Methods for forming a coated component, along with the resulting coated components, are provided. The method may include forming a silicon-based bond coating on a surface of a substrate and forming a barrier coating on the silicon-based bond coating. The silicon-based bond coating comprises columnar grains of crystalline silicon. Chemical vapor depositing (CVD) may be used to form the silicon-based bond coating through CVD of a silicon-containing precursor at a deposition temperature and deposition pressure that causes crystallization of the silicon material during the deposition of the silicon-based bond coating. The silicon-containing precursor may be silane, monochlorosilane, dichlorosilane, and/or trichlorosilane.

Methods for forming a coated component, along with the resulting coated components, are provided. The method may include forming a silicon-based bond coating on a surface of a substrate and forming a barrier coating on the silicon-based bond coating. The silicon-based bond coating comprises columnar grains of crystalline silicon. Chemical vapor depositing (CVD) may be used to form the silicon-based bond coating through CVD of a silicon-containing precursor at a deposition temperature and deposition pressure that causes crystallization of the silicon material during the deposition of the silicon-based bond coating. The silicon-containing precursor may be silane, monochlorosilane, dichlorosilane, and/or trichlorosilane.

A cubic boron nitride sintered body including cubic boron nitride and a binder phase, wherein a content of the cubic boron nitride is 40 volume % or more and 80 volume % or less; a content of the binder phase is 20 volume % or more and 60 volume % or less; an average particle size of the cubic boron nitride is 0.5 μm or more and 4.0 μm or less; the binder phase contains TiC and TiB.sub.2 and contains substantially no AlN and/or Al.sub.2O.sub.3; a (101) plane of TiB.sub.2 in the binder phase shows a maximum peak position (2θ) in X-ray diffraction of 44.2° or more; and a (200) plane of TiC in the binder phase shows a maximum peak position (2θ) in X-ray diffraction of less than 42.1°.

A solid state heater and methods of manufacturing the heater is disclosed. The heater comprises a unitary component that includes portions that are graphite and other portions that are silicon carbide. Current is conducted through the graphite portion of the unitary structure between two or more terminals. The silicon carbide does not conduct electricity, but is effective at conducting the heat throughout the unitary component. In certain embodiments, chemical vapor conversion (CVC) is used to create the solid state heater. If desired, a coating may be applied to the unitary component to protect it from a harsh environment.

A solid state heater and methods of manufacturing the heater is disclosed. The heater comprises a unitary component that includes portions that are graphite and other portions that are silicon carbide. Current is conducted through the graphite portion of the unitary structure between two or more terminals. The silicon carbide does not conduct electricity, but is effective at conducting the heat throughout the unitary component. In certain embodiments, chemical vapor conversion (CVC) is used to create the solid state heater. If desired, a coating may be applied to the unitary component to protect it from a harsh environment.

A coated cutting tool, comprising: a substrate; and a coating layer formed on a surface of the substrate, wherein the coating layer includes a lower layer and an upper layer in this order from a substrate side toward a surface side, and the upper layer is formed on a surface of the lower layer, the lower layer contains a compound having a composition represented by (Al.sub.xTi.sub.1-x)N, an average thickness of the lower layer is 1.0 μm or more and 15.0 μm or less, the upper layer contains an α-Al.sub.2O.sub.3 layer containing α-Al.sub.2O.sub.3, an average thickness of the upper layer is 0.5 μm or more and 15.0 μm or less, and in grains of the α-Al.sub.2O.sub.3 layer, a proportion of grains of which a grain size is 0.05 μm or more and less than 0.5 μm is 50% by area or more and 80% by area or less.

A coated cutting tool, comprising: a substrate; and a coating layer formed on a surface of the substrate, wherein the coating layer includes a lower layer and an upper layer in this order from a substrate side toward a surface side, and the upper layer is formed on a surface of the lower layer, the lower layer contains a compound having a composition represented by (Al.sub.xTi.sub.1-x)N, an average thickness of the lower layer is 1.0 μm or more and 15.0 μm or less, the upper layer contains an α-Al.sub.2O.sub.3 layer containing α-Al.sub.2O.sub.3, an average thickness of the upper layer is 0.5 μm or more and 15.0 μm or less, and in grains of the α-Al.sub.2O.sub.3 layer, a proportion of grains of which a grain size is 0.05 μm or more and less than 0.5 μm is 50% by area or more and 80% by area or less.

A surface-coated cutting tool according to the present invention includes a tool body and a hard coating layer including a complex carbonitride layer containing a small amount of chlorine and (Ti.sub.(1-x)Zr.sub.xyHf.sub.x(1-y))(N.sub.(1-z)C.sub.z) (0.10≤x≤0.90, 0<y≤1.0, 0.08<z<0.60), a ZrHf and C content ratios in cycles, a cycle distance between a maximum ZrHf content point and an adjacent minimum ZrHf content point and a cycle distance between a maximum C content point and an adjacent minimum C content point are 5 to 100 nm, an average value of content ratio differences Δx and Δz is 0.02 or more, a distance between the maximum ZrHf content point and the maximum C content point is ⅕ or less of the distance between a maximum content point and a minimum content point of adjacent ZrHf components, and a composition fluctuation structure is 10% or more.

A surface-coated cutting tool according to the present invention includes a tool body and a hard coating layer including a complex carbonitride layer containing a small amount of chlorine and (Ti.sub.(1-x)Zr.sub.xyHf.sub.x(1-y))(N.sub.(1-z)C.sub.z) (0.10≤x≤0.90, 0<y≤1.0, 0.08<z<0.60), a ZrHf and C content ratios in cycles, a cycle distance between a maximum ZrHf content point and an adjacent minimum ZrHf content point and a cycle distance between a maximum C content point and an adjacent minimum C content point are 5 to 100 nm, an average value of content ratio differences Δx and Δz is 0.02 or more, a distance between the maximum ZrHf content point and the maximum C content point is ⅕ or less of the distance between a maximum content point and a minimum content point of adjacent ZrHf components, and a composition fluctuation structure is 10% or more.

A method of fabricating a brake component made from a ceramic matrix composite is disclosed. In various embodiments, the method includes infiltrating a carbon fabric with a slurry containing a ceramic powder and a sintering aid; laying up the carbon fabric in a desired geometry to form a raw component; warm pressing the raw component to form a green component; and sintering the green component via a spark plasma sintering process to form a sintered component.