An electrically conductive paste contains: metal nanoparticles which are protected by an organic compound containing an amino group and have an average particle diameter of 30 nm to 400 nm; metal particles which are protected by a higher fatty acid and have an average particle diameter of 1 m to 5 m; an organic solvent; and a resin component consisting of a cellulose derivative. A conductor obtained by firing the electrically conductive paste has a film thickness of 30 m or more and a specific resistance of 5.010.sup.6 .Math.cm or less. In this way, the electrically conductive paste can reduce the resistance of the obtained conductor and to increase the amount of current flowing. A wiring board includes a conductor obtained from the electrically conductive paste.

The present invention relates to a matte coating composition comprising an aqueous dispersion of a) polymer particles having an average particle size in the range of from 80 nm to 500 nm; b) polymeric organic crosslinked microspheres having a particle size in the range of from 1 ?m to 20 ?m; c) polyethylene wax particles having a particle size in the range of from 0.3 ?m to 30 ?m; and d) a rheology modifier. The composition of the present invention gives matte finish coatings with excellent burnish resistance.

Disclosed herein are implementations of a radiative cooling formulation, an apparatus including a substrate coated with the radiative cooling formulation, and a method of applying a coating of the radiative cooling formulation to an object. In one implementation, a radiative cooling formulation includes a binder which includes a first polymer and a second polymer that are practically water insoluble and are substantially non-absorbing to light having wavelengths in a solar spectrum. The radiative cooling formulation further includes a solar reflector material embedded in the binder.

A sliding element for an engine may include a polymer-based overlay layer disposed on a metallic substrate. The polymer-based overlay layer may include a polymer-based matrix and a metal particulate. The metal particulate may be a surface treated metal particulate.

A bearing material may include a polymeric matrix of polyamide-imide (PAI) polymer material and a plurality of melamine cyanurate particles dispersed within the polymeric matrix.

The present invention relates to a pigmented matte coating composition comprising an aqueous dispersion of a) phosphorus acid functionalized polymer particles; b) TiO.sub.2 particles; c) polymeric organic microspheres; and d) a rheology modifier. The composition of the present invention gives matte finish coatings having the stain and scrub resistant attributes similar to coatings formed from semi-gloss paint compositions.

The present invention is related to a method for the production of single crystalline MgTiO.sub.3 flakes, in particular in the geikielite crystal structure, to single crystalline MgTiO.sub.3 flakes obtained by this method as well as to the use thereof, in particular as pigments in several application media.

A coated article comprises a substrate and a self-healing coating disposed on a surface of the substrate, the self-healing coating comprising a metallic matrix; and a plurality of micro- or nano-sized particles dispersed in the metallic matrix; the micro- or nano-sized particles comprising an active agent disposed in a carrier comprising a micro- or nano-sized metallic container, a layered structure, a porous structure, or a combination comprising at least one of the foregoing.

A formulation for an acoustically transparent coating for use on an acoustical substrate comprising a water dispersible binder and relatively large filler particles, and characterized by a high pigment to volume concentration, high viscosity, high shear thinning, and fast drying to enable the formulation to be sprayed in droplets that retain their identity when in mutual contact and in a dry coating can be efficiently sanded flat.

A solid colorant including a. 30-97 wt % of a pigment, b. less than 5 wt % of a solvent c. 3-40 wt % surfactants and wherein: the ratio S/A [Std dev of the particle size distribution/average particle size] of the solid colorant is <25%, preferably <22% and more preferably <20%, wherein wt % is relative to the total weight of the solid colorant, and wherein the particle size distribution is determined with light scattering with fully automated image analysis according to ISO 13322-1 Static image analysis First edition 2004 Dec. 1 by the use of the OCCHIO ZEPHYR ESR analyzer. A process for making the solid colorant, and the use of the solid colorant for tinting base paints by volumetric dosing of the solid colorant to the base paint.