The present invention provides a maleimide-based copolymer, a method for producing same, and a resin composition obtained using same.

This maleimide-based copolymer contains 40-60 mass % of aromatic vinyl monomer units, 5-20 mass % of vinyl cyanide monomer units, and 35-50 mass % of maleimide monomer units, and is such that a 4 mass % tetrahydrofuran solution of the copolymer has a transmittance of 90% or more for light having a wavelength of 450 nm at an optical path length of 10 mm, and the residual maleimide-based monomer amount is less than 300 ppm. This maleimide-based copolymer preferably further contains 0-10 mass % of unsaturated dicarboxylic acid anhydride monomer units, and preferably has a glass transition temperature of 165° C. or higher.

The present invention provides a maleimide-based copolymer, a method for producing same, and a resin composition obtained using same.

This maleimide-based copolymer contains 40-60 mass % of aromatic vinyl monomer units, 5-20 mass % of vinyl cyanide monomer units, and 35-50 mass % of maleimide monomer units, and is such that a 4 mass % tetrahydrofuran solution of the copolymer has a transmittance of 90% or more for light having a wavelength of 450 nm at an optical path length of 10 mm, and the residual maleimide-based monomer amount is less than 300 ppm. This maleimide-based copolymer preferably further contains 0-10 mass % of unsaturated dicarboxylic acid anhydride monomer units, and preferably has a glass transition temperature of 165° C. or higher.

The present invention provides black particles that have high electrical insulation and that can achieve high blackness in the visible light region, as well as a black coating material, a coating film, and a black matrix for a color filter each containing the black particles. Provided are black particles containing a copolymer including a structural unit derived from a pyrrole compound and a structural unit derived from a quinone compound, the black particles having an aqueous dispersion number average particle size of 100 nm or less and a zeta potential of −5 mV or less.

The present invention provides black particles that have high electrical insulation and that can achieve high blackness in the visible light region, as well as a black coating material, a coating film, and a black matrix for a color filter each containing the black particles. Provided are black particles containing a copolymer including a structural unit derived from a pyrrole compound and a structural unit derived from a quinone compound, the black particles having an aqueous dispersion number average particle size of 100 nm or less and a zeta potential of −5 mV or less.

A positive resist composition comprising a base polymer comprising recurring units (a) having the structure of an ammonium salt of a carboxylic acid having an iodized or brominated aromatic ring exhibits a high sensitivity, high resolution, low edge roughness (LER, LWR) and small size variation, and forms a pattern of good profile after exposure and development.

A positive resist composition comprising a base polymer comprising recurring units (a) having the structure of an ammonium salt of a carboxylic acid having an iodized or brominated aromatic ring exhibits a high sensitivity, high resolution, low edge roughness (LER, LWR) and small size variation, and forms a pattern of good profile after exposure and development.

The present invention provides a maleimide-based copolymer, a method for producing same, and a resin composition obtained using same. This maleimide-based copolymer contains 40-60 mass % of aromatic vinyl monomer units, 5-20 mass % of vinyl cyanide monomer units, and 35-50 mass % of maleimide monomer units, and is such that a 4 mass % tetrahydrofuran solution of the copolymer has a transmittance of 90% or more for light having a wavelength of 450 nm at an optical path length of 10 mm, and the residual maleimide-based monomer amount is less than 300 ppm. This maleimide-based copolymer preferably further contains 0-10 mass % of unsaturated dicarboxylic acid anhydride monomer units, and preferably has a glass transition temperature of 165° C. or higher.

The present invention provides a maleimide-based copolymer, a method for producing same, and a resin composition obtained using same. This maleimide-based copolymer contains 40-60 mass % of aromatic vinyl monomer units, 5-20 mass % of vinyl cyanide monomer units, and 35-50 mass % of maleimide monomer units, and is such that a 4 mass % tetrahydrofuran solution of the copolymer has a transmittance of 90% or more for light having a wavelength of 450 nm at an optical path length of 10 mm, and the residual maleimide-based monomer amount is less than 300 ppm. This maleimide-based copolymer preferably further contains 0-10 mass % of unsaturated dicarboxylic acid anhydride monomer units, and preferably has a glass transition temperature of 165° C. or higher.

A maleimide based copolymer, manufacturing method thereof, and a resin composition using the maleimide based copolymer is provided. The maleimide based copolymer includes 40 to 60 mass % of aromatic vinyl monomer unit, 5 to 20 mass % of vinyl cyanide monomer unit, 35 to 50 mass % of maleimide monomer unit, and 0 to 10 mass % of monomer copolymerizable with these monomer units. The maleimide based copolymer has a glass transition temperature of 165° C. or higher and a melt mass flow rate of 25 to 80 g/10 min measured at 265° C. with 98 N load. By using such maleimide based copolymer, flowability can be improved without decreasing heat resistance providing ability.

A maleimide based copolymer, manufacturing method thereof, and a resin composition using the maleimide based copolymer is provided. The maleimide based copolymer includes 40 to 60 mass % of aromatic vinyl monomer unit, 5 to 20 mass % of vinyl cyanide monomer unit, 35 to 50 mass % of maleimide monomer unit, and 0 to 10 mass % of monomer copolymerizable with these monomer units. The maleimide based copolymer has a glass transition temperature of 165° C. or higher and a melt mass flow rate of 25 to 80 g/10 min measured at 265° C. with 98 N load. By using such maleimide based copolymer, flowability can be improved without decreasing heat resistance providing ability.