A coating material of the present invention is a coating material containing: a fluorine-containing polymer having at least one of an iodine atom and a bromine atom; and a solvent, wherein a storage elastic modulus G′ of the fluorine-containing polymer is less than 360 kPa, and a total light transmittance of a mixed liquid obtained by mixing and stirring the fluorine-containing polymer and the solvent contained in the coating material is 1.0% or more, the mixed liquid being left to stand for 3 days, stirred again, and left to stand for 30 minutes to measure the total light transmittance.

Provided is a water repellent coating film, including: an undercoat layer formed on a surface of a base material and containing: at least one type of spherical particles having an average particle diameter of 2 μm or more and 50 μm or less and selected from the group consisting of spherical molten silica particles, spherical molten alumina particles, and spherical silicone resin particles; and an underlying resin; and a topcoat layer formed on the undercoat layer and containing: inorganic fine particles having an average particle diameter of 2 nm or more and 20 nm or less; and a water repellent resin. The underlying resin is preferably a polyurethane resin or a fluororesin. The water repellent resin is preferably a fluororesin or a silicone resin.

This application relates to omniphobic materials which are physically and chemically modified at their surface to create hierarchically structured materials with both nanoscale and microscale structures that provide the omniphobic properties. Methods of making such omniphobic surfaces with hierarchical structures and uses thereof, including as flexible films that repel contaminants are also disclosed in the application.

Provided is a method of producing a fluorosilicone rubber laminate. The method comprises: (1) applying a primer composition onto a substrate, and forming a primer layer on a surface of the substrate; and (2) bringing a fluorosilicone rubber composition into contact with the primer layer, and adhering a fluorosilicone rubber to the primer layer. The fluorosilicone rubber composition comprises a platinum-based catalyst and/or a fluorosiloxane containing a silicon atom-bonded hydrogen atom. The primer composition comprises a platinum-based catalyst or a fluorosiloxane containing a silicon atom-bonded hydrogen atom, however the primer composition does not simultaneously comprise a platinum-based catalyst and a fluorosiloxane containing a silicon atom-bonded hydrogen atom. Either the primer composition or the fluorosilicone rubber composition comprises a platinum-based catalyst or a fluorosiloxane containing a silicon atom-bonded hydrogen atom. A laminate in which a fluorosilicone rubber layer and a base material are favorably adhered to each other can be obtained.

Provided is a method of producing a fluorosilicone rubber laminate. The method comprises: (1) applying a primer composition onto a substrate, and forming a primer layer on a surface of the substrate; and (2) bringing a fluorosilicone rubber composition into contact with the primer layer, and adhering a fluorosilicone rubber to the primer layer. The fluorosilicone rubber composition comprises a platinum-based catalyst and/or a fluorosiloxane containing a silicon atom-bonded hydrogen atom. The primer composition comprises a platinum-based catalyst or a fluorosiloxane containing a silicon atom-bonded hydrogen atom, however the primer composition does not simultaneously comprise a platinum-based catalyst and a fluorosiloxane containing a silicon atom-bonded hydrogen atom. Either the primer composition or the fluorosilicone rubber composition comprises a platinum-based catalyst or a fluorosiloxane containing a silicon atom-bonded hydrogen atom. A laminate in which a fluorosilicone rubber layer and a base material are favorably adhered to each other can be obtained.

The patent application discloses a degradable composite with coatings. The light metal workpiece with enhanced surface protection may comprise a light metal matrix having an exposed surface; a light metal oxide ceramic layer formed in at least a portion of the exposed surface; and a non-transparent metal alloy layer directly on the light metal oxide ceramic layer.

A method of coating a structure is disclosed. Method steps include providing a structure having a first portion of a first material having a first surface and providing a second portion of a second material having a second surface, wherein a mask is provided over the first surface. Another step includes exposing the mask and the second surface to a solution comprising a polymer and a solvent, wherein the solution dewets from the mask and the polymer collects onto the second surface to form a polymer coating over the second surface without forming a polymer coating on the first surface.

Provided is an antireflective member that has a water- and oil-repellent layer on a multi-layered antireflective layer and is capable of exhibiting excellent surface lubricity, water- and oil-repellent properties, and durability. The surface of the multi-layered antireflective layer on a base material has a root-mean-square surface roughness of 0.8 nm to 2.0 nm. The water- and oil-repellent layer has a thickness of 1 to 30 nm and is a cured product of water- and oil-repellents having as principal components a fluorooxyalkylene group-containing polymer modified organosilicon compound with the numerical average molecular weight of 4,500 to 10,000 of a fluoropolymer part and/or partial hydrolysis condensate thereof.

Systems having one or more features that are advantageous for depositing fluorinated polymeric coatings on substrates, and methods of employing such systems to deposit such coatings, are generally provided.

Provided is a low dielectric constant film and a preparation method thereof, where epoxy alkanes, organosilicon compounds and fluorine-containing siloxane compounds are used as raw materials of the low dielectric constant film, and the low dielectric constant film is formed on a substrate surface by a plasma-enhanced chemical deposition method. Accordingly, a nanofilm with a low dielectric constant and excellent hydrophobicity is formed on the substrate surface.