A method of producing a cement composition with reduced carbon emissions may include: defining cement constraints comprising at least one cement property; calculating a set of cement compositions which satisfy the cement constraints, using cement property models corresponding to the cement constraints; calculating a carbon emission associated with each of the cement compositions in the set of cement compositions using a carbon footprint model; selecting a cement composition from the set of cement compositions; and preparing the cement composition.

A cement composition is disclosed that includes a cement slurry and an epoxy resin system that includes at least one epoxy resin and a curing agent. The cement slurry has a density in a range of from 65 pcf to 180 pcf and includes a cement precursor material, silica sand, silica flour, a weighting agent, and manganese tetraoxide. The epoxy resin system includes at least one of 2,3-epoxypropyl o-tolyl ether, alkyl glycidyl ethers having from 12 to 14 carbon atoms, bisphenol-A-epichlorohydrin epoxy resin, or a compound having formula (I): (OC.sub.2H.sub.3)—CH.sub.2—O—R.sup.1—O—CH.sub.2—(C.sub.2H.sub.3O) where R.sup.1 is a linear or branched hydrocarbyl having from 4 to 24 carbon atoms; and a curing agent.

A cement composition is disclosed that includes a cement slurry and an epoxy resin system that includes at least one epoxy resin and a curing agent. The cement slurry has a density in a range of from 65 pcf to 180 pcf and includes a cement precursor material, silica sand, silica flour, a weighting agent, and manganese tetraoxide. The epoxy resin system includes at least one of 2,3-epoxypropyl o-tolyl ether, alkyl glycidyl ethers having from 12 to 14 carbon atoms, bisphenol-A-epichlorohydrin epoxy resin, or a compound having formula (I): (OC.sub.2H.sub.3)—CH.sub.2—O—R.sup.1—O—CH.sub.2—(C.sub.2H.sub.3O) where R.sup.1 is a linear or branched hydrocarbyl having from 4 to 24 carbon atoms; and a curing agent.

The present discloses a water-based gel-consolidation type lost circulation material system suitable for fractured lost circulation formation, preparation method and use thereof.

The present discloses a water-based gel-consolidation type lost circulation material system suitable for fractured lost circulation formation, preparation method and use thereof.

A method may include providing a fluid loss model, providing a fluid loss requirement, generating a cement slurry recipe using the fluid loss model and the fluid loss requirement such that a calculated fluid loss of the cement slurry recipe using the fluid loss model meets or exceeds the fluid loss requirement; and preparing a cement slurry based on the cement slurry recipe.

A method may include providing a fluid loss model, providing a fluid loss requirement, generating a cement slurry recipe using the fluid loss model and the fluid loss requirement such that a calculated fluid loss of the cement slurry recipe using the fluid loss model meets or exceeds the fluid loss requirement; and preparing a cement slurry based on the cement slurry recipe.

A method of reducing lost circulation includes introducing a lost circulation solution comprising Saudi Arabian volcanic ash, a curing agent, and a resin into a subsurface formation through a wellbore, wherein the Saudi Arabian volcanic ash comprises SO.sub.3, CaO, SiO.sub.2, Al.sub.2O.sub.3, Fe.sub.2O.sub.3, MgO, and K.sub.2O; and allowing the lost circulation solution to thicken within the subsurface formation, thereby forming a barrier between the subsurface formation and the wellbore to reduce lost circulation.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350° C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.

The invention provides a high temperature resistant Portland cement slurry and a production method thereof. The high temperature resistant Portland cement slurry comprises the following components by weight: 100 parts of an oil well Portland cement, 60-85 parts of a high temperature reinforcing material, 68-80 parts of fresh water, 1-200 parts of a density adjuster, 0.1-1.5 parts of a suspension stabilizer, 0.8-1.5 parts of a dispersant, 3-4 parts of a fluid loss agent, 0-3 parts of a retarder and 0.2-0.8 part of a defoamer. The high temperature resistant Portland cement slurry has a good sedimentation stability at normal temperature, and develops strength rapidly at a low temperature. The compressive strength is up to 40 MPa or more at a high temperature of 350° C., and the long-term high-temperature compressive strength develops stably without degradation. Therefore, it can meet the requirements for field application in heavy oil thermal recovery wells, reaching the level of Grade G Portland cement for cementing oil and gas wells.