C21D1/673

HOT STAMPED BODY

A hot stamped body with high strength and good bendability, comprising a chemical composition consisting of: in mass %, C: 0.06% or more to less than 0.20%, Si: 0.010 to 1.00%, Mn: 1.20 to 3.00%, P: 0.100% or less, S: 0.010% or less, Al: 0.010 to 0.500%, N: 0.010% or less, Nb: 0.0010 to 0.020%, Ti: 0 to 0.10%, V: 0 to 0.10%, Cr: 0 to 0.50%, Mo: 0 to 1.00%, B: 0 to 0.0100%, Ni: 0 to 0.50%, REM: 0 to 0.0100%, Mg: 0 to 0.010%, Ca: 0 to 0.0100%, and Co: 0 to 2.0%, with the balance: Fe and impurities, wherein a microstructure includes martensite: 85% or more, a proportion of regions in the martensite where GAIQ values are 35000 or more to less than 45000 is 30 area % or more, and TS×α, is 105000 or more, and α is 75 or more.

METHOD OF MANUFACTURING OVERLAPPED HOT STAMP MOLDED BODY, AND OVERLAPPED HOT STAMP MOLDED BODY

To solve a problem about warpage of a steel sheet due to a difference in temperature raising rate between an overlapped part and a one-sheet part. This manufacturing method includes: a step of heating an overlapped blank; a step of transferring the heated overlapped blank; and a step of performing presswork on the heated overlapped blank by using a die, in which in the heating step, when sheet thicknesses of the first and second steel sheets are set to t1 and t2, respectively, and an average heating rate at a sheet temperature from 20 to 800° C. of a portion with a total sheet thickness (t1+t2) of an overlapped portion, and that of a non-overlapped portion are set to V and v1, respectively, the total sheet thickness (t1+t2) is 2.5 to 5.0 mm, a maximum length L of the overlapped portion is 100 to 1100 mm, an area S1 of the first steel sheet, an area S2 of a portion, of the second steel sheet, which is overlapped with the first steel sheet, and the average heating rates V and v1 satisfy Expressions (1) to (3), and the heating is performed at a heating temperature and for a heating time within a specific range on a plane of coordinates defined by the heating time and the heating temperature.

A press hardening method

press hardening method includes the following steps: A. the provision of a steel sheet for heat-treatment, precoated with a zinc- or aluminum-based pre-coating, B. the deposition of a hydrogen barrier pre-coating over a thickness from 10 to 550 nm, and comprising at least one element chosen from among: nickel, chromium, magnesium, aluminum and yttrium, C. batch annealing of the precoated steel sheet to obtain a pre-alloyed steel sheet, the cooling after the batch annealing being performed at a speed of 29.0° C.h.sup.−1 or less, D. the cutting of the pre-alloyed steel sheet to obtain blank, E. thermal treatment of the blank to obtain a fully austenitic microstructure in the steel, F. the transfer of the blank into a press tool, G. the hot-forming of the blank to obtain a part, H. the cooling of the part obtained at step G).

A FORMING SHEET METAL PART FOR A VEHICLE FRAME AND CORRESPONDING PRODUCTION METHOD

A forming sheet metal part (1) for a vehicle frame includes: a first portion (2) being locally heat-softened after the sheet metal part (1) has been formed out. The part (1) further includes a dedicated three-dimensional distortion-absorbing area (4), defining an internal boundary (6) within which the first portion (2) is to be locally heat-softened after the sheet metal part (1) has been formed out. The distortion-absorbing area (4) is dimensioned such that once said locally heat-softening step has been performed, the internal boundary (6) is adjacent to the first portion (2) and encloses the first portion (2) to absorb the dimensional distortions induced by the locally heat-softened first portion. The invention further relates to a method for producing a forming sheet metal part (1).

Method of shaping an article from a zinc or zinc alloy coated steel blank
11519044 · 2022-12-06 · ·

A method of shaping an article from a zinc or zinc alloy coated steel blank, including the steps of: a) providing a blank of the zinc or zinc alloy coated steel; b) reheating of the blank obtained in step a) to a reheating temperature T.sub.RH in the range Ac3-200° C. of the steel; c) soaking the blank for a time up to 3 minutes at the reheating temperature T.sub.RH; d) shaping the article in a press; and e) cooling the article. The steel includes (in wt. %) C: 0.01-0.2; Mn: 3.1-9.0; Al: 0.5-3.0; and optionally further alloying elements selected from Si, Cr, V, Nb, Ti and Mo; inevitable impurities and the balance is Fe.

Method of shaping an article from a zinc or zinc alloy coated steel blank
11519044 · 2022-12-06 · ·

A method of shaping an article from a zinc or zinc alloy coated steel blank, including the steps of: a) providing a blank of the zinc or zinc alloy coated steel; b) reheating of the blank obtained in step a) to a reheating temperature T.sub.RH in the range Ac3-200° C. of the steel; c) soaking the blank for a time up to 3 minutes at the reheating temperature T.sub.RH; d) shaping the article in a press; and e) cooling the article. The steel includes (in wt. %) C: 0.01-0.2; Mn: 3.1-9.0; Al: 0.5-3.0; and optionally further alloying elements selected from Si, Cr, V, Nb, Ti and Mo; inevitable impurities and the balance is Fe.

A press hardening method

A press hardening method includes the following steps: A. the provision of a steel sheet for heat treatment, precoated with a zinc- or aluminum-based pre-coating for anti-corrosion purpose, B. the deposition of a hydrogen barrier pre-coating over a thickness from 10 to 550 nm, C. the batch annealing of the precoated steel sheet in an inert atmosphere to obtain a pre-alloyed steel sheet, D. the cutting of the pre-alloyed steel sheet to obtain blank, E. the thermal treatment of the blank to obtain a fully austenitic microstructure in the steel, F. the transfer of the blank into a press tool, G. the hot-forming of the blank to obtain a part, H. the cooling of the part obtained at step G).

A press hardening method

A press hardening method including: A. provision of a steel sheet for heat treatment, being optionally precoated with a zinc- or aluminum-based pre-coating, B. deposition of a hydrogen barrier pre-coating comprising chromium and not comprising nickel over a thickness from 10 to 550 nm, C. cutting of the precoated steel sheet to obtain a blank, D. heat treatment of the blank at a furnace temperature from 800 to 970° C., during a dwell time from 1 to 12 minutes, in an atmosphere having an oxidizing power equal or higher than that of an atmosphere consisting of 1% by volume of oxygen and equal or smaller than that of an atmosphere consisting of 50% by volume of oxygen, such atmosphere having a dew point between −30 and +30° C., E. transfer of the blank into a press tool, F. hot-forming at a temperature from 600 to 830° C. to obtain a part, G. cooling of the part obtained at step E).

ALUMINUM ALLOY-PLATED STEEL SHEET, HOT-FORMED MEMBER, AND METHODS FOR MANUFACTURING ALUMINUM ALLOY-PLATED STEEL SHEET AND HOT-FORMED MEMBER

Embodiments of the present disclosure provides an aluminum alloy-plated steel sheet having high surface quality and weldability, a hot-formed member, and methods for manufacturing the aluminum alloy-plated steel sheet and the hot-formed member. The aluminum alloy-plated steel sheet includes: a base steel sheet; and an aluminum alloy plating layer formed on the base steel sheet, wherein the aluminum alloy plating layer includes, by weight %, Zn: 21% to 35%, Si: 1% to 6.9%, Fe: 2% to 12%, and the balance of Al and inevitable impurities.

Hot stamped part and manufacturing method thereof

A blank material is formed from a steel sheet, a first quenching of the blank material is performed, and a second quenching of the blank material is performed after the first quenching. When the first quenching is performed, the blank material is heated to a first temperature of not lower than (Ac3 point—50)° C. nor higher than 1200° C. at an average heating rate of 2° C./sec or more, and the blank material is cooled from the first temperature to a second temperature of 250° C. or lower. When the second quenching is performed, the blank material is heated from the second temperature to a third temperature of not lower than (Ac3 point—50)° C. nor higher than 1200° C. at an average heating rate of 2° C./sec or more, and the blank material is cooled from the third temperature to a fourth temperature of 250° C. or lower. Forming of the blank material is performed in the first quenching or the second quenching or both of the above.