the electrolyte colloidal solution containing 20% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 5

[0060] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0061] Lithium carbonate and potassium carbonate were mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte was mixed with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% under stirring to prepare the electrolyte colloidal solution containing 10% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 6

[0062] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0063] Lithium carbonate and potassium carbonate were mixed in a molar ratio of 62:38 to form an electrolyte, and the obtained electrolyte was mixed with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% under stirring to prepare the electrolyte colloidal solution containing 13% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 7

[0064] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0065] Lithium carbonate and sodium carbonate were mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte was mixed with an aqueous solution of polyvinyl alcohol with a concentration of 1.5% under stirring to prepare the electrolyte colloidal solution containing 15% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 8

[0066] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0067] Lithium carbonate and sodium carbonate were mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte was mixed with an aqueous solution of polyvinyl alcohol with a concentration of 3% under stirring to prepare the electrolyte colloidal solution containing 20% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 9

[0068] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0069] Lithium carbonate and sodium carbonate were mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte was mixed with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% under stirring to prepare the electrolyte colloidal solution containing 20% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 10

[0070] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0071] Lithium carbonate and sodium carbonate were mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte was mixed with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% under stirring to prepare the electrolyte colloidal solution containing 10% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 11

[0072] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0073] Lithium carbonate and sodium carbonate were mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte was mixed with a mixed solution of polyvinyl butyral and ethanol with a concentration of 95% under stirring to prepare the electrolyte colloidal solution containing 13% of the electrolyte and having a viscosity of 200 Pa.Math.s.

EXAMPLE 12

[0074] This example is the same as example 1, but the difference lies in that the electrolyte colloidal solution was prepared as follows.

[0075] Lithium carbonate and sodium carbonate were mixed in a molar ratio of 53:47 to form an electrolyte, and the obtained electrolyte was mixed with an aqueous solution of polyvinyl alcohol with a concentration of 0.5% under stirring to prepare the electrolyte colloidal solution containing 13% of the electrolyte and having a viscosity of 200 Pa.Math.s.