A method of performing heteroepitaxy comprises exposing a substrate to a carrier gas, a first precursor gas, a Group II/III element, and a second precursor gas, to form a heteroepitaxial growth of one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN on the substrate; wherein the substrate comprises one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN; wherein the carrier gas is Hz, wherein the first precursor is HCl, the Group II/III element comprises at least one of Zn, Cd, Hg, Al, Ga, and In; and wherein the second precursor is one of AsH.sub.3 (arsine), PH.sub.3 (phosphine), H.sub.2Se (hydrogen selenide), H.sub.2Te (hydrogen telluride), SbH.sub.3 (hydrogen antimonide), H.sub.2S (hydrogen sulfide), and NH.sub.3 (ammonia). The process may be an HVPE (hydride vapor phase epitaxy) process.

A method of performing heteroepitaxy comprises exposing a substrate to a carrier gas, a first precursor gas, a Group II/III element, and a second precursor gas, to form a heteroepitaxial growth of one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN on the substrate; wherein the substrate comprises one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN; wherein the carrier gas is Hz, wherein the first precursor is HCl, the Group II/III element comprises at least one of Zn, Cd, Hg, Al, Ga, and In; and wherein the second precursor is one of AsH.sub.3 (arsine), PH.sub.3 (phosphine), H.sub.2Se (hydrogen selenide), HzTe (hydrogen telluride), SbH.sub.3 (hydrogen antimonide), H.sub.2S (hydrogen sulfide), and NH.sub.3 (ammonia). The process may be an HVPE (hydride vapor phase epitaxy) process.

A method of performing heteroepitaxy comprises exposing a substrate to a carrier gas, a first precursor gas, a Group II/III element, and a second precursor gas, to form a heteroepitaxial growth of one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN on the substrate; wherein the substrate comprises one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN; wherein the carrier gas is H.sub.2, wherein the first precursor is HCl, the Group II/III element comprises at least one of Zn, Cd, Hg, Al, Ga, and In; and wherein the second precursor is one of AsH.sub.3 (arsine), PH.sub.3 (phosphine), H.sub.2Se (hydrogen selenide), H.sub.2Te (hydrogen telluride), SbH.sub.3 (hydrogen antimonide), H.sub.2S (hydrogen sulfide), and NH.sub.3 (ammonia). The process may be an HVPE (hydride vapor phase epitaxy) process.

A method of performing heteroepitaxy comprises exposing a substrate to a carrier gas, a first precursor gas, a Group II/III element, and a second precursor gas, to form a heteroepitaxial growth of one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN on the substrate; wherein the substrate comprises one of GaAs, AlAs, InAs, GaP, InP, ZnSe, GaSe, CdSe, InSe, ZnTe, CdTe, GaTe, HgTe, GaSb, InSb, AlSb, CdS, GaN, and AlN; wherein the carrier gas is Hz, wherein the first precursor is HCl, the Group II/III element comprises at least one of Zn, Cd, Hg, Al, Ga, and In; and wherein the second precursor is one of AsH.sub.3 (arsine), PH.sub.3 (phosphine), H.sub.2Se (hydrogen selenide), H.sub.2Te (hydrogen telluride), SbH.sub.3 (hydrogen antimonide), H.sub.2S (hydrogen sulfide), and NH.sub.3 (ammonia). The process may be an HVPE (hydride vapor phase epitaxy) process.

Methods and structures includes providing a substrate, forming a prelayer over a substrate, forming a barrier layer over the prelayer, and forming a channel layer over the barrier layer. Forming the prelayer may include growing the prelayer at a graded temperature. Forming the barrier layer is such that the barrier layer may include GaAs or InGaAs. Forming the channel layer is such that the channel layer may include InAs or an Sb-based heterostructure. Thereby structures are formed.

Aspects of the disclosure relate to processes for epitaxial growth of Group III/V materials at high rates, such as about 30 μm/hr or greater, for example, about 40 μm/hr, about 50 μm/hr, about 55 μm/hr, about 60 μm/hr, about 70 μm/hr, about 80 μm/hr, and about 90-120 μm/hr deposition rates. The Group III/V materials or films may be utilized in solar, semiconductor, or other electronic device applications. The Group III/V materials may be formed or grown on a sacrificial layer disposed on or over the support substrate during a vapor deposition process. Subsequently, the Group III/V materials may be removed from the support substrate during an epitaxial lift off (ELO) process. The Group III/V materials are thin films of epitaxially grown layers containing gallium arsenide, gallium aluminum arsenide, gallium indium arsenide, gallium indium arsenide nitride, gallium aluminum indium phosphide, phosphides thereof, nitrides thereof, derivatives thereof, alloys thereof, or combinations thereof.

A semiconductor laminated structure includes a first buffer layer formed on a substrate, an insulating layer formed on the first buffer layer, a second buffer layer, an oxide layer formed on the second buffer layer, and a semiconductor layer formed on the oxide layer. The second buffer layer is formed by being regrown through an opening portion from a surface of the substrate which is exposed through the opening portion. A total thickness of the second buffer layer and the oxide layer is larger than a value obtained by multiplying a width of the opening portion by the square root of two (√{square root over (2)}).

A multijunction solar cell including a metamorphic layer, and particularly the design and specification of the composition, lattice constant, and band gaps of various layers above the metamorphic layer in order to achieve reduction in “bowing” of the semiconductor wafer caused by the lattice mismatch of layers associated with the metamorphic layer.

A nanowire structure includes a substrate, a patterned mask layer on the substrate, and a nanowire. The patterned mask layer is on the substrate and includes an opening through which the substrate is exposed. The nanowire is on the substrate in the opening of the patterned mask layer. The nanowire includes a buffer layer on the substrate, a defect filtering layer on the buffer layer, and an active layer on the defect filtering layer. The defect filtering layer is a strained layer. By providing the defect filtering layer between the buffer layer and the active layer of the nanowire, defects present in the buffer layer can be prevented from propagating into the active layer. Accordingly, defects in the active layer of the nanowire are reduced, thereby improving the performance of the nanowire structure.

A nanoscale thin film structure and implementing method thereof, and, more specifically, a nanoscale thin film structure of which target structure is designed with quantized thickness, and a method to implement the nanoscale thin film structure by which the performance of the manufactured nanodevice can be implemented the same as the designed performance, thereby applicable to high sensitivity high performance electronic/optical sensor devices.