A glass article has a refractive index n.sub.G≥1.95 and an R-number in a range of from 0.900 to 1.050. The R-number is calculated according to the following formula:

[00001]$R=\left(n_G-1\right)\left(\frac{\ln \left[\frac{{\lambda }_G^2-{\lambda }_{\min }^2}{{\lambda }_G^2-{\lambda }_{\max }^2}.Math.\frac{{\lambda }_{\max }^2}{{\lambda }_{\min }^2}\right]}{42\ln \left[\frac{{\lambda }_B^2-{\lambda }_{\min }^2}{{\lambda }_B^2-{\lambda }_{\max }^2}.Math.\frac{{\lambda }_R^2-{\lambda }_{\max }^2}{{\lambda }_R^2-{\lambda }_{\min }^2}\right]}+\frac{1}{2.8}\right).$

λ.sub.R=656 nm, λ.sub.G=587 nm and λ.sub.B=486 nm, λ.sub.min=33 nm, and n.sub.G is a refractive index of the glass article at a wavelength of 587 nm.

A method of manufacturing a resorbable, macroporous bioactive glass scaffold comprising approximately 15-45% CaO, 30-70% SiO.sub.2, 0-25% Na.sub.2O, 0-17% P.sub.2O.sub.5, 0-10% MgO and 0-5% CaF.sub.2 by mass percent, produced by mixing with pore forming agents and specified heat treatments.

A method of producing flint glass using submerged combustion melting involves introducing a vitrifiable feed material into a glass melt contained within a submerged combustion melter. The vitrifiable feed material is formulated to provide the glass melt with a glass chemical composition suitable for producing flint glass articles. To that end, the glass melt comprises a total iron content expressed as Fe.sub.2O.sub.3 in an amount ranging from 0.04 wt % to 0.06 wt % and also has a redox ratio that ranges from 0.1 to 0.4, and the vitrifiable feed material further includes between 0.008 wt % and 0.016 wt % of selenium or between 0.1 wt % and 0.2 wt % of manganese oxide in order to achieve an appropriate content of selenium or manganese oxide in the glass melt.

A borophosphate glass composition including B.sub.2O.sub.3, P.sub.2O.sub.5, and CaO, and optionally a source additive selected from: Li.sub.2O, Na.sub.2O, K.sub.2O, Al.sub.2O.sub.3, ZnO, MgO, Fe.sub.2O.sub.3/FeO, CuO/Cu.sub.2O, and mixtures thereof, as defined herein. Also disclosed are bioactive compositions or substrates including the disclosed borophosphate glass composition, and at least one live cell. Also disclosed are methods of inhibiting or increasing the relative amount of species containing boron, phosphorous, or both, being released into an aqueous solution from aborophosphate glass composition defined herein. Also disclosed is a method of proliferating cells on a bioactive substrate as defined herein. Also disclosed are related glass compositions that exclude one of B.sub.2O.sub.3, P.sub.2O.sub.5, and CaO.

Provided is a silica glass member which exhibits high optical transparency to vacuum ultraviolet light and has a low thermal expansion coefficient of 4.0−10.sup.−7/K or less at near room temperature, particularly a silica glass member which is suitable as a photomask substrate to be used in a double patterning exposure process using an ArF excimer laser (193 nm) as a light source. The silica glass member is used in a photolithography process using a vacuum ultraviolet light source, in which the fluorine concentration is 1 wt % or more and 5 wt % or less, and the thermal expansion coefficient at from 20° C. to 50° C. is 4.0×10.sup.−7/K or less.

The present invention provides a glass sheet having soda-lime-silica glass composition with a high visible light transmittance (L.sub.tC) of at least 89% with a dominant wavelength (DW) from about 490 to 505 nanometers and purity (Pe) of no more than 1% for control thickness of 5.66 mm and methods of making the same. The glass composition comprising a low iron raw material, a total iron oxide (Fe.sub.2O.sub.3) of 0.02 to 0.06 wt. %, ferrous (FeO) from 0.006 to 0.02 wt. %, redox (FeO/Fe.sub.2O.sub.3) from about 0.30 to 0.55, Cr.sub.2O.sub.3 from about 0.3 to 10 ppm, TiO.sub.2 from about 50 to 500 ppm, SnO.sub.2 from about 10 to 500 ppm, and a critical amount from about 0.10 to 0.25 wt. % of SO.sub.3. The low content of iron oxide is achieved by the partial substitution of regular raw materials by low iron raw materials, with a complete substitution of regular dolomite by a low iron dolomite with a maximum content of 0.020 wt. % Fe.sub.2O.sub.3.

An aluminoborate glass composition, including B.sub.2O.sub.3, Al.sub.2O.sub.3, P.sub.2O.sub.5, Na.sub.2O, and CaO, as defined herein. Also disclosed are bioactive compositions including the disclosed aluminoborate glass composition, a suitable fluid, and at least one live cell. Also disclosed is method of limiting the amount of boron released into an aqueous solution from a disclosed aluminoborate-containing glass composition as defined herein. Also disclosed is a method of proliferating cells on a bioactive substrate as defined herein.

A bioactive glass-ceramic composition as defined herein. Also disclosed are methods of making and using the disclosed compositions.

An aluminoborate composition, an alumino-borosilicate glass composition, or a mixture thereof, and solid or hollow microspheres thereof, as defined herein. Also disclosed are methods of making and using the disclosed compositions, for example, forming microspheres for use in bioactive applications, and composition extracts for use in treating or healing wounds.

A glass-ceramic-ferrite composition containing a glass, a ferrite, and a ceramic filler, in which the glass contains, by weight, about 0.5% to about 5.0% R.sub.2O (R represents at least one selected from the group consisting of Li, Na, and K), about 5.0% or less Al.sub.2O.sub.3, about 10.0% to about 25.0% B.sub.2O.sub.3, and about 70.0% to 85.0% SiO.sub.2 with respect to the total weight of the glass, the percentage by weight of the ferrite is about 10% to 80% with respect to the total weight of the composition, the ceramic filler contains at least forsterite selected from forsterite and quartz, the percentage by weight of the forsterite is about 1% to about 10% with respect to the total weight of the composition, and the percentage by weight of the quartz is about 40% or less with respect to the total weight of the composition.