High strength steel sheet having a tensile strength of 800 MPa or more comprising a middle part in sheet thickness and a soft surface layer arranged at one side or both sides of the middle part in sheet thickness, wherein each soft surface layer has a thickness of more than 10 μm and 30% or less of the sheet thickness, the soft surface layer has an average Vickers hardness of 0.60 time or less the average Vickers hardness of the sheet thickness ½ position, and the soft surface layer has a nano-hardness standard deviation of 0.8 or less is provided.

A hot-dip galvanized steel sheet wherein the hot-dip galvanized steel sheet comprises a base steel sheet and a hot-dip galvanized layer, a ferrite phase is, by volume fraction, 50% or less in a range of ⅛ thickness to ⅜ thickness centered at a position of ¼ thickness from the surface of the base steel sheet, a hard structure is 50% or more, wherein the hot-dip galvanized steel sheet has the hot-dip galvanized layer in which Fe is 5.0% or less and Al is 1.0% or less, and columnar grains formed of a ζ phase is 20% or more in an entire interface between the plated layer and the base steel sheet, on the surface of the base steel sheet in which a volume fraction of a residual austenite is 3% or less and a ratio of a volume fraction of the hard structure is 0.10 times or more to 0.90 times or less of that of the hard structure in the range of ⅛ thickness to ⅜ thickness in a range of 20 μm depth in a steel sheet direction originating an interface between the hot-dip galvanized layer and the base steel sheet, and wherein the hot-dip galvanized steel sheet has a refined layer at the side of the interface in the base steel sheet, and wherein an average thickness of the refined layer, an average grain size of ferrite in the refined layer and a maximum size of the oxide included in the refined layer are defined respectively.

The present invention relates to a steel sheet for a hot press formed member having excellent coating adhesion, and a method for manufacturing the same. A steel sheet for hot press forming according to one aspect of the present invention is an aluminum alloy plated steel sheet, wherein an average Fe content in a plating layer may be 40 wt % or more, and a concentration gradient of a section having a Fe content of 45 wt % to 80 wt % in the plating layer may 7 wt %/μm or less of a concentration gradient at a section having an Fe content of 45% to 80% in the plating layer in a thickness direction from a surface of the plating layer according to a result of GDS analysis.

Provided is a zinc-based plated steel sheet having a post-treated coating filmed thereon including: a steel sheet; a zinc plated layer formed on the steel sheet; and a post-treated coating formed on the plated layer, wherein the atomic ratio (O/M) of oxygen (O) to metals (M) contained in the post-treated coating is greater than 2 and less than 20, and a method for post-treating a zinc-based plated steel sheet. According to this, the zinc-based plated steel sheet having the post-treated coating formed thereon has the effects excellent in lubricity, weldability, adhesiveness, film-removing property and paintability. As the method of post-treating a zinc-based plated steel sheet of the present invention employs a simple coating method irrespective of the kind of plating layer, the process is simple and economical and the process operation cost is low.

A process of fabricating a shield, a process of preparing a component, and an erosion shield are disclosed. The process of fabricating the shield includes forming a near-net shape shield. The near-net shape shield includes a nickel-based layer and an erosion-resistant alloy layer. The nickel-based layer is configured to facilitate secure attachment of the near-net shaped to a component. The process of preparing the component includes securing a near-net shape shield to a substrate of a component.

Mixed powder that contains first hard particles, second hard particles, graphite particles, and iron particles is used to manufacture a sintered alloy. The first hard particle is a Fe—Mo—Cr—Mn based alloy particle, the second hard particle is a Fe—Mo—Si based alloy particle. The mixed powder contains 5 to 50 mass % of the first hard particles, 1 to 8 mass % of the second hard particles, and 0.5 to 1.0 mass % of the graphite particles when total mass of the first hard particles, the second hard particles, the graphite particles, and the iron particles is set as 100 mass %.

A galvannealed steel sheet includes: a steel sheet; a coating layer on a surface of the steel sheet; and a mixed layer formed between the steel sheet and the coating layer, in which the mixed layer includes a base iron portion having fine grains having a size of greater than 0 μm and equal to or smaller than 2 μm, a Zn—Fe alloy phase, and oxides containing one or more types of Mn, Si, Al, and Cr, and in the mixed layer, the oxides and the Zn—Fe alloy phase are present in grain boundaries that form the fine grains and the Zn—Fe alloy phase is tangled with the base iron portion.
[Mn]+[Si]+[Al]+[Cr]≧0.4  (Expression 1)

The present invention relates generally to a coated jewelry article or a coated component of a jewelry article, comprising a jewelry article or a component of a jewelry article, a first metallic coating, and a second metallic coating.

The present invention relates to aluminum plated steel sheet which does not require coating after plating and is high in production flexibility enabling application of conventional production processes as they are or exhibits excellent corrosion resistance to flex fuels and further is excellent in appearance and to fuel tanks characterized by being produced using the steel sheet. The Si, Mg, Ca, and Ti ingredients in the aluminum plating layer are defined and the cooling method after hot dip aluminum coating is controlled to make Mg.sub.2Si particles with a long axis of 10 μm or less and an aspect ratio of 1 to 3 finely disperse in the plating layer. Due to the Mg.sub.2Si particles, it is possible to give an excellent corrosion resistance to flex fuels and suppress the deterioration in appearance due to MgO.

A method for producing a flat steel product with high reflectivity, in which at least one surface has an arithmetic mean roughness Ra of less than 0.03 μm includes providing a flat steel product, at least one surface of which has an arithmetic mean roughness Ra of less than 2.5 μm. The flat steel product is cold rolled in a plurality of rolling passes. Also a flat steel product with high reflectivity in the finished re-rolled state on at least one of its surface has a low arithmetic mean roughness, a high gloss, and a high directed reflection. A solar concentrator is produced from such a flat steel product.