A sand additive for use in a “no bake” foundry mix composition having a polyurethane-based binder system reduces the amount of smoke emitted when molds and cores formed from the composition are exposed to molten metal, as compared to when the sand additive is not used. The sand additive comprises yellow iron oxide having the chemical formula Fe(OH).sub.3. It can also comprise at least one of red iron oxide, black iron oxide and wüstite. In such cases, the yellow iron oxide accounts for about 10 to about 40 weight percent of the combined weight of the yellow iron oxide, red iron oxide, black iron oxide and wüstite, and preferably, about 20 to about 30 weight percent of the combined weight of the yellow iron oxide, red iron oxide, black iron oxide and wüstite.

A sand additive for use in a “no bake” foundry mix composition having a polyurethane-based binder system reduces the amount of smoke emitted when molds and cores formed from the composition are exposed to molten metal, as compared to when the sand additive is not used. The sand additive comprises yellow iron oxide having the chemical formula Fe(OH).sub.3. It can also comprise at least one of red iron oxide, black iron oxide and wüstite. In such cases, the yellow iron oxide accounts for about 10 to about 40 weight percent of the combined weight of the yellow iron oxide, red iron oxide, black iron oxide and wüstite, and preferably, about 20 to about 30 weight percent of the combined weight of the yellow iron oxide, red iron oxide, black iron oxide and wüstite.

An amount of a halloysite clay, used as an additive in a foundry mix composition having a polyurethane-based binder system, reduces the amount of smoke emitted when molds and cores formed from the composition are exposed to molten metal, as compared to when the halloysite clay is not used.

An amount of a halloysite clay, used as an additive in a foundry mix composition having a polyurethane-based binder system, reduces the amount of smoke emitted when molds and cores formed from the composition are exposed to molten metal, as compared to when the halloysite clay is not used.

The present invention relates to the use of closed-pore microspheres of expanded perlite as a filler for producing moldings for the foundry industry, to a composition for producing moldings for the foundry industry, comprising closed-pore microspheres of expanded perlite as a filler, and a binder, the binder being selected from the group consisting of water glass, phenol-formaldehyde resins, two-component systems comprising as reactants a polyisocyanate and a polyol component containing free hydroxyl groups (OH groups), and starch, and also to moldings for the foundry industry and to a process for producing a molding for the foundry industry.

The present invention relates to the use of closed-pore microspheres of expanded perlite as a filler for producing moldings for the foundry industry, to a composition for producing moldings for the foundry industry, comprising closed-pore microspheres of expanded perlite as a filler, and a binder, the binder being selected from the group consisting of water glass, phenol-formaldehyde resins, two-component systems comprising as reactants a polyisocyanate and a polyol component containing free hydroxyl groups (OH groups), and starch, and also to moldings for the foundry industry and to a process for producing a molding for the foundry industry.

Described is a method of preparing a particulate refractory composition for use in the manufacture of foundry moulds and cores from spent foundry moulds or cores formed of refractory material and a binder containing water glass, the method comprising the following steps: providing broken material from spent foundry moulds or cores or preparing broken material from spent foundry moulds or cores, wherein the broken material comprises particles and/or aggregates of particles of refractory material having hardened water glass binder on their surface, mixing the broken material with particulate amorphous oxide comprising silicon dioxide in an amount of 85% by weight or more, based on the total amount of the particulate amorphous oxide, to give a mixture and subjecting the mixture to a heat treatment at a temperature of 400° C. or higher. Also described are a corresponding use, a reclamation mixture, and a method of making a foundry mould or core.

Described is a method of preparing a particulate refractory composition for use in the manufacture of foundry moulds and cores from spent foundry moulds or cores formed of refractory material and a binder containing water glass, the method comprising the following steps: providing broken material from spent foundry moulds or cores or preparing broken material from spent foundry moulds or cores, wherein the broken material comprises particles and/or aggregates of particles of refractory material having hardened water glass binder on their surface, mixing the broken material with particulate amorphous oxide comprising silicon dioxide in an amount of 85% by weight or more, based on the total amount of the particulate amorphous oxide, to give a mixture and subjecting the mixture to a heat treatment at a temperature of 400° C. or higher. Also described are a corresponding use, a reclamation mixture, and a method of making a foundry mould or core.

“Lost” cores for use high pressure die casting, the cores preferably having a water-soluble synthetic ceramic aggregate having an appropriate strength and tolerance for various casting pressures and temperatures, an inorganic binder having sodium silicate, an additive having particulate amorphous silicon dioxide, and a refractory coating, wherein the cores have the capacity to be removed from a casting by dissolution with water.

“Lost” cores for use high pressure die casting, the cores preferably having a water-soluble synthetic ceramic aggregate having an appropriate strength and tolerance for various casting pressures and temperatures, an inorganic binder having sodium silicate, an additive having particulate amorphous silicon dioxide, and a refractory coating, wherein the cores have the capacity to be removed from a casting by dissolution with water.