Systems and methods for forming an oxidation protection system on a composite structure are provided. In various embodiments, the oxidation protection system comprises a boron-glass layer formed on the composite substrate and a silicon-glass layer formed over the boron-glass layer. Each of the boron-glass layer and the silicon-glass layer include a glass former and a glass modifier.

A method for forming a protective coating on a surface of a ceramic substrate includes combining a rare-earth oxide, alumina, and silica to form a powder, etching the surface of the ceramic substrate, applying the powder on the etched surface in an amount of from about 0.001 to about 0.1 g/cm.sup.2 to reduce capture of bubbles from off-gassing of the ceramic substrate, heating the powder for a time of from about 5 to about 60 minutes to a temperature at or above the melting point such that the powder melts and forms a molten coating on the surface that has a minimized number of bubbles, and cooling the molten coating to ambient temperature to form the protective coating disposed on and in direct contact with the surface of the ceramic substrate such that the protective coating has a thickness of less than about 1 mil.

A method for forming a protective coating on a surface of a ceramic substrate includes combining a rare-earth oxide, alumina, and silica to form a powder, etching the surface of the ceramic substrate, applying the powder on the etched surface in an amount of from about 0.001 to about 0.1 g/cm.sup.2 to reduce capture of bubbles from off-gassing of the ceramic substrate, heating the powder for a time of from about 5 to about 60 minutes to a temperature at or above the melting point such that the powder melts and forms a molten coating on the surface that has a minimized number of bubbles, and cooling the molten coating to ambient temperature to form the protective coating disposed on and in direct contact with the surface of the ceramic substrate such that the protective coating has a thickness of less than about 1 mil.

A sandwich-structured dielectric material for pulse energy storage is provided as well as a preparation method thereof. Employing a sandwich structure and combining the properties of ceramic-glass materials prepares a high performance dielectric material for pulse energy storage, in which the ceramic dielectric is core-shell structured powder of Ba.sub.xSr.sub.1-xTiO.sub.3 coated with SiO.sub.2, and the glass material is alkali-free glass AF45, of which the chemical composition is 63% SiO.sub.2-12% BaO-16% B.sub.2O.sub.3-9% Al.sub.2O.sub.3. AF45 alkali-free glass paste is spin-coated on both sides of the ceramic and calcined to get a layer-structured material of glass-ceramic-glass.

Systems and methods for forming an oxidation protection system on a composite structure are provided. In various embodiments, an oxidation protection system disposed on a substrate may comprise a boron-silicon-glass layer or a boron layer and a silicon layer. The boron-silicon-glass layer, boron layer, the silicon layer, or a pretreatment layer may include an oxygen reactant compound.

Systems and methods for forming an oxidation protection system on a composite structure are provided. In various embodiments, an oxidation protection system disposed on a substrate may comprise a boron-silicon-glass layer formed directly on the composite structure. The boron-silicon-glass layer may comprise a boron compound, a silicon compound, and a glass compound.

A process of coating a substrate containing silicon with an environmental barrier coating, comprising altering a surface of the substrate and applying an environmental barrier layer to the surface of the substrate.

A method for coating a composite structure, comprising applying a first slurry onto a surface of the composite structure, wherein the first slurry is a sol gel comprising a metal organic salt, a first carrier fluid, and a ceramic material, and heating the composite structure to a first sol gel temperature sufficient to form a sol gel-derived base layer on the composite structure.

The present invention relates to a glass ceramic for veneering a dental frame structure, wherein said glass ceramic is characterized by a high content of B.sub.2O.sub.3, to a process for the preparation thereof, and to the use thereof in the production of dental restorations.

A method for coating a composite structure, comprising applying a first slurry onto a surface of the composite structure, wherein the first slurry is a sol gel comprising a metal organic salt, a first carrier fluid, and a ceramic material, and heating the composite structure to a first sol gel temperature sufficient to form a sol gel-derived base layer on the composite structure.