A group-III-nitride structure and a manufacturing method thereof are provided. In the manufacturing method, a first mask layer is first formed on a substrate; an uncoalesced second group-III-nitride epitaxial layer is formed by performing a first epitaxial growth with the first mask layer as a mask; and a second mask layer is formed at least on the second group-III-nitride epitaxial layer; a third group-III-nitride epitaxial layer is laterally grown and formed by performing a second epitaxial growth on the second group-III-nitride epitaxial layer with the second mask layer as a mask, where the second group-III-nitride epitaxial layer is coalesced by the third group-III-nitride epitaxial layer; a fourth group-III-nitride epitaxial layer is formed by performing a third epitaxial growth on the third group-III-nitride epitaxial layer.

A method of fabricating a heterostructure includes providing a substrate, and implementing a non-sputtered, epitaxial growth procedure at a growth temperature to form a wurtzite structure supported by the substrate. The wurtzite structure includes an alloy of gallium nitride. The non-sputtered, epitaxial growth procedure is configured to incorporate a group IIIB element into the alloy. The wurtzite structure exhibits a breakdown field strength greater than a ferroelectric coercive field strength of the wurtzite structure.

Epitaxial growth of materials, and related systems and articles, are generally described.

Epitaxial growth of materials, and related systems and articles, are generally described.

A laser activated luminescence system is provided. Another aspect pertains to a system employing a plasma assisted vapor deposition reactor which creates diamond layers on a substrate, in combination with a laser system to at least photoactivate and anneal the diamond layers. Yet another aspect of the present system uses a laser to assist with placement of color centers, such as nitrogen vacancy centers, in diamond. The present method uses lasers to manufacture more than two activated nitrogen vacancy center nodes in a diamond substrate, with nanometer spatial resolution and at a predetermined depth.

A laser activated luminescence system is provided. Another aspect pertains to a system employing a plasma assisted vapor deposition reactor which creates diamond layers on a substrate, in combination with a laser system to at least photoactivate and anneal the diamond layers. Yet another aspect of the present system uses a laser to assist with placement of color centers, such as nitrogen vacancy centers, in diamond. The present method uses lasers to manufacture more than two activated nitrogen vacancy center nodes in a diamond substrate, with nanometer spatial resolution and at a predetermined depth.

A method of a growing an embedded single crystal diamond structure, comprising: disposing a single crystal diamond on a non-diamond substrate, wherein the non-diamond substrate is larger than the single crystal diamond; masking a top portion of the single crystal diamond using a masking material; and using a chemical vapor deposition (CVD) growth chamber, growing polycrystalline diamond material surrounding the single crystal diamond in order to join the single crystal diamond to the polycrystalline diamond material.

High quality ammonothermal group III metal nitride crystals having a pattern of locally-approximately-linear arrays of threading dislocations, methods of manufacturing high quality ammonothermal group III metal nitride crystals, and methods of using such crystals are disclosed. The crystals are useful for seed bulk crystal growth and as substrates for light emitting diodes, laser diodes, transistors, photodetectors, solar cells, and for photoelectrochemical water splitting for hydrogen generation devices.

A method for manufacturing a compound semiconductor substrate that can achieve thinning of SiC film, wherein the method includes forming a SiC film on one principal surface side of a Si substrate and forming a recessed part in which a bottom surface is Si in a central part of another principal surface of the Si substrate.

A method for forming a laterally-grown group III metal nitride crystal includes providing a substrate, the substrate including one of sapphire, silicon carbide, gallium arsenide, silicon, germanium, a silicon-germanium alloy, MgAl.sub.2O.sub.4 spinel, ZnO, ZrB.sub.2, BP, InP, AlON, ScAlMgO.sub.4, YFeZnO.sub.4, MgO, Fe.sub.2NiO.sub.4, LiGa.sub.5O.sub.8, Na.sub.2MoO.sub.4, Na.sub.2WO.sub.4, In.sub.2CdO.sub.4, lithium aluminate (LiAlO.sub.2), LiGaO.sub.2, Ca.sub.8La.sub.2(PO.sub.4).sub.6O.sub.2, gallium nitride, or aluminum nitride (AlN), forming a pattern on the substrate, the pattern comprising growth centers having a minimum dimension between 1 micrometer and 100 micrometers, and being characterized by at least one pitch dimension between 20 micrometers and 5 millimeters, growing a group III metal nitride from the pattern of growth centers vertically and laterally, and removing the laterally-grown group III metal nitride layer from the substrate. A laterally-grown group III metal nitride layer coalesces, leaving an air gap between the laterally-grown group III metal nitride layer and the substrate or a mask thereupon.