A process of modifying a passage in a component is provided. The process includes inserting a first material into the passage; blocking at least one end of the passage; inserting an elongated member into the passage through the first material; heat treating the passage, the first material, and the elongated member to form a solid interior in component; and machining through the solid interior to form a modified passage in the component.

A process for room temperature substrate bonding employs a first substrate substantially transparent to a laser wavelength is selected. A second substrate for mating at an interface with the first substrate is then selected. A transmissivity change at the interface is created and the first and second substrates are mated at the interface. The first substrate is then irradiated with a laser of the transparency wavelength substantially focused at the interface and a localized high temperature at the interface from energy supplied by the laser is created. The first and second substrates immediately adjacent the interface are softened with diffusion across the interface to fuse the substrates.

The invention relates to a method for theiiiially stable joining of a glass element to a support element, wherein the glass element has a first coefficient of expansion and the support element has a second coefficient of expansion differing from the first coefficient of expansion. The method thus comprises a step of attaching an intermediate glass material to the support element, wherein the intermediate glass material has a third coefficient of expansion which substantially corresponds to the second coefficient of expansion. In addition, the method comprises a step of local heating of the intermediate glass material in order to join the glass element to the support element via the intermediate glass material.

The invention relates to a method for theiiiially stable joining of a glass element to a support element, wherein the glass element has a first coefficient of expansion and the support element has a second coefficient of expansion differing from the first coefficient of expansion. The method thus comprises a step of attaching an intermediate glass material to the support element, wherein the intermediate glass material has a third coefficient of expansion which substantially corresponds to the second coefficient of expansion. In addition, the method comprises a step of local heating of the intermediate glass material in order to join the glass element to the support element via the intermediate glass material.

A process for producing an amorphous ductile brazing foil is provided. According to one example embodiment, the method includes providing a molten mass, and rapidly solidifying the molten mass on a moving cooling surface with a cooling speed of more than approximately 10.sup.5° C./sec to produce an amorphous ductile brazing foil. A process for joining two or more parts is also provided. The process includes inserting a brazing foil between two or more parts to be joined, wherein the parts to be joined have a higher melting temperature than that the brazing foil to form a solder joint and the brazing foil comprises an amorphous, ductile Ni-based brazing foil; heating the solder joint to a temperature above the liquidus temperature of the brazing foil to form a heated solder joint; and cooling the heated solder joint, thereby forming a brazed joint between the parts to be joined.

A process for producing an amorphous ductile brazing foil is provided. According to one example embodiment, the method includes providing a molten mass, and rapidly solidifying the molten mass on a moving cooling surface with a cooling speed of more than approximately 10.sup.5° C./sec to produce an amorphous ductile brazing foil. A process for joining two or more parts is also provided. The process includes inserting a brazing foil between two or more parts to be joined, wherein the parts to be joined have a higher melting temperature than that the brazing foil to form a solder joint and the brazing foil comprises an amorphous, ductile Ni-based brazing foil; heating the solder joint to a temperature above the liquidus temperature of the brazing foil to form a heated solder joint; and cooling the heated solder joint, thereby forming a brazed joint between the parts to be joined.

The present invention relates to a process for the production of an aluminium multilayer brazing sheet which comprises a core layer made of a 3xxx alloy comprising 0.1 to 0.25 wt. % Mg, a brazing layer made of a 4xxx alloy on one or both sides of the core layer, and optionally an interlayer between the core layer and the brazing layer on one or both sides of the core layer, the process comprising the successive steps of: providing the layers to be assembled or simultaneous casting of the layers to obtain a sandwich; rolling of the resulting sandwich to obtain a sheet; and treating the surface of the sheet with an alkaline or acidic etchant.

A method of joining a semiconductor die to a substrate includes: applying a solder preform to a metal region of the semiconductor die or to a metal region of the substrate, the solder preform having a maximum thickness of 30 μm and a lower melting point than both metal regions; forming a soldered joint between the metal region of the semiconductor die and the metal region of the substrate via a diffusion soldering process and without applying pressure directly to the die; and setting a soldering temperature of the diffusion soldering process so that the solder preform melts and fully reacts with the metal region of the semiconductor die and the metal region of the substrate to form one or more intermetallic phases throughout the entire soldered joint, each intermetallic phase having a melting point above the melting point of the preform and the soldering temperature.

A wear-protected substrate includes a substrate and a continuous wear protection layer brazed to the substrate. The continuous wear protection layer includes components having interlocking features that are configured to interlock the components side-by-side to form the continuous wear protection layer.

A wear-protected substrate includes a substrate and a continuous wear protection layer brazed to the substrate. The continuous wear protection layer includes components having interlocking features that are configured to interlock the components side-by-side to form the continuous wear protection layer.