Provided is a high-strength hot-rolled steel sheet containing, by mass %, C: 0.050 to 0.200%, Si: 0.01 to 1.5%, Mn: 1.0 to 3.0%, B: 0.0002 to 0.0030%, Ti: 0.03 to 0.20%, P: limited to 0.05% or less, S: limited to 0.005% or less, Al: limited to 0.5% or less, N: limited to 0.009% or less, and one or more of Nb: 0.01 to 0.20%, V: 0.01 to 0.20%, and Mo: 0.01 to 0.20%, with the balance being composed of Fe and inevitable impurities. In the high-strength hot-rolled steel sheet, a ratio of a length of small-angle crystal grain boundaries that are boundaries having a crystal orientation angle of 5° or more but less than 15° to a length of large-angle crystal grain boundaries that are boundaries having a crystal orientation angle of 15° or more is 1:1 to 1:4, an total segregation amount of C and B in the large-angle grain boundaries is 4 to 20 atoms/nm.sup.2, tensile strength is 850 MPa or higher, and a hole expansion ratio is 25% or more.

Provided are a high-strength galvanized steel sheet containing 0.12% to 0.25% C, 0.01% to 1.00% Si, 1.5% to 4.0% Mn, 0.100% or less P, 0.02% or less S, 0.01% to 0.10% Al, 0.001% to 0.010% N, 0.005% to 0.100% Ti, and 0.0005% to 0.0050% B, the remainder being Fe and inevitable impurities, Ti>4N being satisfied. The high-strength galvanized steel sheet contains 80% to 100% martensite in terms of area fraction, 5% or less (including 0%) polygonal ferrite in terms of area fraction, and less than 3% (including 0%) retained austenite in terms of area fraction. The average hardness of martensite is 400 to 500 in terms of Vickers hardness (Hv). The average grain size of martensite is 20 μm or less. The standard deviation of the grain size of martensite is 7.0 μm or less.

The invention relates to a steel sheet having a tensile strength of 1180 MPa or more, which excels in workability and cold brittleness resistance. The high-strength steel sheet contains 0.10% to 0.30% of C, 1.40% to 3.0% of Si, 0.5% to 3.0% of Mn, 0.1% or less of P, 0.05% or less of S, 0.005% to 0.20% of Al, 0.01% or less of N, 0.01% or less of O, as well as Fe and inevitable impurities. The steel sheet has: (i) a ferrite volume fraction of 5% to 35% and a bainitic ferrite and/or tempered martensite volume fraction of 60% or more; (ii) a MA constituent volume fraction of 6% or less (excluding 0%); and (iii) a retained austenite volume fraction of 5% or more.

The high strength steel sheet has a chemical composition including 0.08% to 0.20% of C, 0.3% or less of Si, 0.1% to 3.0% of Mn, 0.10% or less of P, 0.030% or less of S, 0.10% or less of Al, 0.010% or less of N, 0.20% to 0.80% of V, and the remainder composed of Fe and incidental impurities on a percent by mass basis, and a microstructure which includes 95% or more of ferrite phase on an area percentage basis, in which fine precipitates are dispersed having a distribution in such a way that the number density of precipitates having a particle size of less than 10 nm is 1.0×10.sup.5/μm.sup.3 or more and the standard deviation of natural logarithm values of precipitate particle sizes with respect to precipitates having a particle size of less than 10 nm is 1.5 or less.

Provided is a high-strength cold rolled steel sheet, a high-strength hot-dip galvanized steel sheet manufactured using the cold rolled steel sheet, and manufacturing methods therefor, the high-strength cold rolled steel sheet comprising, by wt %, 0.17-0.21% of carbon (C), 0.3-0.8% of silicon (Si), 2.7-3.3% of manganese (Mn), 0.3-0.7% of chromium (Cr), 0.01-0.3% of aluminum (Al), 0.01-0.03% of titanium (Ti), 0.001-0.003% of boron (B), 0.04% or less of phosphorus (P), 0.02% or less of sulfur (S), 0.01% or less of nitrogen (N) and the balance of iron (Fe) and other inevitable impurities, wherein the amounts of carbon (C), silicon (Si) and aluminum (Al) satisfy the following mathematical relation (1). [Mathematical relation (1)] [C]+([Si]+[Al])/5≤0.35% (wherein [C], [Si] and [Al] respectively mean the wt % of C, Si and Al.)

Provided is a hot rolled steel sheet comprising a predetermined chemical composition, and a metallic structure comprising, by area ratio, pearlite: 90 to 100%, pseudo pearlite: 0 to 10%, and pro-eutectoid ferrite: 0 to 1%, wherein the pearlite has an average lamellar spacing of 0.20 μm or less, and the pearlite has an average pearlite block size of 20.0 μm or less. Provided is a method for producing a hot rolled steel sheet comprising heating a slab to 1100° C. or more, hot rolling where an exit side temperature of finishing rolling is 820 to 920° C., primary cooling the steel sheet down to an Ae1 point by an average cooling rate of 40 to 80° C./s, then secondary cooling the steel sheet from the Ae1 point down to a coiling temperature by an average cooling rate of less than 20° C./s, and coiling the steel sheet at a coiling temperature of 540 to 700° C.

Disclosed is a hot-pressed member that can exhibit very high tensile strength after hot pressing as high as TS: 1780 MPa or more, and excellent indentation peeling strength at projection welds by properly adjusting its chemical composition and its microstructure such that a prior austenite average grain size is 7 μm or less within a range of 50 μm or less in a thickness direction from a surface of the member, a volume fraction of martensite is 90% or more, and an average intergrain distance of Nb and Ti carbonitrides having a grain size of less than 0.10 μm within a depth range of 20 μm to 100 μm in the thickness direction from the surface of the member is 5 μm or less.

A warm-workable high-strength steel sheet having superior warm workability and residual ductility after warm working, and a method for manufacturing such steel sheets. The warm-workable high-strength steel sheet has a chemical composition including, in mass %, C: 0.05 to 0.20%, Si: not more than 3.0%, Mn: 3.5 to 8.0%, P: not more than 0.100%, S: not more than 0.02%, Al: 0.01 to 3.0% and N: not more than 0.010%, the balance being Fe and inevitable impurities. The steel sheet has a microstructure that includes, in area fractions, 10 to 60% retained austenite, 10 to 80% ferrite, 5 to 50% martensite and 0 to 5% bainite, the C content in the retained austenite being less than 0.40 mass %.

A high-strength cold-rolled steel sheet having a specified chemical composition and a microstructure including ferrite having an average crystal grain diameter of 2 μm or less in an amount of 10% to 25% in terms of volume fraction, retained austenite in an amount of 5% to 20% in terms of volume fraction, martensite having an average crystal grain diameter of 2 μm or less in an amount of 5% to 15% in terms of volume fraction, and the balance being a multi-phase structure including bainite and tempered martensite having an average crystal grain diameter of 5 μm or less, in which a relational expression, 0.35≦V2/V1≦0.75 (1), is satisfied, where V1 is a volume fraction of phases which are different from ferrite and V2 is a volume fraction of tempered martensite.

A steel sheet suitable as a starting material for a vehicle impact absorbing member with high absorption of impact energy and resistance to cracking contains, by mass %, C: 0.08-0.30%, Mn: 1.5-3.5%; Si+Al: 0.50-3.0%, P: 0.10% or less, S: at most 0.010%, and N: at most 0.010%, and optionally, one or more types selected from Cr: at most 0.5%, Mo: at most 0.5% , B: at most 0.010%, Ti: less than 0.04%, Nb: less than 0.030%, V: less than 0.5%, Ca: at most 0.010%, Mg: at most 0.010%, REM: at most 0.050%, and Bi: at most 0.050%. The microstructure contains, by area %, bainite: more than 50%, martensite: 3-30%, and retained austenite: 3-15%, the remainder comprising ferrite having an average grain diameter of less than 5 mm. The product of uniform elongation and hole expansion ratio is at least 300%.sup.2 and 5% effective flow stress is at least 900 MPa.