The present disclosure relates to a method for manufacturing a semiconductor package including vacuum-laminating a non-conductive film on a substrate on which a plurality of through silicon vias are provided and bump electrodes are formed, and then performing UV irradiation, wherein an increase in melt viscosity before and after UV irradiation can be adjusted to 30% or less, whereby a bonding can be performed without voids during thermo-compression bonding, and resin-insertion phenomenon between solders can be prevented, fillets can be minimized and reliability can be improved.

The present disclosure relates to a method for manufacturing a semiconductor package including vacuum-laminating a non-conductive film on a substrate on which a plurality of through silicon vias are provided and bump electrodes are formed, and then performing UV irradiation, wherein an increase in melt viscosity before and after UV irradiation can be adjusted to 30% or less, whereby a bonding can be performed without voids during thermo-compression bonding, and resin-insertion phenomenon between solders can be prevented, fillets can be minimized and reliability can be improved.

A printed structure includes a destination substrate comprising two or more contact pads disposed on or in a surface of the destination substrate, a component disposed on the surface, and two or more electrically conductive connection posts. Each of the connection posts extends from a common side of the component. Each of the connection posts is in electrical and physical contact with one of the contact pads. The component is tilted with respect to the surface of the destination substrate. Each of the connection posts has a flat distal surface.

A printed structure includes a destination substrate comprising two or more contact pads disposed on or in a surface of the destination substrate, a component disposed on the surface, and two or more electrically conductive connection posts. Each of the connection posts extends from a common side of the component. Each of the connection posts is in electrical and physical contact with one of the contact pads. The component is tilted with respect to the surface of the destination substrate. Each of the connection posts has a flat distal surface.

A semiconductor device and method is disclosed. Devices shown include a die coupled to an integrated routing layer, wherein the integrated routing layer includes a first width that is wider than the die. Devices shown further included a molded routing layer coupled to the integrated routing layer.

A semiconductor device and method is disclosed. Devices shown include a die coupled to an integrated routing layer, wherein the integrated routing layer includes a first width that is wider than the die. Devices shown further included a molded routing layer coupled to the integrated routing layer.

A method includes forming a solder layer on a surface of one or more chips. A lid is positioned over the solder layer on each of the one or more chips. Heat and pressure are applied to melt the solder layer and attach each lid to a corresponding solder layer. The solder layer has a thermal conductivity of ≥50 W/mK.

A method includes forming a solder layer on a surface of one or more chips. A lid is positioned over the solder layer on each of the one or more chips. Heat and pressure are applied to melt the solder layer and attach each lid to a corresponding solder layer. The solder layer has a thermal conductivity of ≥50 W/mK.

A dicing die attach film including a dicing film and a die attach film laminated on the dicing film, in which the die attach film has an arithmetic average roughness Ra1 of from 0.05 to 2.50 μm at a surface in contact with the dicing film, and a value of ratio of Ra1 to an arithmetic average roughness Ra2 at a surface that is of the die attach film and is opposite to the surface in contact with the dicing film is from 1.05 to 28.00.

A dicing die attach film including a dicing film and a die attach film laminated on the dicing film, in which the die attach film has an arithmetic average roughness Ra1 of from 0.05 to 2.50 μm at a surface in contact with the dicing film, and a value of ratio of Ra1 to an arithmetic average roughness Ra2 at a surface that is of the die attach film and is opposite to the surface in contact with the dicing film is from 1.05 to 28.00.