A sliding element for an internal combustion engine may include a base material having an annular external surface. The external surface may include a bonding layer, a first layer of coating, and a second layer of coating sequentially disposed thereon. The first layer of coating and the second layer of coating may include hard amorphous carbon (DLC) of a combined matrix having a plurality of sp3/sp2 bonds. The first layer of coating may include 45% sp3 bonds or less and may have a thickness of at least 10 micrometers. The second layer of coating may include at least 55% sp3 bonds and may have a thickness of at least 3 micrometers.

A device comprising: a substrate; a first coating deposited on the substrate; an intermediate coating deposited on the first coating, wherein the first coating is interposed between the substrate and the intermediate coating; and a second coating deposited on the intermediate coating, wherein the intermediate coating is interposed between the first coating and the second coating, and the second coating is outermost and black. The substrate, the first coating, the intermediate coating and the second coating define at least one of a jewelry item and a component of a jewelry item.

An electrical contact part comprising, a carrier substrate of a metallic material, a metallic coating applied to the carrier substrate, and a coating barrier material applied to the carrier substrate in a partial area of the carrier substrate, wherein the coating barrier material substantially prevents coating of the carrier substrate in the portion.

A steel sheet has a hot-dip Zn—Al—Mg-based coating film, the coating film containing 1 mass % to 22 mass % of Al and 0.1 mass % to 10 mass % of Mg on a surface of the steel sheet, in which an X-ray diffraction peak intensity ratio of a Mg—Zn compound phase in the coating film, that is, MgZn.sub.2/Mg.sub.2Zn.sub.11, is 0.2 or less.

Provided is a multilayer zinc alloy plated steel material comprising a base steel material and multiple plating layers formed on the base steel material, wherein each of the multiple plating layers includes one of a Zn plating layer, a Mg plating layer, and a Zn—Mg alloy plating layer, and the ratio of the weight of Mg contained in the multiple plating layers to the total weight of the multiple plating layers is from 0.13 to 0.24.

A process of forming an erosion, oxidation, and wear resistant shot chamber, either a gooseneck or a shot sleeve, is provided. The process utilizes a shrink fitting process for forming a one-piece shot chamber having a liner bonded to the bulk portion of the shot chamber. Channels of predetermined shape and layout are built on the tubular external surface of the liner for facilitating thermal management of the shot chamber during die casting operations.

Provided is an Al-plated hot stamped steel material comprising a steel base material, an Al-plating layer formed on at least one surface of the steel base material, and a chemical conversion coating formed on the Al-plating layer and containing zinc phosphate-based crystals and Ce-based compounds deposited on the surfaces of the zinc phosphate-based crystals, wherein an amount of deposition of the zinc phosphate-based crystals in the chemical conversion coating is, converted to metal Zn, 0.3 to 4.0 g/m.sup.2 and an area ratio of the Ce-based compounds in the chemical conversion coating is 0.5 to 25%.

The present invention relates to an ultra-high strength, hot-dip galvanized steel sheet having excellent surface quality and coating adherence and to a method for manufacturing thereof, the ultra-high strength, hot-dip galvanized steel sheet comprising: 0.1-0.3% by weight carbon (C); 0.1-2.0% by weight silicon (Si); 0.005-1.5% by weight aluminum (Al); 1.5-3.5% by weight manganese (Mn); 0.04% by weight or less phosphorus (P) (excluding 0% by weight); 0.015% by weight or less sulphur (S) (excluding 0% by weight); 0.02% by weight or less nitrogen (N) (excluding 0% by weight); the balance being Fe; and other inevitable impurities, and further comprising 0.01 wt.% to 0.07 wt.% of at least one kind of element selected from the group consisting of bismuth (Bi), tin (Sn) and antimony (Sb).

A method of forming a multilayered zinc alloy coating comprises steps of providing a bath of an aqueous electrolyte including zinc and a second electrodepositable component in an electrolytic cell having an anode and a cathode; applying a current or voltage between the anode and the cathode; modulating the applied current or voltage over time between at least two current or voltage values to thereby modulate the current density over multiple cycles between at least two current density values, wherein a first current density value is in a range of 0.3 to less than 2 A/dm.sup.2 and a second current density value is higher than the first current density value and is in a range of 0.6 to less than 5 A/dm.sup.2; and controlling the modulation of the applied current or voltage to obtain a multilayered structure having multiple layers of one or more of alternating proportions of the second component, alternating corrosion potential, alternating grain size, and alternating grain orientation, wherein one or more of the multiple layers has a thickness in the range of 1 to 10 μm.

A steel sheet for a fuel tank includes: a Zn—Ni alloy plated layer which is placed on one surface or each of both surfaces of a base metal and formed on at least one surface; and an inorganic chromate-free chemical conversion coating film which is placed over the Zn—Ni alloy plated layer. The Zn—Ni alloy plated layer has a crack starting from an interface between the Zn—Ni alloy plated layer and the inorganic chromate-free chemical conversion coating film and reaching an interface between the Zn—Ni alloy plated layer and the steel sheet, and a water contact angle on a surface of the inorganic chromate-free chemical conversion coating film is more than or equal to 50 degrees.