Disclosed are methods for forming thin polymeric films on a surface of an article by deposition from the vapor phase. In certain embodiments, the method comprises depositing the polymeric film in situ inside a space or enclosure contained within the article. In other embodiments, the method comprises depositing a film from vapor phase by thermal degradation of an initiator precursor without the need for an external filament.

There is described an acrylic polyester resin, obtainable by grafting an acrylic polymer with a polyester material. The polyester material is obtainable by polymerizing (i) a polyacid component, with (ii) a polyol component. At least one of the polyacid component and/or the polyol component comprises a monomer having an aliphatic group containing at least 15 carbon atoms. At least one of the polyacid component and/or the polyol component comprises a functional monomer operable to impart functionality on to the polyester resin, such that an acrylic polymer may be grafted with the polyester material via the use of said functionality. Also provided is an aqueous coating composition comprising the acrylic polyester resin and a packaging coated with the composition.

A zirconium nitride powder having a volume resistivity of 107 Ω.Math.cm or more in the state of the pressurized powder body hardened at a pressure of 5 MPa, and a particle size distribution D90 of 10 μm or less when ultrasonically dispersed for 5 minutes in a state of being diluted with water or an alcohol having a carbon number of which is in a range of 2 to 5. Also, the zirconium nitride powder is dispersed in an acrylic monomer or an epoxy monomer to prepare a monomer dispersion. Further, the zirconium nitride powder is dispersed in a dispersing medium as a black pigment and further a resin is mixed to prepare a black composition.

The present invention addresses the problem of providing an aqueous paint composition that has a relatively high solid content ratio and that is capable of forming a coating film having excellent brilliance. The present invention provides an aqueous paint composition that contains (A) a water-dispersible hydroxy-containing acrylic resin, (B) a flake-effect pigment, and (C) a water-dispersible cellulose-based rheology control agent, wherein the content of the flake-effect pigment (B) is within a range of 1 to 50 parts by mass based on 100 parts by mass of the resin solids content in the aqueous paint composition, and the aqueous paint composition has a solids content of more than 10 mass % and 35 mass % or less.

The present invention addresses the problem of providing an aqueous paint composition that has a relatively high solid content ratio and that is capable of forming a coating film having excellent brilliance. The present invention provides an aqueous paint composition that contains (A) a water-dispersible hydroxy-containing acrylic resin, (B) a flake-effect pigment, and (C) a water-dispersible cellulose-based rheology control agent, wherein the content of the flake-effect pigment (B) is within a range of 1 to 50 parts by mass based on 100 parts by mass of the resin solids content in the aqueous paint composition, and the aqueous paint composition has a solids content of more than 10 mass % and 35 mass % or less.

The present invention provides a method for printing energy-curable ink and coating compositions that have good adhesion to substrates, good print quality, solvent and scratch resistance, and low potential for migration of uncured monomers. The method comprises the steps of printing the ink or coating onto a substrate; partially curing the printed ink or coating by irradiating with UV energy; optionally printing and partially UV curing additional ink layers printed on the first layer; and completing curing via exposure to electron beam radiation, wherein the EB cure dose is greater than or equal to 20 kGy, and the accelerating voltage is greater than or equal to 70 keV.

The present invention relates to a peelable coating film having silica particles fixed to a surface thereof, a coating material for hydrophilic-coating-film formation which includes colloidal silica, an alkali metal silicate, and an aqueous medium, and a coating-material set including the coating material for hydrophilic-coating-film formation and a coating material for peelable-coating-film formation including an aqueous dispersion type resin composition.

The present invention relates to a peelable coating film having silica particles fixed to a surface thereof, a coating material for hydrophilic-coating-film formation which includes colloidal silica, an alkali metal silicate, and an aqueous medium, and a coating-material set including the coating material for hydrophilic-coating-film formation and a coating material for peelable-coating-film formation including an aqueous dispersion type resin composition.

Provided is an aqueous coating composition which has excellent storage stability and whereby high coating film performance in terms of hardness, water resistance, etc., can be exhibited even when the aqueous coating composition is cured at a relatively low temperature. Disclosed is an aqueous coating composition which contains (A) a resin containing hydroxyl groups and carboxyl groups, (B) a blocked polyisocyanate compound, (C) a phosphate-group-containing compound, and (D) a basic compound, and which has a pH in the range of 7.0-8.2, wherein the basic compound (D) contains a specific quantity of (D1) a basic compound which has an acid dissociation constant (PKa) in the range of 7.0-8.5 and a boiling point in the range of 100-200° C.

A laminate including a base material and a resin layer provided on at least one surface of the base material. The resin layer is formed of a heat- or active energy ray-curable resin composition, and an outermost surface of the laminate on the one surface side of the base material has an unevenness containing a wrinkle structure.