A steel sheet for the manufacture of a press hardened part is provided, having a composition of: 0.15%≤C≤0.22%, 3.5%≤Mn<4.2%, 0.001%≤Si≤1.5%, 0.020%≤Al≤0.9%, 0.001%≤Cr≤1%, 0.001%≤Mo≤0.3%, 0.001%≤Ti≤0.040%, 0.0003%≤B≤0.004%, 0.001%≤Nb≤0.060%, 0.001%≤N≤0.009%, 0.0005%≤S≤0.003%, 0.001%≤P≤0.020%. A microstructure has less than 50% ferrite, 1% to 20% retained austenite, cementite, such that the surface density of cementite particles larger than 60 nm is lower than 10{circumflex over ( )}7/mm.sup.2, and a complement of bainite and/or martensite, the retained austenite having an average Mn content of at least 1.1*Mn %. Press-hardened steel part obtained by hot forming the steel sheet, and manufacturing methods thereof.

A steel sheet for the manufacture of a press hardened part is provided, having a composition of: 0.15%≤C≤0.22%, 3.5%≤Mn<4.2%, 0.001%≤Si≤1.5%, 0.020%≤Al≤0.9%, 0.001%≤Cr≤1%, 0.001%≤Mo≤0.3%, 0.001%≤Ti≤0.040%, 0.0003%≤B≤0.004%, 0.001%≤Nb≤0.060%, 0.001%≤N≤0.009%, 0.0005%≤S≤0.003%, 0.001%≤P≤0.020%. A microstructure has less than 50% ferrite, 1% to 20% retained austenite, cementite, such that the surface density of cementite particles larger than 60 nm is lower than 10{circumflex over ( )}7/mm.sup.2, and a complement of bainite and/or martensite, the retained austenite having an average Mn content of at least 1.1*Mn %. Press-hardened steel part obtained by hot forming the steel sheet, and manufacturing methods thereof.

The present disclosure relates generally to welding alloys and, more specifically, to welding consumables (e.g., welding wires and rods) for arc welding operations. In an embodiment, a welding consumable includes less than approximately 1 wt % manganese as well as one or more strengthening agents selected from the group: nickel, cobalt, copper, carbon, molybdenum, chromium, vanadium, silicon, and boron. The welding consumable also includes one or more grain control agents selected from the group: niobium, tantalum, titanium, zirconium, and boron, wherein the welding consumable includes less than approximately 0.6 wt % grain control agents. Additionally, the welding consumable has a carbon equivalence (CE) value that is less than approximately 0.23. The welding consumable is designed to provide a manganese fume generation rate that is less than approximately 0.01 grams per minute during a welding operation.

One aspect of the disclosure provides an iron-based hardfacing layer which includes hard or wear resistant phases resulting at least in part from dissolution of silicon and/or boron carbide particles into a liquid iron-based metal during the fabrication process. In an embodiment, the hardfacing layer is formed by a fusion welding process in which carbide particles are added to the molten weld pool. In an example, the filler metal supplied to the welding process is a mild steel. In an embodiment, the hardness as measured at the surface of the hardfacing ranges from 40 to 65 HRC. In an example, the iron-based hardfacing layer also includes tungsten carbide particles.

The present invention concerns a new metal powder which is useful for coating cast iron parts. The invention also relates to a method for coating cast iron parts by using the new metal powder. Of special importance is the possibility to use the metal powder for coating the surfaces of glass moulds. The invention also relates to metal parts, such as cast iron parts, or glass moulds which are coated by the metal powder.

A flux-cored wire for are welding of a duplex stainless steel includes a stainless-steel sheath filled with a flux and contains, with respect to the total mass of the wire, predetermined amounts of Cr, Ni, Mo, N, Mn, and Si, in which letting a Ti alloy content in terms of Ti be [Ti] and letting an Al alloy content in terms of Al be [Al], [Ti] and [Al] are predetermined values, and in which parameter A expressed as A=[Ti]+2×[Al] satisfies a predetermined value, and the balance is composed of Fe, a slag-forming component, and incidental impurities.

Disclosed are non-magnetic metal alloy compositions and applications that relate to non-magnetic metal alloys with excellent wear properties for use in dynamic three-body tribological wear environments where an absence of magnetic interference is required. In one aspect, the disclosure can relate to a drilling component for use in directional drilling applications capable of withstanding service abrasion. In a second aspect, a hardbanding for protecting a drilling component for use in directional drilling can be provided. In a third aspect, a method for prolonging service life of a drilling component for use in directional drilling can be provided.

Embodiments of the present invention relate to an inner casing component configured to form part of a steam flow path of a last stage of an axial flow steam turbine, the steam turbine inner casing component having a base made of nodular cast iron and a coating, on the base, in a region exposed to the steam flow path, consisting of manganese austenitic steel.

Various embodiments of a metal cored wires, hardband alloys, and methods are disclosed. In one embodiment of the present invention, a hardbanding wire comprises from about from about 16% to about 30% by weight chromium; from about 4% to about 10% by weight nickel; from about 0.05% to about 0.8% by weight nitrogen; from about 1% to about 4% by weight manganese; from about 1% to about 4% by weight carbon from about 0.5% to about 5% by weight molybdenum; from about 0.25% to about 2% by weight silicon; and the remainder is iron including trace elements. The hardband alloy produced by the metal cored wire meets API magnetic permeability specifications and has improved metal to metal, adhesive wear resistance compared to conventional hardband alloys.

Various embodiments of a metal cored wires and methods are disclosed. In one embodiment of the present invention, a metal cored wire comprises a metal sheath and a metal-powder core material comprising manganese particles. The manganese particles are coated with a coating material to reduce the manganese fumes and exposure during welding.