An ink of the formula: 60-80% by weight BaTiO.sub.3 particles coated with SiO.sub.2; 5-50% by weight high dielectric constant glass; 0.1-5% by weight surfactant; 5-25% by weight solvent; and 5-25% weight organic vehicle. Also a method of manufacturing a capacitor comprising the steps of: heating particles of BaTiO.sub.3 for a special heating cycle, under a mixture of 70-96% by volume N.sub.2 and 4-30% by volume H.sub.2 gas; depositing a film of SiO.sub.2 over the particles; mechanically separating the particles; incorporating them into the above described ink formulation; depositing the ink on a substrate; and heating at 850-900° C. for less than 5 minutes and allowing the ink and substrate to cool to ambient in N.sub.2 atmosphere. Also a dielectric made by: heating particles of BaTiO.sub.3 for a special heating cycle, under a mixture of 70-96% by volume N.sub.2 and 4-30% by volume H.sub.2 gas; depositing a film of SiO.sub.2 over the particles; mechanically separating the particles; forming them into a layer; and heating at 850-900° C. for less than 5 minutes and allowing the layer to cool to ambient in N.sub.2 atmosphere.

A Dielectric Energy Storage System (DESS) and method that stores energy for a wide variety of applications.

A method of manufacturing a silicon-containing oxide-coated aluminum nitride particle; a method of manufacturing a heat dispersing resin composition containing the silicon-containing oxide-coated aluminum nitride particle; and the silicon-containing oxide-coated aluminum nitride particle. The method of manufacturing includes: a first step of covering the surface of the aluminum nitride particle with an organic silicone compound including a specific structure; and a second step of heating the aluminum nitride particle covered with the organic silicone compound at a temperature of 300° C. or more and less than 1000° C., wherein the content of carbon atoms in the silicon-containing oxide-coated aluminum nitride particle is less than 1000 ppm by mass.

A porous material includes an aggregate, and a binding material that binds the aggregate together in a state where pores are formed. The porous material contains 0.1 to 10.0 mass % of an MgO component, 0.5 to 25.0 mass % of an Al.sub.2O.sub.3 component, and 5.0 to 45.0 mass % of an SiO.sub.2 component with respect to the mass of the whole porous material, and further contains 0.01 to 5.5 mass % of an Sr component in terms of SrO.

A sandwich-structured dielectric material for pulse energy storage is provided as well as a preparation method thereof. Employing a sandwich structure and combining the properties of ceramic-glass materials prepares a high performance dielectric material for pulse energy storage, in which the ceramic dielectric is core-shell structured powder of Ba.sub.xSr.sub.1-xTiO.sub.3 coated with SiO.sub.2, and the glass material is alkali-free glass AF45, of which the chemical composition is 63% SiO.sub.2-12% BaO-16% B.sub.2O.sub.3-9% Al.sub.2O.sub.3. AF45 alkali-free glass paste is spin-coated on both sides of the ceramic and calcined to get a layer-structured material of glass-ceramic-glass.

A nanoparticle cluster reduction method yields a new composition of matter including a large percentage (e.g., 75% or higher percentage) of primary nanoparticles in the new composition of matter. The particle reduction method reduces the size of nanoparticle clusters in material of the new composition of matter, allows particle reduction of specific nanoparticle cluster sizes, and allows particle reduction to primary nanoparticles. This new composition of matter can include a high permittivity and high resistivity dielectric compound. This new composition of matter, according to certain examples, has high permittivity, high resistivity, and low leakage current. In certain examples, the new composition of matter constitutes a dielectric energy storage device that is a battery with very high energy density, high operating voltage per cell, and an extended battery life cycle. An example method can include a controlled gas evolution reaction to reduce the size of nanoparticle clusters.

A multilayer ceramic capacitor that includes a ceramic body including a stack of a plurality of dielectric layers and a plurality of first and second internal electrodes; and first and second external electrodes provided at each of both end faces of the ceramic body. Each of the plurality of dielectric layers contain Ba, Ti, P and Si. The plurality of dielectric layers include an outer dielectric layer located on an outermost side in the stacking direction; an inner dielectric layer located between the first and second internal electrodes; and a side margin portion in a region where the first and second internal electrodes do not exist. In at least one of the outer dielectric layer, the inner dielectric layer and the side margin portion, the P and the Si segregate in at least one of grain-boundary triple points of three ceramic particles.

Nano-sized particles of barium-titanate are heated as a gas mixture of 25% hydrogen and 75% nitrogen is passed there through yielding particles of barium-titanate having oxygen vacancies therein. The particles of barium-titanate having oxygen vacancies therein are coated with silica yielding silica-coated particles having a silica coating thickness in a range of 2-5 nanometers. The silica-coated particles are sintered by application of pressure in a range of 35-50 megapascals and temperature in a range of 950-1050° C. The sintered quantity of material is cooled at a cooling rate in a range of 1-3° C. per minute at least until the temperature thereof is less than 120° C.

A composition based on a certain chromium-free silicate-based binder is described. The composition is an aqueous solution of lithium-doped potassium silicate in combination with an aluminum or aluminum alloy powder, zinc powder or a combination thereof. The coatings of the present invention are capable of achieving a full cure at temperatures as low as 350-450 degrees F. by the inclusion of a colloidal solution of a nano-sized ceria, thus making the coatings especially suitable for application on temperature sensitive base materials.

A dielectric substance includes a core-shell grain having a twin crystal structure. An interface of the twin crystal structure of the core-shell grain extends from a shell on one side, passes through a core, and extends to the shell on the other side.