Implementations of the disclosure are directed to a lead-free mixed solder powder paste suitable for low temperature to middle temperature soldering applications. The lead-free solder paste may consist of: an amount of a first solder alloy powder between 44 wt % and 83 wt %, the first solder alloy powder comprising Sn; an amount of a second solder alloy powder between 5 wt % to 44 wt %, the second alloy powder comprising Sn, where the first solder alloy powder has a liquidus temperature lower than a solidus temperature of the second solder alloy powder; and a remainder of flux. The solder paste may be used for reflow at a peak temperature below the solidus temperature of the higher solidus temperature solder powder but above the melting temperature of the lower solidus temperature one.

Undercooled liquid metallic core-shell particles, whose core is stable against solidification at ambient conditions, i.e. under near ambient temperature and pressure conditions, are used to join or repair metallic non-particulate components. The undercooled-shell particles in the form of nano-size or micro-size particles comprise an undercooled stable liquid metallic core encapsulated inside an outer shell, which can comprise an oxide or other stabilizer shell typically formed in-situ on the undercooled liquid metallic core. The shell is ruptured to release the liquid phase core material to join or repair a component(s).

Invention compositions are a replacement for high melting temperature solder pastes and preforms in high operating temperature and step-soldering applications. In the use of the invention, a mixture of metallic powders reacts below 350 degrees C. to form a dense metallic joint that does not remelt at the original process temperature.

Undercooled liquid metallic core-shell particles, whose core is stable against solidification at ambient conditions, i.e. under near ambient temperature and pressure conditions, are used to join or repair metallic non-particulate components. The undercooled-shell particles in the form of nano-size or micro-size particles comprise an undercooled stable liquid metallic core encapsulated inside an outer shell, which can comprise an oxide or other stabilizer shell typically formed in-situ on the undercooled liquid metallic core. The shell is ruptured to release the liquid phase core material to join or repair a component(s).

A core material has a core 12; a solder layer 16 made of a (Sn—Bi)-based solder alloy provided on an outer side of the core 12; and a Sn layer 20 provided on an outer side of the solder layer 16. The core contains metal or a resin. When a concentration ratio of Bi contained in the solder layer 16 is a concentration ratio (%)=a measured value of Bi (% by mass)/a target Bi content (% by mass), or a concentration ratio (%)=an average value of measured values of Bi (% by mass)/a target Bi content (% by mass), the concentration ratio is 91.4% to 106.7%. The thickness of the Sn layer 20 is 0.215% or more and 36% or less of the thickness of the solder layer 16.

Undercooled liquid metallic core-shell particles, whose core is stable against solidification at ambient conditions, i.e. under near ambient temperature and pressure conditions, are used to join or repair metallic non-particulate components. The undercooled-shell particles in the form of nano-size or micro-size particles comprise an undercooled stable liquid metallic core encapsulated inside an outer shell, which can comprise an oxide or other stabilizer shell typically formed in-situ on the undercooled liquid metallic core. The shell is ruptured to release the liquid phase core material to join or repair a component(s).

An object of the present invention is to provide an Sn—Bi—Cu—Ni solder alloy or the like which has a low melting point, excellent ductility, and high tensile strength, and in which if soldering is performed on a Cu electrode subjected to electroless Ni plating treatment, a solder joint formed through this soldering exhibits high shear strength. In addition, another object of the present invention is to provide an Sn—Bi—Cu—Ni solder alloy in which a solder joint formed through soldering exhibits high shear strength even for a Cu electrode which has not been subjected to plating treatment. Furthermore, still another object of the present invention is to provide, in addition to the above-described objects, a solder alloy or the like of which yellowish discoloration can be suppressed and in which change in viscosity of a solder paste over time can be suppressed. The solder alloy has an alloy composition consisting of, by mass %, 31% to 59% of Bi, 0.3% to 1.0% of Cu, 0.01% to 0.06% of Ni, 0.0040% to 0.025% of As, and a balance of Sn.

Implementations of the disclosure are directed to a lead-free mixed solder powder paste suitable for low temperature to middle temperature soldering applications. The lead-free solder paste may consist of: an amount of a first solder alloy powder between 44 wt % and 83 wt %, the first solder alloy powder comprising Sn; an amount of a second solder alloy powder between 5 wt % to 44 wt %, the second alloy powder comprising Sn, where the first solder alloy powder has a liquidus temperature lower than a solidus temperature of the second solder alloy powder; and a remainder of flux. The solder paste may be used for reflow at a peak temperature below the solidus temperature of the higher solidus temperature solder powder but above the melting temperature of the lower solidus temperature one.

A piston for an internal combustion engine may include a piston crown having a closed circumferential cooling channel, a piston skirt, a first metallic coolant arranged in the cooling channel and having a metal or metal alloy with a melting point below 250° C., and a second nonmetallic coolant arranged in the cooling channel and having a melting point below 40° C. and a density which is lower than a density of the first coolant.

A solder alloy comprising: from 40 to 65 wt. % bismuth; from I to IO wt. % indium; at least one of: from 0.1 to 5 wt. % gallium, from 0.1 to 5 wt. % zinc, from 0.1 to 2 wt. % copper, from 0.01 to 0.1 wt. % cobalt, from 0.1 to 2 wt. % silver, from 0.005 to 0.05 wt. % titanium, and from 0.01 to 1 wt. % nickel; optionally up to 1 wt. % of one or more of: vanadium, rare earth metals, neodymium, chromium, iron, aluminium, phosphorus, gold, tellurium, selenium, calcium, vanadium, molybdenum, platinum, magnesium, silicon, and manganese; and the balance tin together with any unavoidable impurities.