Foam Reefer Wall Using "Loop" Scrim Fabric Backing

Abstract

An improved fabric backing for the manufacture of glass-reinforced thermoplastic panels that exhibits significantly greater foam adhesion than its scrim counterpart. That fabric backing includes a plurality of looped section extending upwardly (and inwardly) from its base for enhancing adhesion thereto. The combination is subjected to lamination for making an improved glass-reinforced thermoplastic interior wall panel. That wall panel can be used in a storage unit, such as a refrigerated trailer, railcar, shipping container and/or box truck.

Claims

1. An improved fabric using loops for connecting to a back side of a wall during manufacture of a glass-reinforced thermoplastic wall panel, said loop fabric comprising: a plurality of fully looped sections adhered at both loop ends into a polymer woven wall substrate, said looped sections adapted for extending outwardly above the polymer woven wall substrate prior to having a thermoplastic resin injected thereabout to form an improved, laminated wall panel therefrom.

2. The loop fabric of claim 1 wherein the looped sections extend between about 3-6 mm above the polymer woven wall substrate.

3. The loop fabric of claim 2 wherein the looped sections extend at a substantially consistent height above the polymer woven wall substrate.

4. The loop fabric of claim 1 wherein the fully looped sections consist essentially of a polyester blend.

5. The loop fabric of claim 1, which includes between about 40 to 75 loops/sq. inch of fully looped sections.

6. The loop fabric of claim 1, which includes between about 100 to 140 loops/sq. inch of fully looped sections.

7. The loop fabric of claim 1, which connects to a backside of the wall panel by: lamination, gluing or combinations thereof.

8. A composite sheet comprised of: a) a base layer of reinforcing woven or non-woven fibers for impregnating with a thermoplastic resin, said base layer having a substrate into which a plurality of fully looped sections are interwoven for extending about 0.5 to 6 mm outwardly beyond the substrate; and b) a thermoplastic resin injected about the base layer to create an improved mechanical bond between the injected thermoplastic resin and the base layer.

9. The composite sheet of claim 8, which exhibits at least about 50% greater thermoplastic resin adhesion than its scrim counterpart.

10. The composite sheet of claim 8 wherein the thermoplastic resin is a resin selected from the group consisting of ABS, nylon, polyester, polyolefin, polypropylene, PVC and polystyrene and the looped sections are made from a material selected from the group consisting of polypropylene, fiberglass, polyester, and nylon.

11. The composite sheet of claim 8 wherein the mat includes between about 40 to 180 loops/sq. inch of fully looped sections.

12. The composite sheet of claim 11, which includes between about 40 to 75 loops/sq. inch of fully looped sections.

13. The composite sheet of claim 11, which includes between about 100 to 140 loops/sq. inch of fully looped sections.

14. An improved storage unit made from a plurality of glass-reinforced interior wall panels, said interior wall panels being made from a thermoplastic foam adhered to a wall backing having a substrate which includes a plurality of fully looped sections which extend outwardly beyond the wall backing for greater adhesion of the thermoplastic foam thereto.

15. The storage unit of claim 14 wherein the fully looped sections extend about 0.5-6 mm outwardly beyond the wall backing.

16. The storage unit of claim 14 wherein the fully looped sections are adhered at both ends to the wall backing at a rate between about 40 to 180 loops/sq. inch.

17. The storage unit of claim 14, which is selected from the group consisting of: a refrigerated trailer, a railcar, a shipping container and a box truck.

18. The storage unit of claim 14 wherein the fully looped sections consist essentially of a polyester blend.

19. The storage unit of claim 18 wherein the fully looped sections consist essentially of polypropylene.

20. The storage unit of claim 14 wherein the wall backing adheres to an interior wall of the storage unit by: lamination, gluing or combinations thereof.

Description

SUMMARY OF THE DRAWINGS

[0019] Further features, objectives and advantages of this invention will become clearer from the following Detailed Description made with reference to the accompanying drawings in which:

[0020] FIG. 1 is a top view photograph showing the prior art adhesion of foam after being pulled from standard scrim backing;

[0021] FIG. 2 is a comparative top view photograph showing the foam adhesion to new loop scrim fabric per one embodiment of this invention;

[0022] FIG. 3 is a diagrammatic representation of one prior art variety of multiple thread/strand fabric inter-looped to one another but with no base connection, per FIG. 3a of U.S. Pat. No. 3,934,064;

[0023] FIG. 4 is a diagrammatic representation of a second prior art foam backing system, this time with a single thread/strand having one end into a polymer base but no interweaving therethrough, per FIG. 7 of U.S. Pat. No. 3,934,064;

[0024] FIG. 5 is a cross-sectional diagram of a third prior art variety of material showing means for randomly embedding continuous strands of fabric into and at least partially below an innermost layer; but it exhibits no connection on randomness, per FIG. 8A of U.S. Published Application No. 20150246511;

[0025] FIG. 6 is a cross-sectional diagram of a fourth prior art variety of material showing embedding strands of fabric with multiple downward extensions (in one common direction) from its innermost layer, per FIG. 8B of U.S. Published Application No. 20150246511;

[0026] FIG. 7 is a front perspective view showing one system of foam reefer wall according to this invention, said foam reefer wall employing one embodiment of loop scrim fabric backing for improved foam adhesion thereto, all interconnected using one continuous fiber creating base and loop together;

[0027] FIG. 7A is a close-up sectional view of the circled area 7A from FIG. 7, showing loops of a substantially uniform or constant height;

[0028] FIG. 7B is a cross-sectional view of a first alternative embodiment showing loops with purposefully variable heights, 118a, 118b and 118c;

[0029] FIG. 8 is a top perspective photograph showing, from one edge, an embodiment of loop scrim fabric backing per this invention;

[0030] FIG. 9 is a close-up diagram showing or how the loops are interwoven into the base per one embodiment of this invention;

[0031] FIG. 10 is a close-up diagram focusing on one row of preferred loops with base material per this invention; and

[0032] FIG. 11 is a perspective, sectional view of a refrigerated vehicle trailer showing the improved loop scrim fabric backing of this invention installed on the interior of same.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0033] When referring to alternate embodiments, like that shown in FIG. 7B, common elements are commonly numbered though in the next hundred series.

[0034] When referring to any numerical length, width, percent improvement or other quantitative comparison number (or number range) herein, it should be noted that all such numbers are representative of embodiments of the invention as shown. Furthermore, any such range of numbers should expressly include each and every fraction or decimal between its stated minimum and maximum. For instance, any one component (of loop material) having from about 40 to 70 loops per square inch, should also specifically cover fabric backing substrates having about 41, 42 and 45 loops/in.sup.2 . . . and so on, up to about 65, 67 and 69.6 loops/in.sup.2. And for loop heights between abut 0.5 to 6 mm or more, preferably about 3 to 5 mm each, those loops would include all values between the aforementioned minimum and maximum loop heights. It is to be understood, however, that Applicant considers the mere aspect of creating such looped scrim fabric backing, regardless of loop size/consistency and/or relative loop density to be a truly novel, game-changer aspect of the present invention.

[0035] A fabric backing with at least about 30% greater foam adhesion as compared to its scrim counterpart, would also exhibit about 35, 40 and 50%+ improvement. The same applies for every other quantitative range herein.

[0036] FIG. 1 shows a standard scrim bond as might be made and sold by Xamax Industries, Matterworks and/or OXCO Industries to name a few. Unfortunately, therein, the underlying material M had its foam F separated therefrom with the application of nominal pull pressure due to a weakness of adhesion at the interface I between.

[0037] Note the following difficulties/disadvantages with that product:

[0038] 1) fibers are very small—in only the X- and Y-Axes;

[0039] 2) there are indentations where the fibers have been connected via a heated “point bond” roller;

[0040] 3) it is a much denser product—harder to soak into during foaming therefore resulting in worse bonding; and

[0041] 4) this point bond product is made of two layers bonded together, which could allow separation. It is especially vulnerable to separation especially when moisture is introduced.

[0042] Accompanying FIG. 2 shows Applicant's newest development. It exhibits much advancement and improvement over the current scrim of FIG. 1. The underlying material M′ has a plurality of loops L extending upwardly therefrom before being combined with foam F by injection during the manufacture of trailer and other GRTP materials/component parts. The resulting product exhibits much greater adhesion at its interface I′.

[0043] Still other advantages of this improved product include:

[0044] 1) a fiber loop design that has been woven into a pattern extending far beyond the surface of the panel. That allows for the foam to cure around the loops to the bottom connection point and create a much deeper “grab factor”. That, in turn, allows for the wall to exceed the surface bond obtained by the current methods of scrim and create a more permanent bond, deep into the cured foam, for solving the delamination issue of prior products.

[0045] This is truly a game-changing, MAJOR improvement! When the foam attaches to the wall, the raised “loop” fibers of this invention will grab and hold much better than just an X and Y axis product. The present invention adds a looped dimension to the equation thus making for an overall stronger interior panel. Even if the standard scrim was lofted or roughed up to provide an exposed Z-fiber, as per accompanying FIG. 6, there is still no loop mechanism equivalent that can provide the mechanical grab and reconnection to an interwoven base/bottom that this concept does.

[0046] 2) The design of the new “loop” has a uniform grid base (loop density can be varied to accommodate different foam compositions and densities) that allows for excellent attachment to applicant's base polypropylene wall and glass mat products so that it holds better.

[0047] 3) The “loop” design is impervious to moisture unlike old scrim material that can separate when wet into two point bond layers from its point bond.

[0048] 4) Applicant's polypropylene can soak through this product during the lamination process thereby allowing for a better grab to the trailer interior GRTP wall than the traditional scrim product, a potentially 50%, 75%, even 100% or more adhesion than standard scrim, in fact.

[0049] 5) Loop fabric can be applied by either laminating on OR gluing to the backside surface of the wall allowing for maximum optional usages in the field.

[0050] 6) Loop fabric can be of any material such as a polyester, nylon, polypropylene, polyethylene, etc., but should be stiff enough to hold its shape without flattening out as the trailer wall is rolled for shipping or placed into a foaming chamber.

[0051] One set of preferred method steps for making this improved material product commences with: (a) providing an improved fabric backing substrate having a plurality of loops interwoven therewith; (b) orienting the plurality of loops in the backing substrate to “stand” in a raised (rather than flattened) condition; and (c) injecting a polymer (preferably, polypropylene) foam about the raised loops for greater impregnation of the polymer into the backing substrate for the manufacture of a trailer scrim/glass-reinforced thermoplastic interior wall panel.

[0052] A further novel method entails making an improved storage unit, such as a refrigerated trailer, railcar, shipping container and/or box truck using a plurality of such glass-reinforced thermoplastic interior wall panels. That unit will exhibit greater foam adhesion within said interior wall panels, resulting in less potential damage from container packers and/or during packaging transport. And, due to this increased foam adhesion, such units will have reduced repair/replacement costs and a prolonged useful life.

[0053] Applicant believes his improvement fully exploits the revolutionary “loop” fabric that his method employs. That looped design is not the same typical Velcro® underlayment nor even one half of what makes up standard Velcro tape, i.e. the hook OR the partnering loop side. The latter's loops are much smaller and merely intended to coordinate (i.e. mesh) with the hooks of the other material half. It would not be possible, nor practical, to incorporate a full or half portion of typical Velcro® tape for achieving the desired adhesion levels observed with the present invention.

[0054] The aforementioned loops may be standard/uniform or continuous in relative height to the interwoven base as per FIG. 7A. Alternately, another embodiment would address improvements using loops of variable heights, such as the short, medium and tall loop heights 118a, 118b and 118c for product 110 in accompanying FIG. 7B.

[0055] This invention improves the performance of reinforced and non-reinforced panels used for interiors of refrigerated transportation equipment. Admittedly, surface treatments are used all the time for improving adhesion with glues, etc., but this new dimensional “loop” is truly novel in its unique improvements in this field of use.

[0056] Two representative sizes of fully looped materials, made for Applicant by Apex Mills, were manufactured for size comparison purposes. The first was designated RH87 loop material (as seen below):

TABLE-US-00001 TEST STYLE CONTENT: RH87 METHOD 100% POLYESTER ASTM D629 WEIGHT (oz/sq yd):  5.3 +/− 10% ASTM D3776 WALES (width)/inch: 9 +/− 1 ASTM D3887 COURSES (length)/inch: 27 +/− 3  ASTM D3887 INSTRON BALL BURST MIN 75 ASTM D3787 (lbf): MULLEN BURST: N/A ASTM D3786 THICKNESS (inch): 0.18 +/− 0.02 ASTM D1777 TENSILE (LENGTH) N/A ASTM D5034 (WIDTH) N/A ASTM D5034 117 Loops/sq inch +/− 12 Loops Loop height: 6 mm +/− 0.6 mm AT BASE Loop height: 4 mm +/− 0.4 mm

[0057] For a smaller, more compact style of fabric backing, a second scale of substrate was made and tested. Called RJ30, its particulars are as follows:

TABLE-US-00002 TEST STYLE CONTENT: RJ30 METHOD 100% POLYESTER ASTM D629 WEIGHT (oz/sq yd): 4.3 +/− 10% ASTM D3776 WALES (width)/inch: 9 +/− 1  ASTM D3887 COURSES (length)/inch: 27 +/− 3  ASTM D3887 INSTRON BALL BURST MIN 75 ASTM D3787 (lbf): MULLEN BURST: N/A ASTM D3786 THICKNESS (inch): 0.11 +/− 0.011 ASTM D1777 TENSILE (LENGTH) N/A ASTM D5034 (WIDTH) N/A ASTM D5034 63 Loops/sq inch +/− 6.5 Loops Loop height: 5 mm +/− 0.5 mm AT BASE Loop height: 3 mm +/− 0.3 mm

[0058] RH87 and RJ30 are both warp knitted fabrics utilizing a unique construction where 2 multifilament yarn systems form the substrate and a 3.sup.rd heavy gauge monofilament yarn system is anchored on 1 needle and cast off on the alternate needle to form a loop on one side of the fabric while leaving the alternate side of the fabric smooth. Both RJ30 and RH87 are made with 100% Polyester but other yarn types can be substituted therefor.

[0059] FIGS. 3 through 6 show other relevant material modifications prior to the present invention. FIG. 3 shows looped layers L onto one another in a typical fabric material. FIG. 4 shows a prior art substrate S from which a single strand of line is embedded from only the adjoining base elements B. FIG. 5 shows a prior art scrim section with its non-woven mat M beneath composite sheet C, similar to the main disclosure of Applicant's U.S. Pat. No. 6,743,742. And FIG. 6 is a modified variation of FIG. 5 with an intentionally roughed up outer fibrous layer O which still does not achieve the bond adhesion levels observed with the present invention.

[0060] FIGS. 7 and 7A show one preferred embodiment of interior wall panel 10 made according to this invention. The exterior, metal wall to this panel is indicated with a TM designation and its innermost wall panel interior with a TI designation.

[0061] Said wall panel 10 has a base material 12, into which is sewn a special looped fabric backing, generally 14, consisting of an underlying substrate layer 16 from which a plurality of polymer loops 18 are interwoven and outwardly extend. The latter loops are encased in an outer foam layer 20 for subsequent lamination to form the wall panel proper. Such loops are necessary and critical for integration into the base for making an improved GRTP product hereby.

[0062] FIG. 7B shows an alternate embodiment of wall panel 110, with its own fabric backing 114, and corresponding substrate layer 116 from which three representative heights of variably sized loops, 118a, 118b and 118c are interwoven, and then combed or brushed upward to “stand at attention” prior to being foamed about.

[0063] FIG. 8 is a photograph depicting a forward edge to a representative section of the base material from FIGS. 7 and 7A with its rows of interwoven fabric backing attached thereto and its plurality of consistently-sized loops 18 extending upwardly therefrom . . . all before encasement in the foam to make the improved interior wall panel of this invention.

[0064] FIG. 9 shows an underside of substrate layer 16 (lined) from which the respective rows of loops 18 (unlined, for better illustration) are interwoven. Note how all of the loops tie into the base or weave of substrate layer 16. That base is necessary for embedding into the laminate product: the base sticks to the trailer backing interior TI while the loops of that product “stick” firmly into the foam injected between the interior TI and metal exterior TM.

[0065] FIG. 10 shows a close up view of one representative row of loops 18 with a single braid of the substrate layer 16 wrapped thereabout consistently lined like the two components in preceding FIG. 9.

[0066] Finally, FIG. 11 is a representative trailer product with an exterior metal TM surface, showing in cutaway to expose one of its interior walls TI made using the panel improvements 10 of this invention.

[0067] Having described the currently preferred embodiments, it is to be understood that the scope of this invention may be further described by the scope of the appended claims.