An aluminum-based plated steel sheet according to an aspect of the present invention includes: a base material; an aluminum-based plating layer located above the base material; and an intermetallic compound layer that is located between the base material and the aluminum-based plating layer and contains an intermetallic compound of Al and Fe, in which the base material has a chemical component within a predetermined range, the aluminum-based plating layer contains, on average, 80 mass % or more and 97 mass % or less of Al, 3 mass % or more and 15 mass % or less of Si, 0 mass % or more and 5 mass % or less of Zn, 0 mass % or more and 5 mass % or less of Fe, 0 mass % or more and 3 mass % or less in total of one or more selected from the group consisting of Mg and Ca, and impurities so that a total amount thereof is 100 mass %, an average value of a thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less, a maximum value of the thickness of the intermetallic compound layer is 10 μm or more and 25 μm or less, and a standard deviation of the thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less.

Disclosed herein are compositions, methods, and systems for resistance spot welding or brazing an aluminum member to a steel member using a chromium layer disposed between the aluminum member and the steel member.

A cold-rolled and heat-treated steel sheet having a microstructure consisting of, in surface fraction: between 10% and 30% of retained austenite, the retained austenite being present as films having an aspect ratio of at least 3 and as Martensite Austenite islands, less than 8% of the Martensite Austenite islands having a size above 0.5 μm, at most 1% of fresh martensite, at most 50% of tempered martensite, and recovered martensite containing precipitates of at least one element chosen among niobium, titanium and vanadium. A method for manufacturing the cold-rolled and heat-treated steel sheet is also described.

Provided is a highly corrosion-resistant plated steel sheet having plating adhesion and resistance to liquid metal embrittlement. A highly corrosion-resistant plated steel sheet comprises a base steel sheet and a plated layer, which sequentially comprises an Fe—Al alloy layer and an MgZn.sub.2 layer from an interface with the base steel sheet.

Method for joining of at least two unweldable materials, non-weldable directly to each other with thermal joining processes in a lap joint configuration, where a two step sequence is used consisting of a first step to apply a thermomechanical or mechanical surface protection layer on the surface of an unweldable material and a second step, where a thermal joining process is used to joint the sprayed layer with an applied layer sheet.

A press hardening method including the following steps: A. the provision of a steel sheet for heat treatment being optionally coated with a zinc- or aluminum-based pre-coating, B. the flexible rolling of the steel sheet in the rolling direction so as to obtain a steel sheet having a variable thickness, C. the cutting of the rolled steel sheet to obtain a tailored rolled blank, D. the deposition of a hydrogen barrier pre-coating over a thickness from 10 to 550 nm, E. the heat treatment of the tailored rolled blank to obtain a fully austenitic microstructure in the steel, F. the transfer of the tailored rolled blank into a press tool, G. the hot-forming of the tailored rolled blank to obtain a part having a variable thickness,H. the cooling of the part having a variable thickness obtained at step G).

The present invention provides a method for manufacturing more beautiful black coated steel sheets by uniformly blackening the coating layer. Specifically, the present invention provides a method for manufacturing black coated steel sheets, which brings Zn—Al—Mg alloy coated steel sheets (1) into contact with steam in a closed container (10), wherein said closed container (10) can maintain a predefined internal pressure through variable control of the amount of steam flowing into said closed container (10) and/or the amount of steam flowing out of said closed container (10), and in said closed container (10) that can maintain said predefined pressure, said Zn—Al—Mg alloy coated steel sheets (1) have contact with the steam introduced into said closed container (10).

A multi-material component joined by a high entropy alloy is provided, as well as methods of making a multi-material component by joining dissimilar materials with high entropy alloys.

The present invention relates to a surface treatment composition comprising, on the basis of 100 wt % of the solid part of the composition, 20-40 wt % of a water-soluble polyurethane resin, 40-60 wt % of a silane-based sol-gel resin in which three types of silane compounds are cross-linked, 5-15 wt % of a curing agent, 0.5-1.5 wt % of a corrosion inhibitor, 0.1-1.0 wt % of a molybdenum-based compound, 1.0-3.0 wt % of a silane coupling agent; 1.0-2.0 wt % of an organometallic complex, 1.0-2.0 wt % of an acid scavenger, 0.1-1.0 wt % of an aluminum-based compound, and 1.0-2.0 wt % of a lubricant. A ternary hot-dip galvannealed steel sheet treated with a chromium-free surface treatment coating agent, according to an exemplary embodiment in the present invention, has excellent resistance to blackening, alkali and corrosion, and provides excellent effects without concern for problems, in chromium treatment, of additional equipment installation, an increase in manufacturing costs and environmental pollution.

Embodiments of the present disclosure provides an aluminum alloy-plated steel sheet having high surface quality and weldability, a hot-formed member, and methods for manufacturing the aluminum alloy-plated steel sheet and the hot-formed member. The aluminum alloy-plated steel sheet includes: a base steel sheet; and an aluminum alloy plating layer formed on the base steel sheet, wherein the aluminum alloy plating layer includes, by weight %, Zn: 21% to 35%, Si: 1% to 6.9%, Fe: 2% to 12%, and the balance of Al and inevitable impurities.