A method of manufacturing steel strip including the steps of: casting molten steel into slabs; reheating the slabs at 1150° C. or more for 1 hour or more; hot rolling the steel into a strip, preferably with an average F1 slab entry temperature above 1000° C.; coiling the hot rolled steel strip; batch annealing the steel strip: at an intercritical temperature (i.e. between Ac1 and Ac3), preferably below 700° C.; in non-oxidising and non-nitrogenated atmosphere; total annealing time at least 5 hours, preferably at least 10 hours to get Mn enrichment in austenite such that Mn content is at least 1.25 times bulk Mn content of the steel and C enrichment such that C content is at least 1.2 times bulk C content of the steel; cooling the steel after batch annealing in air, forced air or water quench.

A method of manufacturing steel strip including the steps of: casting molten steel into slabs; reheating the slabs at 1150° C. or more for 1 hour or more; hot rolling the steel into a strip, preferably with an average F1 slab entry temperature above 1000° C.; coiling the hot rolled steel strip; batch annealing the steel strip: at an intercritical temperature (i.e. between Ac1 and Ac3), preferably below 700° C.; in non-oxidising and non-nitrogenated atmosphere; total annealing time at least 5 hours, preferably at least 10 hours to get Mn enrichment in austenite such that Mn content is at least 1.25 times bulk Mn content of the steel and C enrichment such that C content is at least 1.2 times bulk C content of the steel; cooling the steel after batch annealing in air, forced air or water quench.

Provided is a high-strength steel sheet having high impact resistance. The steel sheet includes: by weight %, carbon (C): 0.05% to 0.14%, silicon (Si): 0.01% to 1.0%, manganese (Mn): 1.5% to 2.5%, aluminum (Al): 0.01% to 0.1%, chromium (Cr): 0.005% to 1.0%, phosphorus (P): 0.001% to 0.05%, sulfur (S): 0.001% to 0.01%, nitrogen (N): 0.001% to 0.01%, niobium (Nb): 0.005% to 0.06%, titanium (Ti): 0.005% to 0.11%, and the balance of iron (Fe) and inevitable impurities. The steel sheet has a microstructure comprising ferrite and bainite in a total area fraction of 90% or more. The steel sheet has a value of 0.05 to 1.0 as a shear texture ({110}<112>, {112}<111>) area ratio of a center region (ranging deeper than 1/10t to ½t in a thickness direction, t refers to thickness (mm)) and a surface region (ranging from a surface to 1/10t in the thickness direction).

A method for manufacturing a grain-oriented electrical steel sheet, according to an embodiment of the present invention includes: heating a slab, based on 100 wt % of a total composition thereof, including N at 0.0005 wt % to 0.015 wt %, Ti at 0.0001 wt % to 0.020 wt %, V at 0.0001 wt % to 0.020 wt %, Nb at 0.0001 wt % to 0.020 wt %, B at 0.0001 wt % to 0.020 wt %, and the remaining portion including Fe and other impurities, and then hot rolling it to prepare a hot-rolled steel sheet; annealing the hot-rolled steel sheet; after the hot-rolled steel sheet is annealed, cooling the hot-rolled steel sheet, and then cold rolling it to prepare a cold-rolled steel sheet; decarburization-annealing the cold-rolled steel sheet and then nitriding-annealing it, or simultaneously performing the decarburization-annealing and the nitriding-annealing; and final-annealing the decarburization-annealed and nitriding-annealed steel sheet.

The present invention relates to a formed product used in vehicle components and the like, and to a method for manufacturing the same. The present invention provides heat treatable steel, a formed product using the same having ultra-high strength and excellent durability, and a method for manufacturing the same, wherein the heat treatable steel contains, in wt %, C (0.22-0.42%), Si (0.05-0.3%), Mn (1.0-1.5%), Al (0.01-0.1%), P (0.01% or less (including 0), S (0.005% or less), Mo (0.05-0.3%), Ti (0.01-0.1%), Cr (0.05-0.5%), B (0.0005-0.005%), N (0.01% or less), the balance Fe, and other inevitable impurities, Mn and Si satisfying Relationship formula (1), below, Mo/p satisfying Relationship formula (2), below: [Relationship formula 1] Mn/Si≧5 [Relationship formula 2] Mo/P≧15.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 30% or more of a ferrite phase, 40% to 65% of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 40% to 55% and the total area ratio of a bainite phase having a grain diameter of more than 5 μm and/or a martensite phase having a grain diameter of more than 5 μm is 20% or less, and a tensile strength is 980 MPa or more.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 30% or more of a ferrite phase, 40% to 65% of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 40% to 55% and the total area ratio of a bainite phase having a grain diameter of more than 5 μm and/or a martensite phase having a grain diameter of more than 5 μm is 20% or less, and a tensile strength is 980 MPa or more.

A high-strength galvanized steel sheet that includes a chemical composition containing, by mass %, C: 0.15% or more and 0.25% or less, Si: 0.50% or more and 2.5% or less, Mn: 2.3% or more and 4.0% or less, P: 0.100% or less, S: 0.02% or less, Al: 0.01% or more and 2.5% or less, and Fe and inevitable impurities. The steel sheet having a microstructure containing, by an area percentage basis, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 20% or less, and other phases: 10% or less (including 0%), the other phases containing a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%).

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 25% or less of a ferrite phase, 75% or more of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 5% to 20%, and a tensile strength is 1180 MPa or more.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 25% or less of a ferrite phase, 75% or more of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 5% to 20%, and a tensile strength is 1180 MPa or more.