A resin composition includes (A) a polyolefin epoxy resin, (B) an epoxy resin having a condensed polycyclic aromatic hydrocarbon, (C) a nitrogen-containing novolak resin, and (D) an inorganic filler, in which an epoxy equivalent of the (A) component is 200 g/eq. or more, a nitrogen content in the (C) component is 13% by mass or more and/or the (C) component has a cresol novolak structure, and a content of the (D) component is 60% by mass or more on the basis of 100% by mass of non-volatile components in the resin composition.

A thermosetting resin composition and a prepreg are provided. The thermosetting resin composition includes a maleimide resin, a cyanate ester resin, and a crosslinking agent. The crosslinking agent is a silane-modified diallyl bisphenol compound whose structure is represented by Formula (1): ##STR00001## in Formula (1), X is a linear or branched C1 to C6 alkyl, cycloalkyl, or sulfonyl group, R1 is a linear or branched C1 to C6 alkyl or aryl group, R2 is a C1 to C6 alkyl group, R3 is a functional group with a crosslinkable double bond, and n+m is a positive integer from 1 to 8.

A thermosetting resin composition and a prepreg are provided. The thermosetting resin composition includes a maleimide resin, a cyanate ester resin, and a crosslinking agent. The crosslinking agent is a silane-modified diallyl bisphenol compound whose structure is represented by Formula (1): ##STR00001## in Formula (1), X is a linear or branched C1 to C6 alkyl, cycloalkyl, or sulfonyl group, R1 is a linear or branched C1 to C6 alkyl or aryl group, R2 is a C1 to C6 alkyl group, R3 is a functional group with a crosslinkable double bond, and n+m is a positive integer from 1 to 8.

Provided is a thermosetting resin composition which exhibits excellent workability, and which is capable of obtaining, as a result of being cured, a highly reliable cured product (molded article) exhibiting excellent heat resistance and mechanical strength. This thermosetting resin composition includes: a polyalkenyl phenol resin (A); an aromatic polymaleimide compound (B); and a polymerization initiator (C). The polyalkenyl phenol resin (A) has, in a molecule thereof, at least one aromatic ring unit (al) which has a phenolic hydroxyl group having a 2-alkenyl group bonded thereto, and at least one aromatic ring unit (a2) having a phenolic hydroxyl group which does not have a 2-alkenyl group bonded thereto. Each of the aromatic ring units is bonded by a linking group having a main chain which is not formed by an aromatic ring. When m represents the number of the aromatic ring units (a1), and n represents the number of the aromatic ring units (a2), the ratio of m to (m+n) is 40-90%. The polyalkenyl phenol resin (A) is included in an amount at which the amount of 2-alkenyl groups becomes 0.4-1.5 mol per mol of maleimide groups in the aromatic polymaleimide compound (B).

Provided is a thermosetting resin composition which exhibits excellent workability, and which is capable of obtaining, as a result of being cured, a highly reliable cured product (molded article) exhibiting excellent heat resistance and mechanical strength. This thermosetting resin composition includes: a polyalkenyl phenol resin (A); an aromatic polymaleimide compound (B); and a polymerization initiator (C). The polyalkenyl phenol resin (A) has, in a molecule thereof, at least one aromatic ring unit (al) which has a phenolic hydroxyl group having a 2-alkenyl group bonded thereto, and at least one aromatic ring unit (a2) having a phenolic hydroxyl group which does not have a 2-alkenyl group bonded thereto. Each of the aromatic ring units is bonded by a linking group having a main chain which is not formed by an aromatic ring. When m represents the number of the aromatic ring units (a1), and n represents the number of the aromatic ring units (a2), the ratio of m to (m+n) is 40-90%. The polyalkenyl phenol resin (A) is included in an amount at which the amount of 2-alkenyl groups becomes 0.4-1.5 mol per mol of maleimide groups in the aromatic polymaleimide compound (B).

A run flat tire having a side reinforcing rubber part is disclosed. The side reinforcing rubber part is formed by a rubber composition having a ratio (M50H/M50N) of tensile stress (M50H) in 50% elongation at a measurement temperature of 100° C. to tensile stress (M50N) in 50% elongation at a measurement temperature of 23° C. of from 1.0 to 1.3. A cushion rubber layer interposed between the side reinforcing rubber part and a bead filler is provided, and tensile stress in 50% elongation at a measurement temperature of 23° C. of a rubber composition forming the cushion rubber layer is larger than tensile stress in 50% elongation at a measurement temperature of 23° C. of the rubber composition forming the side reinforcing rubber part, and is smaller than tensile stress in 50% elongation at a measurement temperature of 23° C. of a rubber composition forming the bead filler.

The present invention provides a resin composition for a printed wiring board comprising a cyanate compound (A) represented by following general formula (1):

##STR00001##

wherein n represents an integer of 1 or more; and an epoxy resin (B).

Polyphenolic condensates and epoxidized products prepared from said condensates are prepared by a reaction utilizing multi catalysts to control the weight average molecular weight (Mw) and the number average molecular weight (Mn). Improved color and ultraviolet absorbance are possessed by the condensates described herein.

Polyphenolic condensates and epoxidized products prepared from said condensates are prepared by a reaction utilizing multi catalysts to control the weight average molecular weight (Mw) and the number average molecular weight (Mn). Improved color and ultraviolet absorbance are possessed by the condensates described herein.

There is provided a phenolic resin composition as a molding material. It includes a resol-type phenolic resin (A) and a novolac-type phenolic resin (B). The novolac-type phenolic resin (B) includes a novolac-type phenolic resin (B1) represented by General Formula (1) and a modified novolac-type phenolic resin (B2) represented by General Formula (2).

##STR00001##