There are provided a lithium-containing garnet crystal high in density and ionic conductivity, and an all-solid-state lithium ion secondary battery using the lithium-containing garnet crystal. The lithium-containing garnet crystal has a chemical composition represented by Li.sub.7-xLa.sub.3Zr.sub.2-xTa.sub.xO.sub.12 (0.2≦x≦1), and has a relative density of 99% or higher, belongs to a cubic system, and has a garnet-related structure. The lithium-containing garnet crystal has a lithium ion conductivity of 1.0×10.sup.−3 S/cm or higher. Further, this solid electrolyte material has a lattice constant a of 1.28 nm≦a≦1.30 nm, and lithium ions occupy 96h-sites in the crystal structure. The all-solid-state lithium ion secondary battery has a positive electrode, a negative electrode and a solid electrolyte, and the solid electrolyte is constituted of the lithium-containing garnet crystal according to the present invention.

A technique for exfoliating a transition metal dichalcogenide material to produce separated nano-scale platelets includes combining the transition metal dichalcogenide material with a liquid to form a slurry, wherein the transition metal dichalcogenide material includes layers of nano-scale platelets and has a general chemical formula MX.sub.2, and wherein M is a transition metal and X is sulfur, selenium, or tellurium. The slurry of the transition metal dichalcogenide material is treated with an oxidant to form peroxo-metalate intermediates on an edge region of the layers of nano-scale platelets of the transition metal dichalcogenide material. The peroxo-metalate intermediates is treated with a reducing agent to form negatively charged poly-oxo-metalates to induce separation of the transition metal dichalcogenide material into the separated nano-scale platelets of the transition metal dichalcogenide material.

A lithium ion-conducting compound, having a garnet-like crystal structure, and having the general formula: Li.sub.n[A.sub.(3-a′-a″)A′.sub.(a′)A″.sub.(a″)][B.sub.(2-b′-b″)B′.sub.(b′)B″.sub.(b″)][C′.sub.(c′)C″.sub.(c″)]O.sub.12, where A, A′, A″ stand for a dodecahedral position of the crystal structure, where A stands for La, Y, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm and/or Yb, A′ stands for Ca, Sr and/or Ba, A″ stands for Na and/or K, 0<a′<2 and 0<a″<1, where B, B′, B″ stand for an octahedral position of the crystal structure, where B stands for Zr, Hf and/or Sn, B′ stands for Ta, Nb, Sb and/or Bi, B″ stands for at least one element selected from the group including Te, W and Mo, 0<b′<2 and 0<b″<2, where C and C″ stand for a tetrahedral position of the crystal structure, where C stands for Al and Ga, C″ stands for Si and/or Ge, 0<c′<0.5 and 0<c″<0.4, and where n=7+a′+2.Math.a″−b′−2.Math.b″−3.Math.c′−4.Math.c″ and 5.5<n<6.875.

A mesoporous metal oxide materials with a chiral organization; and a method for producing it, in the method a polymerizable metal oxide precursor is condensed inside the pores of chiral nematic mesoporous silica by the so-called “hard templating” method. As a specific example, mesoporous titanium dioxide is formed inside of a chiral nematic silica film templated by nanocrystalline cellulose (NCC). After removing the silica template such as by dissolving the silica in concentrated aqueous base, the resulting product is a mesoporous titania with a high surface area. These mesoporous metal oxide materials with high surface area and chiral nematic structures that lead to photonic properties may be useful for photonic applications as well as enantioselective catalysis, photocatalysis, photovoltaics, UV filters, batteries, and sensors.

A mesoporous metal oxide materials with a chiral organization; and a method for producing it, in the method a polymerizable metal oxide precursor is condensed inside the pores of chiral nematic mesoporous silica by the so-called “hard templating” method. As a specific example, mesoporous titanium dioxide is formed inside of a chiral nematic silica film templated by nanocrystalline cellulose (NCC). After removing the silica template such as by dissolving the silica in concentrated aqueous base, the resulting product is a mesoporous titania with a high surface area. These mesoporous metal oxide materials with high surface area and chiral nematic structures that lead to photonic properties may be useful for photonic applications as well as enantioselective catalysis, photocatalysis, photovoltaics, UV filters, batteries, and sensors.

The invention relates to Eu.sup.2+-activated phosphors, to a process of its preparation, the use of these phosphors in electronic and electro optical devices, such as light emitting diodes (LEDs) and solar cells and especially to illumination units comprising said magnesium alumosilicate-based phosphors.

The present invention discloses a dielectric ceramic formula enabling one to obtain a multilayer ceramic capacitor by alternatively stacking the ceramic dielectric layers and base metal internal electrodes. The dielectric ceramic composition comprises a primary ingredient:

[(Na.sub.1-xK.sub.x).sub.sA.sub.1-s].sub.m[(Nb.sub.1-yTa.sub.y).sub.uB1.sub.vB2.sub.w)]O.sub.3

wherein:
A is at least one selected from the alkaline-earth element group of Mg, Ca, Sr, and Ba;
B1 is at least one selected from the group of Ti, Zr, Hf and Sn;
B2 is at least one selected from transition metal elements;
and wherein:
x, y, s, u, v, and w are molar fractions of respective elements, and m is the molar ratio of [(Na.sub.1-xK.sub.x).sub.sA.sub.1-s] and [(Nb.sub.1-yTa.sub.y).sub.uB1.sub.vB2.sub.w)]. They are in the following respective range:
0.93≤m≤1.07;
0.7≤s≤1.0;
0.00≤x≤0.05; 0.00≤y≤0.65;
0.7≤u≤1.0; 0.0≤v≤0.3; 0.001≤w≤0.100;
a first sub-component composes of at least one selected from the rare-earth compound,
wherein the rare-earth element is no more than 10 mol % parts with respect to the main component; and
a second sub-component composes a compound with low melting temperature to assist the ceramic sintering process, said frit, which is Li free and could be at least one selected from fluorides, silicates, borides, and oxides. The content of frit is within the range of 0.01 mol % to 15.00 mol % parts with respect to the main component.

A composite wafer having an oxide single-crystal film transferred onto a support wafer, the film being a lithium tantalate or lithium niobate film, and the composite wafer being unlikely to have cracking or peeling caused in the lamination interface between the film and the support wafer. More specifically, a method of producing the composite wafer, including steps of: implanting hydrogen atom ions or molecule ions from a surface of the oxide wafer to form an ion-implanted layer inside thereof; subjecting at least one of the surface of the oxide wafer and a surface of the support wafer to surface activation treatment; bonding the surfaces together to obtain a laminate; heat-treating the laminate at 90° C. or higher at which cracking is not caused; and exposing the heat-treated laminate to visible light to split along the ion-implanted layer to obtain the composite wafer.

A dielectric material, a method of manufacturing thereof, and a dielectric device and an electronic device including the same. A dielectric material includes a layered metal oxide including a first layer having a positive charge and a second layer having a negative charge which are laminated, a monolayer nanosheet exfoliated from the layered metal oxide, a nanosheet laminate of the monolayer nanosheets, or a combination thereof, wherein the dielectric material includes a two-dimensional layered material having a two-dimensional crystal structure and the two-dimensional layered material is represented by Chemical Formula 1.

A dielectric material, a method of manufacturing thereof, and a dielectric device and an electronic device including the same. A dielectric material includes a layered metal oxide including a first layer having a positive charge and a second layer having a negative charge which are laminated, a monolayer nanosheet exfoliated from the layered metal oxide, a nanosheet laminate of the monolayer nanosheets, or a combination thereof, wherein the dielectric material includes a two-dimensional layered material having a two-dimensional crystal structure and the two-dimensional layered material is represented by Chemical Formula 1.