The present disclosure is directed to a catalytic composite that comprises porous supported catalyst particles durably enmeshed in a porous fibrillated polymer membrane. The supported catalyst particles are composed of at least one metal or metal oxide catalyst dispersed on a porous support substrate. In some embodiments, the porous fibrillated polymer membrane is perforated or otherwise contains mechanically formed holes therein. The supported catalyst particles have a large particle population based, at least in part, a D90 value greater than 60 microns. The catalytic membrane composite may be used in filtration applications to remove air-polluting substances such as SOx, NOx, dioxin/furan, CO, and others and convert them into non-polluting or less-polluting gas components. Additionally, the catalytic article may be in the form of a filter bag, a honeycomb, a monolith or any other suitable geometrically structured forms.

A wall-flow honeycomb catalyst for dust removal and low-temperature denitrification of flue gas, and a preparation process thereof are provided. The catalyst is prepared from the following raw materials in parts by weight: calcined titanium dioxide: 30 to 60 parts; crude titanium dioxide: 30 to 50 parts; boehmite: 3 to 5 parts; fused silica powder: 2 to 4 parts; binder: 0.5 to 2 parts; lubricant: 0.5 to 2 parts; vanadium-molybdenum composite oxide: 5 to 10 parts; and water: 150 to 200 parts; and the vanadium-molybdenum composite oxide is obtained by dissolving ammonium metavanadate and ammonium molybdate in an oxalic acid solution and spray-drying a resulting solution. The preparation process of the catalyst of the present disclosure is simple and low in cost.

Proposed are a low-temperature de-NOx catalyst for treating exhaust gas from a stationary source and a method of manufacturing the same. The low-temperature de-NOx catalyst can promote the reduction reaction of nitrogen oxide even at a low temperature despite supporting vanadium in a small amount, can increase resistance to sulfur poisoning, and can be easily manufactured in a manner that does not deteriorate nitrogen oxide removal efficiency even after long-term operation because it prevents secondary environmental pollution due to the treated gas and has superior abrasion resistance, thereby contributing to commercialization.

Proposed are a low-temperature de-NOx catalyst for treating exhaust gas from a stationary source and a method of manufacturing the same. The low-temperature de-NOx catalyst can promote the reduction reaction of nitrogen oxide even at a low temperature despite supporting vanadium in a small amount, can increase resistance to sulfur poisoning, and can be easily manufactured in a manner that does not deteriorate nitrogen oxide removal efficiency even after long-term operation because it prevents secondary environmental pollution due to the treated gas and has superior abrasion resistance, thereby contributing to commercialization.

A plugged honeycomb structure includes a honeycomb structure body having a porous partition wall disposed to surround a plurality of cells; and a plugging portion disposed at one end of the cells, wherein, in a section orthogonal to the extending direction of the cell, the cells each have a shape that is polygon, and one of the inflow cells and another are adjacent to each other with the partition wall therebetween, and in the section orthogonal to the extending direction of the cell, a total area of the inflow cell is larger than a total area of the outflow cell, a porosity of the partition wall is 38% or more, a thickness of the partition wall is 125 μm or more and 280 μm or less, a cell density of the honeycomb structure body is 31.0 cells/cm.sup.2 or more, and an air-permeability resistance of the partition wall is 4.5×10.sup.7Pa.Math.s/m.sup.2 or less.

Proposed are a low-temperature DeNOx catalyst for selective catalytic reduction having improved sulfur resistance and a method of manufacturing the same. The low-temperature DeNOx catalyst for selective catalytic reduction having improved sulfur resistance accelerates the reduction reaction of nitrogen oxides even at low temperatures despite the small amount of vanadium supported, improves sulfur poisoning resistance, does not cause secondary environmental pollution by treated gas, has excellent abrasion resistance and strength and thus the removal efficiency of nitrogen oxides is not reduced even during long-term operation, and is easy to manufacture, thus contributing to commercialization.

Proposed are a low-temperature DeNOx catalyst for selective catalytic reduction having improved sulfur resistance and a method of manufacturing the same. The low-temperature DeNOx catalyst for selective catalytic reduction having improved sulfur resistance accelerates the reduction reaction of nitrogen oxides even at low temperatures despite the small amount of vanadium supported, improves sulfur poisoning resistance, does not cause secondary environmental pollution by treated gas, has excellent abrasion resistance and strength and thus the removal efficiency of nitrogen oxides is not reduced even during long-term operation, and is easy to manufacture, thus contributing to commercialization.

A hybrid photoactive heterojunction including a copper vanadate, Cu.sub.2V.sub.2O.sub.7 (CVO) and a zinc vanadate, Zn.sub.2V.sub.2O.sub.6 (ZVO). Particles of the ZVO are dispersed in particles of the CVO to form the hybrid photoactive heterojunction. The hybrid photoactive heterojunction in the form of a photoactive film includes a substrate which is at least partially coated with the hybrid photoactive heterojunction. A method of photodegrading a dye includes contacting the photoactive film and the dye in a solution and exposing the solution to light. A method of photoelectrochemically oxidizing water includes contacting the photoactive film with water in a solution and exposing the solution to light.

A hybrid photoactive heterojunction including a copper vanadate, Cu.sub.2V.sub.2O.sub.7 (CVO) and a zinc vanadate, Zn.sub.2V.sub.2O.sub.6 (ZVO). Particles of the ZVO are dispersed in particles of the CVO to form the hybrid photoactive heterojunction. The hybrid photoactive heterojunction in the form of a photoactive film includes a substrate which is at least partially coated with the hybrid photoactive heterojunction. A method of photodegrading a dye includes contacting the photoactive film and the dye in a solution and exposing the solution to light. A method of photoelectrochemically oxidizing water includes contacting the photoactive film with water in a solution and exposing the solution to light.

Provided is a catalyst which, when used in a selective catalytic reduction reaction in which ammonia serves as the reducing agent, further improves denitration efficiency at low temperatures compared to the prior art.

The denitration catalyst comprises vanadium oxide as a main component, and has a content of a second metal, in teams of oxide, of 1-40 wt %. The second metal is at least one type of metal element selected from the group consisting of Co, W, Mo, Nb, Ce, Sn, Ni, Fe, Cu, Zn, and Mn.