Provided is a method comprises: continuously forming an elongated, glass film having marginal portions from molten glass into a given shape having two marginal portions, in width-directional opposite edge regions thereof, wherein the glass film having marginal portions has the marginal portions, and an effective portion formed in a width-directional central region of the glass film having marginal portions; annealing the glass film having marginal portions; continuously forming resin tapes on the glass film having marginal portions at positions adjacent to and away by a given distance from the respective marginal portions, to extend in a length direction of the glass film having marginal portions; and continuously removing each of the marginal portions from the glass film having marginal portions, along a position between the marginal portion and a corresponding one of the resin tapes, or at a given width-directional position within the corresponding resin tape.

The present invention relates to a resin composition, comprising: a modified vinyl acetal resin which comprises 20 to 80 mol % of ethylene units and 4 to 76 mol % of vinyl alcohol units based on all monomer units constituting the resin, and has an acetalization degree of 5 to 80 mol %; and an alkali metal salt and/or an alkaline earth metal salt of a strong acid, wherein a total content of the alkali metal salt and/or the alkaline earth metal salt of the strong acid is 0.0005 to 0.06 part by mass with respect to 100 parts by mass of the modified vinyl acetal resin.

A biodegradable cellulose fiber-based substrate, at least one side of which is coated with a release coating including: a) at least one water-soluble polymer (WSP) containing hydroxyl groups, and b) at least one lactone substituted with at least one linear or branched and/or cyclic C.sub.8-C.sub.30 hydrocarbon chain which may contain heteroatoms. The biodegradable substrate is certified biodegradable in accordance with EN 13432. A method of production thereof is also disclosed.

Provided is an interlayer film for laminated glass capable of effectively enhancing the sound insulating property at 6300 Hz while effectively preventing deterioration in sound insulating property at 3150 Hz in laminated glass. An interlayer film for laminated glass according to the present invention has a one-layer structure or a two or more-layer structure and includes a resin layer containing a resin and a plasticizer. The interlayer film has a resonance frequency X of 550 Hz or more and 740 Hz or less, a loss factor Y in a secondary mode of 0.35 or more, and satisfies a formula: Y>0.0008X−0.142 in a measurement of resonance frequency in a secondary mode in a damping test for laminated glass according to a central exciting method of laminated glass, when the laminated glass is obtained by arranging the interlayer film between two glass plates of 25 mm wide, 300 mm long and 2 mm thick.

A cellulose fiber-based substrate, at least one side of which is coated with an aqueous mixture composed of: a) at least one water-soluble polymer (WSP) containing hydroxyl groups, b) at least one lactone substituted with at least one linear or branched and/or cyclic C.sub.8-C.sub.30 hydrocarbon chain which may contain heteroatoms, c)at least one crosslinking agent. A method of production and use thereof.

Resin compositions, layers, and interlayers comprising a poly(vinyl acetal) resin that includes residues of an aldehyde other than n-butyraldehyde are provided. Such compositions, layers, and interlayers can exhibit enhanced or optimized properties as compared to those formulated with comparable poly(vinyl n-butyral) resins.

A glass laminate includes a non-glass substrate with a first surface and a second surface opposite the first surface. A glass sheet is laminated to the first surface of the non-glass substrate. A barrier film is laminated to the second surface of the non-glass substrate and includes a first surface adjacent to the non-glass substrate, a second surface opposite the first surface. A thickness of the barrier film can be at most about 0.5 mm. The second surface of the barrier film can define an outer surface of the glass laminate. The barrier film can be a multi-layer barrier film with a metal layer and a polymer layer. An absolute value of a flatness of the glass laminate determined according to European Standard EN 438 after exposure to 23° C. and 90% relative humidity for 7 days can be at most about 3 mm/m.

Provided is an interlayer film for laminated glass capable of effectively enhancing the sound insulating property at 6300 Hz while effectively preventing deterioration in sound insulating property at 3150 Hz in laminated glass. An interlayer film for laminated glass according to the present invention has a one-layer structure or a two or more-layer structure and includes a resin layer containing a resin and a plasticizer. The interlayer film has a resonance frequency X of 550 Hz or more and 740 Hz or less, a loss factor Y in a secondary mode of 0.35 or more, and satisfies a formula: Y>0.0008X−0.142 in a measurement of resonance frequency in a secondary mode in a damping test for laminated glass according to a central exciting method of laminated glass, when the laminated glass is obtained by arranging the interlayer film between two glass plates of 25 mm wide, 300 mm long and 2 mm thick.

A pigmented aqueous inkjet ink set for manufacturing decorative panels includes a cyan aqueous inkjet ink containing a copper phthalocyanine pigment; a red aqueous inkjet ink containing a red pigment selected from the group consisting of C.I. Pigment Red 254, C.I. Pigment Red 122, C.I. Pigment Red 176 and mixed crystals thereof; a yellow aqueous inkjet ink containing a pigment C.I Pigment Yellow 150 or a mixed crystal thereof; and a black aqueous inkjet ink containing a carbon black pigment, wherein the aqueous inkjet inks contain a surfactant. An inkjet printing method for manufacturing decorative panels is also disclosed.

The present invention aims to provide a filling-bonding material that is suitably used to fill a space between parts, while bonding the parts, in optical devices in various shapes not limited to flat shapes. The present invention also aims to provide a protective sheet-equipped filling-bonding material, a laminate, an optical device, and a protective panel for an optical device each including the filling-bonding material. Provided is a filling-bonding material having a shape with an uneven thickness.