The disclosure relates to microchemical (or microfluidic) apparatus as well as related methods for making the same. The methods generally include partial sintering of sintering powder (e.g., binderless or otherwise free-flowing sintering powder) that encloses a fugitive phase material having a shape corresponding to a desired cavity structure in the formed apparatus. Partial sintering removes the fugitive phase and produces a porous compact, which can then be machined if desired and then further fully sintered to form the final apparatus. The process can produce apparatus with small, controllable cavities shaped as desired for various microchemical or microfluidic unit operations, with a generally smooth interior cavity finish, and with materials (e.g., ceramics) able to withstand harsh environments for such unit operations.

A method for making a dielectric substrate configured for incorporation into a hermetically sealed feedthrough is described. The method includes forming a via hole through a green-state dielectric substrate. A platinum-containing paste is filled into at least 90% of the volume of the via hole. The green-state dielectric substrate is then subjected to a heating protocol including: a binder bake-out heating portion performed at a temperature ranging from about 400 C. to about 700 C. for a minimum of 4 hours; a sintering heating portion performed at a temperature ranging from about 1,400 C. to about 1,900 C. for up to 6 hours; and a cool down portion at a rate of up to 5/minute from a maximum sintering temperature down to about 1,000 C., then naturally to room temperature. The thusly manufacture dielectric substrate is then positioned in an opening in a ferrule that is configured to be attached to a metal housing of an active implantable medical device. The dielectric substrate is hermetically sealed to the ferrule with the sintered platinum material in the via hole providing a conductive pathway from a body fluid side to a device side of the ferrule.

A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.

A process for producing a silicon nitride powder characterized by comprising a step of providing a starting material powder containing not less than 90% by mass of a silicon powder; the step of filling a heat-resistant reaction vessel with the starting material powder; a step of obtaining a massive product thereof by a combustion synthesis reaction by igniting the starting material powder filled in the reaction vessel in a nitrogen atmosphere and permitting a heat of nitriding combustion of silicon to propagate to the whole starting material powder; and a step of mechanically milling the massive product by a dry method.

A particle composition according to the present invention contains: hydraulic alumina particles; and a water-absorbing polymer.

The present invention relates to a method of forming a 3D ceramic structure by adding a 3D structure with one or more layer(s) of ceramic mixture onto a ceramic substrate. The present invention also relates to a 3D ceramic structure as well as to a green 3D ceramic structure.

Method for producing ceramic components, more particularly ceramic components having recesses and/or hollow spaces, there being at least one sintered ceramic part present. In order to improve the handling qualities of ceramic components, the sintered ceramic part can include a carrier or carrying section which is removed in the further processing from at least one ceramic component.

A dental zirconia system to produce translucent zirconia sintered bodies comprises at least two separate zirconia green bodies. At least one zirconia green body comprises zirconium oxide and a lower content of at least one other oxide summing to between 6.5 wt % to 20 wt % based on a total weight percent of the zirconia green body. At least another zirconia green body comprises zirconium oxide and a higher content of at least one other oxide summing to between 7.5 wt % to 20 wt % based on a total weight percent of the zirconia green body. The at least two zirconia green bodies each have at least some particles with a diameter of 100 nanometers to 1000 nanometers. The at least two zirconia green bodies have different amounts of the at least one other oxide with respect to one another.

Disclosed are a low-shrinkage, high-strength, and large ceramic plate and a manufacturing method thereof. The method comprises the following steps: (1) preparing a ceramic raw material powder; (2) subjecting an acicular wollastonite to surface coating with a silane coupling agent and to pre-dispersion with a fumed silica to obtain a pre-treated acicular wollastonite; and (3) thoroughly mixing the ceramic raw material powder and the pre-treated acicular wollastonite and granulating the resulting mixture, the amount of the pre-treated acicular wollastonite added being 10 wt % to 30 wt % of the ceramic raw material powder, and subjecting the resulting granules to dry pressing and sintering to obtain the large ceramic plate. The acicular wollastonite is incorporated into the manufacturing of the large ceramic plate to take full advantage of the reinforcing effect and low sintering shrinkage characteristics of the acicular wollastonite. The invention reduces sintering shrinkage and increases product strength.

A manufacturing line includes a tape of green material that is directed through a furnace so that the furnace burns off organic binder material and then partially sinters the tape without the use of a setter board. Sintered articles resulting from the manufacturing line may be thin with relatively large surface areas; and, while substantially unpolished, have few sintering-induced surface defects. Tension may be applied to the partially sintered tape as it passes through a second furnace on the manufacturing line to shape resulting sintered articles.