The present invention relates to novel cementitious slurries that remain flexible after hardening.

A cementitious composition including: a binder containing (a) 60-94%, by weight, of at least one pozzolanic material; (b) at least 0.5% calcium sulfoaluminate (CSA), by weight; (c) 1.2-11% by weight, expressed as SO.sub.3, of at least one inorganic sulfate selected from the group of sulfates consisting of a calcium sulfate hemihydrate, an anhydrous calcium sulfate, a calcium sulfate dihydrate, a sodium sulfate, and a sodium calcium sulfate; and (d) a total sulfate content of at least 3%, by weight, expressed as SO.sub.3, the cementitious composition including, at most, 3% natural lime, the cementitious composition including, at most, 10% alumina cement, the contents of the composition being calculated on a dry, aggregateless basis.

A cementitious composition including: a binder containing (a) 60-94%, by weight, of at least one pozzolanic material; (b) at least 0.5% calcium sulfoaluminate (CSA), by weight; (c) 1.2-11% by weight, expressed as SO.sub.3, of at least one inorganic sulfate selected from the group of sulfates consisting of a calcium sulfate hemihydrate, an anhydrous calcium sulfate, a calcium sulfate dihydrate, a sodium sulfate, and a sodium calcium sulfate; and (d) a total sulfate content of at least 3%, by weight, expressed as SO.sub.3, the cementitious composition including, at most, 3% natural lime, the cementitious composition including, at most, 10% alumina cement, the contents of the composition being calculated on a dry, aggregateless basis.

A floor construction including a floor covering and a sealing layer applied to the floor covering, wherein one or more primers are arranged between the substrate and the floor covering and the floor covering is formed of a filling compound which includes an aluminate binder, a calcium sulfate binder, one or more fillers, ethyl hydroxyethyl cellulose as thickening agent, comb polymer having sidechains with an ionic group and sidechains with an ether group bonded to a polymer backbone, as plasticizer, and one or more color pigments as coloring agent.

A cementitious composition including: a binder containing (a) 60-94%, by weight, of at least one pozzolanic material; (b) at least 0.5% calcium sulfoaluminate (CSA), by weight; (c) 1.2-11% by weight, expressed as SO.sub.3, of at least one inorganic sulfate selected from the group of sulfates consisting of a calcium sulfate hemihydrate, an anhydrous calcium sulfate, a calcium sulfate dihydrate, a sodium sulfate, and a sodium calcium sulfate; and (d) a total sulfate content of at least 3%, by weight, expressed as SO.sub.3, the cementitious composition including, at most, 3% natural lime, the cementitious composition including, at most, 10% alumina cement, the contents of the composition being calculated on a dry, aggregateless basis.

A cementitious composition including: a binder containing (a) 60-94%, by weight, of at least one pozzolanic material; (b) at least 0.5% calcium sulfoaluminate (CSA), by weight; (c) 1.2-11% by weight, expressed as SO.sub.3, of at least one inorganic sulfate selected from the group of sulfates consisting of a calcium sulfate hemihydrate, an anhydrous calcium sulfate, a calcium sulfate dihydrate, a sodium sulfate, and a sodium calcium sulfate; and (d) a total sulfate content of at least 3%, by weight, expressed as SO.sub.3, the cementitious composition including, at most, 3% natural lime, the cementitious composition including, at most, 10% alumina cement, the contents of the composition being calculated on a dry, aggregateless basis.

A cementitious composition including: a binder containing (a) 60-94%, by weight, of at least one pozzolanic material; (b) at least 0.5% calcium sulfoaluminate (CSA), by weight; (c) 1.2-11% by weight, expressed as SO.sub.3, of at least one inorganic sulfate selected from the group of sulfates consisting of a calcium sulfate hemihydrate, an anhydrous calcium sulfate, a calcium sulfate dihydrate, a sodium sulfate, and a sodium calcium sulfate; and (d) a total sulfate content of at least 3%, by weight, expressed as SO.sub.3, the cementitious composition including, at most, 3% natural lime, the cementitious composition including, at most, 10% alumina cement, the contents of the composition being calculated on a dry, aggregateless basis.

A cementitious composition including: a binder containing (a) 60-94%, by weight, of at least one pozzolanic material; (b) at least 0.5% calcium sulfoaluminate (CSA), by weight; (c) 1.2-11% by weight, expressed as SO.sub.3, of at least one inorganic sulfate selected from the group of sulfates consisting of a calcium sulfate hemihydrate, an anhydrous calcium sulfate, a calcium sulfate dihydrate, a sodium sulfate, and a sodium calcium sulfate; and (d) a total sulfate content of at least 3%, by weight, expressed as SO.sub.3, the cementitious composition including, at most, 3% natural lime, the cementitious composition including, at most, 10% alumina cement, the contents of the composition being calculated on a dry, aggregateless basis.

A foaming agent is used for foaming a building material binder paste or a building material slurry for producing porous lightweight-construction and insulating materials. On curing of the foamed slurry, the foam bubbles generate pores in the building material. The foam obtained from the foaming agent is stabilized using a long-chain or medium-chain polycarboxylate ether (PCE). The foaming agent includes a foam-forming ionic surfactant component, at least one fatty alcohol and at least one PCE in an aqueous-organic solvent which is selected from the group of alkyl glycols, alkylene glycols up to C6 alkyl, diglycols and diglycol ethers, and also, optionally, up to a maximum of 20 wt %, based on the mixture, of further ingredients.

A foaming agent is used for foaming a building material binder paste or a building material slurry for producing porous lightweight-construction and insulating materials. On curing of the foamed slurry, the foam bubbles generate pores in the building material. The foam obtained from the foaming agent is stabilized using a long-chain or medium-chain polycarboxylate ether (PCE). The foaming agent includes a foam-forming ionic surfactant component, at least one fatty alcohol and at least one PCE in an aqueous-organic solvent which is selected from the group of alkyl glycols, alkylene glycols up to C6 alkyl, diglycols and diglycol ethers, and also, optionally, up to a maximum of 20 wt %, based on the mixture, of further ingredients.