Process for the preparation of a catalyst and a catalyst comprising the use of more than one silica source is provided herein. Thus, in one embodiment, the invention provides a particulate FCC catalyst comprising about 5 to about 60 wt % one or more zeolites, about 15 to about 35 wt % quasicrystalline boehmite (QCB), about 0 to about 35 wt % microcrystalline boehmite (MCB), greater than about 0 to about 15 wt % silica from sodium stabilized basic colloidal silica, greater than about 0 to about 30 wt % silica from acidic colloidal silica or polysilicic acid, and the balance clay and the process for making the same. This process results in attrition resistant catalysts with a good accessibility.

Process for the preparation of a catalyst and a catalyst comprising the use of more than one silica source is provided herein. Thus, in one embodiment, the invention provides a particulate FCC catalyst comprising about 5 to about 60 wt % one or more zeolites, about 15 to about 35 wt % quasicrystalline boehmite (QCB), about 0 to about 35 wt % microcrystalline boehmite (MCB), greater than about 0 to about 15 wt % silica from sodium stabilized basic colloidal silica, greater than about 0 to about 30 wt % silica from acidic colloidal silica or polysilicic acid, and the balance clay and the process for making the same. This process results in attrition resistant catalysts with a good accessibility.

Provided is a method for preparing a zeolite having a Si/Al ratio of at least 10 by interzeolite transformation in the absence of an organic structure directing agent. The method is more cost effective and less equipment intensive as it eliminates the costly organic structure directing agent and the waste treatment at the plant.

Disclosed are a catalyst system and its use in a process for the conversion of a feedstock containing C.sub.8+ aromatic hydrocarbons to produce light aromatic products, comprising benzene, toluene and xylene. The catalyst system comprises (a) a first catalyst bed comprising a first catalyst composition, said first catalyst composition comprising a zeolite having a constraint index of 3 to 12 combined (i) optionally with at least one first metal of Group 10 of the IUPAC Periodic Table, and (ii) optionally with at least one second metal of Group 11 to 15 of the IUPAC Periodic Table; and (b) a second catalyst bed comprising a second catalyst composition, said second catalyst composition comprising (i) a meso-mordenite zeolite, combined (ii) optionally with at least one first metal of Group 10 of the IUPAC Periodic Table, and (iii) optionally with at least one second metal of Group 11 to 15 of the IUPAC Periodic Table, wherein said meso-mordenite zeolite is synthesized from TEA or MTEA and having a mesopore surface area of greater than 30 m.sup.2/g and said meso-mordenite zeolite comprises agglomerates composed of primary crystallites, wherein said primary crystallites have an average primary crystal size as measured by TEM of less than 80 nm and an aspect ratio of less than 2.

Disclosed are a catalyst system and its use in a process for the conversion of a feedstock containing C.sub.8+ aromatic hydrocarbons to produce light aromatic products, comprising benzene, toluene and xylene. The catalyst system comprises (a) a first catalyst bed comprising a first catalyst composition, said first catalyst composition comprising a zeolite having a constraint index of 3 to 12 combined (i) optionally with at least one first metal of Group 10 of the IUPAC Periodic Table, and (ii) optionally with at least one second metal of Group 11 to 15 of the IUPAC Periodic Table; and (b) a second catalyst bed comprising a second catalyst composition, said second catalyst composition comprising (i) a meso-mordenite zeolite, combined (ii) optionally with at least one first metal of Group 10 of the IUPAC Periodic Table, and (iii) optionally with at least one second metal of Group 11 to 15 of the IUPAC Periodic Table, wherein said meso-mordenite zeolite is synthesized from TEA or MTEA and having a mesopore surface area of greater than 30 m.sup.2/g and said meso-mordenite zeolite comprises agglomerates composed of primary crystallites, wherein said primary crystallites have an average primary crystal size as measured by TEM of less than 80 nm and an aspect ratio of less than 2.

A process for reducing haze in a heavy base oil includes: obtaining a first effluent oil by contacting a hydrocarbon feedstock with a first catalyst including a zeolite of the ZSM-12 family; and obtaining a second effluent oil by contacting the first effluent oil with a second catalyst including a zeolite of the ZSM-48 family. A hydroisomerization catalyst system having reduced haze includes: a first catalytic region having a first catalyst disposed therein, the first catalyst including a zeolite of the ZSM-12 family; and a second catalytic region having a second catalyst disposed therein, the second catalyst including a zeolite of the ZSM-48 family. The first catalytic region is disposed upstream of the second catalytic region.

A catalytic converter includes a hydrocarbon catalyst trap including BEA zeolite configured to adsorb iso-octane at ambient temperatures and desorb iso-octane at temperatures between 150° C. and 170° C., and active metal supercage impregnated USY zeolite configured to adsorb and coke iso-octane at temperatures greater than 150° C.

A catalytic converter includes a hydrocarbon catalyst trap including BEA zeolite configured to adsorb iso-octane at ambient temperatures and desorb iso-octane at temperatures between 150° C. and 170° C., and active metal supercage impregnated USY zeolite configured to adsorb and coke iso-octane at temperatures greater than 150° C.

A catalyst article having an extruded support having a plurality of channels through which exhaust gas flows during operation of an engine, and a single layer coating or a bi-layer coating on the support, where the extruded support contains a third SCR catalyst, the single layer coating and the bilayer-coating contain platinum on a support with low ammonia storage and a first SCR catalyst. The catalytic articles are useful for selective catalytic reduction (SCR) of NOx in exhaust gases and in reducing the amount of ammonia slip. Methods for producing such articles are described. Methods of using the catalytic articles in an SCR process, where the amount of ammonia slip is reduced, are also described.

A catalyst article having an extruded support having a plurality of channels through which exhaust gas flows during operation of an engine, and a single layer coating or a bi-layer coating on the support, where the extruded support contains a third SCR catalyst, the single layer coating and the bilayer-coating contain platinum on a support with low ammonia storage and a first SCR catalyst. The catalytic articles are useful for selective catalytic reduction (SCR) of NOx in exhaust gases and in reducing the amount of ammonia slip. Methods for producing such articles are described. Methods of using the catalytic articles in an SCR process, where the amount of ammonia slip is reduced, are also described.