The present disclosure relates to a semiconductor device and a manufacturing method thereof, and more particularly to an interlayer dielectric (ILD) layer in a semiconductor device. In one example, the ILD layer is over a substrate and includes a dielectric with a dielectric constant of less than about 3.3 and a hardness of at least about 3 GPa. The semiconductor device also includes an interconnect formed in the ILD layer.

The present disclosure describes a method for forming a nitrogen-rich protective layer within a low-k layer of a metallization layer to prevent damage to the low-k layer from subsequent processing operations. The method includes forming, on a substrate, a metallization layer having conductive structures in a low-k dielectric. The method further includes forming a capping layer on the conductive structures, where forming the capping layer includes exposing the metallization layer to a first plasma process to form a nitrogen-rich protective layer below a top surface of the low-k dielectric, releasing a precursor on the metallization layer to cover top surfaces of the conductive structures with precursor molecules, and treating the precursor molecules with a second plasma process to dissociate the precursor molecules and form the capping layer. Additionally, the method includes forming an etch stop layer to cover the capping layer and top surfaces of the low-k dielectric.

A method for manufacturing a semiconductor device is provided. The method includes a step of performing a chemical mechanical polishing process on a first silicon oxide layer to form a planar surface layer; surface treatment is performed on the planar surface layer to form a treated planarization layer, and a second silicon oxide layer is formed on the treated planarization layer.

The present disclosure describes an interconnect structure and a method forming the same. The interconnect structure can include a substrate, a layer of conductive material over the substrate, a metallic capping layer over the layer of conductive material, a layer of insulating material over top and side surfaces of the metallic capping layer, and a layer of trench conductor formed in the layer of insulating material and the metallic capping layer.

Films are modified to include deuterium in an inductive high density plasma chamber. Chamber hardware designs enable tunability of the deuterium concentration uniformity in the film across a substrate. Manufacturing of solid state electronic devices include integrated process flows to modify a film that is substantially free of hydrogen and deuterium to include deuterium.

An integrated circuit includes a substrate, an isolation feature disposed over the substrate, a fin extending from the substrate alongside the isolation feature such that the fin extends above the isolation feature, and a dielectric layer disposed over the isolation feature. A top surface of the dielectric layer is at a same level as a top surface of the fin or below a top surface of the fin by less than or equal to 15 nanometers.

A semiconductor device manufacturing method of forming a trench and a via in a porous low dielectric constant film formed on a substrate as an interlayer insulating film, includes: embedding a polymer having a urea bond in pores of the porous low dielectric constant film by supplying a raw material for polymerization to the porous low dielectric constant film; forming the via by etching the porous low dielectric constant film; subsequently, embedding a protective filling material made of an organic substance in the via; subsequently, forming the trench by etching the porous low dielectric constant film; subsequently, removing the protective filling material; and after the forming a trench, removing the polymer from the pores of the porous low dielectric constant film by heating the substrate to depolymerize the polymer, wherein the embedding a polymer having a urea bond in pores is performed before the forming a trench.

Integrated circuit structures including an interconnect feature without a higher-resistance liner material. In absence of a liner, metal of low resistance directly contacts an adjacent dielectric material, enabling lower resistance interconnect. Even for low-k dielectric compositions, adhesion of the metal to the dielectric material is improved through the incorporation of nitrogen proximal to the interface. Prior to deposition of the metal upon a surface of the dielectric, the surface is exposed to nitrogen species to form a nitrogen-rich compound at the surface. The metal deposited upon the surface may then be nitrogen-lean, for example a substantially pure elemental metal or metal alloy.

Semiconductor devices and methods of manufacturing are provided. In some embodiments the method includes depositing an etch stop layer over a first hard mask material, the first hard mask material over a gate stack, depositing an interlayer dielectric over the etch stop layer, forming a first opening through the interlayer dielectric, the etch stop layer, and the first hard mask material, the first opening exposing a conductive portion of the gate stack, and treating sidewalls of the first opening with a first dopant to form a first treated region within the interlayer dielectric, a second treated region within the etch stop layer, a third treated region within the first hard mask material, and a fourth treated region within the conductive portion, wherein after the treating the fourth treated region has a higher concentration of the first dopant than the first treated region.

Methods open etch stop layers in an integrated environment along with metallization processes. In some embodiments, a method for opening an etch stop layer (ESL) prior to metallization may include etching the ESL with an anisotropic process using direct plasma to form helium ions that are configured to roughen the ESL for a first duration of approximately 10 seconds to approximately 30 seconds, forming aluminum fluoride on the ESL using remote plasma and nitrogen trifluoride gas for a second duration of approximately 10 seconds to approximately 30 seconds, and exposing the ESL to a gas mixture of boron trichloride, trimethylaluminum, and/or dimethylaluminum chloride at a temperature of approximately 100 degrees Celsius to approximately 350 degrees Celsius to remove aluminum fluoride from the ESL and a portion of a material of the ESL for a third duration of approximately 30 seconds to approximately 60 seconds.