Disclosed is a two-component silicone composition, which can cure via two part moisture cure organosiloxanc composition. The composition generally has which could improved cure speed while whilst maintaining good storage stability.

Disclosed is a two-component silicone composition, which can cure via two part moisture cure organosiloxanc composition. The composition generally has which could improved cure speed while whilst maintaining good storage stability.

According to the present disclosure, there are provided a surface treatment agent having the advantage that the raw material components can be dissolved in a short time during preparation of the surface treatment agent and capable of exerting a good water repellency imparting effect, and a method of manufacturing a surface-treated body with the use of the surface treatment agent. The surface treatment agent according to the present disclosure includes the following components: (I) at least one kind selected from the group consisting of silicon compounds represented by the following general formulas [1], [2] and [3]; (II) at least one kind selected from the group consisting of a nitrogen-containing heterocyclic compound represented by the following general formula [4], a nitrogen-containing heterocyclic compound represented by the following general formula [5], and imidazole; and (III) an organic solvent.

##STR00001##

Resin particles include resin base particles and silica particles on surfaces of the resin base particles. The silica particles contain a quaternary ammonium salt and have hydrophobized surfaces. A difference (detection temperature Adetection temperature B) between a detection temperature A and a detection temperature B is more than 50 C., where the detection temperature A is a detection temperature from a pyrolysis product of the quaternary ammonium salt determined by pyrolysis mass spectrometry of the resin particles before cleaning, and the detection temperature B is a detection temperature from the pyrolysis product of the quaternary ammonium salt determined by pyrolysis mass spectrometry of the resin particles after cleaning.

Resin particles include resin base particles and silica particles on surfaces of the resin base particles. The silica particles contain a quaternary ammonium salt and have hydrophobized surfaces. A difference (detection temperature Adetection temperature B) between a detection temperature A and a detection temperature B is more than 50 C., where the detection temperature A is a detection temperature from a pyrolysis product of the quaternary ammonium salt determined by pyrolysis mass spectrometry of the resin particles before cleaning, and the detection temperature B is a detection temperature from the pyrolysis product of the quaternary ammonium salt determined by pyrolysis mass spectrometry of the resin particles after cleaning.

[Problem] To provide a composition for forming a coating layer having excellent gas barrier performance and a method of forming the coating layer. [Means for Solution] A composition for forming a coating film comprising a specific silicon compound which reacts with a polysilazane by exposure, a polysilazane and an organic solvent, and a method for forming a coating layer comprising coating the composition on a substrate and exposing.

[Problem] To provide a composition for forming a coating layer having excellent gas barrier performance and a method of forming the coating layer. [Means for Solution] A composition for forming a coating film comprising a specific silicon compound which reacts with a polysilazane by exposure, a polysilazane and an organic solvent, and a method for forming a coating layer comprising coating the composition on a substrate and exposing.

An addition-curable silicone rubber composition which contains: 100 parts by weight of (A) an organopolysiloxane that is represented by average composition formula (1) R.sup.1.sub.aSiO.sub.(4a)/2 (wherein R.sup.1 represent monovalent hydrocarbon groups that are the same as or different from each other, and a represents a positive number of 1.5-2.8) and has at least two alkenyl groups, each of which is bonded to a silicon atom, in each molecule; 0.3-20 parts by weight of (B) an organohydrogen polysiloxane that has at least two hydrogen atoms (SiH functional groups), each of which is bonded to a silicon atom, in each molecule; 5-80 parts by weight of (C) a reinforcing silica; and (D) an addition reaction catalyst, which is configured of a platinum group metal, in an amount of 0.5-1,000 ppm relative to the total weight of the components (A) and (B). This addition-curable silicone rubber composition also contains (E) an organopolysiloxane, which has one or more SiOH functional groups in each molecule, while having a polymerization degree of 10 or less, in an amount of 0.005-0.3% by weight relative to the total weight of the composition.

The present disclosure relates to an encapsulant film made from a curable composition comprising: (A) a polyolefin polymer; (B) an organic peroxide; (C) a silane coupling agent; and (D) a co-agent comprising a monocyclic organosilazane of formula (I).

The present disclosure relates to an encapsulant film made from a curable composition comprising: (A) a polyolefin polymer; (B) an organic peroxide; (C) a silane coupling agent; and (D) a co-agent comprising a monocyclic organosilazane of formula (I).