To provide a sliding member comprising a coating film exhibiting constant and stable chipping resistance and wear resistance and excellent in peeling resistance (adhesion), and the coating film thereof. The above-described problem is solved by a sliding member (10) comprising a coating film (1) on a sliding surface (16) on a base material (11). The coating film (1) has, when a cross section thereof is observed by a bright-field TEM image, a total thickness within a range of 1 ?m to 50 ?m, in repeating units including black hard carbon layers (B), relatively shown in black, and white hard carbon layers (W), relatively shown in white, and laminated in a thickness direction (Y). In the black hard carbon layer (B) and the white hard carbon layer (W) adjacent to each other, the white hard carbon layer (W) has higher hardness and a larger [sp.sup.2/(sp.sup.2+sp.sup.3)] ratio than the black hard carbon layer (B).

A sliding component may include an overlay. The overlay may include graphene platelets functionalised with at least one of O functional groups and F functional groups within a matrix of at least one of a polymeric material and a plastics material.

A low friction wear surface with a coefficient of friction in the superlubric regime including graphene and nanoparticles on the wear surface is provided, and methods of producing the low friction wear surface are also provided. A long lifetime wear resistant surface including graphene exposed to hydrogen is provided, including methods of increasing the lifetime of graphene containing wear surfaces by providing hydrogen to the wear surface.

Articles comprising carbon composites are disclosed. The carbon composites contain carbon microstructures having interstitial spaces among the carbon microstructures; and a binder disposed in at least some of the interstitial spaces; wherein the carbon microstructures comprise unfilled voids within the carbon microstructures. Alternatively, the carbon composites contain: at least two carbon microstructures; and a binding phase disposed between the at least two carbon microstructures; wherein the binding phase comprises a binder comprising one or more of the following: SiO.sub.2; Si; B; B.sub.2O.sub.3; a metal; or an alloy of the metal; and wherein the metal is at least one of aluminum; copper; titanium; nickel; tungsten; chromium; iron; manganese; zirconium; hafnium; vanadium; niobium; molybdenum; tin; bismuth; antimony; lead; cadmium; or selenium.

Embodiments described herein generally relate to compositions including discrete nanostructures (e.g., nanostructures including a functionalized graphene layer and a core species bound to the functionalized graphene layer), and related articles and methods. A composition may have a coefficient of friction of less than or equal to 0.02. Discrete nanostructures may have a substantially non-planar configuration. A core species may reversibly covalently bind a first portion of a functionalized graphene layer to a second portion of the functionalized graphene layer. Articles, e.g., articles including a plurality of discrete nanostructures and a means for depositing the plurality of discrete nanostructures on a surface, are also provided. Methods (e.g., methods of forming a layer) are also provided, including depositing a composition onto a substrate surface and/or applying a mechanical force to the composition, e.g., such that the composition exhibits a coefficient of friction of less than or equal to 0.02.

Provided are a coating film, a manufacturing method for the same, and a PVD device that not only sufficiently improve the balance of low-friction properties and wear resistance, but also improve chipping resistance and peeling resistance. This film is coated on a substrate surface, wherein the coating film has a hard carbon that presents relatively black and white when observed in a cross-sectional bright-field TEM image, a mesh-shaped hard carbon layer is formed using a PVD method, said layer having white-colored hard carbon in a mesh shape extending in the thickness direction and black-colored hard carbon dispersed into the cavities in the mesh, and the ID/IG ratio is 1-6 when the mesh-shaped hard carbon layer is measured using Raman spectroscopy, said ratio being the ratio of the Raman spectrum D band peak area intensity and G band peak area intensity.

Anaerobic sealant lubricant compositions and uses are disclosed. The anaerobic sealant lubricant compositions cure anaerobically but have lubricity for easy disassembly, making the compositions well suited for fasteners and threaded components.

A method including substituting an atmosphere in a space, in which a sliding surface formed of a metal or a ceramic material, and a slid surface are disposed, with a gas atmosphere containing a hydroxyl group-containing compound and at least one of hydrogen and nitrogen, and relatively sliding the sliding surface against the slid surface by a Hertzian contact stress of 1.0 GPa or more in the space under the gas atmosphere containing the hydroxyl group-containing compound at least one of hydrogen and nitrogen. As a result, it is possible to form, on the sliding surface, a low-friction coating that stably exhibits a significantly low friction coefficient, for example, of 10.sup.4 order (less than 0.001).

A resin composition includes: a binder resin made of a thermosetting resin; an additive dispersed in the binder resin, wherein the additive includes PTFE (polytetrafluoroethylene), and at least one of graphite and MoS.sub.2, an average particle size of each of the additive is less than 10 m, and an average particle size of the PTFE is larger than the average particle size of graphite and MoS.sub.2.

A sliding member includes: a base material; a coating layer formed on the base material and made of a resin composition including: a binder resin including polyamideimide; PTFE dispersed in the binder resin; and at least one of graphite and MoS.sub.2 dispersed in the binder resin; wherein a surface roughness of the coating layer after a sliding test is equal to or less than the surface roughness of the coating layer before the sliding test.