A coated substrate has a substrate and a coating system having one or more ceramic layers. At least a first layer of one of the one or more ceramic layers is a columnar layer having as-deposited columns and intercolumn gaps. The intercolumn gaps have a mean width at least one of: at least 4.0 micrometers; and at least 1.5% of a thickness of said first layer.

Provided is a galvanized steel sheet having excellent plating adhesion, having a plated layer with improved friction characteristics by means of a predetermined level of Fe elution, and having excellent corrosion resistance; and a manufacturing method therefor.

Provided is a multilayer zinc alloy plated steel material comprising a base steel material and multiple plating layers formed on the base steel material, wherein each of the multiple plating layers includes one of a Zn plating layer, a Mg plating layer, and a Zn—Mg alloy plating layer, and the ratio of the weight of Mg contained in the multiple plating layers to the total weight of the multiple plating layers is from 0.13 to 0.24.

The present disclosure relates to a plated steel material that can be used in an automobile, a household appliance, a building material, and the like, and more particularly, to a zinc alloy plated steel material having excellent surface quality and corrosion resistance, and a method for manufacturing the same.

An embodiment relates to an ultrasonic additive manufacturing process, comprising joining a foil comprising a bulk metallic glass to a substrate; and forming a cladded composite comprising the foil and the substrate; wherein a thickness of the cladded composite is greater than a critical casting thickness of the bulk metallic glass, wherein the cladded composite comprises a cladding layer of the bulk metallic glass on the substrate and the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.

A high-strength thick-walled electric resistance welded steel pipe has excellent low-temperature toughness and excellent HIC resistance and a yield strength of 400 MPa or more. The steel has a chemical composition consisting of C: 0.025% to 0.084%, Si: 0.10% to 0.30%, Mn: 0.70% to 1.80%, controlled amounts of P, S, Al, N, and O, Nb: 0.001% to 0.065%, V: 0.001% to 0.065%, Ti: 0.001% to 0.033%, and Ca: 0.0001% to 0.0035% on a mass percent basis and the remainder being Fe and incidental impurities, and satisfies Pcm of 0.20 or less.

A coating system for a surface of a superalloy component is provided. The coating system includes a MCrAlY coating on the surface of the superalloy component, where M is Ni, Fe, Co, or a combination thereof. The MCrAlY coating generally has a higher chromium content than the superalloy component. The MCrAlY coating also includes a platinum-group metal aluminide diffusion layer. The MCrAlY coating includes Re, Ta, or a mixture thereof. Methods are also provided for forming a coating system on a surface of a superalloy component.

One aspect of the disclosure provides an iron-based hardfacing layer which includes hard or wear resistant phases resulting at least in part from dissolution of silicon and/or boron carbide particles into a liquid iron-based metal during the fabrication process. In an embodiment, the hardfacing layer is formed by a fusion welding process in which carbide particles are added to the molten weld pool. In an example, the filler metal supplied to the welding process is a mild steel. In an embodiment, the hardness as measured at the surface of the hardfacing ranges from 40 to 65 HRC. In an example, the iron-based hardfacing layer also includes tungsten carbide particles.

An example hydraulic system component of a machine includes a protective coating deposited by high velocity air fuel (HVAF) thermal spray, exhibiting high adhesion strengths and surface morphologies that promote lubricant adhesion and reduce the leakage of oil and/or hydraulic fluid from the hydraulic system. The coating may have surface roughness with Rz values less than 2 μm and hardness of 1000 Vickers or greater. The HVAF coating may be thinner than conventional coatings with thicknesses less than 100 μm. The HVAF coating may be deposited on a variety of steel components with adhesion strengths greater than those achieved by high velocity oxygen fuel (HVOF). The HVAF coating may be formed without time consuming roughening and/or post-grind operations, resulting in cost savings compared to conventional coatings. The coatings may have operational lifetimes of 1000 hours or more.

A process for producing a thermal barrier coating having an excellent thermal barrier effect and superior durability to thermal cycling. Also, a turbine member having a thermal barrier coating that has been formed using the production process, and a gas turbine. The process for producing a thermal barrier coating includes: forming a metal bonding layer (12) on a heat-resistant alloy substrate (11), and forming a ceramic layer (13) on the metal bonding layer (12) by thermal spraying of thermal spray particles having a particle size distribution in which the 10% cumulative particle size is not less than 30 μm and not more than 100 μm.