There are provided a cubic boron nitride sintered body having a surface also excellent in adhesiveness to a ceramic coating film, while having excellent wear resistance and defect resistance, and a manufacturing method thereof, and a tool. The cubic boron nitride sintered body of the present invention includes 60.0 to 90.0% by volume of cubic boron nitride, the remainder being a binder phase, wherein the binder phase contains: at least any of a nitride, a boride, and an oxide of Al; at least any of a carbide, a nitride, a carbonitride, and a boride of Ti; and a compound represented by the following formula (1):
W.sub.2Ni.sub.xCo.sub.(1-x)B.sub.2(0.40≤x<1)  (1).

The object of the present invention is an integrally bonded composite component, a method for the production thereof, and the use thereof. The invention particularly relates to integrally bonded transparent ceramic composite components, to a method for the production of such ceramic composite components, and to the use thereof.

A target for sputtering which enables to attain high rate film-formation of a transparent conductive film suitable for a blue LED or a solar cell. A oxide sintered body includes an indium oxide and a cerium oxide, and one or more oxide of titanium, zirconium, hafnium, molybdenum and tungsten. The cerium content is 0.3 to 9% by atom, as an atomicity ratio of Ce/(In+Ce), and the content of cerium is equal to or lower than 9% by atom, as an atomicity ratio of Ce/(In+Ce). The oxide sintered body has an In.sub.2O.sub.3 phase of a bixbyite structure has a CeO.sub.2 phase of a fluorite-type structure finely dispersed as crystal grains having an average particle diameter of equal to or smaller than 3 μm.

Provided are a sintered ceramic and a ceramic sphere which are inhibited from suffering surface peeling due to fatigue resulting from repetitions of loading and can attain an improvement in dimensional accuracy when subjected to surface processing and which have excellent wear resistance and durability.

The invention relates to a method of joining substrates. It is the object of the invention in this respect to join substrates of substrate materials together without having to exert an increased effort for a coating with additional coating processes to be carried out and to be able to achieve a good quality of the join connection in so doing. In the method in accordance with the invention a pretreatment of at least one join surface of a substrate to be joined is carried out in low pressure oxygen plasma prior to the actual joining. On the joining, a contact force acts on the substrates to be joined in the range 2 kPa to 5 MPa and in this process a heat treatment is carried out at an elevated temperature of at least 100° C. and at under pressure conditions of a maximum of 10 mbar, preferably <10.sup.−3 mbar.

In an X-ray diffraction diagram of a cordierite sintered body of the present invention, the ratio of the total of the maximum peak intensities of components other than cordierite components to the peak top intensity of the (110) plane of cordierite is 0.0025 or less. Since having a significantly small amount of different phases other than the cordierite components, this cordierite sintered body has a high surface flatness when the surface thereof is mirror-polished.

A support rack can include a first component comprising a ceramic material and a second component comprising a ceramic material. The first component can intersect at least one wall of the second component and the first and second components can be coupled via a ceramic weld. A method of making a support rack can include providing a first component comprising a sintered ceramic material, providing a second component comprising an un-sintered or partially-sintered ceramic material, arranging the first and second component so that the first component intersects at least one wall of the second component, sinter bonding the first and second components together to form a ceramic weld at the intersection. In an embodiment, the support rack can be a piece of kiln furniture.

A refractory, coarse ceramic product including at least one granular refractory material, has an open porosity of between 22 and 45 vol.-%, in particular of between 23 and 29 vol.-%, and a grain structure of the refractory material, wherein the medium grain size fraction with grain sizes of between 0.1 and 0.5 mm is 10 to 55 wt.-%, in particular 35 to 50 wt.-%, and wherein the remainder of the grain structure is a finest grain fraction with grain sizes of up to 0.1 mm and/or coarse-grain fraction with grain sizes of more than 0.5 mm.

Provided herein is a method for forming a periodic microstructure on a surface of zirconia-based ceramics, which are not easily mechanically workable, without causing thermal adverse effects. A zirconia-based ceramic having a surface periodic microstructure is also provided. A linearly or circularly polarized laser beam is irradiated to a zirconia-based ceramic surface, and periodic irregularities are formed in a spot of the laser beam. Stripe-pattern irregularities parallel to the direction of polarization can be formed in a spot of a laser beam by irradiating a linearly polarized ultrashort pulsed-laser beam to a zirconia-based ceramic surface. A mesh-like raised region and a dot-like recessed region can be periodically formed by irradiating a circularly polarized ultrashort pulsed-laser beam to a ceramic surface.

Provided is a medical device including a porous portion and a dense portion, wherein an arithmetic average roughness of a surface of the porous portion is 2.0 μm or greater but 20 μm or less, and wherein an arithmetic average roughness of a surface of the dense portion is less than 2.0 μm.