A flame retardant with which fire retardancy is improved and the fire retardancy is able to be secured stably for a long time is provided. An internal layer 11 containing a polymer and a flame retardant factor layer 12 that is formed outside of the internal layer 11 and that contains a polymer to which at least one of a sulfonate group and a sulfonate base is bonded are included. Thereby, compared to a case that the flame retardant factor layer 12 is not included, moisture is hardly absorbed, and respective particles of the flame retardant are inhibited from being adhered to each other. Accordingly, blocking is inhibited.

A flame retardant with which fire retardancy is improved and the fire retardancy is able to be secured stably for a long time is provided. An internal layer 11 containing a polymer and a flame retardant factor layer 12 that is formed outside of the internal layer 11 and that contains a polymer to which at least one of a sulfonate group and a sulfonate base is bonded are included. Thereby, compared to a case that the flame retardant factor layer 12 is not included, moisture is hardly absorbed, and respective particles of the flame retardant are inhibited from being adhered to each other. Accordingly, blocking is inhibited.

Provided is a cell culture scaffold material having excellent cell adhesion. The cell culture scaffold material according to the present invention contains a peptide-conjugated polyvinyl alcohol derivative having a polyvinyl alcohol derivative portion and a peptide portion, and the peptide portion has a cyclic peptide skeleton.

Provided is a cell culture scaffold material having excellent cell adhesion. The cell culture scaffold material according to the present invention contains a peptide-conjugated polyvinyl alcohol derivative having a polyvinyl alcohol derivative portion and a peptide portion, and the peptide portion has a cyclic peptide skeleton.

Provided are a heat-resistant synthetic resin microporous film that has both good heat resistance and good mechanical strength and exhibits a suppressed decrease in mechanical strength over time, and a method for producing the heat-resistant synthetic resin microporous film. The heat-resistant synthetic resin microporous film of the present invention includes a synthetic resin microporous film, and a coating layer formed on at least part of the surface of the synthetic resin microporous film and containing a polymer of a polymerizable compound having two or more radically polymerizable functional groups per molecule. The maximum thermal shrinkage rate of the heat-resistant synthetic resin microporous film when heated from 25° C. to 180° C. at a temperature rising rate of 5° C./min is 15% or less. The piercing strength thereof is 0.6 N or more. The rate of retention of the piercing strength after heating at 70° C. for 168 hours is 85% or more.

The present invention relates to a decorative material having excellent printability, and the decorative material according to the present invention has an ink-receiving layer having a radially fine sloping structure having a dendritic shape, whereby the absorbing and/or fixing property, i.e., printability, of the ink printed on the ink-receiving layer is improved, and clarity is excellent, so that aesthetic effects are excellent. In addition, since the ink-receiving layer is manufactured through UV curing, it can be directly coated on a substrate layer, and can include various kinds of substrate layers; and since it is manufactured using a solvent-free type resin composition without using an organic solvent, and has an excellent absorbing and/or fixing property with respect to a water soluble ink, it has environmental friendly advantages.

The present invention provides an optical member comprising a silicone material having excellent antifouling property while having good light transmittance, heat resistance, and strength, and an optical semiconductor device and illumination apparatus having excellent antifouling property. The present invention is an optical member comprising a silicone material containing a fluorinated surface, the proportion of F atoms being from 0.1 to 45 at % and/or the ratio of F atoms relative to C atoms being from 0.01 to 1.00 in the atomic composition percentage according to X-ray photoelectron spectroscopy (XPS) of the fluorinated surface.

A method is used to provide an electrically-conductive polyaniline pattern by providing a uniform layer of a photocurable composition on a substrate. The photocurable composition comprises a water-soluble reactive polymer comprising (a) greater than 40 mol % of recurring units comprising sulfonic acid or sulfonate groups, and (b) at least 5 mol % of recurring units comprising a pendant group capable of crosslinking via [2+2] photocycloaddition. The photocurable composition is exposed to cause crosslinking via [2+2] photocycloaddition of the (b) recurring units, thereby forming a crosslinked polymer. Any remaining water-soluble reactive polymer is removed. The crosslinked polymer is contacted with an aniline reactive composition having aniline monomer and up to 0.5 molar of an aniline oxidizing agent, thereby forming an electrically-conductive polyaniline disposed either within, on top of, or both within and on top of, the crosslinked polymer.

A polymer formed of at least one phenylphosphine oxide functional epoxide crosslinked with at least one phenylphosphine oxide amine such that the polymer has phosphorous concentrations of at least about 8 percent by weight, at least about 8.5 percent by weight, or any value or range of values therebetween.

A polymer formed of at least one phenylphosphine oxide functional epoxide crosslinked with at least one phenylphosphine oxide amine such that the polymer has phosphorous concentrations of at least about 8 percent by weight, at least about 8.5 percent by weight, or any value or range of values therebetween.