A silver-coated resin particle including a heat-resistant resin core particle and a silver coating layer formed on the surface of the resin core particle. The average grain diameter of the resin core particle is 0.1 to 10 μm, the amount of silver contained in the silver coating layer is 60 to 90 parts by mass, relative to 100 parts by mass of the silver-coated resin particle, and the exothermic peak temperature of the silver-coated resin particle by differential thermal analysis is 265° C. or higher.

Provided is a composition for forming a plating base on which plating is applied without a pretreatment, especially any activation process for the plating base, conventionally believed to be necessary, as well as a thus-formed plating base and a method of forming a plating coat over the plating base. The plating base is a coating film formed by applying and drying a metal nanoparticle dispersion liquid or a metal nanoparticle dispersion ink in which metal nanoparticles are protected with a small amount of protecting agent. Thus, a metal film can be formed by plating without operations such as substrate cleaning or catalyst imparting and activating. Since it is not necessary to wash the substrate with acid or base solution or to heat-treat it at a high temperature, many variations of materials become available for the substrate.

Two-dimensional conductive nanoparticles may facilitate preparation of metal coatings prepared via electroless plating. Articles having a metal coating may comprise: a polymer body, and a metal coating on at least a portion of an outer surface of the polymer body. The metal coating comprises a plating metal and overlays a plurality of two-dimensional conductive nanoparticles and a catalyst metal.

The invention provides a process for forming crack-free dielectric films on a substrate. The process comprises the application of a dielectric precursor layer of a thickness from about 0.3 μm to about 1.0 μm to a substrate. The deposition is followed by low temperature heat pretreatment, prepyrolysis, pyrolysis and crystallization step for each layer. The deposition, heat pretreatment, prepyrolysis, pyrolysis and crystallization are repeated until the dielectric film forms an overall thickness of from about 1.5 μm to about 20.0 μm and providing a final crystallization treatment to form a thick dielectric film. The process provides a thick crack-free dielectric film on a substrate, the dielectric forming a dense thick crack-free dielectric having an overall dielectric thickness of from about 1.5 μm to about 20.0 μm.

Solid state light emitting micropixels array structures having hydrogen barrier layers to minimize or eliminate undesirable passivation of doped GaN structures due to hydrogen diffusion.

A method of coating an electroplating rack used for supporting non-conductive substrates during a plating process. The method comprises the steps of contacting at least a portion of the electroplating rack with a plastisol composition, the plastisol composition having dispersed therein an effective amount of an additive; and heating the electroplating rack with the plastisol composition thereon to a suitable temperature and for a sufficient time to cure the plastisol and form a solid insulating coating on the electroplating rack. The coated electroplating rack may then be used for mounting non-conductive substrates for subsequent metallization steps.

This application relates to a metal coating method for plastic outer part requiring robustness. In the metal coating method, first, provide a plastic outer part as a motion assistance tool. Thereafter, a cold plasma treatment is performed to introduce a polar functional group to a surface of the plastic outer part by treating the plastic outer part with cold plasma. Next, a metal coating layer is formed on the surface of the plastic outer part treated with the cold plasma by an electroless plating method. Thereafter, an adhesive strength improvement process of improving an adhesive strength between the metal coating layer and the plastic outer part to 1,000 g/cm.sup.2 or more by heat treatment of the plastic outer part with the metal coating layer thereon is performed.

A process of pretreatment for selective application of electroless metallization to a surface of a non-conductive material and a solution useful for the pretreatment are provided. The process achieves good coverage in areas to be plated on the surface of non-conductive materials without skip plating or over plating.

The present invention relates to a composition for forming a conductive pattern by irradiation of electromagnetic waves capable of allowing excellent formation of a conductive micro-pattern on various polymer resin products comprising a polycarbonate resin or on resin layers by a simple method such as irradiation of electromagnetic waves and plating, and capable of reducing the degradation of the physical properties of the resin products or resin layers caused by the irradiation of electromagnetic waves, a method for forming a conductive pattern using the same, and a resin structure having a conductive pattern. The composition for forming a conductive pattern by irradiation of electromagnetic waves comprises: a polymer resin comprising a polycarbonate resin; and an electromagnetic wave-absorbing inorganic additive which absorbs an electromagnetic wave having a wavelength in the infrared region and satisfies the characteristic that a laser sensitivity Ls defined by a predetermined relational expression is 1.6<−log(Ls)<6.0.

The present invention relates to a composition for forming a conductive pattern by irradiation of electromagnetic waves capable of allowing excellent formation of a conductive micro-pattern on various polymer resin products comprising a polycarbonate resin or on resin layers by a simple method such as irradiation of electromagnetic waves and plating, and capable of reducing the degradation of the physical properties of the resin products or resin layers caused by the irradiation of electromagnetic waves, a method for forming a conductive pattern using the same, and a resin structure having a conductive pattern. The composition for forming a conductive pattern by irradiation of electromagnetic waves comprises: a polymer resin comprising a polycarbonate resin; and an electromagnetic wave-absorbing inorganic additive which absorbs an electromagnetic wave having a wavelength in the infrared region and satisfies the characteristic that a laser sensitivity Ls defined by a predetermined relational expression is 1.6<−log(Ls)<6.0.