A method for producing a hierarchical mesoporous beta includes mixing a beta zeolite with an aqueous metal hydroxide solution and heating the beta zeolite and the aqueous metal hydroxide mixture to produce a desilicated beta zeolite, contacting the desilicated beta zeolite with an ammonium salt solution to produce an intermediate hierarchical mesoporous beta zeolite, and treating the intermediate hierarchical mesoporous beta zeolite with an acidic solution to produce the hierarchical mesoporous beta zeolite. The hierarchical mesoporous beta zeolite includes a molar ratio of silicon to aluminum of greater than 12.5, a total pore volume of greater than or equal to the total pore volume of the intermediate hierarchical mesoporous beta zeolite, and an average mesopore size of greater than or equal to the average mesopore size of the hierarchical mesoporous beta zeolite. The method may also include calcining the intermediate hierarchical mesoporous beta zeolite.

The present invention is directed to the synthesis of novel delaminated layered zeolite precursor materials prepared by fluoride/chloride anion-promoted exfoliation. The method comprises, for example, using a combination of fluoride and chloride anions at a mild pH in aqueous solution to affect delamination of a layered zeolite precursor. The method can also comprise using a combination of fluoride and chloride anions in a non-aqueous solution comprising an organic solvent. The method may be used in conjunction with either acidification or sonication, or both. The resulting delaminated zeolite precursors are then isolated. Precursors that are then isolated lack amorphous silica content. The UCB-1 product is an example of such a novel oxide material and is obtained in yields in excess of 90% without the need for sonication.

A method of making a zeolite with encapsulated platinum is provided. The method includes dissolving an aluminum source in water to form a first solution, dissolving a hydroxide in water to form a second solution, dissolving a templating agent in water to form a third solution, and adding a silica source to the first solution to form a fourth solution. The method further includes adding the second solution to the fourth solution to form a fifth solution, adding the third solution to the fifth solution to form a sixth solution, and adding a platinum source to the sixth solution. The sixth solution is crystallized to form a solid product, which is recovered. The solid product is calcined. An ammonium ion exchange is performed on the solid product to form a second solid product, and the second solid product is calcined.

A molecular sieve of MFI structure has a ratio of n(SiO2)/n(Al2O3) of more than 15 and less than 70. It has a content of phosphorus of 1-15 wt %, calculated as P.sub.2O.sub.5 and based on the dry weight of the molecular sieve and a content of the supported metal in the molecular sieve 1-10 wt % based on the oxide of the supported metal and the dry weight of the molecular sieve. The supported metal is one or two selected from lanthanum and cerium. The volume of mesopores in the molecular sieve represents 40-70% by volume of the total pore volume of the molecular sieve by volume, measured by a nitrogen adsorption BET specific surface area method, and the volume of mesopores means the pore volume of the pores having a diameter of more than 2 nm and less than 100 nm.

Embodiments of zeolite composite catalysts and methods of producing the zeolite composite catalysts are provided, where the methods comprise dissolving in an alkaline solution a catalyst precursor comprising at least one mesoporous zeolite while heating, stirring, or both to yield a dissolved zeolite solution, where the mesoporous zeolite has a molar ratio of SiO.sub.2/Al.sub.2O.sub.3 of at least 30, where the mesoporous zeolite comprises zeolite beta, adjusting the pH of the dissolved zeolite solution, aging the pH adjusted dissolved zeolite solution to yield solid zeolite composite from the dissolved zeolite solution, and calcining the solid zeolite composite to produce the zeolite composite catalyst, where the zeolite composite catalyst has a mesostructure comprising at least one disordered mesophase and at least one ordered mesophase, and where the zeolite composite catalyst has a surface area defined by the Brunauer-Emmett-Teller (BET) analysis of at least 600 m.sup.2/g.

Provided herein are methods for converting CBD to a product mixture comprising Δ.sup.8-THC, Δ.sup.9-THC, or a combination thereof. The methods provided herein may comprise one or more of (1) a contacting step wherein a starting material comprising CBD, a catalyst comprising a zeolite, and optionally a solvent are added to a reaction vessel, thereby forming a reaction mixture; (2) a conversion step wherein at least a portion of the CBD is converted to THC, thereby forming a product mixture; and (3) optionally, a separation step wherein at least a portion of the catalyst is removed from the product mixture. Advantageously, the methods do not require the use of catalysts or other reagents that are hazardous to human health.

The present invention relates to the use, in a method for in-situ activation of at least one hydrotreating, in particular hydrocracking, catalyst, of at least one nitrogen compound having at least one of the following characteristics: a) a nitrogen content by weight in the range from 15 to 35 wt %, relative to the total weight of the nitrogen compound; b) a number of nitrogen atoms in the range from 2 to 20; c) a boiling point in the range from 140° C. to 300° C.; and d) said nitrogen compound being in liquid form at room temperature and atmospheric pressure. The present invention also relates to the method for in-situ activation of at least one hydrotreating catalyst comprising at least one step of sulphiding said hydrotreating catalyst in the presence of a sulphiding agent, and a step of passivation of said hydrotreating catalyst in the presence of said at least one nitrogen compound.

The present disclosure provides mesoporous catalyst compounds and compositions having one or more group 13 atoms. The present disclosure further relates to processes for converting hydrocarbon feedstocks to small olefins. In one aspect, a catalyst compound includes a zeolite having a structural type selected from MFI, MSE, MTW, Theta-One (TON), Ferrierite (FER), AFI, AFS, ATO, BEA, BEC, BOG, BPH, CAN, CON, EMT, EON, EZT, FAU, GME, GON, IFR, ISV, ITN, IWR, IWW, LTL, MAZ, MEI, MOR, MOZ, OFF, OKO, OSI, SAF, SAO, SEW, SFE, SFO, SSF, SSY, and USI, or a combination thereof, the zeolite having a silicon to aluminum molar ratio (Si/Al ratio) of from about 5 to about 40. In one aspect, a catalyst composition includes the catalyst compound and one or more group 13 metal.

A method for preparing a zeolite catalyst for catalytic cracking of hydrocarbons to produce propylene is provided, which specifically includes steps of mixing a silicon source, a templating agent, an aluminium source, and a solvent to form a zeolite precursor solution, which is then subjected to hydrothermal crystallization, washing, drying, and calcination to obtain a zeolite precursor; ion-exchanging the zeolite precursor with ammonium ions, followed by drying and calcination; and loading aluminum onto the ion-exchanged zeolite precursor as a carrier via incipient-wetness impregnation by using an aluminium-containing solution, followed by drying and calcination. Zeolite catalysts prepared by the method and use of the catalysts in catalytic cracking of hydrocarbons to produce propylene are also provided.

Disclosed are a catalyst for preparing hydrocarbons from carbon dioxide by one-step hydrogenation and a method for preparing same. The catalyst includes nano-metal oxides and hierarchical zeolites, where the mass fraction of the nano-metal oxides in the catalyst is 10%-90%, and the mass fraction of the hierarchical zeolites in the catalyst is 10%-90%. The catalyst has excellent catalytic performance, good reaction stability and high selectivity for desired products, and in the hydrocarbons, C.sub.2.sup.=-C.sub.4.sup.= reach up to 80%, C.sub.5+ reach up to 80%, and aromatics reach up to 65%.