The present invention relates to a curable silicone composition comprising: (A) at least one organopolysiloxane having at least two alkenyl groups per molecule; (B) at least one mercapto functional organopolysiloxane having at least two thiol groups per molecule; (C) at least one photopolymerization initiator; and, (D) 2,6-di-tert-butyl-4-methylphenol (BHT), wherein the composition has a viscosity of less than 200 mPa.Math.s at 25° C.

The invention relates to a method for preparing polyurethanes containing alkoxysilane groups, said method comprising the step of reacting a compound containing at least one NCO group with a compound containing at least one Zerewitinoff-active H atom in the presence of a catalyst component, the at least one compound containing an NCO group and/or the compound containing at least one Zerewitinoff-active H atom containing at least one alkoxysilane group, so as to obtain a polyurethane containing alkoxysilane groups. The invention also relates to a polymer containing alkoxysilane groups, a method for preparing a curable polymer, a curable polymer, a cured polymer, and use thereof. The polyurethanes are prepared with use of a thermally labile tin catalyst.

The present invention relates to an adhesive, a preparation method and application thereof, particularly the application for bonding glass fiber composites, and a bonded article obtained by using the adhesive. The adhesive comprises: a polyisocyanate having an isocyanate functionality of not less than 2; an epoxy-modified polyether polyol; a hydroxyl-containing acrylate; a redox catalyst; a silane coupling agent; optionally a polyol containing bisphenol A structure; and optionally a polymer polyol different from the epoxy-modified polyether polyol. The adhesive according to the present invention has the advantages of being insensitive to moisture, good bonding properties and a long pot life.

The present invention relates to a poly(ester-urethane), to a poly(ester-urea-urethane), and also to aqueous dispersions of these and to their uses in aqueous coatings, adhesives or sealants, in particular as binder in paints or varnishes.

An adhesive sealant composition of at least one moisture-crosslinkable prepolymer and an anti-sagging agent of 5% to 30% by weight of a thixotropic composition of 10% to 40% by weight of a bisurea a) obtained by reaction of a primary aliphatic amine a1) with a diisocyanate a2) having a molar mass of less than 500 g/mol, and 60% to 90% by weight of an ester b) of formula (I): ##STR00001##
in which R.sup.1, R.sup.2 and R.sup.3 are an oxycarbonylalkyl radical having from 4 to 20 carbon atoms, R.sup.4 is hydrogen, methyl or ethyl or —CH.sub.2—R.sup.5 in which R.sup.5 is oxycarbonylalkyl having from 4 to 20 carbon atoms, in the form of a suspension of solid particles of bisurea a) in a continuous phase formed by ester b).

The present invention relates to a method for producing polyether carbonates containing alkoxysilyl groups in which (a) an unsaturated polyether carbonate polyol is reacted with (b) an alkoxysilane compound of formula (II) Si(X).sub.m(R1).sub.n(R2).sub.o (II), where X=H, Y—S—H and Y=C1-C22 alkylene, C6-C14 arylene, C7-C14 aralkylene, C7-C14 alkylarylene; R1=C1-C8 alkoxy, C7-C20-aralkoxy, C6-C14 aroxy, C7-C20 alkylaroxy; R2=C1-C22 alkyl, C6-C14 aryl, C7-C14 aralkyl, C7-C14 alkylaryl, and m and n represent, independently of one another, an integer ≧1, o is zero or an integer ≧1 and m+n+o=4. The invention further relates to the production of a polyurethane polymer using such a polyether carbonate, a cross-linked, siloxane group containing polymer and a molded part containing or consisting of said cross-linked polymer.

An asphalt composition comprising 0.1 to 10.0 wt.-% monomeric MDI based on the total weight of the composition.

The present application relates to a cured product and the use thereof. The cured product has excellent processability, workability, and adhesive properties or the like, and does not cause whitening and surface stickiness, etc. The cured product has excellent transparency, moisture resistance, mechanical properties, and cracking resistance, etc. The cured product, for example, may be applied as an encapsulant or an adhesive material of a semiconductor device to provide a device having high long-term reliability.

Disclosed by the present invention is a method for preparing a reactive sealant resin, the method comprising: (1) under the action of an alkali catalyst, polymerizing a hydroxyl-containing initiator with an epoxy compound to obtain a polyether polyol; (2) adding an alkoxide reagent and a halogenated end-capping agent containing a double bond to the polyether polyol obtained in step (1) for reaction, so as to obtain a crude double-bonded polyether product, and refining the crude product to obtain a modified polyether product; and (3) subjecting the modified polyether and hydrogen-containing silane to silane end-capping reaction under the action of a hydrosilylation catalyst, so as to obtain the target product, i.e., a reactive sealant resin. The resin has excellent properties as well as good adhesion and paintability.

A sealing material composition for LED has excellent heat-resistant transparency, adhesion, and crack resistance, and low sulfur gas permeability. A sealing material composition for LED has the following (A), (B), (C), and (D):

(A): polysiloxane containing units (1-1), (1-2), and (1-3):

##STR00001##

wherein R.sup.1 is C.sub.1-12 alkyl or C.sub.6-20 aryl, R.sup.2 is hydrogen, C.sub.1-12 alkyl, or Si constituting main chain of polysiloxane as (A); (B): polysiloxane containing units (2-1), (2-2), and (2-3):

##STR00002##

wherein R.sup.3 and R.sup.4 are each hydrogen, C.sub.1-12 alkyl, or Si constituting main chain of polysiloxane as (B); (C): adhesive; and (D): condensation catalyst for silanol group.