Provided is a steel component with excellent surface fatigue strength. The steel component has a nitride compound layer with a thickness of 5.0 μm to 30.0 μm and a hardened layer in an order from a component surface to a component inside, where a thickness of a porous layer on an outermost surface of the nitride compound layer is 3.0 μm or less and 40.0% or less of a thickness of the nitride compound layer, and the hardened layer has a hardness of HV600 or more at a position of 50 μm inward from the component surface, a hardness of HV400 or more at a position from the component surface to the component inside of 400 μm, and a hardness of HV250 or more at a position from the component surface to the component inside of 600 μm.

There is provided a duplex stainless steel tube including a chemical composition consisting of, in mass %, C: 0.008 to 0.030%, Si: 0.10 to 0.70%, Mn: 0.80 to 2.60%, P: 0.030% or less, S: 0.0001 to 0.0050%, O: 0.0004 to 0.0150%, Sn: 0.0001% or more to less than 0.0100%, Cu: 0.10 to 2.50%, Ni: more than 2.50 to 5.50% or less, Cr: 21.5 to 25.5%, Mo: 0.10 to 0.50%, N: 0.050 to 0.200%, Al: 0.200% or less, and optional elements, with the balance: Fe and impurities, wherein 4S+8O+Sn is 0.0040 to 0.0900, and 4S+Sn is 0.0180 or less.

There is provided a duplex stainless steel tube including a chemical composition consisting of, in mass %, C: 0.008 to 0.030%, Si: 0.10 to 0.70%, Mn: 0.80 to 2.60%, P: 0.030% or less, S: 0.0001 to 0.0050%, O: 0.0004 to 0.0150%, Sn: 0.0001% or more to less than 0.0100%, Cu: 0.10 to 2.50%, Ni: more than 2.50 to 5.50% or less, Cr: 21.5 to 25.5%, Mo: 0.10 to 0.50%, N: 0.050 to 0.200%, Al: 0.200% or less, and optional elements, with the balance: Fe and impurities, wherein 4S+8O+Sn is 0.0040 to 0.0900, and 4S+Sn is 0.0180 or less.

Provided is a solid wire for gas metal arc welding, solid wire being suitable as a welding material for high-Mn steel materials and generating less fume during welding. The solid wire of the present invention has a composition containing, in mass %, C: 0.20 to 0.80%, Si: 0.15 to 0.90%, Mn: 15.0 to 30.0%, P: 0.030% or less, S: 0.030% or less, Al: 0.020% or less, Ni: 0.01 to 10.00%, Cr: 6.0 to 15.0%, Mo: 0.01 to 3.50%, O: 0.010% or less, N: 0.120% or less, and the balance being Fe and incidental impurities.

Provided is a solid wire for gas metal arc welding, solid wire being suitable as a welding material for high-Mn steel materials and generating less fume during welding. The solid wire of the present invention has a composition containing, in mass %, C: 0.20 to 0.80%, Si: 0.15 to 0.90%, Mn: 15.0 to 30.0%, P: 0.030% or less, S: 0.030% or less, Al: 0.020% or less, Ni: 0.01 to 10.00%, Cr: 6.0 to 15.0%, Mo: 0.01 to 3.50%, O: 0.010% or less, N: 0.120% or less, and the balance being Fe and incidental impurities.

A high permeability grain oriented electrical steel having a chemistry comprising, all in weight percent, 2.5% to 4.5% silicon, 0.02% to 0.08% carbon, 0.01 to 0.05% aluminum, 0.005% to 0.050% sulfur or selenium, 0.02 to 0.20% manganese, 0.05 to 0.20% tin, 0.05 to 1% copper, 0.5% to 2.0% chromium, up to 0.10% phosphorus and up to 0.20% antimony with the balance being essentially iron and residual elements. The steel contains chromium and phosphorus in such amounts that a Cr:(P+0.25Sb) ratio is below 80:1 or, below 50:1, or below 30:1 which provides highly stable magnetic properties in the finished steel sheet. A hot processed band comprised of such steel is annealed and rapidly cooled after such annealing at a rate of at least 50° C. per second from 875-950° C. to a temperature below 400° C. prior to cold rolling to final thickness. Such steel forming a hot processed band having a thickness of from 1.5 to 4.0 mm and having a volume resistivity of at least 50 μΩ-cm, an austenite volume fraction (γ1150° C.) of at least 20%, and an isomorphic layer thickness of at least 2% of the total thickness on at least one surface of the hot processed band.

A duplex ferritic austenitic stainless steel having high formability utilizing the TRIP effect and high corrosion resistance with the balanced pitting resistance equivalent is formed with less than 0.04 weight % carbon, 0.2-0.8 weight % silicon, less than 2.0 weight % manganese, 16.5-19.5 weight % chromium, 3.0-4.7 weight % nickel, 1.5-4.0 weight % molybdenum, less than 3.5 weight % tungsten, less than 1 weight % copper, 0.13-0.26 weight % nitrogen, the rest being iron and inevitable impurities occurring in stainless steels.

A duplex ferritic austenitic stainless steel having high formability utilizing the TRIP effect and high corrosion resistance with the balanced pitting resistance equivalent is formed with less than 0.04 weight % carbon, 0.2-0.8 weight % silicon, less than 2.0 weight % manganese, 16.5-19.5 weight % chromium, 3.0-4.7 weight % nickel, 1.5-4.0 weight % molybdenum, less than 3.5 weight % tungsten, less than 1 weight % copper, 0.13-0.26 weight % nitrogen, the rest being iron and inevitable impurities occurring in stainless steels.

Novel High-Entropy Alloy (HEA) compositions are particularly suited to welding applications. The mixtures contain at least the elements nickel, manganese, cobalt, chromium, vanadium, molybdenum, and iron. The % weight of the constituents varies in accordance with the detailed description contained herein, with tolerances in the range of ±4% for major alloying elements and ±1% for minor alloying elements. The mixture may also contain a small amount of Aluminum, Titanium, and Boron with a tolerance in the range of +/−1% or, more preferably, +/−0.5% In accordance with the invention, the compositions above may be integrated into HEA welding products using cored wire and welding electrode manufacturing techniques, preferably starting with vacuum melted rolled alloys. One manufacturing process uses the compositions as an alloyed strip formed around the appropriate ground/crushed alloys to make commercially viable fabricated welding products.

Novel High-Entropy Alloy (HEA) compositions are particularly suited to welding applications. The mixtures contain at least the elements nickel, manganese, cobalt, chromium, vanadium, molybdenum, and iron. The % weight of the constituents varies in accordance with the detailed description contained herein, with tolerances in the range of ±4% for major alloying elements and ±1% for minor alloying elements. The mixture may also contain a small amount of Aluminum, Titanium, and Boron with a tolerance in the range of +/−1% or, more preferably, +/−0.5% In accordance with the invention, the compositions above may be integrated into HEA welding products using cored wire and welding electrode manufacturing techniques, preferably starting with vacuum melted rolled alloys. One manufacturing process uses the compositions as an alloyed strip formed around the appropriate ground/crushed alloys to make commercially viable fabricated welding products.