To provide a powder coating material composition capable of forming a fluororesin layer excellent in adhesion to a base material and having foaming or cracking suppressed even when the firing temperature is as high as at least 380° C.

A powder coating material composition comprising a resin powder with an average particle size of from 10 to 800 μm containing polymer A and heat stabilizer B, wherein the proportion of the heat stabilizer B to 100 parts by mass of the polymer A is from 0.01 to 30 parts by mass. Polymer A: A tetrafluoroethylene/perfluoro (alkyl vinyl ether) copolymer having at least one type of functional group selected from the group consisting of a carbonyl group-containing group, etc., or a tetrafluoroethylene/hexafluoropropylene copolymer, having the functional group, and having a melting point of from 260 to 320° C. Heat stabilizer B: A heat stabilizer selected from the group consisting of an aromatic polyether compound, an aromatic amine compound, an aromatic sulfur compound and a polysilane compound.

The present application discloses a thermal insulation coating and a method for applying the same. Raw materials for preparing the thermal insulation coating includes PVDF resin, water-based epoxy resin solution, hollow glass microbead, ytterbium modified nano-powder, diluent, polyvinyl alcohol, titanium dioxide powder, rare earth, negative ion powder, and leveling agent.

The present application discloses a thermal insulation coating and a method for applying the same. Raw materials for preparing the thermal insulation coating includes PVDF resin, water-based epoxy resin solution, hollow glass microbead, ytterbium modified nano-powder, diluent, polyvinyl alcohol, titanium dioxide powder, rare earth, negative ion powder, and leveling agent.

The purpose of the present invention is the use of (Bi.sub.1-xA.sub.x)(V.sub.1-yM.sub.y)0.sub.4 in a non-stick coating for a household article so as to reduce or prevent the color change of said coating during the manufacturing process thereof, characterised in that: —x is equal to 0 or x is from 0.001 to 0.999; —y is equal to 0 or y is from 0.001 to 0.999; —A and Mare selected from the group consisting of nitrogen, phosphorus, an alkali metal, an alkaline earth metal, a transition metal, a poor metal, a metalloid or a lanthanide; —A and M are different from each other.

A unique fiber core sampler composition, related systems, and techniques for designing, making, and using the same are described. The sampler is used to interface with existing field instrumentation, such as Ion Mobility Spectrometer (IMS) equipment. Desired sampler characteristics include its: stiffness/flexibility; thermal mass and conductivity; specific heat; trace substance collection/release dependability, sensitivity and repeatability; thickness; reusability; durability; stability for thermal cleaning; and the like. In one form the sampler has a glass fiber core with a thickness less than 0.3 millimeter that is coated with a polymer including one or more of: polymeric organofluorine, polyimide, polyamide, PolyBenzImidazole (PBI), PolyDiMethylSiloxane (PDMS), sulfonated tetrafluoroethylene (PFSA) and Poly(2,6-diphenyl-p-phenylene Oxide) (PPPO). Multiple polymer coatings with the same or different polymer types may be included, core/substrate surface functionalization utilized, and/or the core/substrate may be at partially filled with thermally conductive particles.

A method is provided that forms a solid film on a bearing component of a rolling bearing. A solution containing a fluorine compound and a lubricant having no functional group is allowed to adhere to the bearing component as a liquid film, the fluorine compound containing 3-(trimethoxysilyl) propyl methacrylate, hexafluoropropene, and methyl methacrylate as components. The solid film is formed on the at least one of the bearing components by hardening the adhering liquid film.

A method of forming a surface texture includes arranging a flexible mask (610, 920) with a pattern over a surface (621) of a component (620); and performing electrochemical etching on the surface (621) of the component (620) to form a surface texture on the surface (621) according to the pattern of the flexible mask.

A method of forming a dirt repellant panel coated with a powder coating composition that includes a polymeric binder and an anionic fluorosurfactant present in an amount ranging from about 0.1 wt. % to about 4 wt. %.

A composition that is easily applied, clear, well-bonded, and superhydrophobic is disclosed. In one aspect, the composition includes a hydrophobic fluorinated solvent, a binder comprising a hydrophobic fluorinated polymer, and hydrophobic fumed silica nanoparticles. Also disclosed is a structure including a substrate coated with the composition, as well as a method for making the composition and a method of coating a substrate with the composition.

Coating compositions are provided that eject droplets of condensed fluid from a surface. The coatings include a nanostructured coating layer and in some embodiments, also include a hydrophobic layer deposited thereon. The coating materials eject droplets from the surface in the presence of non-condensing gases such as air and may be deployed under conditions of supersaturation of the condensed fluid to be ejected. A heat exchanger design utilizing the coating is described herein.