A process for preparing C.sub.2 to C.sub.3 hydrocarbons may include introducing a feed stream including hydrogen gas and a carbon-containing gas comprising carbon monoxide, carbon dioxide, and mixtures thereof into a reaction zone of a reactor, and converting the feed stream into a product stream comprising C.sub.2 to C.sub.3 hydrocarbons in the reaction zone in the presence of a hybrid catalyst. The hybrid catalyst may include a metal oxide catalyst component and a microporous catalyst component comprising 8-MR pore openings and may be derived from a natural mineral, the product stream comprises a combined C.sub.2 and C.sub.3 selectivity greater than 40 carbon mol%.

A process for preparing C.sub.2 to C.sub.5 paraffins includes introducing a feed stream comprising hydrogen gas and a carbon-containing gas into a reaction zone of a reactor, and converting the feed stream into a product stream comprising C.sub.2 to C.sub.5 paraffins in the reaction zone in the presence of a hybrid catalyst. The hybrid catalyst includes a metal oxide catalyst component and a microporous catalyst component. The metal oxide catalyst component satisfies: an atomic ratio of Cu/Zn from 0.01 to 3.00; an atomic ratio of Cr/Zn from 0.01 to 1.50; and percentage of (Al+Cr) from greater than 0.0 at % to 50.0 at % based on a total amount of metal in the metal oxide catalyst component.

The present disclosure recognizes a correlation between zeolitic surface area (ZSA) of a catalyst composition and its catalytic activity. Particularly, the disclosure provides catalyst articles for diesel NO.sub.x abatement, including a substrate and a washcoat layer containing metal-promoted molecular sieves, wherein the zeolitic surface area (ZSA) of the catalyst article is about 100 m.sup.2/g or greater, the volumetric surface area is about 900 m.sup.2/in.sup.3 or greater, and/or the total zeolitic surface area (tZSA) is about 1200 m.sup.2 or greater. The disclosure further relates to methods for evaluating ZSA, volumetric ZSA, and tZSA, e.g., including the steps of coating a catalyst composition comprising metal-promoted molecular sieves onto a substrate; calcining and aging the catalyst composition; determining the ZSA (or volumetric ZSA or tZSA) thereof; and correlating the ZSA (or volumetric ZSA or tZSA) with catalyst composition NO.sub.x abatement activity to determine whether the catalyst composition is suitable for an intended use.

Disclosed are a catalyst for preparing hydrocarbons from carbon dioxide by one-step hydrogenation and a method for preparing same. The catalyst includes nano-metal oxides and hierarchical zeolites, where the mass fraction of the nano-metal oxides in the catalyst is 10%-90%, and the mass fraction of the hierarchical zeolites in the catalyst is 10%-90%. The catalyst has excellent catalytic performance, good reaction stability and high selectivity for desired products, and in the hydrocarbons, C.sub.2.sup.=-C.sub.4.sup.= reach up to 80%, C.sub.5+ reach up to 80%, and aromatics reach up to 65%.

Molecular sieves comprising intergrowths of cha and aft having an “sfw-GME tail”, at least one structure directing agent (SDA) within the framework of the molecular sieve, an intergrowth of CHA and GME framework structures, cha cavities, and aft cavities are described. A first SDA comprising either an N,N-dimethyl-3,5-dimethylpiperidinium cation or a N,N-diethyl-2,6-dimethylpiperidinium cation is required. A second SDA, which can further be present, is a CHA or an SFW generating cation. The amount of the second SDA-2 used can change the proportion of the components in the cha-aft-“sfw-GME tail”. Activated molecular sieves formed from SDA containing molecular sieves are also described. Compositions for preparing these molecular sieves are described. Methods of preparing a SDA containing JMZ-11, an activated JMZ-11, and metal containing activated JMZ-11 are described. Methods of using activated JMZ-11 and metal containing activated JMZ-11 in a variety of processes, such as treating exhaust gases and converting methanol to olefins are described.

A catalyst includes a zeolite, wherein the zeolite has: a CHA framework; a particle size less than or equal to 100 nanometers; and a silica to alumina mole ratio in the range of about 50:1 to about 150:1. The catalyst can include a metal dopant. The catalyst can be used for purifying a product by flowing a reactant across the catalyst to form the product; and condensing or separating the product. The product can be an olefin or alkenes with an increased carbon chain. The catalyst can be used for selective catalytic reduction of nitrogen oxide or a gas to liquid reaction. A method of producing the catalyst can include selecting the concentration of a crystal growth inhibitor based on the ratio of the silica precursor and an alumina precursor such that the zeolite crystals have a mean particle size less than or equal to 100 nanometers.

The present invention relates to a method for producing automobile exhaust gas catalytic converters, to the catalytic converters as such and to the use thereof. In particular, the method comprises a step which results, independently of the actual drying process, in the catalytically active material used being dried. The invention is especially used in the coating of wall-flow filters.

The present invention is directed to methods of producing THC from CBD utilizing non-harsh methodology and resulting in substantially increased yields, as well as devices built upon these novel methods. The methods and devices are material efficient, and in certain embodiments, solvent-free. In particular, in certain embodiments, these methods and related devices are suitable for commercial production of THC from CBD. Furthermore, in certain embodiments, the present invention provides methods of producing THC from CBD in manner that affords tunability to select the ratio of THC-8 to THC-9.

A method for producing a cluster-supporting catalyst, the cluster-supporting catalyst including porous carrier particles that has acid sites, and catalyst metal clusters supported within the pores of the porous carrier particles, includes the following steps: providing a dispersion liquid containing a dispersion medium and the porous carrier particles dispersed in the dispersion medium; and in the dispersion liquid, forming catalyst metal clusters having a positive charge, and supporting the catalyst metal clusters on the acid sites within the pores of the porous carrier particles through an electrostatic interaction.

An oxidation catalyst for treating an exhaust gas from a diesel engine comprises: a first washcoat region for oxidising carbon monoxide (CO) and hydrocarbons (HCs), wherein the first washcoat region comprises a first platinum group metal (PGM) and a first support material, and wherein the first washcoat region does not comprise manganese or an oxide thereof; a second washcoat region for oxidising nitric oxide (NO), wherein the second washcoat region comprises platinum (Pt), manganese (Mn) and a second support material comprising a refractory metal oxide, which is silica-alumina or alumina doped with silica in a total amount of 0.5 to 45% by weight of the alumina, wherein the platinum (Pt) is disposed or supported on the second support material and the manganese (Mn) is disposed or supported on the second support material; and a substrate having an inlet end and an outlet end, and wherein the first washcoat region is a first washcoat layer and the second washcoat region is a second washcoat layer, and the second washcoat layer is disposed on the first washcoat layer; and wherein when the oxidation catalyst comprises a hydrocarbon adsorbent, which is a zeolite, then the first washcoat region further comprises the hydrocarbon adsorbent.