An apparatus for manufacturing glass includes a furnace. A doghouse of the furnace receives and melts solid-glass forming material using one or more submerged combustion burners. An elongated tank positioned downstream of the doghouse includes a melting chamber, a refining chamber, and a thermal conditioning. The melting chamber has in inlet through which molten glass is received from the doghouse. The refining chamber is positioned downstream of the melting chamber and receives molten glass from the melting chamber. The thermal conditioning chamber is positioned downstream of the refining chamber and receives molten glass from the refining chamber. Additionally, the thermal conditioning chamber delivers molten glass to a glass forming machine.

A method for forming a laminated glass article may include flowing a molten first glass composition having a first R.sub.2O concentration and a first fining agent with a first fining agent concentration. The method may also include flowing a molten second glass composition having a second R.sub.2O concentration less than the first R.sub.2O concentration of the first glass composition and a second fining agent with a second fining agent concentration that is greater than or equal to the first fining agent concentration of the first glass composition. The molten first glass composition may be contacted with the molten second glass composition to form an interface between the molten first glass composition and the molten second glass composition.

A composite plate is mainly made from the following raw materials in percentage by weight: 35% to 45% of calcium carbonate, 45% to 55% of cullet, 5% to 15% of unsaturated polyester resin, 0.1% to 1% of a curing agent, 0.1% to 1% of an auxiliary agent, wherein a ratio of an amount of the calcium carbonate to an amount of the cullet is 0.75%. The invention employs cullet, calcium carbonate, and resin as the main raw materials to prepare an artificial stone plate; no natural quartz is used, and hence the raw material cost is low. A reasonable ratio of cullet to calcium carbonate reduces the use of resin, which further reduces the raw material cost. Through a reasonable combination of different raw materials, the composite plate of the invention has physical and chemical properties and decorative abilities that are similar to those of traditional artificial quartz stone.

The present invention relates to a black quartz glass comprising Si of 0.5 to 10 mass %, SiO of 0.1 to 5 mass % and SiO.sub.2 of the residue, wherein the SCE reflectance at a wavelength of 350 nm to 750 nm is 10% or less; a method for producing the black quartz glass, comprising: pressure-molding a powder obtained by mixing and consolidating (1) fumed silica, or (2) a mixture powder of fumed silica and a synthetic silica powder, or (3) a mixture powder of fumed silica, spherical silica and a synthetic silica powder, with a Si powder of 0.5 to 10 mass % and a SiO powder of 0.1 to 5 mass %, and heating and sintering the pressure-molded product in the atmosphere; and a product comprising a black quartz glass member made of the black quartz glass. The present invention allows to provide a black quartz glass which has an excellent light-shielding property, has no risk of causing contamination in a step of using it, has sufficient color uniformity when the size is enlarged, and is capable of producing a large ingot, and to provide a method for producing the black quartz glass with excellent productivity even in the large ingot, and to provide a black quartz glass product made of the black quartz glass.

The coated glass sheet of the present invention includes: a glass sheet; and a coating film provided on at least one principal surface of the glass sheet and having a smooth surface. The coating film includes: isolated closed pores present within the coating film; and a matrix. The coating film is substantially free of open pores open at the surface of the coating film. For the coated glass sheet of the present invention, a transmittance gain is 2.5% or more, the transmittance gain being calculated by subtracting an average transmittance of the glass sheet as determined by applying light having wavelengths of 380 to 1100 nm to the glass sheet in the absence of the coating film on the surface of the glass sheet from an average transmittance of the coated glass sheet as determined by applying light having the wavelengths to the coated glass sheet from a side on which the coating film lies.

A glass composition with low thermal radiative conductivity at high temperature has the following components in weight percentage, expressed with respect to the total weight of the glass composition: SiO.sub.2 50-85%; Al.sub.2O.sub.3 0-30%, B.sub.2O.sub.3 0-20%; Na.sub.2O 0-25%; CaO 0-25%; MgO 0-15%; K.sub.2O 0-20%; BaO 0-20%; Fe.sub.2O.sub.3 total 0.002-0.1%. The glass also includes NiO at a level of 0.0001% to 0.0020% by weight of the total glass composition.

One aspect of the present invention provides a powder containing three components of ZnO, Al.sub.2O.sub.3 and SiO.sub.2, wherein each content of the three components is ZnO: 17 to 43% by mole, Al.sub.2O.sub.3: 9 to 20% by mole and SiO.sub.2: 48 to 63% by mole, based on the sum of the contents of the three components.

The present invention provides a ceramic powder, in which -eucryptite or a -quartz solid solution is precipitated as a main crystal phase, and which includes TiO.sub.2 and/or ZrO.sub.2.

The present invention provides a ceramic powder, in which -eucryptite or a -quartz solid solution is precipitated as a main crystal phase, and which includes TiO.sub.2 and/or ZrO.sub.2.

To provide a method for recycling a solar cell module glass, which enables development of other novel applications of a waste glass of a solar cell module while controlling an elution amount of Sb from the waste glass into water. Disclosed is a method for recycling a solar cell module glass, the method comprising: grinding a solar cell module glass into a glass powder; adding at least one foaming agent selected from SiC, CaCO.sub.3 and a seashell, and a particular inhibitor to the glass powder to produce a mixture; and heating the mixture to 700 to 1,100 C. to produce a foam glass.