Disclosed is a manufacturing method for a high silicon grain oriented electrical steel sheet, the silicon content of the high silicon grain oriented electrical steel is greater than 4 wt %, comprising the steps of: (1) performing decarburization annealing of a cold-rolled steel plate; (2) allowing high silicon alloy particles in a completely solid state to collide at a high speed with the surface of the decarburization annealed steel plate to be sprayed, thus forming a high silicon alloy coating on the surface of the steel plate to be sprayed; (3) coating a release agent and drying; and (4) annealing. The manufacturing method for the high silicon grain oriented electrical steel sheet of the present invention is inexpensive, and, the high silicon grain oriented electrical steel sheet produced is of stable quality and is provided with great magnetic performance.

A grain-oriented electrical steel sheet includes: a silicon steel sheet including Si and Mn; a glass film arranged on a surface of the silicon steel sheet; and an insulation coating arranged on a surface of the glass film, wherein the glass film includes a Mn-containing oxide.

A method for manufacturing a grain-oriented electrical steel sheet according to an embodiment of the present invention comprises: a step for hot-rolling a slab to produce a hot-rolled sheet; a step for cold-rolling the hot-rolled sheet to produce a cold-rolled sheet; a step for subjecting the cold-rolled sheet to primary recrystallization annealing; and a step for subjecting the primary recrystallization annealing-completed cold-rolled sheet to secondary recrystallization annealing, wherein the primary recrystallization annealing step includes a preceding step and a subsequent step, and the amount (A) of nitriding gas introduced in the preceding step with respect to the total amount (B) of nitriding gas introduced in the primary recrystallization annealing step satisfies expression 1 below.
0.05≤[A]/[B]≤[t]  [Expression 1] (In expression 1, the amount of nitriding gas introduced is in units of Nm.sup.3/hr, and [t] represents the thickness (mm) of a cold-rolled sheet.)

Method for manufacturing a thin strip in a soft magnetic alloy and strip obtained A method for manufacturing a strip in a soft magnetic alloy capable of being cut out mechanically, the chemical composition of which comprises by weight: TABLE-US-00001 18% ≤ Co ≤ 55% 0% ≤ V + W ≤ 3% 0% ≤ Cr ≤ 3% 0% ≤ Si ≤ 3% 0% ≤ Nb ≤ 0.5% 0% ≤ B ≤ 0.05% 0% ≤ C ≤ 0.1% 0% ≤ Zr + Ta ≤ 0.5% 0% ≤ Ni ≤ 5% 0% ≤ Mn ≤ 2% The remainder being iron and impurities resulting from the elaboration, according to which a strip obtained by hot rolling is cold-rolled in order to obtain a cold-rolled strip with a thickness of less than 0.6 mm. After cold rolling, a continuous annealing treatment is carried out by passing into a continuous oven, at a temperature comprised between the order/disorder transition temperature of the alloy and the onset temperature of ferritic/austenitic transformation of the alloy, followed by rapid cooling down to a temperature below 200° C. Strip obtained.

An oriented silicon steel product with a low iron loss for a low-noise transformer, and manufacturing method thereof are provided. The oriented silicon steel product comprises: a silicon steel substrate, a magnesium silicate bottom layer formed on a surface of the silicon steel substrate, and an insulation coating applied on the magnesium silicate bottom layer. The magnesium silicate bottom layer has a visible light normal reflectivity (R) of 40-60% for. By strictly controlling the visible light normal reflectivity of the magnesium silicate bottom layer of the silicon steel substrate and the evenness of the gloss of magnesium silicate bottom layer, lower iron loss, and reduced magnetostriction can be achieved, and thus a silicon steel product with low noise and particularly suitable for transformers can be obtained.

A non-oriented electrical steel sheet according to an exemplary embodiment of the present invention includes, by weight, Si: 2.0 to 3.5%, Al: 0.3 to 2.5%, Mn: 0.3 to 3.5%, Sn: 0.0030 to 0.2%, Sb: 0.0030 to 0.15%, P: 0.0040 to 0.18%, individually or in a total amount of 0.0005 to 0.03% of at least one of Ga and Ge, and a remainder including Fe and unavoidable impurities, and satisfies Equation 1 below.
0.05≤([Sn]+[Sb])/[P]≤25  [Equation 1] ([Sn], [Sb], and [P] respectively represent the content (% by weight) of Sn, Sb, and P.)

Grain-oriented electrical steel sheet excellent in magnetic properties and excellent in adhesion of a primary coating to a base steel sheet, an annealing separator utilized for manufacture of grain-oriented electrical steel sheet, and a method for manufacturing grain-oriented electrical steel sheet are proposed. The grain-oriented electrical steel sheet is provided with a base metal steel sheet containing comprising a predetermined chemical composition and a primary coating formed on a surface of the base steel sheet and comprising Mg.sub.2SiO.sub.4 as a main constituent. The primary coating satisfies the conditions of (1) the number density D3 of the Al concentrated region: 0.020 to 0.180/μm.sup.2, (2) (total area S5 of regions which is anchoring oxide layer regions and is also Al concentrated regions)/(total area S3 of Al concentrated regions)≥33%, (3) distance H5 of mean value of length in thickness direction of regions which is anchoring oxide layer regions and is also Al concentrated regions minus H0: 0.4 to 4.0 μm, (4) (total area S1 of anchoring oxide layer regions)/(observed area S0)≥15%.

A non-oriented electrical steel sheet with an average magnetostriction λ.sub.p-p at 400 Hz and 1.0 T of not more than 4.5×10.sup.−6, and area ratio of recrystallized grains at a section in rolling direction of steel sheet of 40 to 95% and an average grain size of 10 to 40 μm is obtained by subjecting a steel slab containing, in mass %, C: not more than 0.005%, Si: 2.8 to 6.5%, Mn: 0.05 to 2.0%, Al: not more than 3.0%, P: not more than 0.20%, S: not more than 0.005%, N: not more than 0.005%, Ti: not more than 0.003%, V: not more than 0.005% and Nb: not more than 0.005% and satisfying Si-2Al-Mn≥0 to hot rolling, hot-band annealing, cold rolling and finish annealing under adequate cold rolling and finish annealing conditions, and a motor core is manufactured by such a steel sheet.

A hot-rolled steel sheet for a non-oriented electrical steel sheet according to one aspect of the present invention contains, by mass %, C: 0.0050% or less, Si: 0.5% or more and 3.5% or less, Mn: 0.1% or more and 1.5% or less, Al: 0.1% or more and 1.5% or less, Cu: 0.01% or more and 0.10% or less, Sn: 0.01% or more and 0.20% or less, and a remainder including Fe and impurities, in which the hot-rolled steel sheet has a Cu concentration peak value of 0.12% or more in a range from a surface thereof to a depth of 10 μm.

A method for manufacturing a grain-oriented electrical steel sheet according to an aspect of the present invention includes a step of obtaining a hot-rolled steel sheet by carrying out hot rolling on a slab containing a predetermined component composition with a remainder including Fe and impurities, a step of obtaining a hot-rolled annealed sheet by carrying out hot-rolled sheet annealing as necessary, a step of carrying out pickling to obtain a pickled sheet, a step of carrying out cold rolling to obtain a cold-rolled steel sheet, a step of carrying out primary recrystallization annealing, a step of applying an annealing separating agent including MgO to a surface and then carrying out final annealing to obtain a final-annealed sheet, and a step of applying an insulating coating and then carrying out flattening annealing.